CN103333591A - 一种耐冲击性cc440聚酯树脂的粉末涂料及其制备方法 - Google Patents

一种耐冲击性cc440聚酯树脂的粉末涂料及其制备方法 Download PDF

Info

Publication number
CN103333591A
CN103333591A CN2013102076119A CN201310207611A CN103333591A CN 103333591 A CN103333591 A CN 103333591A CN 2013102076119 A CN2013102076119 A CN 2013102076119A CN 201310207611 A CN201310207611 A CN 201310207611A CN 103333591 A CN103333591 A CN 103333591A
Authority
CN
China
Prior art keywords
parts
powder coating
vibrin
pvc
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102076119A
Other languages
English (en)
Other versions
CN103333591B (zh
Inventor
张洪滨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU HONGAN PRECISION MACHINERY Co Ltd
Original Assignee
BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU HONGAN PRECISION MACHINERY Co Ltd filed Critical BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority to CN201310207611.9A priority Critical patent/CN103333591B/zh
Publication of CN103333591A publication Critical patent/CN103333591A/zh
Application granted granted Critical
Publication of CN103333591B publication Critical patent/CN103333591B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种耐冲击性CC440聚酯树脂的粉末涂料及其制备方法。本发明公开了耐冲击性CC440聚酯树脂的粉末涂料，其特征在于其组成原料的重量份为：CC440聚酯树脂55-60、安息香1.5-2.5、三甲基羟乙基乙二胺2-3、SG-1聚氯乙烯树脂1.3-1.5、二甲基硅油0.5-1.0、纳米砖渣粉末2.3-2.8、纳米碳酸钙8-9、三聚磷酸钠5.0-7.0、月桂醇聚氧乙烯醚0.9-1.1、乙二醇单丁醚2-3、氨丙基三乙氧基硅烷2-3、交联剂 TAC1-2。本发明添加了少量的聚氯乙烯树脂，通过氨丙基三乙氧基硅烷与纳米砖渣粉末的结合，对于粉末涂料的成膜能力、耐冲击性具有较好改善作用。

