CN103352374B - 透气性好的高档运动鞋用面料及其制备方法 - Google Patents
透气性好的高档运动鞋用面料及其制备方法 Download PDFInfo
- Publication number
- CN103352374B CN103352374B CN201310276766.8A CN201310276766A CN103352374B CN 103352374 B CN103352374 B CN 103352374B CN 201310276766 A CN201310276766 A CN 201310276766A CN 103352374 B CN103352374 B CN 103352374B
- Authority
- CN
- China
- Prior art keywords
- upper strata
- minute
- morpholine
- polyvinyl chloride
- sport footwear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种透气性好的高档运动鞋用面料,其特征在于由二层复合构成,基材是布,上层为PVC树脂层,上层由下列重量份的原料制成:SG-4型PVC树脂70-80、二异丙醇胺1-2、吗啉1-2、耐冲击性聚苯乙烯4-5、二月桂酸二丁基锡2-3、氧化锌2-3、氧化镁1-2、氧化铝2-3、硫酸钡5-7、甲基三乙氧基硅烷2-3、乙烯基三乙氧基硅烷1-2、异氰脲酸三缩水甘油酯5-7、二盐基亚磷酸铅1-2、一缩二乙二醇苯甲酸酯2-3、古马隆1-2、2-乙氨基十七烯基咪唑啉1-2、蛋白质粉10-12、聚乙烯醇2-3、改性粘土粉末3-4本发明通过配方与工艺改进,蛋白质增加合成革的透气性,耐冲击性聚苯乙烯增加了合成革的韧性与强度,具有类似于天然皮革所具有的自然舒适手感;3-5年不容易破损或撕裂损坏,适合于作为运动鞋面料。
Description
技术领域
本发明属于一种化学合成革面料加工技术领域,具体是一种聚氯乙烯合成革及其制备方法。
背景技术
聚氯乙烯合成革具有的耐水解、耐磨、耐刮、阻燃等优势,广泛用于高档运动鞋、箱包、沙发等方面,但其在柔软性、透气性、手感、耐曲折等诸方面仍有许多不足,需要对其配方与工艺进行改进。
发明内容
本发明的目的在于提供一种透气性好的高档运动鞋用面料及其制备方法,生产的合成革产品质量好。
本发明的目的可以通过以下技术方案实现:
一种透气性好的高档运动鞋用面料,其特征在于由二层复合构成,基材是布,上层为PVC树脂层,上层由下列重量份的原料制成:
SG-4型PVC树脂70-80、二异丙醇胺1-2、吗啉1-2、耐冲击性聚苯乙烯4-5、二月桂酸二丁基锡2-3、氧化锌2-3、氧化镁1-2、氧化铝2-3、硫酸钡5-7、甲基三乙氧基硅烷2-3、乙烯基三乙氧基硅烷1-2、异氰脲酸三缩水甘油酯5-7、二盐基亚磷酸铅1-2、一缩二乙二醇苯甲酸酯2-3、古马隆1-2、2-乙氨基十七烯基咪唑啉1-2、蛋白质粉10-12、聚乙烯醇2-3、改性粘土粉末3-4;
所述的改性粘土粉末通过以下方法制得:
将粘土放入460-480℃下煅烧3-4小时,取出,冷却,研成粉末;再加入相当于粘土粉末重量5-8%的氮化铝、3-4%的三聚磷酸钠、2-3%的玫瑰精油、2-3%的吗啉、3-4%的二正辛基-4-异噻唑啉-3-酮,混合搅拌30-40分钟,然后再喷入相当于粘土粉末重量3-5%的硅烷偶联剂KH550,在13000-16000转/分下搅拌60-70分钟,即得。
所述的透气性好的高档运动鞋用面料的制备方法,其特征在于包括以下步骤:
