CN103321054B - 一种聚酯纤维用蓬松柔软整理剂及其制备方法 - Google Patents
一种聚酯纤维用蓬松柔软整理剂及其制备方法 Download PDFInfo
- Publication number
- CN103321054B CN103321054B CN201310224509.XA CN201310224509A CN103321054B CN 103321054 B CN103321054 B CN 103321054B CN 201310224509 A CN201310224509 A CN 201310224509A CN 103321054 B CN103321054 B CN 103321054B
- Authority
- CN
- China
- Prior art keywords
- bgreatt
- polyester fiber
- gre
- grams
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
<b>本发明涉及一种聚酯纤维用蓬松整理剂及其制备方法,以重量份计,整理剂的原料配方为:聚乙二醇</b><b>120~160</b><b>份、乙二醇</b><b>18~30</b><b>份、二羟基聚醚</b><b>15~25</b><b>份、对苯二甲酸二甲酯</b><b>20~28</b><b>份、端氨基双封头剂有机硅</b><b>10~30</b><b>份、</b><b>3-</b><b>哌嗪丙基甲基二甲氧基硅烷</b><b>5~10</b><b>份以及作为催化剂的醋酸金属盐</b><b>0.2~2</b><b>份;所述聚酯纤维用蓬松整理剂为原料反应生成的数均分子量为</b><b>8000~20000</b><b>的聚酯聚醚硅油嵌段共聚物。使用本发明提供的聚酯纤维用蓬松整理剂对聚酯进行整理,可以使聚酯纤维具有超级蓬松柔软感,同时,还可改善聚酯纤维的抗静电性能和亲水性能,因此,其可大大提高改性后聚酯纤维的舒适性。此外,本发明的聚酯纤维的成本较低。</b>
Description
技术领域
本发明涉及织物整理剂技术领域,特别涉及一种聚酯纤维用蓬松柔软整理剂及其制备方法。
背景技术
众所周知,聚酯纤维的蓬松柔软性、吸湿排汗性、抗静电性能、易去污性能都较差。因此,用聚酯纤维加工而成的纺织品的服用性较差、易粘污、易起静电的特点。这无疑将对人体的健康造成一定的危害。为了克服聚酯纤维所存在的不足和为了满足市场对于纺织品越来越高的要求,必须对聚酯纤维进行后整理,以期改善其性能。
针对聚酯纤维吸湿排汗性的不足,本申请人于2008年4月24日提出一篇名称为“吸湿排汗舒适整理剂及其生产工艺和应用”的发明专利申请,其中公开的吸湿排汗舒适整理剂由如下重量份的组份组成:聚乙二醇80~100份,乙二醇10~15份,二羟基聚醚10~14份,对苯二甲酸二甲酯15~18份和作为催化剂的醋酸金属盐0.2~1份。吸湿排汗舒适整理剂是由上述原料在一定条件下反应所得分子量为30000~50000的聚酯/聚醚嵌段共聚物。该吸湿排汗舒适整理剂可对聚酯纤维进行改性,使改性后的聚酯纤维具有良好的吸湿排汗性能和蓬松柔软,提高了织物的舒适性。该整理剂虽然对聚酯纤维的蓬松柔软性有一定的改善,但是这种改善较为有限,必须配合氨基硅油等方可成为蓬松整理剂。即便如此,蓬松整理的效果还需进一步提高。
发明内容
本发明所要解决的技术问题是克服现有技术的不足,提供一种可使整理后的纤维具有超级蓬松柔软感的聚酯纤维用蓬松柔软整理剂,该整理剂同时还可有效改善聚酯纤维的抗静电性能和亲水性能。
本发明同时还要提供一种聚酯纤维用蓬松柔软整理剂的制备方法。
为解决上述技术问题,本发明采取的一种技术方案是:
