CN103465713A - Machining process for inlaying mother-of-pearl inlay - Google Patents
Machining process for inlaying mother-of-pearl inlay Download PDFInfo
- Publication number
- CN103465713A CN103465713A CN201310429545XA CN201310429545A CN103465713A CN 103465713 A CN103465713 A CN 103465713A CN 201310429545X A CN201310429545X A CN 201310429545XA CN 201310429545 A CN201310429545 A CN 201310429545A CN 103465713 A CN103465713 A CN 103465713A
- Authority
- CN
- China
- Prior art keywords
- mother
- inlaying
- inlay
- pearl inlay
- pearl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a machining process for inlaying a mother of pearl inlay. The machining process comprises the following steps: pasting polished shells, abalone pieces or spiral shells on a standby paper sample, so as to form a pattern; polishing a surface in which a body of the mother of pearl inlay is inlaid; smearing glue on the surface of the pattern, pasting the pattern on the body for 22-26 hours, and then washing off the standby paper sample by utilizing hot water; polishing by utilizing the water abrasive paper after moisture is dry, primarily spraying paint and baking to 130-150 DEG C, thoroughly cooling after the baked objected is taken out, spraying the paint again after polishing, and repeating three times to obtain a finished product. The machining process for inlaying the mother of pearl inlay, provided by, the invention is simple, part of lines of the pattern part are lively, vivid and lifelike, and the machining process overcomes the defects that an existing processing method is rigidity and inflexible.
Description
Technical field
The present invention relates to make the technology field of ornament, particularly a kind of processing technology of inlaying mother-of-pearl inlay.
Background technology
Mother-of-pearl inlay, claim again " Luo Dian ", " spiral shell is filled out ", " coin embedding ", " falling into freshwater mussel ", " bank spiral shell " and " sieve coin ", also has in history and be " coin spiral shell ", and it is Chinese distinctive art rarity.So-called " mother-of-pearl inlay ", refer to and grind into the thin slices such as personage, birds and flowers, geometric figure or word with spiral shell shell and sea cowry, need to be embedded in the general name of the decoration technology on implements surface according to picture.Because mother-of-pearl inlay is a kind of natural thing, the outward appearance natural beauty, therefore having ferocious visual effect, is also a kind of modal traditional decoration art, is widely used on lacquerware, furniture, musical instrument, screen, box casket, basin dish, woodcarving and relevant handicraft.
Traditional mother-of-pearl inlay mosaic technology: execute flax silk on the surface of wood paint thing, execute cinder, paste cotton paper, execute thin ash, execute pitch-dark multipass, inlay mother-of-pearl inlay (the spiral shell freshwater mussel cut out and gold and silver, colored stone sheet), cover pitch-dark multipass, polishing pushes away light again, until mother-of-pearl inlay exposes, become plane.Though present this technology has improvement, but still has complex process, the handicraft surface poor flatness, there is stiff, stiff defect in pattern.
Summary of the invention
The invention provides a kind of processing technology of inlaying mother-of-pearl inlay, solve existingly inlay the mother-of-pearl inlay complex process, there is stiff, stiff defect in pattern.
Technical scheme of the present invention is achieved in that a kind of processing technology of inlaying mother-of-pearl inlay, comprises the following steps:
1) will stick on standby pattern through shell, awabi sheet or the spiral shell shell be polished to, make it to become pattern;
2) surface that polishing wants to inlay the mother-of-pearl inlay body;
3) step 1 gained patterned surfaces is applied glue, stick on body;
4) after 22～26 hours, with hot water, standby pattern is washed off;
5) after moisture content is dry, uses liquid honing, and spray paint first and be baked to 130～150 ℃, taking-up cools completely;
6), after the polishing, the baking of again spraying paint is arrived finished product 3 times repeatedly.
Wherein, preferably, described to want to inlay the mother-of-pearl inlay body be porcelain utensil.
Wherein, preferably, described porcelain utensil is porcelain dish or porcelain vase.
Wherein, preferably, in described step 1, the thickness of the shell be polished to, awabi sheet or spiral shell shell is 0.02～0.07mm.
Wherein, preferably, in described step 1, the thickness of the shell be polished to, awabi sheet or spiral shell shell is 1～5mm.
