Prior art keywords
parts
pvc plastics
preparation
insulate
reactor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN2013102295046A
Other languages
English (en)
Inventor
董建中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUJIANG DONGXIN PLASTIC PACKAGING FACTORY
Original Assignee
WUJIANG DONGXIN PLASTIC PACKAGING FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIANG DONGXIN PLASTIC PACKAGING FACTORY filed Critical WUJIANG DONGXIN PLASTIC PACKAGING FACTORY
Priority to CN2013102295046A priority Critical patent/CN103319797A/zh
Publication of CN103319797A publication Critical patent/CN103319797A/zh
Withdrawn legal-status Critical Current

Links

Landscapes

  • Organic Insulating Materials (AREA)
  • Compositions Of Macromolecular Compounds (AREA)

Abstract

本发明公开了一种绝缘PVC塑料的制备方法，按如下步骤进行：(1)将50份PVC树脂、10~30份氯醋树脂和10~15份硬脂酸加入到反应釜中，搅拌混合均匀后，加热升温到120℃后，再加入1.5份纳米碳酸钙和3~5份增塑剂，保温1个小时；(2)将反应釜内的温度降低至60℃，加入2.5份钛白粉、0.6份抗氧剂、1~3份热稳定剂和0.01份润滑剂，充分搅拌反应10分钟；（3）将反应釜的温度升温到150℃进行脱水0.5-1小时，冷却降温到40℃以下后放料得绝缘PVC塑料。本发明提高了绝缘PVC塑料的热稳定性，增加其绝缘性能，工艺简单，便于生产。

Description

一种绝缘PVC塑料的制备方法
技术领域
本发明涉及一种绝缘PVC塑料的制备方法，属于高分子化工技术领域。
背景技术
PVC产业在全世界发展迅速，前景广阔，各国都看好PVC的潜力以及其对生态环境的好处，PVC正以其优越、独特的性能向世人证明其作用和地位是任何其它产品都无法取代的，社会发展需要它，环境保护需要它，它是我们人类社会文明进步的必然趋势。PVC塑料可作低频绝缘材料，其化学稳定性也好，但是由于聚氯乙烯的热稳定性较差，长时间加热会导致分解，放出HCL气体，使聚氯乙烯变色，所以其应用范围较窄，影响PVC塑料的应用范围。
发明内容
发明目的：本发明的目的在于针对现有技术的不足，提供一种热稳定性好，应用范围广的绝缘PVC塑料的制备方法。
技术方案：本发明所述的一种绝缘PVC塑料的制备方法，按如下步骤进行：
(1)将50份PVC树脂、10~30份氯醋树脂和10~15份硬脂酸加入到反应釜中，搅拌混合均匀后，加热升温到120℃后，再加入1.5份纳米碳酸钙和3~5份增塑剂，保温1个小时；
(2)将反应釜内的温度降低至60℃，加入2.5份钛白粉、0.6份抗氧剂、1~3份热稳定剂和0.01份润滑剂，充分搅拌反应10分钟；
（3）将反应釜的温度升温到150℃进行脱水0.5-1小时，冷却降温到40℃以下后放料得绝缘PVC塑料。
步骤（1）中所述增塑剂为邻苯二甲酸酯。
步骤（2）中所述抗氧剂为2，6-三级丁基-4-甲基苯酚。
步骤（2）中所述热稳定剂为水合三盐基硫酸铅。
步骤（2）中所述润滑剂为氟化乙烯丙烯共聚物。
有益效果：本发明提供的一种绝缘PVC塑料的制备方法，使用氯醋树脂和硬脂酸与PVC树脂进行混合，提高绝缘PVC塑料的热稳定性，同时，增加其绝缘性能，使其能够广泛的应用于低频绝缘领域，应用范围广，工艺简单，便于生产。
具体实施方式
下面对本发明技术方案进行详细说明，但是本发明的保护范围不局限于所述实施例。
实施例1：本发明一种绝缘PVC塑料，其组分的重量份数为：PVC树脂：50份；氯醋树脂：10份；硬脂酸：10份；邻苯二甲酸酯：3份；钛白粉：2.5份；纳米碳酸钙：1.5份；2，6-三级丁基-4-甲基苯酚：0.6份；水合三盐基硫酸铅：1~3份；氟化乙烯丙烯共聚物：0.01份。
上述绝缘PVC塑料的制备方法，按如下步骤进行：
(1)将50份PVC树脂、10份氯醋树脂和10份硬脂酸加入到反应釜中，搅拌混合均匀后，加热升温到120℃后，再加入1.5份纳米碳酸钙和3份邻苯二甲酸酯，保温1个小时；
(2)将反应釜内的温度降低至60℃，加入2.5份钛白粉、0.6份2，6-三级丁基-4-甲基苯酚、1~3份水合三盐基硫酸铅和0.01份氟化乙烯丙烯共聚物，充分搅拌反应10分钟；
（3）将反应釜的温度升温到150℃进行脱水0.5-1小时，冷却降温到40℃以下后放料得绝缘PVC塑料。
实施例2：本发明一种绝缘PVC塑料，其组分的重量份数为：PVC树脂：50份；氯醋树脂：18份；硬脂酸：12份；邻苯二甲酸酯：4.5份；钛白粉：2.5份；纳米碳酸钙：1.5份；2，6-三级丁基-4-甲基苯酚：0.6份；水合三盐基硫酸铅：1~3份；氟化乙烯丙烯共聚物：0.01份。
上述绝缘PVC塑料的制备方法，按如下步骤进行：
(1)将50份PVC树脂、18份氯醋树脂和12份硬脂酸加入到反应釜中，搅拌混合均匀后，加热升温到120℃后，再加入1.5份纳米碳酸钙和4.5份邻苯二甲酸酯，保温1个小时；
(2)将反应釜内的温度降低至60℃，加入2.5份钛白粉、0.6份2，6-三级丁基-4-甲基苯酚、1~3份水合三盐基硫酸铅和0.01份氟化乙烯丙烯共聚物，充分搅拌反应10分钟；
（3）将反应釜的温度升温到150℃进行脱水0.5-1小时，冷却降温到40℃以下后放料得绝缘PVC塑料。
实施例3：本发明一种绝缘PVC塑料，其组分的重量份数为：PVC树脂：50份；氯醋树脂：30份；硬脂酸：15份；邻苯二甲酸酯：5份；钛白粉：2.5份；纳米碳酸钙：1.5份；2，6-三级丁基-4-甲基苯酚：0.6份；水合三盐基硫酸铅：1~3份；氟化乙烯丙烯共聚物：0.01份。
上述绝缘PVC塑料的制备方法，按如下步骤进行：
(1)将50份PVC树脂、30份氯醋树脂和15份硬脂酸加入到反应釜中，搅拌混合均匀后，加热升温到120℃后，再加入1.5份纳米碳酸钙和5份邻苯二甲酸酯，保温1个小时；
(2)将反应釜内的温度降低至60℃，加入2.5份钛白粉、0.6份2，6-三级丁基-4-甲基苯酚、1~3份水合三盐基硫酸铅和0.01份氟化乙烯丙烯共聚物，充分搅拌反应10分钟；
（3）将反应釜的温度升温到150℃进行脱水0.5-1小时，冷却降温到40℃以下后放料得绝缘PVC塑料。
如上所述，尽管参照特定的优选实施例已经表示和表述了本发明，但其不得解释为对本发明自身的限制。在不脱离所附权利要求定义的本发明的精神和范围前提下，可对其在形式上和细节上作出各种变化。

