CN103342523A - Concrete with performance improved by using BTC (bis-trichloromethyl carbonate) functional admixture - Google Patents
Concrete with performance improved by using BTC (bis-trichloromethyl carbonate) functional admixture Download PDFInfo
- Publication number
- CN103342523A CN103342523A CN2013103012646A CN201310301264A CN103342523A CN 103342523 A CN103342523 A CN 103342523A CN 2013103012646 A CN2013103012646 A CN 2013103012646A CN 201310301264 A CN201310301264 A CN 201310301264A CN 103342523 A CN103342523 A CN 103342523A
- Authority
- CN
- China
- Prior art keywords
- concrete
- parts
- btc
- admixture
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses concrete with performance improved by using a BTC (bis-trichloromethyl carbonate) functional admixture. The concrete comprises the following components in parts by mass: 200-320 parts of cement, 60-90 parts of mineral powder, 40-60 parts of fly ash, 680-780 parts of sand, 1060-1100 parts of broken stones, 3.3-4.74 parts of a concrete admixture, 1.92-2.58 parts of the BTC functional admixture and 170 parts of water. The BTC functional admixture can improve the cohesiveness of the concrete, reduce the bleeding and segregability of the concrete and enhance the fluidity of the concrete, so that the service life of a pump pipe is prolonged, the use of a cementing material in the concrete is reduced, the cost of the concrete is lowered, the workability of the concrete is improved, and the concrete is convenient to construct.
Description
Technical field
The present invention relates to the concrete that a kind of BTC of utilization functional type admixture improves performance, belong to the concrete technology field.
Background technology
At present, commerical ready-mixed concrete is the high-tech product that modern concrete is combined with modernized construction technology, in order to make commerical ready-mixed concrete stable performance, economy, cost performance height, must strictly select required starting material and optimize concrete proportioning.On the one hand because concrete company is limited by raw material qualities such as local sand, stone, be difficult in when satisfying concrete performance and reduce production costs, on the other hand since in recent years construction market and atrophy appears, competition between the commerical ready-mixed concrete company constantly aggravates, and how to reduce cost under the prerequisite that guarantees concrete quality is the challenge that each company faces.Application novel material, new technology are the good methods of dealing with problems.
Summary of the invention
Technical problem to be solved by this invention is the defective that overcomes prior art, provide a kind of BTC of utilization functional type admixture to improve the concrete of performance, it can improve concrete agglutinating value(of coal), reduce concrete bleeding and segregability, thereby strengthen the work-ing life that concrete flowability prolongs pump line, and the use of gelling material in the minimizing concrete reduces the concrete cost, improves its workability, is convenient to construction.
In order to solve the problems of the technologies described above, technical scheme of the present invention is: a kind of BTC of utilization functional type admixture improves the concrete of performance, and the mass parts of its component and each component is as follows:
Cement: 200 parts ~ 320 parts; Breeze: 60 parts ~ 90 parts;
Flyash: 40 parts ~ 60 parts; Sand: 680 parts ~ 780 parts;
Rubble: 1060 parts ~ 1100 parts; Concrete admixture: 3.3 parts ~ 4.74 parts;
BTC functional type admixture: 1.92 parts ~ 2.58 parts;
Water: 170 parts.
Further, the mass parts of its component and each component is as follows:
Cement: 215 parts; Breeze: 60 parts;
Flyash: 50 parts; Sand: 770 parts;
Rubble: 1100 parts; Concrete admixture: 4.22 parts;
BTC functional type admixture: 1.95 parts;
Water: 170 parts.
Further, described cement is P.O42.5 cement.
After having adopted technique scheme, the present invention has following beneficial effect:
1, the present invention can improve concrete workability: improved concrete agglutinating value(of coal) after adding BTC functional type admixture, the parcel of sand and rubble improves, concrete bleeding and segregability have been reduced, concrete flowability obviously improves, be convenient to pumping, and resistance is little during pumping, prolongs the work-ing life of pump line.
2, the present invention has also improved other performances of concrete simultaneously: after adding BTC functional type admixture, owing to effectively promoted the slurry volume, increased hydrated product, concrete homogeneity, water-retentivity, tensile property etc. are significantly improved, and effectively controlled bleeding, distress in concrete greatly reduces.Concrete self-compacting degree improves, and anti-permeability performance improves, and performances such as later stage freeze-thaw-, anti-carbonization are improved naturally, and the weather resistance of concrete has also improved.
3, the present invention has saved the glue material use quantity greatly, reduced production cost, the present invention is by repeatedly selecting to add BTC functional type admixture after the experiment, BTC functional type admixture is by the complexing chemical action, make cement based finely-powdered minerals material disperse cohesion again, improve concrete mortar and enrich degree, improve concrete cohesiveness; By shielding effect, suppress absorption and the swelling capacity of clay, improve the consistency of the complicated starting material of concrete and water reducer; By slackening water molecules polarity, eliminate the concrete bulla, increase microvesicle quantity, guaranteed concrete intensity and weather resistance effectively; By the lattice distortion effect, hydration reaction is accelerated, and reduces hydrated product crystal mineral quantity, improves jel product quantity, makes the reaction of secondary rubble more abundant, has greatly improved concrete grout-bone interface adhesive structure character.In a word, by the complex combination of multiple different properties functional materials, allow modern concrete can be more reliable with less gelling material production intensity, the concrete of more excellent performance, realize the tap/dip deep into of the low carbon technique of concrete and environmental protection aspect.
