CN103387652A - Method for preparing environmentally-friendly polyurethane plastic for track - Google Patents
Method for preparing environmentally-friendly polyurethane plastic for track Download PDFInfo
- Publication number
- CN103387652A CN103387652A CN2013103422759A CN201310342275A CN103387652A CN 103387652 A CN103387652 A CN 103387652A CN 2013103422759 A CN2013103422759 A CN 2013103422759A CN 201310342275 A CN201310342275 A CN 201310342275A CN 103387652 A CN103387652 A CN 103387652A
- Authority
- CN
- China
- Prior art keywords
- preparation
- polyurethane plastic
- polyether glycol
- environment
- plastic cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing environmentally-friendly polyurethane plastic for a track. Polyether polyol, isocyanate, MDI (diphenyl methane diisocyanate), a polyurethane vulcanizing agent, a plasticizer, padding and pigments are taken as the main raw materials for preparing the polyurethane plastic. The method comprises the following steps of: preparing a polyurethane prepolymer through reaction of polyether polyol and liquefied MDI under the condition of vacuum dewatering; then adding a chain extender, after heating and vacuum degassing, adding the plasticizer, the padding, an antiager, and the pigments, and preparing the polyurethane plastic through stirring and grinding. The method has the advantages of being simple and easy to operate, and the prepared plastics have the characteristics of being good in overall performance, non-toxic, tasteless, and environmentally-friendly.
Description
Technical field
The present invention relates to the plastic cement preparing technical field, particularly relate to the preparation method of a kind of runway with the environment-protecting polyurethane plastic cement.
Background technology
The urethane full name is polyurethane(s), is the general designation that contains the macromolecular cpd of repetition carbamate groups on main chain.Urethane has the excellent properties such as remarkable wear resistance, high strength, high elongation rate, snappiness, oil resistant, anti-x radiation x.Urethane is applied to pavement and has that planeness is good, ultimate compression strength is high, hardness elasticity suitably, the characteristic of stable physical property, and have certain elasticity and color, have certain anti-uv-ray and ageing-resistant ability.
Traditional urethane pavement product is all tolylene diisocyanate (TDI) type, and due to the heavy metal substance that the TDI polyurethane runway contains, meeting is the oxidation stain environment in use.In addition, also contain the toxic and harmful substances such as multiple catalysts (leaded, mercury, tin), binary amine chainextender, organic molecule softening agent, solvent, rubber ingredients and two benzene solvents in the TDI polyurethane component, to human body and all environment cause detrimentally affect.And environment-friendly type '-diphenylmethane diisocyanate (MDI) have toxicity little, little on human health damage, on the advantage such as the impact of environment is less, more meet the needs of current environmental protection.
Summary of the invention
The technical problem that the present invention mainly solves is to provide the preparation method of a kind of runway with the environment-protecting polyurethane plastic cement, can solve traditional runway toxicity large, and human body and environment are produced the problem of harm.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: the preparation method of a kind of runway with the environment-protecting polyurethane plastic cement is provided, it is characterized in that, composition comprises: polyether glycol, isocyanic ester, MDI, urethane vulcanizing agent, softening agent, filler, pigment; Preparation method's step is:
1) preparation of base polyurethane prepolymer for use as: at first make polyether glycol after dehydration certain hour under 100 ℃ of left and right vacuum, after being cooled to 40 ℃, then add a certain amount of MDI, said mixture reacts 2h under 90 ℃, namely obtain performed polymer, and wherein-NCO massfraction of metering;
2) preparation of environment-protecting polyurethane plastic cement: the performed polymer that will prepare, chainextender mix in rational ratio, vacuum outgas 1h again after being heated to 100 ℃, after being cooled to 80 ℃, add softening agent, filler, anti-aging agent, pigment etc. to stir, grind again, and vacuum outgas 0.5h, seal up for safekeeping, namely prepare polyurethane plastic.
In a preferred embodiment of the present invention, described polyether glycol is at least a in polyether glycol A, polyether glycol B, polyether glycol C.
In a preferred embodiment of the present invention, the molecular weight of described polyether glycol A is 2000, and hydroxyl value is 54.5~57.5mg KOH/g; The molecular weight of described polyether glycol B is 5000, and hydroxyl value is 32~35mg KOH/g; The molecular weight of described polyether glycol C is 4000, and hydroxyl value is 26.5~29.5mg KOH/g.
In a preferred embodiment of the present invention, described urethane vulcanizing agent is 3,3 '-two chloro-, 4,4 ' diaminodiphenylmethane.
In a preferred embodiment of the present invention, described rational ratio is 60~80:30.
In a preferred embodiment of the present invention, the described vacuum hydro-extraction time is 1~1.5h.
In a preferred embodiment of the present invention, described MDI is liquefied mdi, and add-on is 50~60g.
