CN103317306B - 一种螺旋缝双金属复合焊管的制造方法 - Google Patents

一种螺旋缝双金属复合焊管的制造方法 Download PDF

Info

Publication number
CN103317306B
CN103317306B CN201310232039.1A CN201310232039A CN103317306B CN 103317306 B CN103317306 B CN 103317306B CN 201310232039 A CN201310232039 A CN 201310232039A CN 103317306 B CN103317306 B CN 103317306B
Authority
CN
China
Prior art keywords
welding
pipe
spiral seam
adopt
manufacture method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310232039.1A
Other languages
English (en)
Other versions
CN103317306A (zh
Inventor
毕宗岳
刘海璋
张万鹏
杨军
张锦刚
牛辉
张君
黄晓辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China National Petroleum Corp
Baoji Petroleum Steel Pipe Co Ltd
Original Assignee
Baoji Petroleum Steel Pipe Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baoji Petroleum Steel Pipe Co Ltd filed Critical Baoji Petroleum Steel Pipe Co Ltd
Priority to CN201310232039.1A priority Critical patent/CN103317306B/zh
Publication of CN103317306A publication Critical patent/CN103317306A/zh
Application granted granted Critical
Publication of CN103317306B publication Critical patent/CN103317306B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种螺旋缝双金属复合焊管的制造方法，第一步：将“***+热轧”工艺制成的复合板材进行矫直、表面处理，并在板材两边加工X型焊接坡口；第二步：将加工后的复合板材连续送入螺旋管成型机组逐渐弯曲成管状，并形成螺旋缝；第三步：对成型的螺旋缝采用MAG焊接工艺进行过渡层的连续预焊；第四步：采用MAG或SAW焊接工艺，在管外进行基层的连续焊接；第五步：采用TIG焊接工艺在管内对复层连续焊接；第六步：经定径、检测、后处理形成产品。本发明采用螺旋成型的方式实现了用同一宽度的复合卷板制造出不同管径的双金属复合管，且采用两步法焊接工艺，适合工业化批量生产。

