CN103467906A - 阻燃增强pom/ptfe组合物及其制备方法 - Google Patents
阻燃增强pom/ptfe组合物及其制备方法 Download PDFInfo
- Publication number
- CN103467906A CN103467906A CN2013103911327A CN201310391132A CN103467906A CN 103467906 A CN103467906 A CN 103467906A CN 2013103911327 A CN2013103911327 A CN 2013103911327A CN 201310391132 A CN201310391132 A CN 201310391132A CN 103467906 A CN103467906 A CN 103467906A
- Authority
- CN
- China
- Prior art keywords
- pom
- ptfe
- fire
- inflaming
- retarding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
阻燃增强POM/PTFE组合物及其制备方法,阻燃增强POM/PTFE组合物包括如下质量份数的原料:POM树脂78-84份、PTFE25-30份、无卤阻燃剂Exolit?OP9350.2-0.5份、双氰胺0.1-0.3份、铝酸锌0.1-0.2份、抗氧剂0.5-1份、马来酸酐接枝聚乙烯0.2-0.6份。本发明将无卤阻燃剂Exolit?OP935、双氰胺和铝酸锌复配作为阻燃剂,具有良好的阻燃效果;本发明具有良好的机械性能,拉伸强度可达50MPa,弯曲强度可达78MPa,且所得材料流动性好,易于加工成型。
Description
技术领域
本发明属于高分子材料技术领域,具体涉及一种阻燃增强POM/PTFE组合物及其制备方法。
背景技术
POM是第三大通用塑料,均具有优异的耐摩擦性能和钢性,物理性能、机械性能和化学性能良好,但是其热稳定性和阻燃性较差;PTFE具有优良的耐腐蚀性和自润滑性,还具有良好的电学性能,其电绝缘性不受温度影响,素有“塑料王”之称,但是其流动性较差,不易加工成型。目前有关改性POM的报道屡见不鲜,但是改性后的POM虽然其某一方面的性能得到的提升,但是其物理性能和机械性能在一定程度上受到了影响,使其应用受到了很大限制。
综上所述如何提升POM的综合性能成为该领域亟待解决的技术难题。
发明内容
本发明的目的在于克服现有技术的不足而提供一种阻燃增强POM/PTFE组合物及其制备方法,本发明成品具有良好的阻燃性,机械性能良好,且加工成型性良好。
本发明的技术方案:
阻燃增强POM/PTFE组合物,包括如下质量份数的原料: POM树脂78-84份、PTFE 25-30份、无卤阻燃剂Exolit™ OP935 0.2-0.5份、双氰胺0.1-0.3份、铝酸锌0.1-0.2份、抗氧剂0.5-1份、马来酸酐接枝聚乙烯0.2-0.6份。
所述抗氧剂为受阻酚类抗氧剂。
所述受阻酚类抗氧剂为2,6-叔丁基-4-甲基苯酚、双(3,5-叔丁基-4-羟基苯基)硫醚或四〔β-(3,5-叔丁基-4-羟基苯基)丙酸〕季戊四醇酯。
阻燃增强POM/PTFE组合物的制备方法,包括以下步骤:按照质量配比称取各原料,将POM树脂、PTFE粉碎至100目与抗氧剂混合搅拌均匀,后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™
OP935、双氰胺和铝酸锌,混合搅拌均匀后出料至双螺杆挤出机中挤出,各段温度控制150-155℃,造粒即可得。
有益效果:本发明将无卤阻燃剂Exolit™ OP935、双氰胺和铝酸锌复配作为阻燃剂,具有良好的阻燃效果;本发明具有良好的机械性能,拉伸强度可达50 MPa,弯曲强度可达78 MPa,且所得材料流动性好,易于加工成型。
具体实施方式
下面结合实施例对本发明作进一步的详细描述。
