CN103382338A - 外墙用抗老化乳胶涂料及其制备方法 - Google Patents
外墙用抗老化乳胶涂料及其制备方法 Download PDFInfo
- Publication number
- CN103382338A CN103382338A CN2013102703810A CN201310270381A CN103382338A CN 103382338 A CN103382338 A CN 103382338A CN 2013102703810 A CN2013102703810 A CN 2013102703810A CN 201310270381 A CN201310270381 A CN 201310270381A CN 103382338 A CN103382338 A CN 103382338A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- exterior wall
- latex coating
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及一种外墙用抗老化乳胶涂料及其制备方法,该涂料以质量份计含有以下成分:纯丙乳液30~40份、钛白粉12~18份、重质碳酸钙7~12份、高岭土6~10份、氯化石蜡0.1~0.2份、三聚磷酸钾0.5~1份、丙二醇单油酸盐1.5~3.7份、消泡剂0.05~0.2份、纤维素0.005~0.015份、增韧剂0.15~0.4份、水23~30份。本发明提供的外墙用抗老化乳胶涂料,其耐候性、耐水性、耐碱性和韧性都很高,并且制备方法简单,施工方便。
Description
技术领域
本发明涉及一种外墙涂料及其制备方法,尤其涉及一种外墙用抗老化乳胶涂料及其制备方法。
背景技术
外墙涂料主要是装饰和保护建筑物的外墙面,使建筑物外貌整洁美观,从而达到美化城市环境的目的。同时能够起到保护建筑物外墙壁的作用,延长使用时间,从而获得良好的装饰和保护效果。市场上外墙涂料的种类有很多,其普遍具有装饰性好、耐候性好、耐沾污性好、耐水性好、耐碱性好等有点,但也存在着一些不足。例如耐洗刷次数不高,长时间使用后涂料表面容易脱落;人工老化时间不够长,使得涂料使用时间变短;韧性不强,涂层容易被破坏。
发明内容
解决的技术问题:针对上述外墙涂料的耐洗刷性、人工老化时间以及韧性存在的不足,本发明提供一种外墙用抗老化乳胶涂料及其制备方法。
技术方案:外墙用抗老化乳胶涂料,以质量份计含有以下成分:
纯丙乳液 30~40份
钛白粉 12~18份
重质碳酸钙 7~12份
高岭土 6~10份
氯化石蜡 0.1~0.2份
三聚磷酸钾 0.5~1份
丙二醇单油酸盐 1.5~3.7份
消泡剂 0.05~0.2份
纤维素 0.005~0.015份
增韧剂 0.15~0.4份
水 23~30份。
上述所述的外墙用抗老化乳胶涂料,以质量份计含有以下成分:
纯丙乳液 32~36份
钛白粉 13~16份
重质碳酸钙 10~12份
高岭土 7~9份
氯化石蜡 0.13~0.15份
三聚磷酸钾 0.7~0.9份
丙二醇单油酸盐 2~3份
消泡剂 0.1~0.15份
纤维素 0.01~0.013份
增韧剂 0.27~0.33份
水 25~29份。
上述所述的重质碳酸钙的细度为1200目。
上述所述的外墙用抗老化乳胶涂料的制备步骤如下:
(1) 在搪瓷桶内加入纯丙乳液,然后加入氯化石蜡、三聚磷酸钾、丙二醇单油酸盐、消泡剂、增韧剂和水,在常温下搅拌0.5~1h;
(2) 再加入钛白粉、重质碳酸钙和高岭土,继续搅拌,然后进行研磨;
(3) 最后加入纤维素,搅拌均匀后过滤出料,得到外墙用抗老化乳胶涂料。
有益效果:本发明提供的外墙用抗老化乳胶涂料及其制备方法,该涂料的耐候性、耐水性、耐碱性和韧性都很高,耐洗刷次数≥3300次,人工老化时间≥1200h,耐碱120h无异常,耐水200h无异常,并且制备方法简单,施工方便。
具体实施方式
实施例1
本实施例提供一种外墙用抗老化乳胶涂料,以质量份计含有以下成分:
纯丙乳液 40份
钛白粉 18份
重质碳酸钙 12份
高岭土 10份
氯化石蜡 0.2份
三聚磷酸钾 1份
丙二醇单油酸盐 3.7份
