CN103274600B - The Decoration production method that can produce concavo-convex embossment in glaze paint and the glaze used thereof - Google Patents
The Decoration production method that can produce concavo-convex embossment in glaze paint and the glaze used thereof Download PDFInfo
- Publication number
- CN103274600B CN103274600B CN201310198930.8A CN201310198930A CN103274600B CN 103274600 B CN103274600 B CN 103274600B CN 201310198930 A CN201310198930 A CN 201310198930A CN 103274600 B CN103274600 B CN 103274600B
- Authority
- CN
- China
- Prior art keywords
- glaze
- parts
- production method
- paint
- silk screen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of Decoration production method that can produce concavo-convex embossment in glaze paint and the glaze used thereof, the step of this Decoration production method is as follows: 1) get the raw materials ready according to following component and each component mass fraction: frit 50 parts ~ 60 parts; Guizhou clay 5 parts ~ 10 parts; 10 parts ~ 20 parts, calcite; 8 parts ~ 16 parts, zinc oxide; 2) by material: ball: water=1: 1.5: 1.5, wet ball grinding 20 ~ 24 hours; 3) 200 mesh sieves crossed by the glaze after ball milling, cross 120 mesh sieves, then added silk-screen ink and be uniformly mixed, obtain silk screen glaze slip after drying; 4) get the chinaware body of the bright and clean first-class color glaze of appearance, after scraping silk screen glaze slip, under the oxidizing atmosphere of 1160 DEG C ~ 1200 DEG C, fire finished product.The glaze paint of the enamal organ obtained by present method presents uneven and clearly demarcated anaglyph, makes glaze paint pattern more vivid, porcelain is become and has feel.
Description
Technical field
The present invention relates to a kind of Decoration production method that can produce concavo-convex embossment in glaze paint and the glaze used thereof.
Background technology
At present, in porcelain industry, the moulding of porcelain base is the basis of quality products, and the allotment of glaze makes porcelain more bright and colourful, and on glaze, decoration makes porcelain become no longer dull, and the vision generation impact in various degree to human consumer.Form concavo-convex embossment at ceramic surface and there is its special cubic appearance, be favourably welcome in household china and bone china.Prior art engraving, landfill or printing transferring method process relief shape on biscuit of ceramics, execute axle again, glaze firing is formed with the pottery of plastic relief sensation, this way needs a lot of artificial and die, complex process, tooling cost is high, and gathers more glaze but concave-convex effect is clear not at recess, thus the pottery made is only applicable to the rough products such as Wall or floor tile usually, can not be suitable for as the field such as household china, artistic porcelain.
Summary of the invention
Technical problem to be solved by this invention overcomes the deficiencies in the prior art, a kind of Decoration production method that can produce concavo-convex embossment in glaze paint is provided, uneven and clearly demarcated anaglyph is presented by the glaze paint of its obtained enamal organ, make glaze paint pattern more vivid, porcelain is become and has feel.
The present invention solves the problems of the technologies described above taked technical scheme: a kind of Decoration production method that can produce concavo-convex embossment in glaze paint, and the step of the method is as follows: 1) get the raw materials ready according to following component and each component mass fraction: frit 50 parts ~ 60 parts; Guizhou clay 5 parts ~ 10 parts; 10 parts ~ 20 parts, calcite; 8 parts ~ 16 parts, zinc oxide; 2) by material: ball: water=1:1.5:1.5, wet ball grinding 20 ~ 24 hours; 3) 200 mesh sieves crossed by the glaze after ball milling, cross 120 mesh sieves, then added silk-screen ink and be uniformly mixed, obtain silk screen glaze slip after drying; 4) get the chinaware body of the bright and clean first-class color glaze of appearance, after scraping silk screen glaze slip, under the oxidizing atmosphere of 1160 DEG C ~ 1200 DEG C, fire finished product.
