CN103333545A - Blue plastic film ink and preparation method thereof - Google Patents
Blue plastic film ink and preparation method thereof Download PDFInfo
- Publication number
- CN103333545A CN103333545A CN2013102204066A CN201310220406A CN103333545A CN 103333545 A CN103333545 A CN 103333545A CN 2013102204066 A CN2013102204066 A CN 2013102204066A CN 201310220406 A CN201310220406 A CN 201310220406A CN 103333545 A CN103333545 A CN 103333545A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- parts
- blue
- printing ink
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to blue plastic film ink and a preparation method thereof. The blue plastic film ink comprises the following components in parts by weight: 32-42 parts of acrylic copolymer resin, 20-28 parts of ethanolamine, 0.5-1.5 parts of trimethyl silicone oil, 9-13 parts of methyl blue, 4-7 parts of hydroxymethyl cellulose, 7-11 parts of nitrocellulose solution, 0.3-1 part of white beeswax, 1.5-3.5 parts of polyamide wax, 4-6.5 parts of isopropyl alcohol, 3.5-6 parts of petroleum ether, 1.3-2.8 parts of ethyl acetate and 2.5-5.5 parts of industrial ethanol. According to the blue plastic film ink and the preparation method thereof, provided by the invention, the obtained ink has the advantages of bright color, good alkali resistance and high speed in decolorization, and is conductive to recycling of a plastic film; meanwhile the preparation process is simple, convenient and low in cost.
Description
Technical field
The present invention relates to a kind of printing ink and preparation method thereof, relate in particular to a kind of blue plastics film printing ink and preparation method thereof.
Background technology
Along with rapid economy development, the market boom, all trades and professions nearly all can relate to the ink printing product, and the consumption of printing ink is fast rise trend.Such as paper bag, plastics bag, food product containers, books etc., these are all closely bound up with our daily life.Wherein, the usage quantity of plastics such as plastics bag is very big, and plastics are again recyclable utilizations, therefore, is used for the function that the printing ink of plastics printing need be easy to degrade.But it is not high to be easy to the printing ink output of degrading in the market, and glossiness is lower, complicated process of preparation.
Summary of the invention
The technical problem that solves:At above-mentioned printing ink output is not high, glossiness is lower and the shortcoming of complicated process of preparation, the invention provides a kind of blue plastics film printing ink and preparation method thereof.
Technical scheme:A kind of blue plastics film printing ink, contain following composition in mass parts: acrylic copolymeric resin 32～42 mass parts, thanomin 20～28 mass parts, trimethylammonium silicone oil 0.5～1.5 mass parts, Methylene blue 9～13 mass parts, Walocel MT 20.000PV 4～7 mass parts, nitro-cotton liquid 7～11 mass parts, cera alba 0.3～1 mass parts, polyamide wax 1.5～3.5 mass parts, Virahol 4～6.5 mass parts, sherwood oil 3.5～6 mass parts, vinyl acetic monomer 1.3～2.8 mass parts, industrial alcohol 2.5～5.5 mass parts.
Acrylic copolymeric resin described above is the caustic solubility acrylic copolymeric resin.
The shared weight ratio of ethanol is 95% in the industrial alcohol described above.
The preparation method of blue plastics film printing ink described above, the preparation process of this method is as follows:
The first step: acrylic copolymeric resin, thanomin and trimethylammonium silicone oil are added in the reactor, and stirring obtains acrylic copolymeric resin liquid, and discharging is standby;
Second step: acrylic copolymeric resin liquid, Methylene blue, the Walocel MT 20.000PV of gained are added reactor, add nitro-cotton liquid, cera alba and polyamide wax after mixing again, continue to stir;
The 3rd step: add Virahol, sherwood oil, vinyl acetic monomer and ethanol at last, the discharging that stirs obtains printing ink.
Beneficial effect:Blue plastics film printing ink provided by the invention and preparation method thereof, resulting printing ink lovely luster, sticking power is big, alkali resistance is good, printing ink can decolour fast, is beneficial to the recycling of plastics film, and has reduced poisonous and harmful solvent pollution on the environment; Its preparation technology is easy, cost is low.
Embodiment
Embodiment 1
Present embodiment provides a kind of blue plastics film printing ink, contains following composition in mass parts: acrylic copolymeric resin 36 mass parts, thanomin 24 mass parts, trimethylammonium silicone oil 1.2 mass parts, Methylene blue 11 mass parts, Walocel MT 20.000PV 5.5 mass parts, nitro-cotton liquid 9 mass parts, cera alba 0.7 mass parts, polyamide wax 1.8 mass parts, Virahol 5 mass parts, sherwood oil 5.2 mass parts, vinyl acetic monomer 2 mass parts, industrial alcohol 3.4 mass parts.
The preparation process of blue plastics film printing ink is as follows: acrylic copolymeric resin, thanomin and trimethylammonium silicone oil are added in the reactor, and stirring obtains acrylic copolymeric resin liquid, and discharging is standby; Acrylic copolymeric resin liquid, Methylene blue, the Walocel MT 20.000PV of gained are added reactor, add nitro-cotton liquid, cera alba and polyamide wax after mixing again, continue to stir; Add Virahol, sherwood oil, vinyl acetic monomer and ethanol at last, the discharging that stirs obtains printing ink.