According to the performance of the environment-protecting polyurethane plastic cement of foregoing invention preparation be:
Have no irritating odor; Shao A hardness 55; Tensile strength 4.0Mpa; Tear strength 25kNm
-1Elongation 450%; Rebound degree 42%.
The invention has the beneficial effects as follows: a kind of runway of the present invention, with the preparation method of environment-protecting polyurethane plastic cement, has the preparation method simple, easy handling, and the plasthetics over-all properties of preparation is better, has advantages of nontoxic, tasteless, environmental protection.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made more explicit defining.
The embodiment of the present invention comprises:
Embodiment 1
Add 80g polyether glycol A in the there-necked flask with heating, thermometer and reflux condensing tube, 20g polyether glycol B, 5g polyether glycol C, 1h dewaters under 100 ℃ of left and right vacuum, after being cooled to 40 ℃, then add the 50g liquefied mdi, said mixture reacts 2h under 90 ℃, namely obtain performed polymer, and wherein-NCO massfraction of metering;
The performed polymer of preparation, chainextender are mixed in the ratio of 60:30, vacuum outgas 1h again after being heated to 100 ℃, after being cooled to 80 ℃, add 50g softening agent clorafin 25,120g kaolin, 0.15g anti-aging agent UV-9,3g pigment to stir, grind again, and vacuum outgas 0.5h, seal up for safekeeping, namely prepare polyurethane plastic.
Embodiment 2
Add 100g polyether glycol A in the there-necked flask with heating, thermometer and reflux condensing tube, 30g polyether glycol B, 10g polyether glycol C, 1.5h dewaters under 100 ℃ of left and right vacuum, after being cooled to 40 ℃, then add the 60g liquefied mdi, said mixture reacts 2h under 90 ℃, namely obtain performed polymer, and wherein-NCO massfraction of metering;
The performed polymer of preparation, chainextender are mixed in the ratio of 80:30, vacuum outgas 1h again after being heated to 100 ℃, after being cooled to 80 ℃, add 60g softening agent clorafin 25,140g kaolin, 0.15g anti-aging agent UV-9,5g pigment to stir, grind again, and vacuum outgas 0.5h, seal up for safekeeping, namely prepare polyurethane plastic.
The performance of the environment-protecting polyurethane plastic cement of preparation is:
Have no irritating odor; Shao A hardness 55; Tensile strength 4.0Mpa; Tear strength 25kNm
-1Elongation 450%; Rebound degree 42%.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in scope of patent protection of the present invention.
Claims (7)
1. the preparation method of a runway use environment-protecting polyurethane plastic cement, is characterized in that, component comprises: polyether glycol, isocyanic ester, MDI, urethane vulcanizing agent, softening agent, filler, pigment; Preparation method's step is:
1) preparation of base polyurethane prepolymer for use as: at first make polyether glycol after dehydration certain hour under 100 ℃ of left and right vacuum, after being cooled to 40 ℃, then add a certain amount of MDI, said mixture reacts 2h under 90 ℃, namely obtain performed polymer, and wherein-NCO massfraction of metering;
2) preparation of environment-protecting polyurethane plastic cement: the performed polymer that will prepare, chainextender mix in rational ratio, vacuum outgas 1h again after being heated to 100 ℃, after being cooled to 80 ℃, add softening agent, filler, anti-aging agent, pigment etc. to stir, grind again, and vacuum outgas 0.5h, seal up for safekeeping, namely prepare polyurethane plastic.
2. runway according to claim 1, with the preparation method of environment-protecting polyurethane plastic cement, is characterized in that, described polyether glycol is at least a in polyether glycol A, polyether glycol B, polyether glycol C.
3. runway according to claim 2, with the preparation method of environment-protecting polyurethane plastic cement, is characterized in that, the molecular weight of described polyether glycol A is 2000, and hydroxyl value is 54.5~57.5mg KOH/g; The molecular weight of described polyether glycol B is 5000, and hydroxyl value is 32~35mg KOH/g; The molecular weight of described polyether glycol C is 4000, and hydroxyl value is 26.5~29.5mg KOH/g.
4. runway according to claim 1, with the preparation method of environment-protecting polyurethane plastic cement, is characterized in that, described urethane vulcanizing agent is 3,3 '-two chloro-, 4,4 ' diaminodiphenylmethane.
5. runway according to claim 1, with the preparation method of environment-protecting polyurethane plastic cement, is characterized in that, described rational ratio is 60~80:30.
6. runway according to claim 1, with the preparation method of environment-protecting polyurethane plastic cement, is characterized in that, the described vacuum hydro-extraction time is 1~1.5h.
7. runway according to claim 1, with the preparation method of environment-protecting polyurethane plastic cement, is characterized in that, described MDI is liquefied mdi, and add-on is 50~60g.