CN103397277A - 水泵壳体用高强度铸钢及其制备方法 - Google Patents

水泵壳体用高强度铸钢及其制备方法 Download PDF

Info

Publication number
CN103397277A
CN103397277A CN2013102713390A CN201310271339A CN103397277A CN 103397277 A CN103397277 A CN 103397277A CN 2013102713390 A CN2013102713390 A CN 2013102713390A CN 201310271339 A CN201310271339 A CN 201310271339A CN 103397277 A CN103397277 A CN 103397277A
Authority
CN
China
Prior art keywords
hour
cast steel
insulation
warming
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102713390A
Other languages
English (en)
Inventor
何祥炎
黄先功
刘彬彬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Sanlian Pump Industry Co Ltd
Original Assignee
Anhui Sanlian Pump Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Sanlian Pump Industry Co Ltd filed Critical Anhui Sanlian Pump Industry Co Ltd
Priority to CN2013102713390A priority Critical patent/CN103397277A/zh
Publication of CN103397277A publication Critical patent/CN103397277A/zh
Pending legal-status Critical Current

Abstract

一种水泵壳体用高强度铸钢，所述铸钢的化学成分及其质量百分比为：碳0.24-0.26、磷≤0.040、锰0.35-0.50、硫≤0.040、镍0.1-0.25、钒0.05-0.015、Si1.2-1.3、Te0.24-0.28、Mn1.5-1.8、Cr3.2-3.3、Pr0.2-0.24、La0.13-0.15、Ho0.16-0.19，基质为铁。本发明的铸钢抗冲击强度高、耐磨性好、耐腐蚀、可与普通碳素钢进行焊接。

Description

水泵壳体用高强度铸钢及其制备方法
技术领域
本发明属于钢铁铸造技术，具体是一种铸钢及制备方法。
背景技术
铸钢是在凝固过程中不经历共晶转变的用于生产铸件的铁基合金的总称。铸钢分为铸造碳钢、铸造低合金钢和铸造特种钢3类。对于强度、塑性和韧性要求更高的机器零件，需要采用铸钢件，现有铸钢存在屈服强度、抗拉强度均较低、抗冲击性等机械力学性能指标较低，已不能满足产品对材料力学性能的要求。
发明内容
本发明的目的是提供一种水泵壳体用高强度铸钢及其制备方法，具有较好的机械力学性能。
本发明的技术方案如下：
一种水泵壳体用高强度铸钢，其特征在于所述铸钢的化学成分及其质量百分比为：碳0.24-0.26、磷≤0.040、锰0.35-0.50、硫≤0.040、镍0.1-0.25、钒0.05-0.015、Si1.2-1.3、Te0.24-0.28、Mn1.5-1.8、Cr3.2-3.3、Pr0.2-0.24 、La0.13-0.15、Ho0.16-0.19，基质为铁。
所述的低成本高强度耐磨铸钢的制备方法，其特征在于：将各配料放入于工业电弧炉中进行熔炼，检测合金成分含量并添加相应成分至达标，加入精炼剂精炼，搅拌10-15分钟，扒渣，并浇注成铸件，浇注温度为1540-1590℃ ；然后进行铸件的后续热处理：先由室温以230-250℃/小时速率升温至955-985℃，保温2-3小时；再以120-140℃/小时速率降温至220-240℃，保温1-2小时；再以150-180℃/小时速率升温至780-830℃，保温2-3小时；再以90-120℃/小时速率降温至360-390℃，保温2-3小时；再以再以110-130℃/小时速率升温至520-540℃，保温2-3小时，取出冷却即得；所述的精炼剂由下列重量份原料混合压块而成：碳酸钡3-3.2、四硼酸钠2.3-2.6、海泡石粉5-6、氟化铝钠1.3-1.5、明矾3-4、SnO21.1-1.3、Bi2O34.1-4.3、二硼化钒1.6-1.8、碳化铌2.3-2.5。
本发明的铸钢抗冲击强度高、耐磨性好、耐腐蚀、可与普通碳素钢进行焊接。
具体实施方式
一种水泵壳体用高强度铸钢，所述铸钢的化学成分及其质量百分比为：碳0.24-0.26、磷≤0.040、锰0.35-0.50、硫≤0.040、镍0.1-0.25、钒0.05-0.015、Si1.2-1.3、Te0.24-0.28、Mn1.5-1.8、Cr3.2-3.3、Pr0.2-0.24 、La0.13-0.15、Ho0.16-0.19，基质为铁。
制备方法，将各配料放入于工业电弧炉中进行熔炼，检测合金成分含量并添加相应成分至达标，加入精炼剂精炼，搅拌10-15分钟，扒渣，并浇注成铸件，浇注温度为1540-1590℃ ；然后进行铸件的后续热处理：先由室温以230-250℃/小时速率升温至955-985℃，保温2-3小时；再以120-140℃/小时速率降温至220-240℃，保温1-2小时；再以150-180℃/小时速率升温至780-830℃，保温2-3小时；再以90-120℃/小时速率降温至360-390℃，保温2-3小时；再以再以110-130℃/小时速率升温至520-540℃，保温2-3小时，取出冷却即得
所述的精炼剂由下列重量份（公斤）原料混合压块而成：碳酸钡3、四硼酸钠2.3、海泡石粉6、氟化铝钠1.3、明矾3、SnO21.1、Bi2O34.1、二硼化钒1.6、碳化铌2.3。
本发明铸钢的机械性能为：拉伸强度980MPa，屈服强度673MPa，延伸率15％，断面收缩率22％，冲击吸收功54J，冲击韧性63J/cm2，硬度271HB。

Claims (2)

1.一种水泵壳体用高强度铸钢，其特征在于所述铸钢的化学成分及其质量百分比为：碳0.24-0.26、磷≤0.040、锰0.35-0.50、硫≤0.040、镍0.1-0.25、钒0.05-0.015、Si1.2-1.3、Te0.24-0.28、Mn1.5-1.8、Cr3.2-3.3、Pr0.2-0.24 、La0.13-0.15、Ho0.16-0.19，基质为铁。
2.根据权利要求1所述的低成本高强度耐磨铸钢的制备方法，其特征在于：将各配料放入于工业电弧炉中进行熔炼，检测合金成分含量并添加相应成分至达标，加入精炼剂精炼，搅拌10-15分钟，扒渣，并浇注成铸件，浇注温度为1540-1590℃ ；然后进行铸件的后续热处理：先由室温以230-250℃/小时速率升温至955-985℃，保温2-3小时；再以120-140℃/小时速率降温至220-240℃，保温1-2小时；再以150-180℃/小时速率升温至780-830℃，保温2-3小时；再以90-120℃/小时速率降温至360-390℃，保温2-3小时；再以再以110-130℃/小时速率升温至520-540℃，保温2-3小时，取出冷却即得。
CN2013102713390A 2013-07-01 2013-07-01 水泵壳体用高强度铸钢及其制备方法 Pending CN103397277A (zh)