CN103351719A - 一种纳米溶剂型有机黄色色浆的制备方法 - Google Patents
一种纳米溶剂型有机黄色色浆的制备方法 Download PDFInfo
- Publication number
- CN103351719A CN103351719A CN2013102677619A CN201310267761A CN103351719A CN 103351719 A CN103351719 A CN 103351719A CN 2013102677619 A CN2013102677619 A CN 2013102677619A CN 201310267761 A CN201310267761 A CN 201310267761A CN 103351719 A CN103351719 A CN 103351719A
- Authority
- CN
- China
- Prior art keywords
- solvent
- organic yellow
- disperbyk
- mill base
- nanometer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及一种纳米溶剂型有机黄色色浆的制备方法,其基本配方是:CAB树脂8%~20%、润湿分散剂8%~16%、有机黄色颜料10%~25%、消泡剂0.2%~1%、溶剂50%~75%;所述的溶剂型纳米有机黄色色浆的粒径D50控制在70~200nm之间。该纳米黄色色浆具有贮存稳定性佳、着色力高、透明性高、相容性好等特点,能代替金属络合染料。广泛用于儿童玩具、家具、皮革布料制品、塑料制品、金属制品、金属卷材、铝箔膜及电镀胶膜、烟包、糖果、食品、卡纸等包装材料表面的涂饰着色剂,也可作为烫金膜、玻璃制品、高档金属烤漆、塑料烤漆、UV真空镀膜涂料的透明着色剂,以及打印油墨和喷绘等着色剂。
Description
技术领域
本发明涉及一种纳米溶剂型有机黄色色浆的制备方法,尤其涉及一种多用途、透明性、能代替金属络合黄色染料的纳米有机黄色色浆。
背景技术
目前儿童玩具、皮革制品、家具、印刷制品、打印油墨或喷绘等大多采用染料或金属络合染料,大多数染料存在诸如重金属严重超标、含有致病物质、耐温性、耐晒性、耐迁移性差,不能满足人们对健康生活质量的追求;许多制品对涂装要求高透明、高性能、环保等,标准要求越来越高,普通的颜料色浆透明性都不符合技术要求。因此开发一种环保、透明、高性能能代替金属络合黄色染料的纳米有机黄色色浆尤其必要。
发明内容
本发明是选用醋酸丁酸纤维素(简称CAB)作为分散树脂,醋酸丁酸纤维素在涂料上有着广泛的应用:在铝、铜、银以及其它金属涂料中加入CAB,可加速溶剂从漆膜中的释放,触干时间可以大幅缩短;作为流平剂,可以改善流平性,减少缩孔,在热塑性丙烯酸型的气干漆涂料中,这种性能更为突出;由于CAB含有羟基,它能在酸催化剂存在下与氨基树脂反应,既不影响本身硬度,又赋予涂膜以柔韧性,且这种清漆具有良好的附着力、光泽性和保光性,使CAB/氨基树脂交联既有交联涂料的特性,又有气干漆的干燥速度;CAB在热再流型涂料中使漆膜再流平,使涂层具有极高的光泽,避免所必需的抛光作业;在木材涂料中,可避免潮湿而引起木材膨胀或翘起;在塑料涂料中,加入CAB能增强耐磨性、颜色稳定性,增加韧性;在汽车的罩光清漆中,加入CAB,可 以使罩面清漆涂上后,避免溶剂穿透到底层,而使汽车漆光亮美观;CAB在汽车修补漆体系中,能缩短干燥时间,提高抗冷裂性,并具有良好的抛光性能;在皮革涂料、紫外光固化涂料中也有着广泛的应用,CAB本身可用于制作透明美观的塑料器具,也可用于制作可剥材料,因此选取CAB作为纳米有机黄色色浆的分散树脂通用性宽、应用性广。
纳米色浆对分散剂的要求高,对色浆稳定性、适用性起很重要的因素。因此本发明是选用含有颜料亲和基团的嵌段高分子共聚物作为分散剂,尤其选用受控自由基合成(CPT)的高分子分散剂,如DISPERBYK-2163、DISPERBYK-2164、DISPERBYK-2000、DISPERBYK-2001、DISPERBYK-2020、DISPERBYK-2022、DISPERBYK-2025、DISPERBYK-2150、 等,该类分散剂具有颜料的吸附部分和在溶媒中伸展部分,吸附牢固度强,吸附层厚度大,因而具有良好的空间位阻效。因此制成的纳米色浆具有贮存稳定性佳、着色力高、透明性高、相容性好等特点。
为了解决上面所述的技术问题,本发明采取以下技术方案:本发明涉及一种纳米溶剂型有机黄色色浆,其基本配方是:CAB树脂8%~20%、润湿分散剂8%~16%、有机黄色颜料10%~25%、消泡剂0.2%~1%、溶剂50%~75%;制成的纳米有机黄色色浆的粒径D50控制在70~200nm之间。
