CN103468137B - A kind of antimicrobial form asphalt waterproofing paint - Google Patents
A kind of antimicrobial form asphalt waterproofing paint Download PDFInfo
- Publication number
- CN103468137B CN103468137B CN201310359233.6A CN201310359233A CN103468137B CN 103468137 B CN103468137 B CN 103468137B CN 201310359233 A CN201310359233 A CN 201310359233A CN 103468137 B CN103468137 B CN 103468137B
- Authority
- CN
- China
- Prior art keywords
- coalescence aid
- film coalescence
- powder
- asphalt waterproofing
- antimicrobial form
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of antimicrobial form asphalt waterproofing paint, it is made up of the raw material of following weight parts: pitch 63-70, acrylate and vinyl acetate emulsion 6-7, polyacrylamide 2-3, Sodium Silicofluoride 1-2, polypropylene glycerol aether 1-2, aminopropyltriethoxywerene werene 1-2, aluminium hydrate powder 1-2, swelling perlite powder 12-20, fluorite powder 10-20, methylisothiazolinone 2-3, film coalescence aid 2-4, water are appropriate, coating and the base face cohesiveness of the present invention are strong, good water-proof effect, weathering resistance, acid-alkali-corrosive-resisting, resistant of high or low temperature, contamination resistance, germ resistance are strong.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of antimicrobial form asphalt waterproofing paint.
Background technology
Emulsified bitumen coating has certain water-repellancy and preservative property, due to the restriction of the performance of pitch own, the work-ing life of Emulsificated asphalt water-proof painting material is short, the poor-performing such as low temperature flexibility and thermotolerance, being applicable to classification of waterproof is waterproof layer and underground is moistureproof, the construction of corrosion protection coating between the industry of III, IV grade and covil construction roofing, lavatory are bathed, and is cheap low-grade waterproof paint, therefore, improve the over-all properties of Emulsificated asphalt water-proof painting material, so that it is necessary for expanding usage range.
Summary of the invention
The object of the invention is just to provide a kind of antimicrobial form asphalt waterproofing paint.
The present invention is achieved by the following technical solutions:
A kind of antimicrobial form asphalt waterproofing paint, it is made up of the raw material of following weight parts:
Pitch 63-70, acrylate and vinyl acetate emulsion 6-7, polyacrylamide 2-3, Sodium Silicofluoride 1-2, polypropylene glycerol aether 1-2, aminopropyltriethoxywerene werene 1-2, aluminium hydrate powder 1-2, swelling perlite powder 12-20, fluorite powder 10-20, methylisothiazolinone 2-3, film coalescence aid 2-4, water are appropriate;
Described film coalescence aid is made up of the raw material of following weight parts:
EVA emulsion 40-50, polyvinyl acetate emulsion 5-6, vinyltriethoxysilane 4-5, dipropylene glycol butyl ether 1-2, cetomacrogol 1000 2-3, aluminium hydroxide 2-4, tin-antiomony oxide 0.1-0.2;
Above-mentioned cetomacrogol 1000 is mixed with aluminium hydroxide, stirring reaction 10-15 minute at 50-60 DEG C, tin-antiomony oxide is added after being cooled to normal temperature, obtain Preblend, EVA emulsion is mixed with polyvinyl acetate emulsion, stir after evenly and add vinyltriethoxysilane, 400-500 rev/min dispersed with stirring 2-4 minute, adding above-mentioned Preblend and each raw material of residue, 100-120 DEG C of insulation leaves standstill 1-2 hour, obtains described film coalescence aid.
A preparation method for antimicrobial form asphalt waterproofing paint, comprises the following steps:
Above-mentioned pitch is heated to 140-150 DEG C, adds polyacrylamide, Sodium Silicofluoride, methylisothiazolinone, obtain Preblend; Swelling perlite powder, fluorite powder are mixed with aminopropyltriethoxywerene werene, 500-600 rev/min dispersed with stirring 4-5 minute, join in above-mentioned Preblend after discharging, by colloidal mill grinding evenly, add each raw material except film coalescence aid, fully it is uniformly mixed at 90-100 DEG C, it is cooled to normal temperature, add film coalescence aid, fully stir, obtain described antimicrobial form asphalt waterproofing paint.
It is an advantage of the invention that:
The coating of the present invention and base face cohesiveness are strong, and good water-proof effect, weathering resistance, acid-alkali-corrosive-resisting, resistant of high or low temperature, contamination resistance, germ resistance are strong.
