CN103466941B - 一种滤紫外石英玻璃板及其制备方法 - Google Patents
一种滤紫外石英玻璃板及其制备方法 Download PDFInfo
- Publication number
- CN103466941B CN103466941B CN201310384892.5A CN201310384892A CN103466941B CN 103466941 B CN103466941 B CN 103466941B CN 201310384892 A CN201310384892 A CN 201310384892A CN 103466941 B CN103466941 B CN 103466941B
- Authority
- CN
- China
- Prior art keywords
- glass plate
- quartz glass
- trace mineral
- mineral supplement
- filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种滤紫外石英玻璃板,以高纯石英砂为基本重量份原料,配以占高纯石英砂17%-28%重量份的微量元素添加剂,微量元素添加剂包括:氢氧化铝AL(OH)3、硝酸钠NaNO3、四氯化钛TiCL4、氧化铈CeO2、氢氧化钾KOH、氧化铕Eu2O3。采用石英板整体着色制备工艺拉制成型的滤紫外线100mm以上石英玻璃板,热膨胀系数小,杂质含量低,耐高温,强度高,耐辐照,吸紫外线范围,吸收波长为304-318nm,吸收系数为5450L/mol.cm。
Description
技术领域
本发明涉及一种石英制品,特别是一种滤紫外石英玻璃板。本发明还涉及该滤紫外石英玻璃板的一种制备方法。
背景技术
高纯石英玻璃的热膨胀系数小,杂质含量低,并具有耐高温、强度高等特点,市场需求量大,已越来越广泛地应用半导体工业、新型电光源、光通讯、航天工业、化工行业及其他民用产品上。目前的石英玻璃有两种,一种是无色石英板,宽度小,不具备滤紫外功能,另一种是黑色石英板,没有滤紫外效果。
发明内容
本发明要解决的技术问题是针对现有技术的不足,提出了一种滤紫外效果好,透过率高、耐辐照的滤紫外石英玻璃板。本发明还提供了该石英玻璃板的一种制备方法。
本发明要解决的技术问题是通过以下技术方案来实现的,一种滤紫外石英玻璃板,其特点是:以高纯石英砂为基本重量份原料,配以占高纯石英砂17%-28%重量份的微量元素添加剂,
其中,微量元素添加剂是由以下重量配比的原料组成:
本发明要解决的技术问题可以通过以下技术方案进一步实现,微量元素添加剂的重量份为高纯石英砂的17.1%-25.4%。
本发明要解决的技术问题还可以通过以下技术方案进一步实现,采用SiO2含量大于99.999%、杂质含量低于2ppm、45目-140目的高纯石英砂,脱羟在1250度不变色。
本发明要解决另一个的技术问题是通过以下技术方案实现的,上述滤紫外石英玻璃板的制备方法,其特点是:将微量元素添加剂中的氢氧化铝Al(OH)3、四氯化钛TiCl4按比例称量后,加酸溶解,制成酸溶液;将微量元素添加剂中的硝酸钠NaNO3、氢氧化钾KOH、氧化铕Eu2O3按比例称量后,加水溶解,制成水溶液;将微量元素添加剂中的氧化铈CeO2加水并加入还原剂羟胺协助溶解,制成溶液,其中羟胺加入的重量占氧化铈重量的0.2%-0.5%。
将上述几种溶液掺入高纯石英砂,充分搅拌混合后,加温至1100℃-1200℃进行烘烤膨化,然后进行筛选和磁选,去除金属杂质,再投入连熔炉熔炼,拉制成型。
本发明要解决的技术问题可以通过以下技术方案进一步实现,所述的酸为盐酸,其质量百分比浓度为36%-38%。
本发明要解决的技术问题还可以通过以下技术方案进一步实现,所述的还原剂羟胺(NH2OH),其质量百分比浓度为100%。
本发明要解决的技术问题还可以通过以下技术方案进一步实现,连熔炉内温度在2100℃-2250℃的条件下,熔炼5-6小时后,拉速控制每小时15kg,进行拉制成型。
