CN103465718A - Colored embossment glass painting and production method thereof - Google Patents
Colored embossment glass painting and production method thereof Download PDFInfo
- Publication number
- CN103465718A CN103465718A CN2013104371862A CN201310437186A CN103465718A CN 103465718 A CN103465718 A CN 103465718A CN 2013104371862 A CN2013104371862 A CN 2013104371862A CN 201310437186 A CN201310437186 A CN 201310437186A CN 103465718 A CN103465718 A CN 103465718A
- Authority
- CN
- China
- Prior art keywords
- glass
- embossment
- painting
- heating
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a colored embossment glass painting and a production method thereof. The colored embossment glass painting is formed by connecting embossment glass, a colored coating and a seal primer layer; the colored coating is formed by mutually connecting a plurality of color blocks which are irregular in shape and are rich in color. The production method comprises the steps of firstly producing a ceramic mold or a metal mold which is similar to a plane painting and has a sense of three-dimensional embossment; coating colorless flat plate glass on the mold, heating the flat plate glass and the mold together to be in the half molten state, and cooling slowly to normal temperature after glass completely covers and attaches the mold; coloring the concave surface of the produced embossment glass by paint or printing ink according to the color of the original plane painting; and drying the colored coating by a heating furnace; and coating a layer of primer paint. The glass painting produced by the invention has an obvious three-dimensional sense, is vivid, and has high artistry.
Description
Technical field
The present invention relates to the manufacturing technology field of glass technology, specifically a kind of embossment colour glass painting and manufacture method thereof.
Background technology
Glass-painting is a kind of glass-painting of making at drafting on glass or imitated famous painting by artificial or machinery, it have advantages of bright and clean, not perishable, easily cleaning and fidelity high, liked by people.Chinese utility model patent successively discloses " regular splicing block composite glass picture (ZL201120178519.0) " and " irregular splicing block composite glass picture (ZL201120178519.0) " two kinds of glass-paintings.The beneficial effect of these two kinds of glass-paintings is to be not easy the broken artistic characteristic with having dim sense.Yet above-mentioned glass-painting is all plane picture, there is no third dimension, authenticity is strong not, and its artistry Bi Jing is slightly more inferior, and this is that existing glass-painting makes the people feel sorry part.
Summary of the invention
The object of the invention is to solve the problems referred to above that existing glass-painting exists, provide that a kind of third dimension is strong, true to nature, artistry is high and embossment colour glass painting and the manufacture method thereof of good decorating effect.
The foregoing invention task realizes by this way:
A kind of embossment colour glass painting, it is formed by connecting from top to bottom by glass, coloured coating and back cover enamelled coating, described coloured coating is irregular by some plate shapes, color different color lump interconnect and form.
Described coloured coating can be colored paint or colored ink.
Its manufacture method of above-mentioned embossment stained glass is as follows:
1. manufacture metal die or ceramic die: find out the position that can demonstrate three-dimensional shape (building after having as the body of far and near mountain peak, trees, fruit, flower, animal, before having and river, grotto etc.) in the plane picture (traditional Chinese Painting or oil painting etc.) of appointment, adopt the manufacture method of prior art to produce identical with original work plane lines, but the mould that the three-dimensional shape jog is arranged, said mould can be identical with the original work plane sizes or dwindle by a certain percentage and the mould amplified;
2. one is positioned on mould with the equirotal colourless transparent plate glass in mould perspective plane, then be put into heating in the Resistant heating stove, heating-up temperature is 650 ~ 800 ℃, heating-up time is 5 ~ 10 hours, and temperature retention time is 20 ~ 30 minutes, fully topped on mould the time in the semi-molten state at glass, stop heating, allow glass slowly be cooled to normal temperature, be 10 ~ 30 hours cool time, makes glass after the demoulding;
The concave surface (being the back side) of glass press color that primary plane draws with colored ink or colored paint by manual or dull and stereotypedly print carefully colouring;
4. with far infrared or Resistant heating stove, coloured coating is dried;
5. finally on coloured coating, by spraying or brushing method, be coated with the last layer bottom closing paint.
The invention has the beneficial effects as follows: because embossment colour glass painting of the present invention is fully by the style of original work plane picture, tone is made, and produce corresponding indent and protrusion can demonstrate jog, make it there is obvious third dimension, fidelity is high, seem very true to nature, there is higher artistry and ornamental.It compares bright and clean and the easily advantage of cleaning in addition with the plane picture of papery in addition.
The relevant parameters of the manufacture method that glass of the present invention is drawn depends primarily on the complexity of the size of glass and thickness, concaveconvex shape.Generally, glass is large and thick, and concavo-convex how and complicated, its heating-up temperature can be higher, and heating is also longer with cool time.Heat time heating time in the time of this, especially cool time, more long reason was that glass easily ftractures in heating and cooling procedure.In addition, when Mold Making, avoid occurring easily producing the place of stress as far as possible.