其中,CAB树脂选用含丁酰基38%的醋酸丁酸纤维素树脂的一种。
润湿分散剂选用含有颜料亲和基团的嵌段高分子共聚物,尤其选用受控自由基合成(CPT)的高分子分散剂,如DISPERBYK-2163、DISPERBYK-2164、DISPERBYK-2000、DISPERBYK-2001、DISPERBYK-2015、DISPERBYK-2020、DISPERBYK-2022、DISPERBYK-2025、 DISPERBYK-2150、的一种或其组合。
有机黄色颜料选用C.I.P.Y.13、C.I.P.Y.74、C.I.P.Y.81、C.I.P.Y.83、C.I.P.Y.97、C.I.P.Y.110、C.I.P.Y.138、C.I.P.Y.139、C.I.P.Y.151、C.I.P.Y.154、C.I.P.Y.180、C.I.P.Y.181、C.I.P.Y.183、C.I.P.Y.191的一种。
溶剂选取用甲乙酮、醋酸丁酯、丙二醇甲醚醋酸酯、二7二醇丁醚醋酸酯、丙酮、正丁醇和甲戊酮的一种或几种的组合。
本发明提出一种纳米溶剂型有机黄色色浆的制备方法,制备工艺如下:按配方重量比计加入溶剂、CAB、润湿分散剂,在高速分散机中以500r/min的速度搅拌均匀,然后在1000~1200r/min的高速下加入有机黄色颜料粉,高速分散45~60min,再到纳米分散机循环研磨8~12h,每隔0.5h用激光粒度仪进行粒度检测,直到色浆的粒径达到要求,过滤包装得到纳米溶剂型有机黄色色浆。
本发明制成的纳米溶剂型有机黄色色浆贮存稳定性佳、着色力高、透明性、相容性好等特点,具有高性能、不含苯和重金属,多用途,能代替金属络合染料。广泛用于儿童玩具(木制、五金、塑料制品)、木器家具、皮革制品表面的涂饰着色剂,塑料制品、金属制品表面的涂饰着色剂(如手机、家电、化妆品包装瓶等),金属卷材、铝箔膜及电镀胶膜表面的涂饰着色剂,烟包、糖果、食品、卡纸等包装材料表面的涂饰着色剂,烫金膜、皮革布料等热转印产品表面的涂饰着色剂(包括热转印油墨涂料的着色,特点:耐迁移性强。)玻璃制品涂层的透明涂饰着色剂,高档金属烤漆、塑料烤漆、汽车漆等的着色剂,UV真空镀膜涂料的透明着色剂,以及打印油墨和喷绘等着色剂。
具体实施方式
按照表1的组分配方准备材料实施。
表1:三个实施例组分配方 质量份
实施例1:
按照表1中实例1按配方重量比把溶剂MIBK、PMA和醋酸正丁酯加入分散桶中,搅拌下加入CAB-381-0.5树脂、分散剂在高速分散机中以500r/min的速度搅拌均匀,然后在1000~1200r/min的高速下加入C.I.P.Y.74中黄粉,高速分散45~60min,再到纳米分散机循环研磨8~12h,每隔0.5h用激光粒度仪进行粒度检测,直到色浆的粒径D50在70~200nm之间,过滤包装得到纳米溶剂型中黄色浆。
实施例2,实施例3制备步骤参照实施例1。
按照国家相关标准,对本发明的纳米溶剂型有机黄色色浆的性能进 行检测,测试结果如表2所示。
表2纳米溶剂型有机红色色浆基本性能测试结果
尽管本发明已作了详细说明并引证了实施例,但对于本领域的普通技术人员,显然可以按照上述说明而做出的各种方案、修改和改动,都应该包括在权利要求的范围之内。
Claims (6)
1.一种纳米溶剂型有机黄色色浆,其特征在于:以重量百分比计,包括如下组分:CAB树脂8%~20%、润湿分散剂8%~16%、有机黄色颜料10%~25%、消泡剂0.2%~1%、溶剂50%~75%;所述的溶剂型纳米有机黄色色浆的粒径D50控制在70~200nm之间。
2.如权利要求1所述的一种纳米溶剂型有机黄色色浆,其特征在于:所说的CAB树脂选用含丁酰基38%的醋酸丁酸纤维素树脂的一种。
4.如权利要求1所述的一种纳米溶剂型有机黄色色浆,其特征在于:所说的黄色颜料选用C.I.P.Y.13、C.I.P.Y.74、C.I.P.Y.81、C.I.P.Y.83、C.I.P.Y.97、C.I.P.Y.110、C.I.P.Y.138、C.I.P.Y.139、C.I.P.Y151、C.I.P.Y.154、C.I.P.Y.180、C.I.P.Y.181、C.I.P.Y.183、C.I.P.Y.191的一种。
5.如权利要求1所述的一种纳米溶剂型有机黄色色浆,其特征在于:所说的溶剂选用甲乙酮、醋酸丁酯、丙二醇甲醚醋酸酯、二乙二醇丁醚醋酸酯、丙酮、正丁醇和甲戊酮的一种或几种的组合。
6.一种如权利要求1所述的一种纳米溶剂型有机黄色色浆的制备方法,其特征在于:所述制备方法包括:按配方重量比计加入溶剂、CAB、润湿分散剂,在高速分散机中以500r/min的速度搅拌均匀,然后在1000~1200r/min的高速下加入有机黄色颜料粉,高速分散45~60min,再到纳米分散机循环研磨8~12h,每隔0.5h用激光粒度仪进行粒度检测,直到色浆的粒径达到要求,过滤包装得到纳米溶剂型有机黄色色浆。