Claims (5)

1.一种绝缘PVC塑料的制备方法，其特征在于，按如下步骤进行：
(1)将50份PVC树脂、10~30份氯醋树脂和10~15份硬脂酸加入到反应釜中，搅拌混合均匀后，加热升温到120℃后，再加入1.5份纳米碳酸钙和3~5份增塑剂，保温1个小时；
(2)将反应釜内的温度降低至60℃，加入2.5份钛白粉、0.6份抗氧剂、1~3份热稳定剂和0.01份润滑剂，充分搅拌反应10分钟；
（3）将反应釜的温度升温到150℃进行脱水0.5-1小时，冷却降温到40℃以下后放料得绝缘PVC塑料。
2.根据权利要求1所述的一种绝缘PVC塑料的制备方法，其特征在于，步骤（1）中所述增塑剂为邻苯二甲酸酯。
3.根据权利要求1所述的一种绝缘PVC塑料的制备方法，其特征在于，步骤（2）中所述抗氧剂为2，6-三级丁基-4-甲基苯酚。
4.根据权利要求1所述的一种绝缘PVC塑料的制备方法，其特征在于，步骤（2）中所述热稳定剂为水合三盐基硫酸铅。
5.根据权利要求1所述的一种绝缘PVC塑料的制备方法，其特征在于，步骤（2）中所述润滑剂为氟化乙烯丙烯共聚物。
CN2013102295046A 2013-06-09 2013-06-09 一种绝缘pvc塑料的制备方法 Withdrawn CN103319797A (zh)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN2013102295046A CN103319797A (zh) 2013-06-09 2013-06-09 一种绝缘pvc塑料的制备方法

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
CN2013102295046A CN103319797A (zh) 2013-06-09 2013-06-09 一种绝缘pvc塑料的制备方法

