CN103289251A - 一种抗静电pvc塑料及其制备方法 - Google Patents
一种抗静电pvc塑料及其制备方法 Download PDFInfo
- Publication number
- CN103289251A CN103289251A CN2013102548321A CN201310254832A CN103289251A CN 103289251 A CN103289251 A CN 103289251A CN 2013102548321 A CN2013102548321 A CN 2013102548321A CN 201310254832 A CN201310254832 A CN 201310254832A CN 103289251 A CN103289251 A CN 103289251A
- Authority
- CN
- China
- Prior art keywords
- pvc
- preparation
- antistatic
- antistatic pvc
- cpe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种抗静电PVC塑料及其制备方法，由PVC、DOP、CPE、金属粉、硬脂酸钡、硬脂酸酰胺、二碱式硫酸铅、炉法炭黑、PE蜡制成，将PVC、DOP、CPE投入高混机，混合均匀，再加入剩余组分，控制转速300～600r/min，温度150～200℃，搅拌15-20min，放料冷却；然后挤出造粒。本发明具有如下有益效果：具有优良的抗静电性能和拉伸强度，耐高温。
Description
技术领域
本发明涉及塑胶领域，尤其涉及一种抗静电PVC塑料及其制备方法。
背景技术
静电，就是一种处于静止状态的电荷或者说不流动的电荷（流动的电荷就形成了电流）。当电荷聚集在某个物体上或表面时就形成了静电，而电荷分为正电荷和负电荷两种，也就是说静电现象也分为两种即正静电和负静电。当正电荷聚集在某个物体上时就形成了正静电，当负电荷聚集在某个物体上时就形成了负静电，但无论是正静电还是负静电，当带静电物体接触零电位物体 （接地物体）或与其有电位差的物体时都会发生电荷转移，就是我们日常见到火花放电现象。例如北方冬天天气干燥，人体容易带上静电，当接触他人或金属导电体时就会出现放电现象，这些静电对人体都有一定的损害。塑料是现代社会广泛使用的高分子合成材料，具有很高的表面电阻率，从而使得塑料一经摩擦就会使静电停留在塑料表面，影响了塑料制品的使用；而且塑料产品的日益普及，静电无处不在，对人们危害极大。为了防止塑料的静电产生，可以在塑料表面涂覆抗静电剂，但是涂层容易刮落，不能从根本上解决静电问题。本发明提供了一种本身带有抗静电效果的塑料。
发明内容
本发明提供了一种抗静电塑料及其制备方法，具有良好的抗静电效果。
本发明采用以下技术方案：
一种抗静电PVC塑料，包括以下重量份计的组分：
PVC 100
DOP 5～8
CPE（氯化聚乙烯） 10～20
金属粉 1～2
硬脂酸钡 0.5～1 硬脂酸酰胺 0.5～1 二碱式硫酸铅 1～2
炉法炭黑 30～45
PE蜡 0.5～1
作为优选，炉法炭黑的粒度大于80目。
作为优选，金属粉为Ba、Cd、Zn粉中的一种或多种。
上述抗静电塑料的制备方法包括以下步骤：将PVC、DOP、CPE投入高混机，混合均匀，再加入剩余组分，控制转速300～600r/min，温度150～200℃，搅拌15-20min，放料冷却；然后挤出造粒。
作为优选，所述的PVC投入高混机之前在60-70℃干燥至水分为0.07%。
作为优选，所述的干燥采用热风干燥。
本发明的表面电阻高达2×108Ω，能很好的防止静电，拉伸强度在50MPa左右，具有良好的力学性能，透光率近90%，浊度较低，小于4%，产品的外观性能良好，变形温度超过200℃，远远大于一般的塑料制品。
具体实施方式
下面结合具体实施例对本发明作进一步详细介绍。
实施例1
一种抗静电PVC塑料，包括以下重量份计的组分：
PVC 100
DOP 8
CPE 20
Ba 2
硬脂酸钡 1 硬脂酸酰胺 1 二碱式硫酸铅 2
炉法炭黑（粒度大于80目） 45
PE蜡 1
上述抗静电塑料的制备方法包括以下步骤：PVC在60℃热风干燥至水分为0.07%，将干燥后的PVC、DOP、CPE投入高混机，混合均匀，再加入剩余组分，控制转速600r/min，温度200℃，搅拌20min，放料冷却；然后挤出造粒。
实施例2
一种抗静电PVC塑料，包括以下重量份计的组分：
PVC 100
DOP 5
CPE 10
Cd 1
硬脂酸钡 0.5
硬脂酸酰胺 0.5 二碱式硫酸铅 1
炉法炭黑（粒度大于80目） 30
PE蜡 0.5
上述抗静电塑料的制备方法包括以下步骤：PVC在70℃热风干燥至水分为0.07%，将干燥后的PVC、DOP、CPE投入高混机，混合均匀，再加入剩余组分，控制转速300r/min，温度150℃，搅拌15min，放料冷却；然后挤出造粒。
实施例3
一种抗静电PVC塑料，包括以下重量份计的组分：
PVC 100
DOP 6
CPE 15
Zn 1.5
硬脂酸钡 0.8 硬脂酸酰胺 0.8 二碱式硫酸铅 1.5
炉法炭黑（粒度大于80目） 35
PE蜡 0.8
上述抗静电塑料的制备方法包括以下步骤：PVC在65℃热风干燥至水分为0.07%，将干燥后的PVC、DOP、CPE投入高混机，混合均匀，再加入剩余组分，控制转速500r/min，温度180℃，搅拌18min，放料冷却；然后挤出造粒。
下面通过试验测试实施例1、2、3制得的产品的性能：
| 测试方法 | 实施例1 | 实施例2 | 实施例3 | |
| 拉伸强度MPa | ASTM D-638 | 52.5 | 53.6 | 53.8 |
| 透光率% | ASTM D-1003 | 86.5 | 87.3 | 88.4 |
| 浊度% | ISO14782 | 3.9 | 3.6 | 3.8 |
| 维卡温度℃ | ASTM D-1525 | 78.8 | 78.8 | 78.7 |
| 表面电阻Ω | GB/T1410-2006 | 2.3×108 | 2.1×108 | 2.2×108 |
| 变形温度℃ | ASTMD-648 | 230 | 225 | 226 |
Claims (6)
1.一种抗静电PVC塑料，其特征在于包括以下重量份计的组分：
PVC 100
DOP 5～8
CPE 10～20
金属粉 1～2
硬脂酸钡 0.5～1
硬脂酸酰胺 0.5～1
二碱式硫酸铅 1～2
炉法炭黑 30～45
PE蜡 0.5～1。
2.根据权利要求1所述的抗静电PVC塑料，其特征在于：炉法炭黑的粒度大于80目。
3.根据权利要求1所述的抗静电PVC塑料，其特征在于：金属粉为Ba、Cd、Zn粉中的一种或多种。
4.基于权利要求1所述的抗静电PVC塑料的制备方法，其特征在于包括以下步骤：将PVC、DOP、CPE投入高混机，混合均匀，再加入剩余组分，控制转速300～600r/min，温度150～200℃，搅拌15-20min，放料冷却；然后挤出造粒。
5.根据权利要求4所述的抗静电PVC塑料的制备方法，其特征在于：所述的PVC投入高混机之前在60-70℃干燥至水分为0.07%。
6.根据权利要求4所述的抗静电PVC塑料的制备方法，其特征在于：所述的干燥采用热风干燥。