A)将二异丙醇胺、吗啉、耐冲击性聚苯乙烯、二月桂酸二丁基锡、氧化锌、氧化镁、氧化铝、硫酸钡、甲基三乙氧基硅烷、乙烯基三乙氧基硅烷、异氰脲酸三缩水甘油酯、二盐基亚磷酸铅,在135-150℃下搅拌10-15分钟,然后,降温100-105℃,加入其它剩余原料,高速混合5-8分钟,然后,下料到开炼机进行充分混炼后到胶布机进行贴合,将上层贴到基材上;
B)产品经表面效果处理;
C)成品检验合格,出厂。
本发明通过配方与工艺改进,蛋白质增加合成革的透气性,耐冲击性聚苯乙烯增加了合成革的韧性与强度,具有类似于天然皮革所具有的自然舒适手感;3-5年不容易破损或撕裂损坏,适合于作为运动鞋面料。
具体实施方式
一种透气性好的高档运动鞋用面料,由二层复合构成,基材是布,上层为PVC树脂层,上层由下列重量份(公斤)的原料制成:
SG-4型PVC树脂70、二异丙醇胺2、吗啉1、耐冲击性聚苯乙烯5、二月桂酸二丁基锡2、氧化锌2、氧化镁1、氧化铝2、硫酸钡7、甲基三乙氧基硅烷2、乙烯基三乙氧基硅烷1、异氰脲酸三缩水甘油酯5、二盐基亚磷酸铅2、一缩二乙二醇苯甲酸酯3、古马隆1、2-乙氨基十七烯基咪唑啉1、蛋白质粉12、聚乙烯醇2、改性粘土粉末4;
所述的透气性好的高档运动鞋用面料的制备方法,包括以下步骤:
A)将二异丙醇胺、吗啉、耐冲击性聚苯乙烯、二月桂酸二丁基锡、氧化锌、氧化镁、氧化铝、硫酸钡、甲基三乙氧基硅烷、乙烯基三乙氧基硅烷、异氰脲酸三缩水甘油酯、二盐基亚磷酸铅,在135-150℃下搅拌10-15分钟,然后,降温100-105℃,加入其它剩余原料,高速混合5-8分钟,然后,下料到开炼机进行充分混炼后到胶布机进行贴合,将上层贴到基材上;
B)产品经表面效果处理;
C)成品检验合格,出厂。
所述的改性粘土粉末通过以下方法制得:
将粘土放入460-480℃下煅烧4小时,取出,冷却,研成粉末;再加入相当于粘土粉末重量5%的氮化铝、3%的三聚磷酸钠、2%的玫瑰精油、3%的吗啉、3%的二正辛基-4-异噻唑啉-3-酮,混合搅拌30-40分钟,然后再喷入相当于粘土粉末重量3%的硅烷偶联剂KH550,在13000-16000转/分下搅拌60-70分钟,即得。
本发明合成革检测:径向拉断强度/纬向拉断强度〉435N/3CM,径/纬向撕裂强度〉29N,-10℃低温曲挠性可达到耐曲折3万次,老化试验不开裂。透气性良好。
Claims (2)
1.一种透气性好的高档运动鞋用面料,其特征在于由二层复合构成,基材是布,上层为PVC树脂层,上层由下列重量份的原料制成:SG-4型PVC树脂70-80、二异丙醇胺1-2、吗啉1-2、耐冲击性聚苯乙烯4-5、二月桂酸二丁基锡2-3、氧化锌2-3、氧化镁1-2、氧化铝2-3、硫酸钡5-7、甲基三乙氧基硅烷2-3、乙烯基三乙氧基硅烷1-2、异氰脲酸三缩水甘油酯5-7、二盐基亚磷酸铅1-2、一缩二乙二醇苯甲酸酯2-3、古马隆1-2、2-乙氨基十七烯基咪唑啉1-2、蛋白质粉10-12、聚乙烯醇2-3、改性粘土粉末3-4;所述的改性粘土粉末通过以下方法制得:将粘土放入460-480℃下煅烧3-4小时,取出,冷却,研成粉末;再加入相当于粘土粉末重量5-8%的氮化铝、3-4%的三聚磷酸钠、2-3%的玫瑰精油、2-3%的吗啉、3-4%的2-正辛基-4-异噻唑啉-3-酮,混合搅拌30-40分钟,然后再喷入相当于粘土粉末重量3-5%的硅烷偶联剂KH550,在13000-16000转/分下搅拌60-70分钟,即得。
2. 根据权利要求1所述的透气性好的高档运动鞋用面料的制备方法,其特征在于包括以下步骤:
A)将二异丙醇胺、吗啉、耐冲击性聚苯乙烯、二月桂酸二丁基锡、氧化锌、氧化镁、氧化铝、硫酸钡、甲基三乙氧基硅烷、乙烯基三乙氧基硅烷、异氰脲酸三缩水甘油酯、二盐基亚磷酸铅,在135-150℃下搅拌10-15分钟,然后,降温100-105℃,加入其它剩余原料,高速混合5-8分钟,然后,下料到开炼机进行充分混炼后到胶布机进行贴合,将上层贴到基材上;
B)产品经表面效果处理;
C)成品检验合格,出厂。