CN103352179B - 一种含碳合金 - Google Patents
一种含碳合金 Download PDFInfo
- Publication number
- CN103352179B CN103352179B CN201310256376.4A CN201310256376A CN103352179B CN 103352179 B CN103352179 B CN 103352179B CN 201310256376 A CN201310256376 A CN 201310256376A CN 103352179 B CN103352179 B CN 103352179B
- Authority
- CN
- China
- Prior art keywords
- phosphorus
- containing alloy
- present
- alloy
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种碳合金,所述碳合金的组成为(以重量%计):0.25%至0.29%的碳;0.10%至1.20%的锰;0.09%至0.13%的磷;0.10%至0.19%的硫;0.60%至1.00%的硅;≤0.09%的铝;≤0.01%的氮;0.45%至0.83%的碲;0.04%至0.07%的铌;≤0.50%的铜;0.05%至0.60%的镍;0.2%至2.00%的钼;0.2%至0.4%的钒;0.0030%至0.0065%的锑;0.010%至0.050%的钛:其余为铁和不可避免的杂质。本发明所述的碳合金具有增强的洛氏硬度,可以广泛用于生产。
Description
技术领域
本发明涉及金属领域,具体地说,涉及一种含碳合金。
背景技术
含碳合金是应用最多的合金,广泛用于碳钢和铸铁。但是由于目前对于合金的要求越来越高,目前的一些合金已经满足不了要求。
发明内容
本发明的目的是提供一种含碳合金。
为了实现本发明的目的,本发明提供一种含碳合金,所述含碳合金的组成为(以重量%计):
0.25%至0.29%的碳;
0.10%至1.20%的锰;
0.09%至0.13%的磷;
0.10%至0.19%的硫;
0.60%至1.00%的硅;
≤0.09%的铝;
≤0.01%的氮;
0.45%至0.83%的碲;
0.04%至0.07%的铌;
≤0.50%的铜;
0.05%至0.60%的镍;
0.2%至2.00%的钼;
0.2%至0.4%的钒;
0.0030%至0.0065%的锑;
0.010%至0.050%的钛:
其余为铁和不可避免的杂质。
优选地,所述含碳合金的组成为(以重量%计):
0.28%的碳;
1.0%的锰;
0.13%的磷;
0.17%的硫;
1.00%的硅;
0.06%的铝;
0.01%的氮;
0.61%的碲;
0.05%的铌;
0.40%的铜;
0.40%的镍;
1.00%的钼;
0.2%的钒;
0.0055%的锑;
0.040%的钛:
其余为铁和不可避免的杂质。
本发明所述的合金具有增强的洛氏硬度,可以广泛用于生产。
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明,但这并非是对本发明的限制,本领域技术人员根据本发明的基本思想,可以做出各种修改或改进,但是只要不脱离本发明的基本思想,均在本发明的范围之内。
实施例1合金的制备
含碳合金的组成为(以重量%计):
0.28%的碳;
1.0%的锰;
0.13%的磷;
0.17%的硫;
1.00%的硅;
0.06%的铝;
0.01%的氮;
0.61%的碲;
0.05%的铌;
0.40%的铜;
0.40%的镍;
1.00%的钼;
0.2%的钒;
0.0055%的锑;
0.040%的钛:
其余为铁和不可避免的杂质。
将具有上述成分组成的30kg钢料在高频真空熔炉中熔融,随后进行浇铸,在该浇铸中冷却速度为1.2℃/min以形成锭料。将锭料在950℃下保持10小时,然后在500℃下保持90分钟。此后使用500吨锤式锻造机进行热锻,这样制得含碳合金1。
实施例2含碳合金的制备
按照和实施例1相同的方式制备含碳合金2,不同之处在于不使用钼。
实施例3含碳合金的制备
按照和实施例1相同的方式制备含碳合金3,不同之处在于不使用锑。
实施例4含碳合金的制备
按照和实施例1相同的方式制备含碳合金4,不同之处在于不使用镍。
实验例1
根据GB/T230.1-2009来测定含碳合金1-4的洛氏硬度。结果如下:含碳合金1的洛氏硬度为91HRC,含碳合金2的洛氏硬度为58HRC,含碳合金3的洛氏硬度为61HRC,含碳合金4的洛氏硬度为62HRC。
实验例2
根据GB/T228-2002测定抗拉强度。结果如下:含碳合金1的抗拉强度Rm为879兆帕,含碳合金2的抗拉强度Rm为611兆帕,含碳合金3的抗拉强度Rm为581兆帕,含碳合金4的抗拉强度Rm为602兆帕。
Claims (1)
1.一种根据GB/T230.1-2009洛氏硬度为91HRC和根据GB/T228-2002抗拉强度Rm为879兆帕的含碳合金,其特征在于,所述含碳合金以重量%计组成为:
0.28%的碳;
1.0%的锰;
0.13%的磷;
0.17%的硫;
1.00%的硅;
0.06%的铝;
0.01%的氮;
0.61%的碲;
0.05%的铌;
0.40%的铜;
0.40%的镍;
1.00%的钼;
0.2%的钒;
0.0055%的锑;
0.040%的钛:
其余为铁和不可避免的杂质。