Embodiment
Content of the present invention is easier to be expressly understood that below according to specific embodiment, the present invention is further detailed explanation in order to make,
Embodiment one
A kind of BTC of utilization functional type admixture improves the concrete of performance, and the mass parts of its component and each component is as follows:
Cement: 200 parts; Breeze: 60 parts;
Flyash: 40 parts; Sand: 680 parts;
Rubble: 1060 parts; Concrete admixture: 3.3 parts;
BTC functional type admixture: 1.92 parts;
Water: 170 parts.
Cement can be selected P.O42.5 cement for use.
After the each component mixing that takes by weighing, drop into stirrer, stir, namely get this concrete.
The gained concrete draws it through detection and has improved concrete agglutinating value(of coal), reduce concrete bleeding and segregability, thereby strengthen the work-ing life that concrete flowability prolongs pump line, and the use of gelling material in the minimizing concrete, reduce the concrete cost, improve its workability, be convenient to construction.
Embodiment two
A kind of BTC of utilization functional type admixture improves the concrete of performance, and the mass parts of its component and each component is as follows:
Cement: 215 parts; Breeze: 60 parts;
Flyash: 50 parts; Sand: 770 parts;
Rubble: 1100 parts; Concrete admixture: 4.22 parts;
BTC functional type admixture: 1.95 parts;
Water: 170 parts.
Cement can be selected P.O42.5 cement for use.
After the each component mixing that takes by weighing, drop into stirrer, stir, namely get this concrete.
The gained concrete draws it through detection and has improved concrete agglutinating value(of coal), reduce concrete bleeding and segregability, thereby strengthen the work-ing life that concrete flowability prolongs pump line, and the use of gelling material in the minimizing concrete, reduce the concrete cost, improve its workability, be convenient to construction.
Embodiment three
A kind of BTC of utilization functional type admixture improves the concrete of performance, and the mass parts of its component and each component is as follows:
Cement: 320 parts; Breeze: 90 parts;
Flyash: 60 parts; Sand: 780 parts;
Rubble: 1100 parts; Concrete admixture: 4.74 parts;
BTC functional type admixture: 2.58 parts;
Water: 170 parts.
Cement can be selected P.O42.5 cement for use.
After the each component mixing that takes by weighing, drop into stirrer, stir, namely get this concrete.
The gained concrete draws it through detection and has improved concrete agglutinating value(of coal), reduce concrete bleeding and segregability, thereby strengthen the work-ing life that concrete flowability prolongs pump line, and the use of gelling material in the minimizing concrete, reduce the concrete cost, improve its workability, be convenient to construction.
Above-mentioned three embodiment, the value of having got three scopes in upper, middle and lower of each component weight part respectively prepares, can draw the preparation repeatedly through the staff, the gained concrete can improve concrete agglutinating value(of coal), reduce concrete bleeding and segregability, thereby strengthen the work-ing life that concrete flowability prolongs pump line, and reduce the use of gelling material in the concrete, reduce the concrete cost, improve its workability, be convenient to construction.
P.O refers to ordinary Portland cement in the P.O42.5 cement, and 42.5 refer to cement intensity (28 days).
Principle of work of the present invention is as follows:
The present invention is by repeatedly selecting to add BTC functional type admixture after the experiment, and BTC functional type admixture makes cement based finely-powdered minerals material disperse cohesion again by the complexing chemical action, and the raising concrete mortar enriches degree, improves concrete cohesiveness; By shielding effect, suppress absorption and the swelling capacity of clay, improve the consistency of the complicated starting material of concrete and water reducer; By slackening water molecules polarity, eliminate the concrete bulla, increase microvesicle quantity, guaranteed concrete intensity and weather resistance effectively; By the lattice distortion effect, hydration reaction is accelerated, and reduces hydrated product crystal mineral quantity, improves jel product quantity, makes the reaction of secondary rubble more abundant, has greatly improved concrete grout-bone interface adhesive structure character.In a word, by the complex combination of multiple different properties functional materials, allow modern concrete can be more reliable with less gelling material production intensity, the concrete of more excellent performance, realize the tap/dip deep into of the low carbon technique of concrete and environmental protection aspect.
Above-described specific embodiment; technical problem, technical scheme and beneficial effect that the present invention is solved further describe; institute is understood that; the above only is specific embodiments of the invention; be not limited to the present invention; within the spirit and principles in the present invention all, any modification of making, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. concrete that utilizes BTC functional type admixture to improve performance is characterized in that its component and the mass parts of each component are as follows:
Cement: 200 parts ~ 320 parts; Breeze: 60 parts ~ 90 parts;
Flyash: 40 parts ~ 60 parts; Sand: 680 parts ~ 780 parts;
Rubble: 1060 parts ~ 1100 parts; Concrete admixture: 3.3 parts ~ 4.74 parts;
BTC functional type admixture: 1.92 parts ~ 2.58 parts;
Water: 170 parts.
2. a kind of BTC of utilization functional type admixture according to claim 1 improves the concrete of performance, and it is characterized in that: the mass parts of its component and each component is as follows:
Cement: 215 parts; Breeze: 60 parts;
Flyash: 50 parts; Sand: 770 parts;
Rubble: 1100 parts; Concrete admixture: 4.22 parts;
BTC functional type admixture: 1.95 parts;
Water: 170 parts.
3. a kind of BTC of utilization functional type admixture according to claim 1 and 2 improves the concrete of performance, and it is characterized in that: described cement is P.O42.5 cement.