CN103304972B - 一种耐高温树脂组合物 - Google Patents
一种耐高温树脂组合物 Download PDFInfo
- Publication number
- CN103304972B CN103304972B CN201310265632.6A CN201310265632A CN103304972B CN 103304972 B CN103304972 B CN 103304972B CN 201310265632 A CN201310265632 A CN 201310265632A CN 103304972 B CN103304972 B CN 103304972B
- Authority
- CN
- China
- Prior art keywords
- resistanresin
- high temperature
- resin composition
- parts
- unsaturated polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种耐高温树脂组合物,包括以下重量配比的组分:不饱和聚酯树脂40-45份、岩棉10-15份、滑石粉1-2份、三氧化二锑5-10份。本发明耐高温树脂组合物具有耐高温阻燃、耐腐蚀、高强度、可常温固化等特点,且制备工艺简单,生产周期短,可广泛用于机械缠绕、浇铸、手糊、模压等工艺,具有广泛的市场价值和巨大的市场潜力。
Description
技术领域
本发明涉及一种耐高温树脂组合物。
背景技术
随着腐蚀与防护的不断发展和工业化程度的提高,复合材料的应用领域也越来越广,使用工况,介质越来越复杂,使用温度也越来越高,市场对其性能的要求也越来越高。
目前,国内外领域采用树脂材料比较单一,主要以不饱和聚酯、乙烯基酯树脂、韧性环氧树脂为主。由于不饱和聚酯树脂存在脆性大、使用温度低、粘接强度低等缺点,难以得到广泛应用。
发明内容
本发明的目的是为了解决现有技术中存在的缺陷,提供一种能有效耐高温的不饱和聚酯树脂。
为了达到上述目的,本发明提供了一种耐高温树脂组合物,包括以下重量配比的组分:不饱和聚酯树脂40-45份、岩棉10-15份、滑石粉1-2份、三氧化二锑5-10份。
上述耐高温树脂组合物还包括异辛酸钴,优选配比为:不饱和聚酯树脂40-42份、岩棉10-12份、滑石粉1-2份、三氧化二锑5-8份、异辛酸钴5-7份。
上述耐高温树脂组合物还包括复合铁钛,最佳配比为:不饱和聚酯树脂40-42份、岩棉10-12份、滑石粉1-2份、三氧化二锑5-8份、异辛酸钴5-7份、复合铁钛10-15份。
本发明相比现有技术具有以下优点:利用岩棉、三氧化二锑等阻燃作用,提高组合物的耐高温性能,同时添加异辛酸钴作为催干剂,能有效加快组合物的固化速度;本发明利用均匀分散的复合铁钛,有效增加了组合物的抗腐蚀性能,增强了粘结性能。本发明耐高温树脂组合物具有耐高温阻燃、耐腐蚀、高强度、可常温固化等特点,且制备工艺简单,生产周期短,可广泛用于机械缠绕、浇铸、手糊、模压等工艺,具有广泛的市场价值和巨大的市场潜力。
具体实施方式
下面结合具体实施例对本发明耐高温树脂组合物进行详细说明。
实施例1
取不饱和聚酯树脂40份、岩棉10份、滑石粉1份、三氧化二锑5份、异辛酸钴5份、复合铁钛10份,球磨机研磨2小时即得本发明耐高温组合物。
实施例2
取不饱和聚酯树脂45份、岩棉15份、滑石粉2份、三氧化二锑10份,搅拌均匀即得本发明耐高温组合物。
实施例3
取不饱和聚酯树脂42份、岩棉12份、滑石粉2份、三氧化二锑8份、异辛酸钴7份,搅拌均匀即得本发明耐高温组合物。
Claims (1)
1.一种耐高温树脂组合物,其特征在于:所述耐高温树脂组合物由以下重量配比的组分组成:不饱和聚酯树脂40份、岩棉10份、滑石粉1份、三氧化二锑5份、异辛酸钴5份、复合铁钛10份。