一种聚酯纤维用蓬松整理剂,以重量份计,该整理剂的原料配方为:聚乙二醇120~160份、乙二醇18~30份、二羟基聚醚15~25份、对苯二甲酸二甲酯20~28份、端氨基双封头剂有机硅10~30份、3-哌嗪丙基甲基二甲氧基硅烷5~10份以及作为催化剂的醋酸金属盐0.2~2份;所述聚酯纤维用蓬松整理剂为所述原料反应生成的数均分子量为8000~20000的聚酯聚醚硅油嵌段共聚物。
优选地,所述的聚酯纤维用蓬松整理剂为数均分子量为10000~15000的聚酯聚醚硅油嵌段共聚物。
优选地,所述的聚酯纤维用蓬松整理剂的制备方法是:按配比向反应釜中投入所述原料,升温至140℃~180℃,保温反应120~180分钟,然后继续升温至220℃~240℃,保温反应50~70分钟,最后使物料在真空度-0.08~-0.1MPa以及温度240℃~300℃下反应,生成所述聚酯聚醚硅油嵌段共聚物,降温至190~220℃后放料,即得所述聚酯纤维用蓬松整理剂。
本发明采取的又一技术方案是:一种上述的聚酯纤维用蓬松整理剂的制备方法,其包括如下步骤:
(1)称取所需量的各原料组份;
(2)按配比向反应釜中投入所述原料,升温至140℃~180℃,保温反应120~180分钟,然后继续升温至220℃~240℃,保温反应50~70分钟,最后使物料在真空度-0.08~-0.1MPa以及温度240℃~300℃下反应,生成所述聚酯聚醚硅油嵌段共聚物,降温至190~220℃后放料,即得聚酯纤维用蓬松整理剂。
本发明还采取的一种技术方案是:一种聚酯纤维用蓬松整理剂,其由数均分子量为8000~20000的聚酯聚醚硅油嵌段共聚物1wt%~5wt%以及余量为水组成,其中,以重量份计,所述聚酯聚醚硅油嵌段共聚物的原料配方为:聚乙二醇120~160份、乙二醇18~30份、二羟基聚醚15~25份、对苯二甲酸二甲酯20~28份、端氨基双封头剂有机硅10~30份、3-哌嗪丙基甲基二甲氧基硅烷5~10份以及作为催化剂的醋酸金属盐0.2~2份。
优选地,所述聚酯聚醚硅油嵌段共聚物的数均分子量为10000~15000。
本发明还提供上述的聚酯纤维用蓬松整理剂的制备方法,其包括如下步骤:
(1)按聚酯聚醚硅油嵌段共聚物的原料配方,向反应釜中投入原料,升温至140℃~180℃,保温反应120~180分钟,然后继续升温至220℃~240℃,保温反应50~70分钟,最后使物料在真空度-0.08~-0.1MPa以及温度240℃~300℃下反应,生成所述聚酯聚醚硅油嵌段共聚物,降温至190~220℃后放料;
(2)将聚酯聚醚硅油嵌段共聚物与水按比例混合均匀,即得聚酯纤维用蓬松整理剂。
根据本发明,全部原料组分均可商购获得。其中:聚乙二醇优选的数均分子量为1000~4000,例如PEG2000,PEG4000。二羟基聚醚又称丙二醇聚醚,其数均分子量一般在1000~4000之间;端氨基双封头剂有机硅为氨基封头的有机硅,具有如下结构式:
本发明所获得的聚酯聚醚硅油嵌段共聚物可能的结构式如下:
上式中,R1,R2,R3独立地为H或甲基,且R1,R2,R3不同时为H或甲基。
由于以上技术方案的实施,本发明与现有技术相比具有如下优势:
使用本发明提供的聚酯纤维用蓬松整理剂对聚酯进行整理,可以使聚酯纤维具有超级蓬松柔软感,同时,还可改善聚酯纤维的抗静电性能和亲水性能,因此,其可大大提高改性后聚酯纤维的舒适性。此外,本发明的聚酯纤维的原料成本和制造成本较低。
具体实施方式
以下结合具体的实施例,对本发明做进一步详细的说明,但本发明不限于以下实施例。
实施例1
一种聚酯纤维用蓬松整理剂,其通过如下步骤制备:
(1)、称取聚乙二醇(PEG4000)800克,乙二醇150克,二羟基聚醚125克,对苯二甲酸二甲酯140克,端氨基双封头剂有机硅150克,3-哌嗪丙基甲基二甲氧基硅烷50g,醋酸镁10克;
(2)、向反应釜中投入上述物料,升温至140℃保持180分钟,继续升温至220℃保持60分钟。然后在真空度为-0.08MPa,温度为240℃下进行聚合,生成聚酯聚醚硅油嵌段共聚物,降温至190℃后放料,得到成品。