Blue plastics film printing ink provided by the invention and preparation method thereof, its color approximate test sample, the glossiness height, viscosity is 26 s/25 ℃, uses corresponding discoloring agent can take off to colourless in 0.5min, it is good to rub fastness.
Embodiment 2
Present embodiment provides a kind of blue plastics film printing ink, contains following composition in mass parts: acrylic copolymeric resin 32 mass parts, thanomin 20 mass parts, trimethylammonium silicone oil 0.5 mass parts, Methylene blue 9 mass parts, Walocel MT 20.000PV 4 mass parts, nitro-cotton liquid 7 mass parts, cera alba 0.3 mass parts, polyamide wax 1.5 mass parts, Virahol 4 mass parts, sherwood oil 3.5 mass parts, vinyl acetic monomer 1.3 mass parts, industrial alcohol 2.5 mass parts.
The preparation process of blue plastics film printing ink is as follows: acrylic copolymeric resin, thanomin and trimethylammonium silicone oil are added in the reactor, and stirring obtains acrylic copolymeric resin liquid, and discharging is standby; Acrylic copolymeric resin liquid, Methylene blue, the Walocel MT 20.000PV of gained are added reactor, add nitro-cotton liquid, cera alba and polyamide wax after mixing again, continue to stir; Add Virahol, sherwood oil, vinyl acetic monomer and ethanol at last, the discharging that stirs obtains printing ink.
Blue plastics film printing ink provided by the invention and preparation method thereof, its color approximate test sample, the glossiness height, viscosity is 24s/25 ℃, uses corresponding discoloring agent can take off to colourless in 1min, it is good to rub fastness.
Embodiment 3
Present embodiment provides a kind of blue plastics film printing ink, contains following composition in mass parts: acrylic copolymeric resin 42 mass parts, thanomin 28 mass parts, trimethylammonium silicone oil 1.5 mass parts, Methylene blue 13 mass parts, Walocel MT 20.000PV 7 mass parts, nitro-cotton liquid 11 mass parts, cera alba 1 mass parts, polyamide wax 3.5 mass parts, Virahol 6.5 mass parts, sherwood oil 6 mass parts, vinyl acetic monomer 2.8 mass parts, industrial alcohol 5.5 mass parts.
The preparation process of blue plastics film printing ink is as follows: acrylic copolymeric resin, thanomin and trimethylammonium silicone oil are added in the reactor, and stirring obtains acrylic copolymeric resin liquid, and discharging is standby; Acrylic copolymeric resin liquid, Methylene blue, the Walocel MT 20.000PV of gained are added reactor, add nitro-cotton liquid, cera alba and polyamide wax after mixing again, continue to stir; Add Virahol, sherwood oil, vinyl acetic monomer and ethanol at last, the discharging that stirs obtains printing ink.
Blue plastics film printing ink provided by the invention and preparation method thereof, its color approximate test sample, the glossiness height, viscosity is 28 s/25 ℃, uses corresponding discoloring agent can take off to colourless in 1.5min, it is good to rub fastness.
The above is the preferred embodiments of the present invention, but the present invention also is not limited to above only embodiment, does improvement slightly and also will be considered as protection scope of the present invention on embodiment.
Claims (4)
1. blue plastics film printing ink, it is characterized in that containing following composition in mass parts: acrylic copolymeric resin 32～42 mass parts, thanomin 20～28 mass parts, trimethylammonium silicone oil 0.5～1.5 mass parts, Methylene blue 9～13 mass parts, Walocel MT 20.000PV 4～7 mass parts, nitro-cotton liquid 7～11 mass parts, cera alba 0.3～1 mass parts, polyamide wax 1.5～3.5 mass parts, Virahol 4～6.5 mass parts, sherwood oil 3.5～6 mass parts, vinyl acetic monomer 1.3～2.8 mass parts, industrial alcohol 2.5～5.5 mass parts.
2. blue plastics film printing ink according to claim 1, it is characterized in that: described acrylic copolymeric resin is the caustic solubility acrylic copolymeric resin.
3. blue plastics film printing ink according to claim 1, it is characterized in that: the shared weight ratio of ethanol is 95% in the described industrial alcohol.
4. the preparation method of blue plastics film printing ink as claimed in claim 1 is characterized in that the preparation process of this method is as follows:
The first step: acrylic copolymeric resin, thanomin and trimethylammonium silicone oil are added in the reactor, and stirring obtains acrylic copolymeric resin liquid, and discharging is standby;
Second step: acrylic copolymeric resin liquid, Methylene blue, the Walocel MT 20.000PV of gained are added reactor, add nitro-cotton liquid, cera alba and polyamide wax after mixing again, continue to stir;
The 3rd step: add Virahol, sherwood oil, vinyl acetic monomer and ethanol at last, the discharging that stirs obtains printing ink.