CN103449788A - 一种外墙保温板粘结砂浆及其制备方法 - Google Patents
一种外墙保温板粘结砂浆及其制备方法 Download PDFInfo
- Publication number
- CN103449788A CN103449788A CN2013102420084A CN201310242008A CN103449788A CN 103449788 A CN103449788 A CN 103449788A CN 2013102420084 A CN2013102420084 A CN 2013102420084A CN 201310242008 A CN201310242008 A CN 201310242008A CN 103449788 A CN103449788 A CN 103449788A
- Authority
- CN
- China
- Prior art keywords
- external wall
- adhesive mortar
- wall insulation
- insulation board
- wall crack
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于建筑材料领域,特别涉及一种外墙保温板粘结砂浆及其制备方法,该外墙保温板粘结砂浆包含以下按重量百分数计的原料:粘结料30%-65%、细骨料30%-65%、聚合物胶结料2%-6%、触变润滑剂0.1%-0.3%及速凝剂0.008-0.012%。该粘结料由硅酸盐水泥和高铝水泥按照重量比为15-25:1的比例组成,所述聚合物胶结料由可分散乳胶、有机硅憎水剂和羟丙基甲基纤维素醚组成。本发明制得的外墙保温板粘结砂浆的粘结强度高、粘结力大、防水抗渗效果好,从而提高了整个保温***的耐久性;早凝效果好,缩短了养护周期,加快了施工速度,而且该保温板粘结砂浆的制备过程简单、价格便宜。
Description
技术领域
本发明属于建筑材料领域,特别涉及一种外墙保温粘结砂浆及其制备方法。
背景技术
外墙的隔热保温对于居住建筑节能起着重要的作用,随着对节约能源与保护环境要求的不断提高,居住建筑的节能已然成为了当务之急。目前,外墙隔热保温方法中,采用保温衬板的方法最为常用,然而保温层与基础墙体之间的粘结层,则关系到整个保温***的稳定性和耐久性。粘结砂浆是由水泥、石英砂、聚合物胶结料,配以多种添加剂经机械混合均匀而成,主要用于粘结保温板的粘结剂。该粘结砂浆要求同基层墙体和聚苯板等保温板均有较强的粘接作用;耐水、耐冻融、耐老化性能好;施工方便,是一种非常安全可靠的保温***粘结材料;施工中不滑坠;具有优良的耐候、抗冲击和防裂性能。
市场上使用的粘结砂浆的粘结力差、粘结强度低,往往会造成外墙保温***的脱落等现象,缩短了外墙保温***的使用寿命;因粘结层的涂层较厚、抗渗性差;凝结时间长,如果建筑施工周期比较急的话,粘结砂浆养护期不够就增加荷载,造成了粘结砂浆的粘结效果。
发明内容
本发明的目的是提供一种外墙保温板粘结砂浆,该粘结砂浆的粘结强度高、早凝、防水抗渗效果好,而且施工方便,施工养护期短。
本发明的另一个目的是提供一种上述外墙保温板粘结砂浆的制备方法。
本发明的目的可以通过以下技术方案来实现:
一种外墙保温板粘结砂浆,其特征在于:包含以下按重量百分数计的原料:
所述粘结料由硅酸盐水泥和高铝水泥组成,硅酸盐水泥和高铝水泥的重量比为15-25:1。
所述细骨料为级配黄砂,该黄砂的粒径为109-212μm。
所述聚合物胶结料由可分散乳胶、有机硅憎水剂和羟丙基甲基纤维素醚组成;可分散乳胶、有机硅憎水剂和羟丙基甲基纤维素醚的重量比为20-25:1-3:1;温度在22℃时,质量浓度为2%的羟丙基甲基纤维素醚水溶液的黏度为20000-40000mPa·s。优选的,温度在22℃时,质量浓度为2%的羟丙基甲基纤维素醚水溶液的黏度为30000mPa·s。
所述触变润滑剂的含水量为9-13%,密度为600-800g/L。
所述速凝剂为碳酸锂或氯化锂中的一种。
一种制备上述建筑外墙抹面抗裂砂浆的方法,其步骤包括:
(1)按配比称量各种原料;
(2)将粘结料、细骨料、聚合物胶结料、触变润滑剂和速凝剂加入到搅拌机中,搅拌3-8分钟即可;使用时,按照抗裂砂浆和水的重量比为1:0.1-0.3的比例混合搅拌1-5分钟,即可用于建筑施工。
本发明的有益效果是:
1、所述外墙保温板粘结砂浆的粘结强度高、粘结力大、防水抗渗效果好,从而提高了整个保温***的耐久性。
2、所述外墙保温板粘结砂浆的早凝效果好,养护7天,该粘结砂浆与水泥砂浆拉伸粘结强度达到1.0Mpa以上,缩短了养护周期,加快了施工速度。
3、所述外墙保温板粘结砂浆的制备过程简单、原料易得、价格便宜。
具体实施方式
下面结合实施例,对本发明作进一步说明:
实施例1
将如下原料按照加入量(重量份)混合,具体为:
