CN103351131A - Preparation method of thermal-insulation elastic exterior wall putty - Google Patents
Preparation method of thermal-insulation elastic exterior wall putty Download PDFInfo
- Publication number
- CN103351131A CN103351131A CN 201310251170 CN201310251170A CN103351131A CN 103351131 A CN103351131 A CN 103351131A CN 201310251170 CN201310251170 CN 201310251170 CN 201310251170 A CN201310251170 A CN 201310251170A CN 103351131 A CN103351131 A CN 103351131A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- exterior wall
- putty
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of thermal-insulation elastic exterior wall putty. The exterior wall putty consists of the following components in parts by weight: 14-16 parts of white cement, 6-8 parts of fly ash, 12-14 parts of ash calcium powder, 20-24 parts of calcium carbonate powder, 11-15 parts of hollow microsphere, 2-3 parts of cellulose ether, 0.8-1.2 parts of lignocellulose, 0.2-0.4 part of starch ether and 13-17 parts of pure acrylic emulsion. The preparation method comprises the steps of adding the white cement, the fly ash, the ash calcium powder, the calcium carbonate powder and the hollow microsphere to a dispersing machine, stirring for 10-20 minutes at a rotating speed of 600-800 rpm, adding the cellulose ether, the lignocellulose, the starch ether and the pure acrylic emulsion, increasing the rotating speed to 1000-1200rpm, and stirring for 30-40 minutes. The exterior wall putty prepared by the method is excellent in thermal-insulation performance, and can maintain conventional performance of the putty.
Description
Technical field
The present invention relates to building material technical field, relate in particular to a kind of preparation method of insulated elastic exterior wall putty.
Background technology
Current, along with social progress and rapid economic development, building trade gets prosperous with every passing day, and putty for building also grows with each passing day as the use of one of material of construction.Putty is as body of wall protective layer alignment material; should have suitable cohesive strength, good anti-cracking performance, water tolerance, permeability resistance and permeability with outer wall heat insulating system; also should have the heat insulation and heat control performance in addition, in order to reduce the generation that temperature becomes the crack, and improve indoor thermal environment.At present, the building energy consumption of China accounts for about 35% of social total energy consumption, and building energy conservation has been put into one of country's ten large energy conservation projects.In order to realize the target of building energy conservation 50% and 65%, to new building and existing building prevalence " external wall insulation project technology ", emphasis is carried out EPS/XPS plate thin plastering exterior wall heat-insulation system and PS particle slurry external thermal insulation system.Through facts have proved in the past few years because above-mentioned heat-insulation system exists that seam is many, the material internal stress greatly, the deflection that causes of poor dimensional stability, thermal stresses is large, therefore, very easily causes thermal insulation dehiscence, then cause protective layer and crackle occurs.And the performance of putty has played keying action to the performance of body of wall.Flexible break resistant putty performance requriements according to regulation among the JG158-2004 " glue powder polyphenyl granule exterior wall outer heat preservation system "; wherein to reach putty membrane curved be qualified around diameter 50mm rod flawless to snappiness; and traditional powdery putty is difficult to reach this requirement; because only have when the volume of latex powder reaches 13%; the snappiness of putty could satisfy the flawless regulation around diameter 〉=50mm; after powdery putty reaches flexible standard; the putty viscosity of making is large; cause difficulty to construction; and this class powdery putty cost performance is also inadvisable; these factors have all caused traditional powdery putty to be not easy to reach flexible standard; cause body of wall protective layer cracking, so that wall insulation performance reduces.How to be prepared into a kind ofly have suitable bonding strength, the excellent elasticity of covering crackle, good water tolerance and permeability resistance, preferably outside the permeability, also have simultaneously phase-changing and temperature-regulating, temperature control and incubation and thermal insulation function concurrently, with exterior wall heat-preserving system the paste phase-change energy-storing heat preservation heat insulating elastic putty of good consistency, matching and synergetic being arranged, then is the vital task that the current urgent need of the art solves.
Summary of the invention
The object of the invention is to propose a kind of preparation method of insulated elastic exterior wall putty, the putty of the method preparation has good thermal and insulating performance, and can keep the traditional performance of putty.
A kind of preparation method of insulated elastic exterior wall putty, this bouncing putty is comprised of following component in weight part: white cement 14-16 part; Flyash 6-8 part; Ash calcium powder 12-14 part; Dicalcium powder 20-24 part; Cenosphere 11-15 part; Ether of cellulose 2-3 part; Lignocellulose 0.8-1.2 part; Starch ethers 0.2-0.4 part; Pure-acrylic emulsion 13-17 part; Described preparation method comprises: white cement, flyash, grey calcium powder, dicalcium powder, cenosphere are joined in the dispersion machine, rotating speed is 600-800 rev/min, stirred 10-20 minute, then add ether of cellulose, lignocellulose, starch ethers and pure-acrylic emulsion, improve rotating speed to 1000-1200 rev/min, stir and got final product in 30-40 minute.
The granularity of described dicalcium powder and grey calcium powder is-200 orders.
Described flyash is ash in class III, and granularity is-300 orders.
Described cenosphere is hollow glass bead or ceramic hollow microballon, and granularity is-150 orders.