实施例1
阻燃增强POM/PTFE组合物,包括如下质量份数的原料: POM树脂78份、PTFE 25份、无卤阻燃剂Exolit™ OP935 0.2份、双氰胺0.1份、铝酸锌0.1份、2,6-叔丁基-4-甲基苯酚0.5份、马来酸酐接枝聚乙烯0.2份。
本发明制备方法:按照质量配比称取各原料,将POM树脂、PTFE粉碎至100目与抗氧剂2,6-叔丁基-4-甲基苯酚混合搅拌均匀,后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™
OP935、双氰胺和铝酸锌,混合搅拌均匀后出料至双螺杆挤出机中挤出,各段温度控制150℃,造粒即可得。
实施例2
阻燃增强POM/PTFE组合物,包括如下质量份数的原料: POM树脂84份、PTFE 30份、无卤阻燃剂Exolit™ OP935 0.5份、双氰胺0.3份、铝酸锌0.2份、双(3,5-叔丁基-4-羟基苯基)硫醚1份、马来酸酐接枝聚乙烯0.6份。
本发明制备方法:按照质量配比称取各原料,将POM树脂、PTFE粉碎至100目与抗氧剂双(3,5-叔丁基-4-羟基苯基)硫醚混合搅拌均匀,后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™
OP935、双氰胺和铝酸锌,混合搅拌均匀后出料至双螺杆挤出机中挤出,各段温度控制155℃,造粒即可得。
实施例3
阻燃增强POM/PTFE组合物,包括如下质量份数的原料: POM树脂82份、PTFE 28份、无卤阻燃剂Exolit™ OP935 0.3份、双氰胺0.2份、铝酸锌0.15份、四〔β-(3,5-叔丁基-4-羟基苯基)丙酸〕季戊四醇酯0.8份、马来酸酐接枝聚乙烯0.4份。
本发明制备方法,包括以下步骤:按照质量配比称取各原料,将POM树脂、PTFE粉碎至100目与抗氧剂四〔β-(3,5-叔丁基-4-羟基苯基)丙酸〕季戊四醇酯混合搅拌均匀,后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™
OP935、双氰胺和铝酸锌,混合搅拌均匀后出料至双螺杆挤出机中挤出,各段温度控制155℃,造粒即可得。
将实施例1-3所得材料按照国际标准注塑成型为测试样条,进行性能测试,测试结果见下表1。
表1 实施例1-3所得材料性能测试数据
性能 | 实施例1 | 实施例2 | 实施例3 |
拉伸强度,MPa | 42.8 | 50 | 48 |
弯曲强度,MPa | 75 | 78 | 74 |
缺口冲击强度,kJ/m2 | 13.6 | 15.6 | 14 |
UL-94 | V0 | V0 | V0 |
由上表可见本发明成品具有良好的阻燃性,阻燃性能为V0级,具有优良的冲击强度、拉伸强度和弯曲强度。
Claims (4)
1.阻燃增强POM/PTFE组合物,其特征在于,包括如下质量份数的原料: POM树脂78-84份、PTFE 25-30份、无卤阻燃剂Exolit™ OP935 0.2-0.5份、双氰胺0.1-0.3份、铝酸锌0.1-0.2份、抗氧剂0.5-1份、马来酸酐接枝聚乙烯0.2-0.6份。
2.根据权利要求1所述的阻燃增强POM/PTFE组合物,其特征在于,所述抗氧剂为受阻酚类抗氧剂。
3.根据权利要求2所述的阻燃增强POM/PTFE组合物,其特征在于,所述受阻酚类抗氧剂为2,6-叔丁基-4-甲基苯酚、双(3,5-叔丁基-4-羟基苯基)硫醚或四〔β-(3,5-叔丁基-4-羟基苯基)丙酸〕季戊四醇酯。
4.如权利要求1所述的阻燃增强POM/PTFE组合物的制备方法,其特征在于,包括以下步骤:按照质量配比称取各原料,将POM树脂、PTFE粉碎至100目与抗氧剂混合搅拌均匀,后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™ OP935、双氰胺和铝酸锌,混合搅拌均匀后出料至双螺杆挤出机中挤出,各段温度控制150-155℃,造粒即可得。