CN103450608A - 一种高耐候阻燃自洁膜的组配方法 - Google Patents
一种高耐候阻燃自洁膜的组配方法 Download PDFInfo
- Publication number
- CN103450608A CN103450608A CN2013104120351A CN201310412035A CN103450608A CN 103450608 A CN103450608 A CN 103450608A CN 2013104120351 A CN2013104120351 A CN 2013104120351A CN 201310412035 A CN201310412035 A CN 201310412035A CN 103450608 A CN103450608 A CN 103450608A
- Authority
- CN
- China
- Prior art keywords
- cleaning
- flame retardant
- self
- pvdf
- membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高耐候阻燃自洁膜的组配方法,组配重量百分比为,聚偏氟乙烯30-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-50%,阻燃剂3-30%,以上各组份按重量配比之和为100%;对聚偏氟乙烯进行改性,当与金属接触后不与金属发生粘结,使聚偏氟乙烯可以压延生产,生产出各式各样的膜制品,所制作的膜具有高耐候性,可保证户外使用三十至五十年不变色;具有阻燃性,离火自熄;具有自洁性、免维护、高耐磨等优良性能;可广泛应用于外墙贴膜、楼顶防水膜、塑料地毯的表层(不沾灰、免清洁、高耐磨)、人造革的表层(不沾灰、免清洁,特别适合做汽车沙发面料)等等。
Description
技术领域
本发明涉及塑料加工技术领域,尤其是一种高耐候阻燃自洁膜的组配方法。
背景技术
目前,聚偏氟乙烯(PVDF)被用来制作氟碳漆用于户外的涂料,由于聚偏氟乙烯(PVDF)具有优良的自洁性、耐候性、阻燃性、耐磨性,所以,这种涂料刷的墙面是免维护的。
在装饰领域,装饰膜和涂料同样重要,由于装饰膜具有更好的纹理,他的装饰效果要好于涂料。所以,如果能把聚偏氟乙烯(PVDF)做成装饰膜用于户外,它的装饰效果要远远好于氟碳涂料。但是,聚偏氟乙烯(PVDF)和金属具有良好的亲合力,当与金属接触后便难以从金属上剥离下来,因此,无法通过压延的方法生产聚偏氟乙烯(PVDF)装饰膜,所以,聚偏氟乙烯(PVDF)的加工性能需要改进。
申请号为201210505355.7的专利文件公布了一种常温氟碳漆及其制备方法,加入有超耐候颜料,可提高氟碳漆的耐候性,但所使用的原料中却没有自洁性、阻燃性、耐磨性等性能,易粘灰,长期使用后,表面脏物难以清理,影响美观。
鉴于上述原因,现发明出一种高耐候阻燃自洁膜的组配方法,对聚偏氟乙烯(PVDF)进行改性,当与金属接触后不与金属发生粘结,使聚偏氟乙烯(PVDF)可以压延生产,生产出的膜制品具有自洁性、免维护、高耐候性、阻燃性、高耐磨等优良性能。
发明内容
本发明的目的是为了克服现有技术中的不足,提供一种高耐候阻燃自洁膜的组配方法,对聚偏氟乙烯(PVDF)进行改性,当与金属接触后不与金属发生粘结,使聚偏氟乙烯(PVDF)可以压延生产,生产出的膜制品具有自洁性、免维护、高耐候性、阻燃性、高耐磨等优良性能。
本发明为了实现上述目的,采用如下技术方案:一种高耐候阻燃自洁膜的组配方法,组配重量百分比为,聚偏氟乙烯30-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-50%,阻燃剂3-30%,以上各组份按重量配比之和为100%。
组配重量百分比为,聚偏氟乙烯40-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-40%,阻燃剂8-25%,以上各组份按重量配比之和为100%。
组配重量百分比为,聚偏氟乙烯50-60%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物20-30%,阻燃剂20-30%,以上各组份按重量配比之和为100%。
组配重量百分比为,聚偏氟乙烯60-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-20%,阻燃剂3-20%,以上各组份按重量配比之和为100%。
本发明的有益效果是:甲基丙烯酸甲酯-丙烯酸丁酯共聚物具有优异的耐候性,可确保材料在户外使用二十年不黄变,并且能保证优良的透明度,韧性好,强度高,和金属的剥离性能非常好。经过测试,甲基丙烯酸甲酯-丙烯酸丁酯共聚物和聚偏氟乙烯(PVDF)的相溶性非常好,因此,甲基丙烯酸甲酯-丙烯酸丁酯共聚物可以作为一种改性材料来改性聚偏氟乙烯(PVDF),甲基丙烯酸甲酯-丙烯酸丁酯共聚物是一种易燃物,须加入阻燃剂可提高阻燃性能。
本发明对聚偏氟乙烯(PVDF)进行改性,当与金属接触后不与金属发生粘结,使聚偏氟乙烯(PVDF)可以压延生产,可以生产出各式各样的膜制品,所制作的膜具有高耐候性,可保证户外使用三十至五十年不变色;具有阻燃性,做到离火自熄;具有自洁性、免维护、高耐磨等优良性能;可以广泛应用于外墙贴膜、楼顶防水膜、塑料地毯的表层(不沾灰、免清洁、高耐磨)、人造革的表层(不沾灰、免清洁,特别适合做汽车沙发面料)等等。
具体实施方式
下面结合实施例与具体实施方式对本发明作进一步详细说明:
实施例1
组配重量百分比为,聚偏氟乙烯30-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-50%,阻燃剂3-30%,以上各组份按重量配比之和为100%。
实施例2
组配重量百分比为,聚偏氟乙烯40-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-40%,阻燃剂8-25%,以上各组份按重量配比之和为100%。
实施例3
组配重量百分比为,聚偏氟乙烯50-60%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物20-30%,阻燃剂20-30%,以上各组份按重量配比之和为100%。
实施例4
组配重量百分比为,聚偏氟乙烯60-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-20%,阻燃剂3-20%,以上各组份按重量配比之和为100%。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的方案之内,所作的任何修改、等同替换、改进,均应包含在本发明的保护范围之内。
Claims (4)
1.一种高耐候阻燃自洁膜的组配方法,其特征在于:组配重量百分比为,聚偏氟乙烯30-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-50%,阻燃剂3-30%,以上各组份按重量配比之和为100%。
2.根据权利要求1所述的一种高耐候阻燃自洁膜的组配方法,其特征在于:组配重量百分比为,聚偏氟乙烯40-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-40%,阻燃剂8-25%,以上各组份按重量配比之和为100%。
3.根据权利要求1所述的一种高耐候阻燃自洁膜的组配方法,其特征在于:组配重量百分比为,聚偏氟乙烯50-60%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物20-30%,阻燃剂20-30%,以上各组份按重量配比之和为100%。
4.根据权利要求1所述的一种高耐候阻燃自洁膜的组配方法,其特征在于:组配重量百分比为,聚偏氟乙烯60-80%,甲基丙烯酸甲酯—丙烯酸丁酯共聚物10-20%,阻燃剂3-20%,以上各组份按重量配比之和为100%。