Description

一种耐冲击性CC440聚酯树脂的粉末涂料及其制备方法
技术领域
本发明涉及粉末涂料领域，尤其涉及一种耐冲击性CC440聚酯树脂的粉末涂料及其制备方法。
背景技术
    随着我国经济的持续稳定增长以及人民生活水平的不断提高，金属构件的粉末涂装业务也不断增加，尤其是家用电器、仪器仪表、交通设施、铝型材、各种车辆以及日用五金等行业，粉末涂层能给金属提供优良的防腐保护及装饰性能，但由于用于上述领域的现有涂料的抗污染性能不理想，涂层上经常附着各类灰尘、污垢甚至是油污；抗粘贴能力也不理想，且现有粉末涂料形成的涂层在户外长期暴晒、雨淋等自然条件影响下易出现起泡、开裂、剥离等现象，因此，涂层的机械性能也不理想。
发明内容
本发明所要解决的技术问题是克服现有技术的不足，提供一种耐冲击性CC440聚酯树脂的粉末涂料及其制备方法。
为了实现上述目的本发明采用如下技术方案：
耐冲击性CC440聚酯树脂的粉末涂料，其特征在于其组成原料的重量份为：CC440聚酯树脂55-60、安息香1.5-2.5、三甲基羟乙基乙二胺2-3、SG-1聚氯乙烯树脂 1.3-1.5、二甲基硅油0.5-1.0、纳米砖渣粉末2.3-2.8、纳米碳酸钙8-9、三聚磷酸钠5.0-7.0、月桂醇聚氧乙烯醚0.9-1.1、乙二醇单丁醚2-3、氨丙基三乙氧基硅烷2-3、交联剂 TAC1-2。
所述的耐冲击性CC440聚酯树脂的粉末涂料，其特征在于其组成原料的重量份为：CC440聚酯树脂58、安息香2.0、三甲基羟乙基乙二胺2、SG-1聚氯乙烯树脂 1.4、二甲基硅油0.8、纳米砖渣粉末2.5、纳米碳酸钙8、三聚磷酸钠6.0、月桂醇聚氧乙烯醚1.0和乙二醇单丁醚2、氨丙基三乙氧基硅烷2、交联剂 TAC1。
所述的耐冲击性CC440聚酯树脂的粉末涂料的制备方法，其特征在于包括以下步骤：
（1）将SG-1聚氯乙烯树脂、二甲基硅油、纳米砖渣粉末混合，在80-90℃下搅拌，加入氨丙基三乙氧基硅烷、交联剂 TAC，搅拌1-2小时；
（2）按组成原料的重量份称取其他剩余组成原料与步骤（1）物料混合，送入挤出机造粒，挤出机温度100-130℃，冷却，然后，研磨至200-300目时；停止研磨，包装。
本发明的有益效果：
本发明CC440聚酯树脂综合性能优异，具有较好的抗低温变形能力、抗疲劳性、抗水损害能力、耐冲击性等综合性能，减少涂料的掉落和开裂现象，延迟涂料的使用寿命，本发明添加了少量的聚氯乙烯树脂，通过氨丙基三乙氧基硅烷与纳米砖渣粉末的结合，对于粉末涂料的成膜能力、耐冲击性具有较好改善作用。
具体实施方式
实施例1：耐冲击性CC440聚酯树脂的粉末涂料，其组成原料的重量份（kg）为：CC440聚酯树脂55-60、安息香1.5-2.5、三甲基羟乙基乙二胺2-3、SG-1聚氯乙烯树脂 1.3-1.5、二甲基硅油0.5-1.0、纳米砖渣粉末2.3-2.8、纳米碳酸钙8-9、三聚磷酸钠5.0-7.0、月桂醇聚氧乙烯醚0.9-1.1、乙二醇单丁醚2-3、氨丙基三乙氧基硅烷2-3、交联剂 TAC1-2。
包括以下步骤：
（1）将SG-1聚氯乙烯树脂、二甲基硅油、纳米砖渣粉末混合，在80-90℃下搅拌，加入氨丙基三乙氧基硅烷、交联剂 TAC，搅拌1-2小时；
（2）按组成原料的重量份称取其他剩余组成原料与步骤（1）物料混合，送入挤出机造粒，挤出机温度100-130℃，冷却，然后，研磨至200-300目时；停止研磨，包装。
将该粉末涂料采用静电喷涂施工方法作用于经喷涂处理的建筑物外墙壁上，经175℃的充分固化，自然冷却至室温，放置20h 后，测定涂层性能，其涂层冲击强度≥ 105cm，耐盐雾时间≥ 2885h，人工加速老化时间≥ 2930h，耐热性能≥562，天然曝晒17个月不起泡、不生锈、不开裂、不剥离，对油污的分解率≥97.1%。

Claims (3)

1.一种耐冲击性CC440聚酯树脂的粉末涂料，其特征在于其组成原料的重量份为：CC440聚酯树脂55-60、安息香1.5-2.5、三甲基羟乙基乙二胺2-3、SG-1聚氯乙烯树脂 1.3-1.5、二甲基硅油0.5-1.0、纳米砖渣粉末2.3-2.8、纳米碳酸钙8-9、三聚磷酸钠5.0-7.0、月桂醇聚氧乙烯醚0.9-1.1、乙二醇单丁醚2-3、氨丙基三乙氧基硅烷2-3、交联剂 TAC1-2。
2.根据权利要求1所述的耐冲击性CC440聚酯树脂的粉末涂料，其特征在于其组成原料的重量份为：CC440聚酯树脂58、安息香2.0、三甲基羟乙基乙二胺2、SG-1聚氯乙烯树脂 1.4、二甲基硅油0.8、纳米砖渣粉末2.5、纳米碳酸钙8、三聚磷酸钠6.0、月桂醇聚氧乙烯醚1.0和乙二醇单丁醚2、氨丙基三乙氧基硅烷2、交联剂 TAC1。
3.一种如权利要求1所述的耐冲击性CC440聚酯树脂的粉末涂料的制备方法，其特征在于包括以下步骤：
（1）将SG-1聚氯乙烯树脂、二甲基硅油、纳米砖渣粉末混合，在80-90℃下搅拌，加入氨丙基三乙氧基硅烷、交联剂 TAC，搅拌1-2小时；
（2）按组成原料的重量份称取其他剩余组成原料与步骤（1）物料混合，送入挤出机造粒，挤出机温度100-130℃，冷却，然后，研磨至200-300目时；停止研磨，包装。
CN201310207611.9A 2013-05-30 2013-05-30 一种耐冲击性cc440聚酯树脂的粉末涂料及其制备方法 Expired - Fee Related CN103333591B (zh)