Compared with prior art, the present invention has following beneficial effect:
Among the present invention, take pure-acrylic emulsion as the elasticity film forming matter, take cenosphere as the insulation filler, and add the resistance to cleavage that an amount of grey calcium powder improves putty, take dicalcium powder and flyash as mineral filler, cooperate other auxiliary agents and filler, so that putty strengthens the insulation insulation effect, improves energy-saving efficiency, the heat insulation and heat control effect is obvious, and resistance to cleavage is good, tension set is high, and physical and chemical performance is good.
Among the present invention, snappiness was good after putty solidified, and can revise the microdeformation of building and the fine cracks of metope, early stage easily sand milling, and later strength is high;
Among the present invention, putty is nontoxic, tasteless, do not fire, and raw material sources are wide, and are cheap, and preparation technology is simple, are easy to construction, good endurance.
Embodiment
Embodiment one
A kind of preparation method of insulated elastic exterior wall putty, this bouncing putty is comprised of following component in weight part: 14 parts of white cements; 8 parts in flyash; 12 parts of ash calcium powders; 24 parts of dicalcium powders; 11 parts of cenospheres; 3 parts of ether of cellulose; 0.8 part of lignocellulose; 0.4 part of starch ethers; 13 parts of pure-acrylic emulsions; Described preparation method comprises: white cement, flyash, grey calcium powder, dicalcium powder, cenosphere are joined in the dispersion machine, rotating speed is 800 rev/mins, stirred 10 minutes, then add ether of cellulose, lignocellulose, starch ethers and pure-acrylic emulsion, improve rotating speed to 1200 rev/min, stir and got final product in 30 minutes.
The granularity of described dicalcium powder and grey calcium powder is-200 orders.
Described flyash is ash in class III, and granularity is-300 orders.
Described cenosphere is hollow glass bead or ceramic hollow microballon, and granularity is-150 orders.
Embodiment two
A kind of preparation method of insulated elastic exterior wall putty, this bouncing putty is comprised of following component in weight part: 16 parts of white cements; 6 parts in flyash; 14 parts of ash calcium powders; 20 parts of dicalcium powders; 15 parts of cenospheres; 2 parts of ether of cellulose; 1.2 parts of lignocelluloses; 0.2 part of starch ethers; 17 parts of pure-acrylic emulsions; Described preparation method comprises: white cement, flyash, grey calcium powder, dicalcium powder, cenosphere are joined in the dispersion machine, rotating speed is 600 rev/mins, stirred 20 minutes, then add ether of cellulose, lignocellulose, starch ethers and pure-acrylic emulsion, improve rotating speed to 1000 rev/min, stir and got final product in 40 minutes.
The granularity of described dicalcium powder and grey calcium powder is-200 orders.
Described flyash is ash in class III, and granularity is-300 orders.
Described cenosphere is hollow glass bead or ceramic hollow microballon, and granularity is-150 orders.
Embodiment three
A kind of preparation method of insulated elastic exterior wall putty, this bouncing putty is comprised of following component in weight part: 15 parts of white cements; 7 parts in flyash; 13 parts of ash calcium powders; 22 parts of dicalcium powders; 13 parts of cenospheres; 2.5 parts of ether of cellulose; 1.0 parts of lignocelluloses; 0.3 part of starch ethers; 15 parts of pure-acrylic emulsions; Described preparation method comprises: white cement, flyash, grey calcium powder, dicalcium powder, cenosphere are joined in the dispersion machine, rotating speed is 700 rev/mins, stirred 15 minutes, then add ether of cellulose, lignocellulose, starch ethers and pure-acrylic emulsion, improve rotating speed to 1100 rev/min, stir and got final product in 35 minutes.
The granularity of described dicalcium powder and grey calcium powder is-200 orders.
Described flyash is ash in class III, and granularity is-300 orders.
Described cenosphere is hollow glass bead or ceramic hollow microballon, and granularity is-150 orders.
The above; only be the better embodiment of the present invention; but protection scope of the present invention is not limited to this; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to replacement or change according to technical scheme of the present invention and inventive concept thereof, all should be encompassed within protection scope of the present invention.
Claims (4)
1. the preparation method of an insulated elastic exterior wall putty is characterized in that, this bouncing putty is comprised of following component in weight part: white cement 14-16 part; Flyash 6-8 part; Ash calcium powder 12-14 part; Dicalcium powder 20-24 part; Cenosphere 11-15 part; Ether of cellulose 2-3 part; Lignocellulose 0.8-1.2 part; Starch ethers 0.2-0.4 part; Pure-acrylic emulsion 13-17 part; Described preparation method comprises: white cement, flyash, grey calcium powder, dicalcium powder, cenosphere are joined in the dispersion machine, rotating speed is 600-800 rev/min, stirred 10-20 minute, then add ether of cellulose, lignocellulose, starch ethers and pure-acrylic emulsion, improve rotating speed to 1000-1200 rev/min, stir and got final product in 30-40 minute.
2. the preparation method of insulated elastic exterior wall putty as claimed in claim 1 is characterized in that, the granularity of described dicalcium powder and grey calcium powder is-200 orders.
3. the preparation method of insulated elastic exterior wall putty as claimed in claim 1 is characterized in that, described flyash is ash in class III, and granularity is-300 orders.
4. the preparation method of insulated elastic exterior wall putty as claimed in claim 1 is characterized in that, described cenosphere is hollow glass bead or ceramic hollow microballon, and granularity is-150 orders.