The accompanying drawing explanation
The cross-sectional schematic that Fig. 1 is a kind of embossment stained glass.
The specific embodiment
With reference to Fig. 1, a kind of embossment stained glass, is characterized in that being formed by connecting from top to bottom by glass 1, coloured coating 2 and back cover enamelled coating 3, described coloured coating 2 be irregular by some plate shapes, color is different, and color lump is formed by connecting.
The manufacture method of above-mentioned embossment stained glass has following embodiment
Embodiment 1
1. manufacture ceramic die: by a width plane picture of appointment, find out and can demonstrate relief part, when manufacturing according to a conventional method onesize ceramic die, can demonstrate according to these ceramic die base that the corresponding female convex form is produced at relief position, make required ceramic die after sintering.
One block size is identical with the ceramic die perspective plane 2., the colourless transparent glass that thickness is 3 millimeters is placed on ceramic die, then in the Resistant heating stove, heat, heating-up temperature is 650 ℃, heat up 10 hours, be incubated 20 minutes and be until glass that molten condition is fully topped stops heating after on mould, allow glass naturally cool to room temperature, be 10 hours cool time, takes out glass after the demoulding;
3. the color of pressing the original work plane picture at the concave surface (being the back side) of the glass of making is printed painted formation coloured coating with colored ink by flat board;
4. with the FAR INFRARED HEATING stove, coloured coating is dried;
5. being coated with the last layer bottom closing paint on coloured coating just can.
1. manufacture metal die: find out and can show relief position by a width plane picture of appointment, with engraving or polishing way, produce corresponding evagination concave shape on the metal form of a corresponding size;
One block size is identical with metal die 2., the colourless transparent glass that thickness is 15 millimeters is placed on metal form, then be put into heating in the Resistant heating stove, heating-up temperature is 720 ℃, and the heating-up time is 20 hours, and temperature retention time is 25 minutes, glass be the semi-molten state fully topped on metal form after, allow glass naturally cool to normal temperature, be 20 hours cool time, takes out the moulding glass after the demoulding;
3. the color of pressing the original work plane picture at the concave surface (being the back side) of the glass made from colored ink by manual color plane coloured coating.
4 and 5 steps are identical with embodiment 1.
1. manufacture ceramic die: a width plane picture is amplified to 2 times, and can show relief position drawing to look for, produce corresponding concaveconvex shape on the ceramic blank of corresponding size, then sinter ceramic die into;
One block size is identical with ceramic die 2., the colourless transparent plate glass that thickness is 30 millimeters is put on ceramic template, then be put into heating in the Resistant heating stove, heating-up temperature is 800 ℃, heating-up time is 30 hours, temperature retention time is within 30 minutes, at glass, to be the semi-molten state to apply note fully and stop heating on ceramic template the time, allows glass plate slowly be cooled to normal temperature; Be 30 hours cool time, the de-taking-up glass of touching.
3. identical with embodiment 2.
4. with the resistance wire heating furnace, coloured coating is dried.
5. identical with embodiment 1.
Claims (3)
1. an embossment colour glass painting, is characterized in that being formed by connecting from top to bottom by glass, coloured coating and back cover enamelled coating, and described coloured coating is irregular by some plate shapes, color different color lump be formed by connecting.
2. embossment colour glass painting according to claim 1, it is characterized in that: described coloured coating is colored paint or colored ink.
3. the manufacture method of embossment colour glass painting claimed in claim 1, the steps include:
1) mfg. moulding die, find out the position that can demonstrate three-dimensional shape in plane picture (traditional Chinese Painting or oil painting etc.) by appointment, adopt the manufacture method of prior art to produce identical with original work plane lines, but metal die or ceramic die that the three-dimensional shape projection is arranged, said mould can be identical with the original work plane sizes or dwindle by a certain percentage and the mould amplified;
2) one is positioned on mould with the equirotal colourless transparent plate glass in mould perspective plane, then be put into heating in the Resistant heating stove, heating-up temperature is 650 ~ 800 ℃, be 10 ~ 30 hours heat time heating time, temperature retention time 20 ~ 30 minutes, stop heating on mould the time at glass in the semi-molten state is fully topped, allow glass slowly be cooled to normal temperature, be that glass is just made in the demoulding in 10 ~ 30 hours cool time;
3) color of drawing by primary plane at the concave surface (being the back side) of glass makes by hand with colored ink or colored paint or flat board is printed carefully painted;
4) with far infrared or Resistant heating stove, coloured coating is dried;
5) finally on coloured coating, by spraying or brushing method, be coated with the last layer bottom closing paint.