CN103342469A - 一种屋顶花园栽培用发泡微孔隙玻璃轻石及其制备方法 - Google Patents
一种屋顶花园栽培用发泡微孔隙玻璃轻石及其制备方法 Download PDFInfo
- Publication number
- CN103342469A CN103342469A CN2013102812038A CN201310281203A CN103342469A CN 103342469 A CN103342469 A CN 103342469A CN 2013102812038 A CN2013102812038 A CN 2013102812038A CN 201310281203 A CN201310281203 A CN 201310281203A CN 103342469 A CN103342469 A CN 103342469A
- Authority
- CN
- China
- Prior art keywords
- foaming
- fineness
- heating
- time
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种屋顶花园栽培用发泡微孔隙玻璃轻石,其特征在于它含有发泡微孔隙,发泡微孔隙孔径为0.2~5mm,吸水率为40~60%,强度为1~2.5MPa,密度为0.15~0.25g/cm3;它由发泡混合物经烧结后制得,发泡混合物包括以下重量百分比的组份:玻璃粉末:80~90、大理石粉:5~10、生石灰:1~5、石英砂粉末3~5;其中玻璃粉末的细度为40~100μm,大理石粉的细度为20~40μm,生石灰的细度为20~40μm;石英砂粉末细度为20~40μm。本发明还涉及该屋顶花园栽培用发泡微孔隙玻璃轻石的制备方法。本发明具有能重量轻、疏松透气、能预防病虫滋生的优点。
Description
技术领域
本发明涉及一种发泡微孔隙玻璃轻石,尤其涉及一种屋顶花园栽培用发泡微孔隙玻璃轻石及其制备方法。
技术背景
目前在房屋屋顶栽培花果蔬菜时需要在屋顶铺设大量泥土,由于泥土的重量教大,使屋顶受的承重比较大,同时在浇水或下雨天,雨水对泥土冲刷后容易造成泥土和泥土中的肥料的流失,在泥土中也容易滋生病虫害;同时铺设的泥土在使用一段时间后会压实板结,其透气性就会变差,由此影响植物的生长。
发明内容
本发明的目的在于提供一种重量轻、疏松透气、能预防病虫滋生的屋顶花园栽培用发泡微孔隙玻璃轻石。
本发明的技术内容为,一种屋顶花园栽培用发泡微孔隙玻璃轻石,其特征在于它含有发泡微孔隙,发泡微孔隙孔径为0.2~5mm,吸水率为40~60%,强度为1~2.5MPa,密度为0.15~0.25g/cm3;它由发泡混合物经烧结后制得,发泡混合物包括以下重量百分比的组份:
玻璃粉末: 80~90
大理石粉: 5~10
生石灰: 1~5
石英砂粉末 3~5
其中玻璃粉末的细度为40~100μm ,大理石粉的细度为20~40μm,生石灰的细度为20~40μm;石英砂粉末细度为20~40μm。
在上述屋顶花园栽培用发泡微孔隙玻璃轻石中采用的烧结工艺为制备玻璃轻石的烧结工艺,具体为:发泡混合物堆积到加热炉中,发泡混合物在加热炉中经预热、第一次升温加热、烧结加热、第二次升温加热和发泡加热后制得烧结发泡加热物,将烧结发泡加热物从加热炉中取出后进行自然冷却至室温即得成品玻璃轻石。
在上述屋顶花园栽培用发泡微孔隙玻璃轻石烧结的泡混合物中的玻璃粉末可以使用废旧玻璃,由此可以大大降低生产成本,同时也回收利用了资源。
在本发明的发泡混合物中的生石灰用以增加玻璃的析晶倾向,从而有效促进发泡,并使气泡形成连通孔,连通孔的数量直接影响璃轻石的吸水率与强度;但是连通孔数量过多会降低产品抗压强度,因此加入一定量的石英砂粉末,通过调节粉料的粘度来控制连通孔的数量,使产品具有轻质的特点以及良好的吸水性和抗压强度。
本发明的另一目的在于提供上述一种屋顶花园栽培用发泡微孔隙玻璃轻石的制备方法。
一种屋顶花园栽培用发泡微孔隙玻璃轻石的制备方法,其步骤为:
(1)、先将以下重量百分比的组份混合制得发泡混合物:
玻璃粉末: 80~90
