CN103467006A - Aerated concrete block with high thermal insulation property - Google Patents
Aerated concrete block with high thermal insulation property Download PDFInfo
- Publication number
- CN103467006A CN103467006A CN2013103356282A CN201310335628A CN103467006A CN 103467006 A CN103467006 A CN 103467006A CN 2013103356282 A CN2013103356282 A CN 2013103356282A CN 201310335628 A CN201310335628 A CN 201310335628A CN 103467006 A CN103467006 A CN 103467006A
- Authority
- CN
- China
- Prior art keywords
- building block
- powder
- rev
- weight
- take out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an aerated concrete block with high thermal insulation property. The aerated concrete block with high thermal insulation property is prepared by the following raw materials by weight: 0.04-0.06 part of nekal BX, 0.003-0.01 part of magnesium powder, 0.04-0.05 part of triethanolamine oleate, 4-5 parts of cement, 0.1-0.3 part of oxidized starch, 0.002-0.006 part of glycerin triacetate, 0.01-0.03 part of ethylene glycol monomethyl ether, 0.1-0.5 part of wood fiber, 10-20 parts of expanded perlite powder, 7-9 parts of slag powder, 17-19 parts of kaolin, 1-2 parts of alum and 0.2-0.4 part of chitosan.
Description
Technical field
The present invention relates to the aerated bricks field, is exactly a kind of high heat preservation performance air-entrained concrete building block.
Background technology
Aerated bricks is the air-entrained concrete building block of producing by the autoclave at high temperature apparatus and process." aerated bricks " can be understood as a simplification or a general title.Its product scope contained should more greatly, adopt the brick product of other various explained hereafter that comprise steam pressure.
Construction market materials for wall used was mainly common brick in the past, and present many advanced areas have been completely forbidden common brick and used.
Existing aerated bricks Development Technology is slow, can't meet the market requirement of diversification.
Summary of the invention
The object of the present invention is to provide a kind of high heat preservation performance air-entrained concrete building block.
Above-mentioned purpose realizes by following scheme:
A kind of high heat preservation performance air-entrained concrete building block, it is characterized in that: it is that raw material by following weight parts makes: Nekal BX 0.04-0.06, magnesium powder 0.003-0.01, triethanolamine oleate 0.04-0.05, cement 4-5, Sumstar 190 0.1-0.3, Vanay 0.002-0.006, ethylene glycol monomethyl ether 0.01-0.03, wood fibre 0.1-0.5, swelling perlite powder 10-20, steel-making slag powder 7-9, kaolin 17-19, alum 1-2, chitosan 0.2-0.4.
Described a kind of high heat preservation performance air-entrained concrete building block is characterized in that:
The preparation method comprises the following steps: after (1) mixes swelling perlite powder, steel-making slag powder, kaolin, alum by weight, under 900-1000 ℃, calcining is after 2-4 hour, take out, cooling, being ground to grain diameter is 1.75mm-1.90mm again, take out, add the ethylene glycol monomethyl ether that is equivalent to material gross weight 1.5-2.2%, the silane coupling agent KH580 of 1.2-1.5%, the Potassium Persulphate of 0.1-0.2%, and suitable quantity of water, after under 100-200 rev/min, stirring mixes in 10-20 minute, granulation, the balling-up particle diameter, at 0.5-1.5mm, obtains the composite minerals particle standby;
(2) take by weight composite minerals particle and all the other all raw materials, stir after 10-20 minute under 50-100 rev/min, then stir 5-8 minute under 100-160 rev/min, take out, obtain mixed slurry;
(3) the gained mixed slurry is poured into the mold moulding, rear precuring, the demoulding, cutting, obtain the building block base;
(4) the building block base is put into to the reactor steam press maintenance, put finished product in storage and get final product.
Beneficial effect of the present invention is: what wood fibre was unordered is distributed in aerated bricks, stops the expansion in crack, has improved the peeling off of this concrete opposing freeze-thaw cycle, separating power and insulated capacity.
Embodiment
A kind of high heat preservation performance air-entrained concrete building block, it is that raw material by following weight parts (kg) makes: Nekal BX 0.05, magnesium powder 0.006, triethanolamine oleate 0.05, cement 5, Sumstar 190 0.3, Vanay 0.005, ethylene glycol monomethyl ether 0.03, wood fibre 0.5, swelling perlite powder 15, steel-making slag powder 8, kaolin 18, alum 1, chitosan 0.4.
Described a kind of high heat preservation performance air-entrained concrete building block,
The preparation method comprises the following steps:
(1) after swelling perlite powder, steel-making slag powder, kaolin, alum are mixed by weight, under 900 ℃, calcining, after 2 hours, is taken out, cooling, being ground to grain diameter is 1.90mm again, take out, add the ethylene glycol monomethyl ether that is equivalent to material gross weight 2.2%, 1.2% silane coupling agent KH580,0.2% Potassium Persulphate, and suitable quantity of water, after under 200 rev/mins, stirring mixes in 20 minutes, granulation, the balling-up particle diameter, at 0.8-1.0mm, obtains the composite minerals particle standby;
(2) take by weight composite minerals particle and all the other all raw materials, stir after 20 minutes under 50 rev/mins, then stir 8 minutes under 100 rev/mins, take out, obtain mixed slurry;
(3) the gained mixed slurry is poured into the mold moulding, rear precuring, the demoulding, cutting, obtain the building block base;
(4) the building block base is put into to the reactor steam press maintenance, put finished product in storage and get final product.
The average unit weight of this building block is 730kg/m
3, good heat insulating, have a large amount of pores and micropore in building block inside, thereby good thermal and insulating performance, mean value ultimate compression strength are arranged is 9.6MPa.
Claims (2)
1. a high heat preservation performance air-entrained concrete building block, it is characterized in that: it is that raw material by following weight parts makes: Nekal BX 0.04-0.06, magnesium powder 0.003-0.01, triethanolamine oleate 0.04-0.05, cement 4-5, Sumstar 190 0.1-0.3, Vanay 0.002-0.006, ethylene glycol monomethyl ether 0.01-0.03, wood fibre 0.1-0.5, swelling perlite powder 10-20, steel-making slag powder 7-9, kaolin 17-19, alum 1-2, chitosan 0.2-0.4.
2. a kind of high heat preservation performance air-entrained concrete building block according to claim 1 is characterized in that:
The preparation method comprises the following steps:
(1) after swelling perlite powder, steel-making slag powder, kaolin, alum are mixed by weight, under 900-1000 ℃, calcining is after 2-4 hour, take out, cooling, being ground to grain diameter is 1.75mm-1.90mm again, take out, add the ethylene glycol monomethyl ether that is equivalent to material gross weight 1.5-2.2%, the silane coupling agent KH580 of 1.2-1.5%, the Potassium Persulphate of 0.1-0.2%, and suitable quantity of water, after under 100-200 rev/min, stirring mixes in 10-20 minute, granulation, the balling-up particle diameter, at 0.5-1.5mm, obtains the composite minerals particle standby;
(2) take by weight composite minerals particle and all the other all raw materials, stir after 10-20 minute under 50-100 rev/min, then stir 5-8 minute under 100-160 rev/min, take out, obtain mixed slurry;
(3) the gained mixed slurry is poured into the mold moulding, rear precuring, the demoulding, cutting, obtain the building block base;
(4) the building block base is put into to the reactor steam press maintenance, put finished product in storage and get final product.