本发明与现有技术相比,采用石英板整体着色制备工艺拉制成型的滤紫外线100mm以上石英玻璃板,热膨胀系数小,杂质含量低,耐高温,强度高,耐辐照,吸紫外线范围,吸收波长为304-318nm,吸收系数为5450L/mol.cm。
具体实施方式
一种滤紫外石英玻璃板,以高纯石英砂为基本重量份原料,配以占高纯石英砂17%-28%重量份的微量元素添加剂,采用SiO2含量大于99.999%、杂质含量低于2ppm、45目-140目的高纯石英砂,脱羟在1250度不变色。其中SiO2含量为质量百分比,杂质含量也是指质量比。ppm表示固体中含量时,专指质量比或重量比。
其中,微量元素添加剂是由以下重量配比的原料组成:
所述微量元素添加剂的最佳加入量为高纯石英砂的17.1%-25.4%重量份。
微量元素添加剂的配方一:
氢氧化铝Al(OH)33.0、硝酸钠NaNO32.0、四氯化钛TiCl45.0、氧化铈CeO24.0、氢氧化钾KOH 2.0、氧化铕Eu2O31.1。
微量元素添加剂的配方二:
氢氧化铝Al(OH)34.0、硝酸钠NaNO33.0、四氯化钛TiCl46.0、氧化铈CeO25.0、氢氧化钾KOH 3.0、氧化铕Eu2O31.2。
微量元素添加剂的配方三:
氢氧化铝Al(OH)34.50、硝酸钠NaNO33.50、四氯化钛TiCl46.50、氧化铈CeO26.0、氢氧化钾KOH 3.6、氧化铕Eu2O31.3。
上述滤紫外石英玻璃板的制备方法,将微量元素添加剂中的氢氧化铝Al(OH)3、四氯化钛TiCl4按比例称量后,加酸溶解,制成酸溶液;将微量元素添加剂中的硝酸钠NaNO3、氢氧化钾KOH、氧化铕Eu2O3按比例称量后,加水溶解,制成水溶液;将微量元素添加剂中的氧化铈CeO2加水并加入还原剂羟胺协助溶解,制成溶液,其中羟胺加入的重量占氧化铈重量的0.2%-0.5%。
将上述几种溶液掺入高纯石英砂,充分搅拌混合后,加温至1100℃-1200℃进行烘烤膨化,然后进行筛选和磁选,去除金属杂质,再投入连熔炉熔炼,连熔炉内温度在2100℃-2250℃的条件下,熔炼5-6小时后,拉速控制每小时15kg,进行拉制成型。
所述的酸为盐酸,其质量百分比浓度为36%-38%。所述的还原剂羟胺(NH2OH),其质量百分比浓度为100%。
Claims (7)
1.一种滤紫外石英玻璃板,其特征在于:以高纯石英砂为基本重量份原料,配以占高纯石英砂17%-28%重量份的微量元素添加剂,
其中,微量元素添加剂是由以下重量配比的原料组成:
氢氧化铝Al(OH)3 3.0-4.50、硝酸钠NaNO3 2.0-3.50、
四氯化钛TiCl4 5.0-6.50、氧化铈CeO2 4.0-6.0、
氢氧化钾KOH 2.0-3.6、氧化铕Eu2O3 1.1-1.3。
2.根据权利要求1所述的滤紫外石英玻璃板,其特征在于:微量元素添加剂的重量份为高纯石英砂的17.1%-25.4%。
3.根据权利要求1所述的滤紫外石英玻璃板,其特征在于:采用SiO2含量大于99.999%、杂质含量低于2ppm、45目-140目的高纯石英砂,脱羟在1250度不变色。
4.权利要求1所述滤紫外石英玻璃板的制备方法,其特征在于:将微量元素添加剂中的氢氧化铝Al(OH)3、四氯化钛TiCl4按比例称量后,加酸溶解,制成酸溶液;将微量元素添加剂中的硝酸钠NaNO3、氢氧化钾KOH、氧化铕Eu2O3按比例称量后,加水溶解,制成水溶液;将微量元素添加剂中的氧化铈CeO2加水并加入还原剂羟胺协助溶解,制成溶液,其中羟胺加入的重量占氧化铈重量的0.2%-0.5%,
将上述几种溶液掺入高纯石英砂,充分搅拌混合后,加温至1100℃-1200℃进行烘烤膨化,然后进行筛选和磁选,去除金属杂质,再投入连熔炉熔炼,拉制成型。
5.根据权利要求4所述的滤紫外石英玻璃板的制备方法,其特征在于:所述的酸为盐酸,其质量百分比浓度为36%-38%。
6.根据权利要求4所述的滤紫外石英玻璃板的制备方法,其特征在于:所述的还原剂羟胺(NH2OH),其质量百分比浓度为100%。
7.根据权利要求4所述的滤紫外石英玻璃板的制备方法,其特征在于:连熔炉内温度在2100℃-2250℃的条件下,熔炼5-6小时后,拉速控制每小时15kg,进行拉制成型。