大理石粉: 5~10
生石灰: 1~5
石英砂粉末 3~5
其中玻璃粉末的细度为40~100μm ,大理石粉的细度为20~40μm,生石灰的细度为20~40μm;石英砂粉末细度为20~40μm;
(2)、将上述制得的发泡混合物堆积到加热炉中,发泡混合物在加热炉中经预热、第一次升温加热、烧结加热、第二次升温加热和发泡加热后制得烧结发泡加热物,将烧结发泡加热物从加热炉中取出后进行自然冷却至室温即得屋顶花园栽培用发泡微孔隙玻璃轻石;其中预热温度为350~450℃,预热时间为5~20分钟;第一次升温加热温度为680~720℃,加热时间为10~30分钟;烧成加热温度为730~770℃,加热时间为5~15分钟;第二次升温加热温度为780~820℃,加热时间为10~30分钟;发泡加热温度为950~1010℃,加热时间为5~10分钟。
在将上述屋顶花园栽培用发泡微孔隙玻璃轻石应用到屋顶花园时,先将玻璃轻石粉碎成不同直径大小的颗粒,铺设在最底层的是直径在5~8cm的颗粒,再往上铺设一层直径在3~6cm的颗粒,再往上铺设一层直径在1~4的颗粒,最后铺设一层0.5~3mm玻璃轻石粉末与泥土的混合层。
本发明所具有的优点是:在进行植物蔬果种植时由于其同体积的泥土重量轻,其对屋顶的压力就小,其具有的发泡微孔隙具有吸附性,可以起到蓄水保肥的作用,同时也使玻璃轻石粉末与泥土的混合层具有良好的透气性;由于该屋顶花园栽培用发泡微孔隙玻璃轻石具有弱碱性所以有杀菌防虫、清洁水质的作用;同时成品生产主要原料为玻璃,尤其是可以利用废旧玻璃,其生产使用成本就比较低。
具体实施例
例1: (1)、先细度为60μm的玻璃粉末0.87Kg、细度为30μm的大理石粉0.07Kg、细度为30μm的生石灰0.02Kg和细度为25μm的石英砂粉末0.04Kg混合制得发泡混合物
(2)、将上述制得的发泡混合物堆积到加热炉中,发泡混合物在加热炉中经预热、第一次升温加热、烧结加热、第二次升温加热和发泡加热后制得烧结发泡加热物,将烧结发泡加热物从加热炉中取出后进行自然冷却至室温即得屋顶花园栽培用发泡微孔隙玻璃轻石;其中预热温度为390℃,预热时间为10分钟;第一次升温加热温度为690℃,加热时间为15分钟;烧成加热温度为750℃,加热时间为10分钟;第二次升温加热温度为810℃,加热时间为15分钟;发泡加热温度为1000℃,加热时间为8分钟;屋顶花园栽培用发泡微孔隙玻璃轻石发泡微孔隙孔径为0.8~2mm ,密度为0.21g/cm3 ,吸水率为54% ,强度为2.3MPa。
Claims (2)
1.一种屋顶花园栽培用发泡微孔隙玻璃轻石,其特征在于它含有发泡微孔隙,发泡微孔隙孔径为0.2~5mm,吸水率为40~60%,强度为1~2.5MPa,密度为0.15~0.25g/cm3;它由发泡混合物经烧结后制得,发泡混合物包括以下重量百分比的组份:
玻璃粉末: 80~90
大理石粉: 5~10
生石灰: 1~5
石英砂粉末 3~5
其中玻璃粉末的细度为40~100μm ,大理石粉的细度为20~40μm,生石灰的细度为20~40μm;石英砂粉末细度为20~40μm。
2.一种屋顶花园栽培用发泡微孔隙玻璃轻石的制备方法,其步骤为:
(1)、先将以下重量百分比的组份混合制得发泡混合物:
玻璃粉末: 80~90
大理石粉: 5~10
生石灰: 1~5
石英砂粉末 3~5
其中玻璃粉末的细度为40~100μm ,大理石粉的细度为20~40μm,生石灰的细度为20~40μm;石英砂粉末细度为20~40μm;
(2)、将上述制得的发泡混合物堆积到加热炉中,发泡混合物在加热炉中经预热、第一次升温加热、烧结加热、第二次升温加热和发泡加热后制得烧结发泡加热物,将烧结发泡加热物从加热炉中取出后进行自然冷却至室温即得屋顶花园栽培用发泡微孔隙玻璃轻石;其中预热温度为350~450℃,预热时间为5~20分钟;第一次升温加热温度为680~720℃,加热时间为10~30分钟;烧成加热温度为730~770℃,加热时间为5~15分钟;第二次升温加热温度为780~820℃,加热时间为10~30分钟;发泡加热温度为950~1010℃,加热时间为5~10分钟。