Embodiment
Embodiment 1
A kind of antimicrobial form asphalt waterproofing paint, it is made up of the raw material of following weight parts (kilogram):
Pitch 70, acrylate and vinyl acetate emulsion 6, polyacrylamide 3, Sodium Silicofluoride 2, polypropylene glycerol aether 1, aminopropyltriethoxywerene werene 1, aluminium hydrate powder 2, swelling perlite powder 20, fluorite powder 10, methylisothiazolinone 2, film coalescence aid 4, water are appropriate;
Described film coalescence aid is made up of the raw material of following weight parts:
EVA emulsion 50, polyvinyl acetate emulsion 6, vinyltriethoxysilane 5, dipropylene glycol butyl ether 2, cetomacrogol 1000 3, aluminium hydroxide 2, tin-antiomony oxide 0.2;
Above-mentioned cetomacrogol 1000 is mixed with aluminium hydroxide, stirring reaction 15 minutes at 60 DEG C, tin-antiomony oxide is added after being cooled to normal temperature, obtain Preblend, EVA emulsion is mixed with polyvinyl acetate emulsion, stir after evenly and add vinyltriethoxysilane, 500 revs/min of dispersed with stirring 2 minutes, adding above-mentioned Preblend and each raw material of residue, 120 DEG C of insulations leave standstill 1 hour, obtain described film coalescence aid.
A preparation method for antimicrobial form asphalt waterproofing paint, comprises the following steps:
Above-mentioned pitch is heated to 150 DEG C, adds polyacrylamide, Sodium Silicofluoride, methylisothiazolinone, obtain Preblend; Swelling perlite powder, fluorite powder are mixed with aminopropyltriethoxywerene werene, 600 revs/min of dispersed with stirring 4 minutes, join in above-mentioned Preblend after discharging, by colloidal mill grinding evenly, add each raw material except film coalescence aid, fully it is uniformly mixed at 100 DEG C, it is cooled to normal temperature, add film coalescence aid, fully stir, obtain described antimicrobial form asphalt waterproofing paint.
Performance test:
Acid resistance: with the H of 5%2SO4Solution soaking 25 days film coated surface are unchanged;
Alkali resistance: soak 25 days film coated surface by the NaOH solution of 5% unchanged;
Watertightness (0.3MPa, 40min): waterproof.
Claims (2)
1. an antimicrobial form asphalt waterproofing paint, it is characterised in that it is made up of the raw material of following weight parts: pitch 63-70, acrylate and vinyl acetate emulsion 6-7, polyacrylamide 2-3, Sodium Silicofluoride 1-2, polypropylene glycerol aether 1-2, aminopropyltriethoxywerene werene 1-2, aluminium hydrate powder 1-2, swelling perlite powder 12-20, fluorite powder 10-20, methylisothiazolinone 2-3, film coalescence aid 2-4, water are appropriate;
Described film coalescence aid is made up of the raw material of following weight parts: EVA emulsion 40-50, polyvinyl acetate emulsion 5-6, vinyltriethoxysilane 4-5, dipropylene glycol butyl ether 1-2, cetomacrogol 1000 2-3, aluminium hydroxide 2-4, tin-antiomony oxide 0.1-0.2; Above-mentioned cetomacrogol 1000 is mixed with aluminium hydroxide, stirring reaction 10-15 minute at 50-60 DEG C, tin-antiomony oxide is added after being cooled to normal temperature, obtain Preblend, EVA emulsion is mixed with polyvinyl acetate emulsion, stir after evenly and add vinyltriethoxysilane, 400-500 rev/min dispersed with stirring 2-4 minute, adding above-mentioned Preblend and surplus stock dipropylene glycol butyl ether, 100-120 DEG C of insulation leaves standstill 1-2 hour, obtains described film coalescence aid.
2. the preparation method of an antimicrobial form asphalt waterproofing paint as claimed in claim 1, it is characterised in that comprise the following steps: above-mentioned pitch is heated to 140-150 DEG C, add polyacrylamide, Sodium Silicofluoride, methylisothiazolinone, obtain Preblend; Swelling perlite powder, fluorite powder are mixed with aminopropyltriethoxywerene werene, 500-600 rev/min dispersed with stirring 4-5 minute, join in above-mentioned Preblend after discharging, by colloidal mill grinding evenly, add each raw material except film coalescence aid, fully it is uniformly mixed at 90-100 DEG C, it is cooled to normal temperature, add film coalescence aid, fully stir, obtain described antimicrobial form asphalt waterproofing paint.