实施例2
一种聚酯纤维用蓬松整理剂,其通过如下步骤制备:
(1)、称取聚乙二醇(PEG2000)900克,乙二醇140克,二羟基聚醚140克,对苯二甲酸二甲酯165克,端氨基双封头剂有机硅180克,3-哌嗪丙基甲基二甲氧基硅烷60g,醋酸锌6克;
(2)、向反应釜中投入上述物料,升温至150℃保持180分钟,继续升温至230℃保持60分钟。然后进行聚合,在真空度为-0.08MPa,温度为260℃下进行聚合,生成聚酯聚醚硅油嵌段共聚物,降温至200℃后放料,得到成品。
实施例3
一种聚酯纤维用蓬松整理剂,其通过如下步骤制备:
(1)、称取聚乙二醇700克,乙二醇125克,二羟基聚醚125克,对苯二甲酸二甲酯130克,端氨基双封头剂有机硅150克,3-哌嗪丙基甲基二甲氧基硅烷50克,醋酸钙10克;
(2)、向反应釜中投入上述物料,升温至170℃保持180分钟,继续升温至220℃保持60分钟,然后进行聚合,在真空度为-0.09MPa,温度为250℃下进行聚合,生成聚酯聚醚硅油嵌段共聚物,降温至200℃后放料,得到成品。
实施例4
一种聚酯纤维用蓬松整理剂,其通过如下步骤制备:
(1)、称取聚乙二醇(PEG2000)800克,乙二醇130克,二羟基聚醚110克,对苯二甲酸二甲酯125克,端氨基双封头剂有机硅150克,3-哌嗪丙基甲基二甲氧基硅烷40g,醋酸锡8克;
(2)、向反应釜中投入上述物料,升温至180℃保持180分钟,继续升温至230℃保持60分钟,然后在真空度为-0.095MPa,温度为240℃下进行聚合,生成聚酯聚醚硅油嵌段共聚物,降温至200℃后放料;
(3)、将步骤(2)所得物料和水按照重量比5:95混合均匀,即得成品。
实施例5
一种聚酯纤维用蓬松整理剂,其通过如下步骤制备:
(1)、称取聚乙二醇(PEG4000)1000克,乙二醇140克,聚醚150克,对苯二甲酸二甲酯170克,端氨基双封头剂有机硅180克,3-哌嗪丙基甲基二甲氧基硅烷80g,醋酸锡6克;
(2)、向反应釜中投入上述物料,升温至150℃,保持180分钟,继续升温至230℃保持60分钟。在真空度为-0.08MPa,温度为280℃下进行聚合,生成聚酯聚醚硅油嵌段共聚物,降温至200℃后放料;
(3)、将步骤(2)所得物料和水按照重量比2:98混合均匀,即得成品。
聚酯聚醚硅油嵌段共聚物的表征及性能测试
1、分别对实施例1~5所制备的聚酯聚醚硅油嵌段共聚物进行了分子量和物理性能的测试,结果参见表1。
表1
2、测试实施例1~5所制备的整理剂对PET聚酯纤维的整理效果
(1)测试方法:
蓬松柔软性手感:专业人士分组触摸评分,共分成五个等级,其中:1—无手感;2—轻微蓬松柔软;3—有一些蓬松柔软;4—较蓬松柔软;5—超级蓬松柔软。
耐洗性,参照AATCC-135标准;
亲水性和毛效法:参考GB/T21655.1-2008。
易去污性能,参照FZ/T10012-1998标准执行。
抗静电性能,参照FZ/T01042-1996标准执行。
(2)测试结果:参见表2。
表2
以上对本发明做了详尽的描述,其目的在于让熟悉此领域技术的人士能够了解本发明的内容并加以实施,并不能以此限制本发明的保护范围,凡根据本发明的精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围内。
Claims (1)
1.一种聚酯纤维用蓬松整理剂,其特征在于:其通过如下步骤制备得到:
(1)、称取聚乙二醇700克,乙二醇125克,二羟基聚醚125克,对苯二甲酸二甲酯130克,端氨基双封头剂有机硅150克,3-哌嗪丙基甲基二甲氧基硅烷50克,醋酸钙10克;
(2)、向反应釜中投入上述物料,升温至170℃保持180分钟,继续升温至220℃保持60分钟,然后进行聚合,在真空度为-0.09MPa,温度为250℃下进行聚合,生成聚酯聚醚硅油嵌段共聚物,降温至200℃后放料,得到成品。