Description

一种螺旋缝双金属复合焊管的制造方法
技术领域
本发明属于复合焊管制造技术领域，具体涉及一种螺旋缝双金属复合焊管的制造方法。
背景技术
输油、输气管道中的H2S、CO2会引起管道严重的均匀腐蚀、点腐蚀、硫化物应力腐蚀开裂和氢致开裂，从而导致输送管道的失效和事故，采用耐腐蚀复合管是最经济的方式之一。采用价格远低于不锈钢的双金属复合管是耐腐蚀油气输送管材发展的方向，由于受到复合板材宽度的限制，直缝成型的复合管无法满足用户需要。
发明内容
本发明提供一种螺旋缝双金属复合焊管的制造方法，以“***+热轧”工艺制成的复合卷板为原料，采用螺旋成型焊接工艺制造，可以实现工业化的批量生产。
本发明采用的技术方案是：一种螺旋缝双金属复合焊管的其制造方法，包括下述工艺步骤：
第一步：将“***+热轧”工艺制成的双金属复合板材耐蚀合金一面朝上碳钢一面朝下进行矫直、表面处理，并在板材两边加工X型焊接坡口；
第二步：将加工有X型焊接坡口的双金属复合板材连续送入螺旋管成型机组逐渐弯曲成管状，并形成螺旋缝；
第三步：对成型的螺旋缝采用MAG焊接工艺在管内进行过渡层的连续预焊，在预焊过程中可随时对钢管的几何形状进行调整；
第四步：采用MAG或SAW焊接工艺，在管外进行基层的连续焊接；
第五步：采用TIG焊接工艺在管内对复层连续焊接；
第六步：经定径、检验、后处理形成产品。
所述复层为不锈钢板材316L、304L、2205，或钛及钛合金板材，且厚度为1-2mm；所述基层为X52、X60、X65、X70管线钢板材。
所述X型焊接坡口的基层面坡口角度b为60-70°，复层面坡口角度c为80-90°。
本发明具有的优点和效果：
1、本发明采用螺旋成型的方式实现了用同一宽度的复合卷板制造出不同管径的双金属复合管，拓宽了双金属复合管的应用领域。
2、本发明采用两步法焊接工艺完成螺旋缝双金属复合管的焊接，防止了基层碳钢成分过渡到复层，采用合理的焊接顺序，避免了复层由于焊接受热而引起的耐腐蚀性能下降，其力学性能和耐腐蚀性能均达到要求，适合工业化批量生产。
附图说明
图1本发明结构示意图，图2本发明断面结构示意图，图3本发明X型焊接坡口结构示意图。
具体实施方式：
一种螺旋缝双金属复合焊管的其制造方法，包括下述工艺步骤：
第一步：将“***+热轧”工艺制成的双金属复合板材耐蚀合金一面朝上碳钢一面朝下进行矫直、表面处理，并在板材两边加工X型焊接坡口；
第二步：将加工有X型焊接坡口的双金属复合板材连续送入螺旋管成型机组逐渐弯曲成管状，并形成螺旋缝3；
第三步：对成型的螺旋缝3采用MAG焊接工艺在管内进行过渡层的连续预焊，在预焊过程中可随时对钢管的几何形状进行调整；
第四步：采用MAG或SAW焊接工艺，在管外进行碳钢基层1的连续焊接；
第五步：采用TIG焊接工艺在管内对耐蚀合金复层2连续焊接；
第六步：经定径、检测、后处理形成产品。
所述复层2为不锈钢板材316L、304L、2205，或钛及钛合金板材，且厚度为1-2mm；所述基层1为X52、X60、X65、X70管线钢板材。
所述X型焊接坡口的基层面坡口角度b为60-70°，复层面坡口角度c为80-90°。
实施例1：以2205/X65双金属复合板为原料（其中2205不锈钢板厚度2mm，X65管线钢板厚度10mm），采用X型复合坡口，且基层面单边坡口角度为35°并留有1mm钝边，复层面单边坡口角度为45°，复合板螺旋成型以后先采用TIG焊的方法焊接过渡层，再采用MAG焊或SAW焊的方法焊接基层，最后采用TIG焊的方法离线焊接复层。具体焊接工艺参数如下：
焊管力学性能试验结果：抗拉强度675MPa，0℃冲击韧性焊缝为105J，热影响区为210J，焊缝正反弯180度无裂纹。腐蚀试验按标准GB/T4334-2008进行，在硫酸-硫酸铜溶液中沸腾72小时，弯曲无裂纹。
实施例2：以纯钛TA1/X65双金属复合板为原料（纯钛TA1厚度2mm，X65厚度10mm），采用X型复合坡口，且基层面单边坡口角度为32°并留有1mm钝边，复层面单边坡口角度为40°，复合板螺旋成型以后先采用TIG焊的方法焊接过渡层，再采用MAG焊或SAW焊的方法焊接基层，最后采用TIG焊的方法离线焊接复层。
焊管力学性能试验结果：抗拉强度705MPa，0℃冲击韧性焊缝为85J，热影响区为180J，焊缝正反弯180度无裂纹。腐蚀试验按照ASTMB898-05进行，在硫酸-硫酸铜溶液中沸腾72小时，弯曲无裂纹。
上述实施例，只是本发明的较佳实施例，并非用来限制本发明实施范围，故凡以本发明权利要求所述内容所做的等同变化，均应包括在本发明权利要求范围之内。

Claims (3)

1.一种螺旋缝双金属复合焊管的制造方法，其特征在于包括下述工艺步骤：
第一步：将“***+热轧”工艺制成的双金属复合板材耐蚀合金一面朝上碳钢一面朝下进行矫直、表面处理，并在板材两边加工X型焊接坡口；
第二步：将加工有X型焊接坡口的双金属复合板材连续送入螺旋管成型机组逐渐弯曲成管状，形成螺旋缝；
第三步：对成型的螺旋缝采用MAG焊接工艺在管内进行过渡层的连续预焊，在预焊过程中可随时对管的几何形状进行调整；
第四步：采用MAG或SAW焊接工艺，在管外进行基层的连续焊接；
第五步：采用TIG焊接工艺在管内对复层连续焊接。
2.按照权利要求1所述的一种螺旋缝双金属复合焊管的制造方法，其特征在于：所述复层为不锈钢板材316L、不锈钢板材304L、不锈钢板材2205，钛或钛合金板材，且厚度为1-2mm；所述基层为X52、X60、X65或X70管线钢板材。
3.按照权利要求1或2所述的一种螺旋缝双金属复合焊管的制造方法，其特征在于：所述X型焊接坡口的基层面坡口角度b为60-70°并留有1mm钝边，复层面坡口角度c为80-90°。
CN201310232039.1A 2013-06-09 2013-06-09 一种螺旋缝双金属复合焊管的制造方法 Active CN103317306B (zh)