Wherein, preferably, the glue in described step 3 is resistant to elevated temperatures super glue.
Wherein, preferably, the temperature of the hot water in described step 4 is more than 80 ℃.
Wherein, preferably, described step 6 also comprises before again spraying paint seven color powder is plotted to the step on mother-of-pearl inlay.
The present invention has following beneficial effect:
1. to inlay the technique of mother-of-pearl inlay simple in the present invention, when the mother-of-pearl inlay thinner thickness, forms a smooth light face that there is no concave-convex sense, and shell pattern part lines are lively, life-like, overcome stiff, the stiff defect of existing process.
2., when the thickest part of mother-of-pearl inlay adopted reaches 4～5mm, adopt mother-of-pearl inlay that the method for this technique is inlayed to reach the artistic effect of embossment.
3. the porcelain had now (porcelain dish, porcelain vase) institute drawing case is Freehandhand-drawing and draws (high temperature) or pattern stickup (low temperature), through baking, forms.And porcelain utensil mother-of-pearl inlay technique is the pattern that shell raw material and awabi thin slice are formed, and can with porcelain utensil, be combined and difficult drop-off preferably, is the another new form of expression of porcelain product.
The specific embodiment
Below the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only the present invention's part embodiment, rather than whole embodiment.Embodiment based in the present invention, those of ordinary skills, not making all other embodiment that obtain under the creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
The present embodiment is to inlay mother-of-pearl inlay on porcelain vase, and the processing technology that it inlays mother-of-pearl inlay comprises the following steps:
1) will stick on through the shell be polished on standby pattern, make it to become pattern; Wherein, shell thickness is 1～5mm, and it is according to the needs of composition, and thin and thick distributes.
2) surface of polishing porcelain vase;
3) step 1 gained patterned surfaces is coated to super glue, stick on porcelain vase;
4), after 22 hours, with 80 ℃ of hot water, standby pattern is washed off;
5) after moisture content is dry, uses liquid honing, and spray paint first and be baked to 150 ℃, taking-up cools completely;
6) after the polishing, by the method for artificial Freehandhand-drawing, seven color powder need to be plotted to according to composition on the shell of porcelain vase, the baking of again spraying paint is arrived finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that the step of spraying paint adopts is varnish.
Adopt this process that mother-of-pearl inlay is mounted on porcelain vase, the porcelain vase of making, because shell thickness is thicker, the rear porcelain vase surface irregularity that sprays paint, reached the effect of embossment, its pattern is more lively.
Embodiment 2
The present embodiment is to inlay mother-of-pearl inlay on porcelain vase, and the processing technology that it inlays mother-of-pearl inlay comprises the following steps:
1) will stick on standby pattern through the awabi sheet be polished to, make it to become pattern; Wherein, the thickness of awabi sheet is 0.02～0.07mm.
2) surface of polishing porcelain vase;
3) step 1 gained patterned surfaces is coated to super glue, stick on porcelain vase;
4), after 24 hours, with 90 ℃ of hot water, standby pattern is washed off;
5) after moisture content is dry, uses liquid honing, and spray paint first and be baked to 140 ℃, taking-up cools completely;
6) after the polishing, by the method for artificial Freehandhand-drawing, seven color powder need to be plotted on the awabi thin slice of porcelain vase according to composition, the baking of again spraying paint is arrived finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that the step of spraying paint adopts is varnish.
The porcelain vase that adopts this process to make, its surface forms a smooth light face that there is no concave-convex sense, and the pattern part lines are lively, life-like, overcome stiff, the stiff defect of existing process.
Embodiment 3
The present embodiment is to inlay mother-of-pearl inlay on porcelain dish, and the processing technology that it inlays mother-of-pearl inlay comprises the following steps:
1) will stick on standby pattern through shell, awabi sheet or the spiral shell shell be polished to, make it to become pattern; Wherein, the thickness of above-mentioned mother-of-pearl inlay is 0.02～0.07mm.
2) surface of polishing porcelain dish;
3) step 1 gained patterned surfaces is coated to super glue, stick on porcelain dish;
4), after 24 hours, with 95 ℃ of hot water, standby pattern is washed off;
5) after porcelain dish moisture content is dry, uses liquid honing, and spray paint first and be baked to 130 ℃, taking-up cools completely;
6), after the polishing, by the method for artificial Freehandhand-drawing, the baking of again spraying paint is arrived finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that the step of spraying paint adopts is varnish.