普通水泥(PO42.5硅酸盐水泥)360份、高铝水泥19份、级配黄砂(70-140目)580份、聚合物胶结料39份、触变润滑剂1.9份和氯化锂0.1份,加入到无重力混合搅拌机中混合5分钟即得到外墙保温板粘结砂浆。使用时,将得到的外墙保温板粘结砂浆与水按照重量比为1:0.25的比例,搅拌2分钟即可用于建筑施工。
聚合物胶结料的组成为:其中可分散乳胶粉、羟丙基甲基纤维素醚及有机硅憎水剂的重量比为45:3:2,其中,羟丙基甲基纤维素醚的2wt%浓度溶液在22℃下的黏度为3万mPa·s。
将本实施例中制得的外墙保温板粘结砂浆进行检测,具体测试结果如下表1所示:
表1
按照DB31/T366-2006的(外墙保温专用砂浆技术要求)的实验方法进行检测:养护28天,所制备的粘结砂浆与水泥砂浆拉伸粘结强度达到1.47Mpa,养护7天,所制备的粘结砂浆与水泥砂浆拉伸粘结强度达到1.1Mpa,浸水48小时后,与保温板的拉伸粘结强度达到0.44Mpa,粘结强度高,粘结力大;所制备的粘结砂浆的早凝效果好,减少了施工养护周期;28天的抗渗压力达到1.2Mpa,可达到防水抗渗效果,提高了整个保温***的耐久性。
实施例2
将如下原料按照加入量(重量份)混合,具体为:
普通水泥(PO42.5硅酸盐水泥)380份、高铝水泥15份、级配黄砂(70-140目)558份、聚合物胶结料45份、触变润滑剂1.91份和碳酸锂0.09份,加入到无重力混合搅拌机中混合5分钟即得到外墙保温板粘结砂浆。使用时,将得到的外墙保温板粘结砂浆与水按照重量比为1:0.25的比例,搅拌2分钟即可用于建筑施工。
其中,聚合物胶结料的组成为:其中可分散乳胶粉、羟丙基甲基纤维素醚及有机硅憎水剂的重量比为45:3:2,其中,羟丙基甲基纤维素醚的2wt%浓度溶液在22℃下的黏度为3万mPa·s。
对所制得的外墙保温板粘结砂浆进行检测,养护28天,所制备的粘结砂浆与水泥砂浆拉伸粘结强度达到1.23Mpa,养护7天,所制备的粘结砂浆与水泥砂浆拉伸粘结强度达到1.0Mpa,浸水48小时后,与保温板的拉伸粘结强度达到0.47Mpa;抗渗压力可以达到1.1Mpa。所制备的粘结砂浆的早凝效果好,减少了施工养护周期,而且粘结强度高、粘结力大、防水抗渗效果好。
实施例3
将如下原料按照加入量(重量份)混合,具体为:
普通水泥(PO42.5硅酸盐水泥)370份、高铝水泥15份、级配黄砂(70-140目)583份、聚合物胶结料30份、触变润滑剂1.9份和氯化锂0.1份,加入到无重力混合搅拌机中混合5分钟即得到外墙保温板粘结砂浆。使用时,将得到的外墙保温板粘结砂浆与水按照重量比为1:0.25的比例,搅拌2分钟即可用于建筑施工。
其中,聚合物胶结料的组成为:其中可分散乳胶粉、羟丙基甲基纤维素醚及有机硅憎水剂的重量比为45:3:2,其中,羟丙基甲基纤维素醚的2wt%浓度溶液在22℃下的黏度为3万mPa·s。
实施例4
将如下原料按照加入量(重量份)混合,具体为:
普通水泥(PO42.5硅酸盐水泥)340份、高铝水泥20份、级配黄砂(70-140目)598份、聚合物胶结料40份、触变润滑剂1.9份和碳酸锂0.1份,加入到无重力混合搅拌机中混合5分钟即得到外墙保温板粘结砂浆。使用时,将得到的外墙保温板粘结砂浆与水按照重量比为1:0.25的比例,搅拌2分钟即可用于建筑施工。
以上所述为本发明的较佳实施例而已,但本发明不应该局限于该实施例所公开的内容。所以凡是不脱离本发明所公开的精神下完成的等效或修改,都落入本发明保护的范围。
Claims (8)
2.根据权利要求1所述的建筑外墙抹面抗裂砂浆,其特征在于:所述粘结料由硅酸盐水泥和高铝水泥组成,硅酸盐水泥和高铝水泥的重量比为15-25:1。
3.根据权利要求1所述的建筑外墙抹面抗裂砂浆,其特征在于:所述细骨料为级配黄砂,该黄砂的粒径为109-212μm。
4.根据权利要求1所述的建筑外墙抹面抗裂砂浆,其特征在于:所述聚合物胶结料由可分散乳胶、有机硅憎水剂和羟丙基甲基纤维素醚组成。
5.根据权利要求4所述的建筑外墙抹面抗裂砂浆,其特征在于:所述可分散乳胶、有机硅憎水剂和羟丙基甲基纤维素醚的重量比为20-25:1-3:1;温度在22℃时,质量浓度为2%的羟丙基甲基纤维素醚水溶液的黏度为20000-40000mPa·s。
6.根据权利要求1所述的建筑外墙抹面抗裂砂浆,其特征在于:所述触变润滑剂的含水量为9-13%,密度为600-800g/L。
7.根据权利要求1所述的建筑外墙抹面抗裂砂浆,其特征在于:所述速凝剂为碳酸锂或氯化锂中的一种。
8.一种制备权利要求1所述的建筑外墙抹面抗裂砂浆的方法,其步骤包括:
(1)按配比称量各种原料;
(2)将粘结料、细骨料、聚合物胶结料、触变润滑剂和速凝剂加入到搅拌机中,搅拌3-8分钟即可;使用时,按照抗裂砂浆和水的重量比为1:0.1-0.3的比例混合搅拌1-5分钟,即可用于建筑施工。