消泡剂 0.2份
纤维素 0.015份
增韧剂 0.4份
水 30份。
外墙用抗老化乳胶涂料的制备步骤如下:
(1) 在搪瓷桶内加入纯丙乳液,然后加入氯化石蜡、三聚磷酸钾、丙二醇单油酸盐、消泡剂、增韧剂和水,在常温下搅拌0.5~1h;
(2) 再加入钛白粉、重质碳酸钙和高岭土,继续搅拌,然后进行研磨;
(3) 最后加入纤维素,搅拌均匀后过滤出料,得到外墙用抗老化乳胶涂料。
实施例2
本实施例提供一种外墙用抗老化乳胶涂料,以质量份计含有以下成分:
纯丙乳液 32份
钛白粉 13份
重质碳酸钙 10份
高岭土 7份
氯化石蜡 0.13份
三聚磷酸钾 0.7份
丙二醇单油酸盐 2份
消泡剂 0.1份
纤维素 0.01份
增韧剂 0.27份
水 25份。
外墙用抗老化乳胶涂料的制备步骤如下:
(1) 在搪瓷桶内加入纯丙乳液,然后加入氯化石蜡、三聚磷酸钾、丙二醇单油酸盐、消泡剂、增韧剂和水,在常温下搅拌0.5~1h;
(2) 再加入钛白粉、重质碳酸钙和高岭土,继续搅拌,然后进行研磨;
(3) 最后加入纤维素,搅拌均匀后过滤出料,得到外墙用抗老化乳胶涂料。
实施例3
本实施例提供一种外墙用抗老化乳胶涂料,以质量份计含有以下成分:
纯丙乳液 36份
钛白粉 16份
重质碳酸钙 12份
高岭土 9份
氯化石蜡 0.15份
三聚磷酸钾 0.9份
丙二醇单油酸盐 3份
消泡剂 0.15份
纤维素 0.013份
增韧剂 0.33份
水 29份。
外墙用抗老化乳胶涂料的制备步骤如下:
(1) 在搪瓷桶内加入纯丙乳液,然后加入氯化石蜡、三聚磷酸钾、丙二醇单油酸盐、消泡剂、增韧剂和水,在常温下搅拌0.5~1h;
(2) 再加入钛白粉、重质碳酸钙和高岭土,继续搅拌,然后进行研磨;
(3) 最后加入纤维素,搅拌均匀后过滤出料,得到外墙用抗老化乳胶涂料。
实施例4
本实施例提供一种外墙用抗老化乳胶涂料,以质量份计含有以下成分:
纯丙乳液 34份
钛白粉 15份
重质碳酸钙 11份
高岭土 8份
氯化石蜡 0.14份
三聚磷酸钾 0.7份
丙二醇单油酸盐 2.6份
消泡剂 0.13份
纤维素 0.012份
增韧剂 0.3份
水 27份。
外墙用抗老化乳胶涂料的制备步骤如下:
(1) 在搪瓷桶内加入纯丙乳液,然后加入氯化石蜡、三聚磷酸钾、丙二醇单油酸盐、消泡剂、增韧剂和水,在常温下搅拌0.5~1h;
(2) 再加入钛白粉、重质碳酸钙和高岭土,继续搅拌,然后进行研磨;
(3) 最后加入纤维素,搅拌均匀后过滤出料,得到外墙用抗老化乳胶涂料。
上述述实施例1~实施例4的外墙用抗老化乳胶涂料的技术性能指标,其检测结果如下:
检测结果
以上对本发明实施例所提供的外墙用抗老化乳胶涂料及其制备方法进行了详细介绍,对于本领域的一般技术人员,依据本发明实施例的思想,在具体实施方式及应用范围上均会有改变之处,综上所述,本说明书内容不应理解为对本发明的限制。
Claims (4)
1.外墙用抗老化乳胶涂料,其特征在于以质量份计含有以下成分:
纯丙乳液 30~40份
钛白粉 12~18份
重质碳酸钙 7~12份
高岭土 6~10份
氯化石蜡 0.1~0.2份
三聚磷酸钾 0.5~1份
丙二醇单油酸盐 1.5~3.7份
消泡剂 0.05~0.2份
纤维素 0.005~0.015份
增韧剂 0.15~0.4份
水 23~30份。
2.根据权利要求1所述的外墙用抗老化乳胶涂料,其特征在于以质量份计含有以下成分:
纯丙乳液 32~36份
钛白粉 13~16份
重质碳酸钙 10~12份
高岭土 7~9份
氯化石蜡 0.13~0.15份
三聚磷酸钾 0.7~0.9份
丙二醇单油酸盐 2~3份
消泡剂 0.1~0.15份
纤维素 0.01~0.013份
增韧剂 0.27~0.33份
水 25~29份。
3.根据权利要求1所述的外墙用抗老化乳胶涂料,其特征在于所述重质碳酸钙的细度为1200目。
4.如权利要求1所述的外墙用抗老化乳胶涂料的制备方法,其特征在于该方法的制备步骤如下:
(1)在搪瓷桶内加入纯丙乳液,然后加入氯化石蜡、三聚磷酸钾、丙二醇单油酸盐、消泡剂、增韧剂和水,在常温下搅拌0.5~1h;
(2)再加入钛白粉、重质碳酸钙和高岭土,继续搅拌,然后进行研磨;
(3)最后加入纤维素,搅拌均匀后过滤出料,得到外墙用抗老化乳胶涂料。