The porcelain dish that adopts this process to make, its surface forms a smooth light face that there is no concave-convex sense, and the pattern part lines are lively, life-like, overcome stiff, the stiff defect of existing process.
Embodiment 4
The present embodiment is to inlay mother-of-pearl inlay at wooden bottle, and the processing technology that it inlays mother-of-pearl inlay comprises the following steps:
1) will stick on standby pattern through shell, awabi sheet or the spiral shell shell be polished to, make it to become pattern; Wherein, the thickness of above-mentioned mother-of-pearl inlay is 0.02～0.07mm.
2) the polish surface of wooden bottle;
3) step 1 gained patterned surfaces is coated to super glue, stick on wooden bottle;
4), after 24 hours, with 85 ℃ of hot water, standby pattern is washed off;
5) after moisture content is dry, uses liquid honing, and spray paint first and be baked to 130 ℃, taking-up cools completely;
6), after the polishing, by the method for artificial Freehandhand-drawing, the baking of again spraying paint is arrived finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that the step of spraying paint adopts is varnish.
The wooden bottle that adopts this process to make, its surface forms a smooth light face that there is no concave-convex sense, and the pattern part lines are lively, life-like, overcome stiff, the stiff defect of existing process.
Embodiment 5
The present embodiment is to inlay mother-of-pearl inlay on wooden bodiless lacquer bottle, and the processing technology that it inlays mother-of-pearl inlay comprises the following steps:
1) will stick on through the shell be polished on standby pattern, make it to become pattern; Wherein, the thickness of above-mentioned mother-of-pearl inlay is 1～5mm.
2) surface of polishing porcelain dish;
3) step 1 gained patterned surfaces is coated to super glue, stick on wooden bodiless lacquer bottle;
4), after 24 hours, with 80 ℃ of hot water, standby pattern is washed off;
5) after porcelain utensil moisture content is dry, uses liquid honing, and spray paint first and be baked to 130 ℃, taking-up cools completely;
6), after the polishing, by the method for artificial Freehandhand-drawing, the baking of again spraying paint is arrived finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that the step of spraying paint adopts is varnish.
The wooden bottle that adopts this process to make, its surface forms a smooth light face that there is no concave-convex sense, and the pattern part lines are lively, life-like, overcome stiff, the stiff defect of existing process.
The foregoing is only preferred embodiment of the present invention, in order to limit the present invention, within the spirit and principles in the present invention not all, any modification of doing, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (9)
1. a processing technology of inlaying mother-of-pearl inlay, is characterized in that, comprises the following steps:
1) will stick on standby pattern through shell, awabi sheet or the spiral shell shell be polished to, make it to become pattern;
2) surface that polishing wants to inlay the mother-of-pearl inlay body;
3) step 1 gained patterned surfaces is applied glue, stick on body;
4) after 22～26 hours, with hot water, standby pattern is washed off;
5) after moisture content is dry, uses liquid honing, and spray paint first and be baked to 130～150 ℃, taking-up cools completely;
6), after the polishing, the baking of again spraying paint is arrived finished product 3 times repeatedly.
2. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1 is characterized in that: described to want to inlay the mother-of-pearl inlay body be porcelain utensil.
3. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 2, it is characterized in that: described porcelain utensil is porcelain dish or porcelain vase.
4. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1 is characterized in that: described to want to inlay the mother-of-pearl inlay body be bodiless lacquer or wooden bottle.
5. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1, it is characterized in that: in described step 1, the thickness of the shell be polished to, awabi sheet or spiral shell shell is 0.02～0.07mm.
6. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1, it is characterized in that: in described step 1, the thickness of the shell be polished to, awabi sheet or spiral shell shell is 1～5mm.
7. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1, it is characterized in that: the glue in described step 3 is resistant to elevated temperatures super glue.
8. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1, it is characterized in that: the temperature of the hot water in described step 4 is more than 80 ℃.
9. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1, is characterized in that: before again spraying paint in described step 6, also comprise seven color powder are plotted to the step on mother-of-pearl inlay.