Publications (1)

Publication Number Publication Date
CN103319797A true CN103319797A (zh) 2013-09-25

Family

ID=49188868

Family Applications (1)

Application Number Title Priority Date Filing Date
CN2013102295046A Withdrawn CN103319797A (zh) 2013-06-09 2013-06-09 一种绝缘pvc塑料的制备方法

Country Status (1)

Country Link
CN (1) CN103319797A (zh)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105896381A (zh) * 2016-06-17 2016-08-24 国网河南桐柏县供电公司 一种输电线路异物清除装置
CN110408147A (zh) * 2019-08-01 2019-11-05 无锡天竺滑导电器制造有限公司 一种耐热抗老化的pvc管材及其制备方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5430699B2 (zh) * 1976-03-29 1979-10-02
CN101348591A (zh) * 2008-07-08 2009-01-21 常州百佳磁卡有限公司 Pvc卡基材料
CN101397382A (zh) * 2007-09-29 2009-04-01 苏州工业园区凯维新材料有限公司 一种抗黄变聚氯乙烯
CN101824193A (zh) * 2010-02-24 2010-09-08 杭州高新绝缘材料有限公司 一种耐寒pvc电缆料及制备方法
US20110065866A1 (en) * 2008-05-07 2011-03-17 Arkema France Composition containing a halogenated vinyl polymer and a copolymer bearing associative groups
US20110077342A1 (en) * 2008-06-03 2011-03-31 Arkema France Method for the multi-step preparation of halogen-containing composite latex having associative groups

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5430699B2 (zh) * 1976-03-29 1979-10-02
CN101397382A (zh) * 2007-09-29 2009-04-01 苏州工业园区凯维新材料有限公司 一种抗黄变聚氯乙烯
US20110065866A1 (en) * 2008-05-07 2011-03-17 Arkema France Composition containing a halogenated vinyl polymer and a copolymer bearing associative groups
US20110077342A1 (en) * 2008-06-03 2011-03-31 Arkema France Method for the multi-step preparation of halogen-containing composite latex having associative groups
CN101348591A (zh) * 2008-07-08 2009-01-21 常州百佳磁卡有限公司 Pvc卡基材料
CN101824193A (zh) * 2010-02-24 2010-09-08 杭州高新绝缘材料有限公司 一种耐寒pvc电缆料及制备方法

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105896381A (zh) * 2016-06-17 2016-08-24 国网河南桐柏县供电公司 一种输电线路异物清除装置
CN110408147A (zh) * 2019-08-01 2019-11-05 无锡天竺滑导电器制造有限公司 一种耐热抗老化的pvc管材及其制备方法

Similar Documents

Publication Publication Date Title
CN104559379A (zh) 一种导电发热涂料
CN104945779A (zh) 高绝缘电缆护套材料
CN109251442A (zh) 一种可拉伸耐弯折pvc软管的制备方法
CN103319797A (zh) 一种绝缘pvc塑料的制备方法
CN109593265A (zh) 一种低收缩硅烷电缆料及其制备方法
CN103319798A (zh) 一种绝缘pvc塑料
CN106046622B (zh) 一种用于制造电缆绝缘层的材料及其制备方法
CN105001448A (zh) 一种耐高温增塑剂
CN112080085A (zh) 一种5g电缆用高阻燃聚氯乙烯绝缘料及其制备方法
CN107141384A (zh) 一种高黑度石墨可发性聚苯乙烯颗粒的生产方法
CN104593071A (zh) 氯化石蜡的制备方法
CN106299006B (zh) 一种太阳能电池背板膜及其制备方法
CN103816636A (zh) 一种以红柱石粉为主料的灭火剂
CN105837631B (zh) 一种含磷改性环氧增塑剂的制备方法及得到的增塑剂
CN107298786A (zh) 一种碳酸钙‑聚乙烯树脂组合物及其制备方法
CN103897290A (zh) 一种绝缘pvc塑料
CN103668667B (zh) 一种保暖透气面料及其制备方法
CN105440542A (zh) 一种高强度pvc板材及其制备方法
CN105837893A (zh) 一种耐寒性无卤阻燃电缆及其制备方法
CN105504560A (zh) 一种耐老化电缆保护套
CN105001502A (zh) 保温塑料桶
CN104393079B (zh) 防老化太阳能电池背板及其制备方法
CN107226929A (zh) 一种塑胶助剂及其生产方法
CN107216678A (zh) 一种具有阻燃性能的覆盖膜的生产方法
CN106117942B (zh) 一种隔热保温的建筑材料及其制备方法

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C04 Withdrawal of patent application after publication (patent law 2001)
WW01 Invention patent application withdrawn after publication

Application publication date: 20130925