Further, in described step 4), the thickness of the silk screen glaze slip on chinaware body is 0.05 millimeter ~ 0.08 millimeter.
Present invention also offers a kind of glaze that can produce concavo-convex embossment in glaze paint, its each component and each component mass fraction as follows: frit 50 parts ~ 60 parts; Guizhou clay 5 parts ~ 10 parts; 10 parts ~ 20 parts, calcite; 8 parts ~ 16 parts, zinc oxide.
After have employed technique scheme, middle lead of getting the raw materials ready in the inventive method, cadmium content meet international standard, the glaze paint of the enamal organ obtained by the inventive method is uneven, and clearly concavo-convex, have feel, exactly like embossment, glaze paint pattern is more vivid, people is looked over so as to check unforgettable, and tooling cost is few, technique is simple.
Embodiment
In order to make content of the present invention more easily be clearly understood, below according to specific embodiment, the present invention is further detailed explanation,
Embodiment one
A glaze for concavo-convex embossment can be produced in glaze paint, its each component and each component mass fraction as follows: frit 50 parts; Guizhou clay 5 parts; 10 parts, calcite; 8 parts, zinc oxide.
Can produce a Decoration production method for concavo-convex embossment in glaze paint, the step of the method is as follows:
1) get the raw materials ready according to above glaze component and each component mass fraction:
2) by material: ball: water=1:1.5:1.5, wet ball grinding 21 hours;
3) 200 mesh sieves crossed by the glaze after ball milling, cross 120 mesh sieves, then added silk-screen ink and be uniformly mixed, obtain silk screen glaze slip, also can suitably add a little additive after drying;
4) get the chinaware body of the bright and clean first-class color glaze of appearance, scrape silk screen glaze slip, the gauge control of the silk screen glaze slip on chinaware body, in 0.05 millimeter ~ 0.08 millimeter, then fires finished product under the oxidizing atmosphere of 1160 DEG C ~ 1200 DEG C.
The glaze paint of the enamal organ obtained by the method for the present embodiment is uneven, and clearly concavo-convex, has feel, exactly likes embossment, and glaze paint pattern is more vivid, and people is looked over so as to check unforgettable, and tooling cost is few, technique is simple.
Embodiment two
A glaze for concavo-convex embossment can be produced in glaze paint, its each component and each component mass fraction as follows: frit 60 parts; Guizhou clay 10 parts; 20 parts, calcite; 16 parts, zinc oxide.
Can produce a Decoration production method for concavo-convex embossment in glaze paint, the step of the method is as follows:
1) get the raw materials ready according to above glaze component and each component mass fraction:
2) by material: ball: water=1:1.5:1.5, wet ball grinding 23 hours;
3) 200 mesh sieves crossed by the glaze after ball milling, cross 120 mesh sieves, then added silk-screen ink and be uniformly mixed, obtain silk screen glaze slip after drying;
4) get the chinaware body of the bright and clean first-class color glaze of appearance, scrape silk screen glaze slip, the gauge control of the silk screen glaze slip on chinaware body, in 0.05 millimeter ~ 0.08 millimeter, then fires finished product under the oxidizing atmosphere of 1160 DEG C ~ 1200 DEG C.
The glaze paint of the enamal organ obtained by the method for the present embodiment is uneven, and clearly concavo-convex, has feel, exactly likes embossment, and glaze paint pattern is more vivid, and people is looked over so as to check unforgettable, and tooling cost is few, technique is simple.
Embodiment three
A glaze for concavo-convex embossment can be produced in glaze paint, its each component and each component mass fraction as follows: frit 55 parts; Guizhou clay 7 parts; 15 parts, calcite; 12 parts, zinc oxide.
Can produce a Decoration production method for concavo-convex embossment in glaze paint, the step of the method is as follows:
1) get the raw materials ready according to above glaze component and each component mass fraction:
2) by material: ball: water=1:1.5:1.5, wet ball grinding 22 hours;
3) 200 mesh sieves crossed by the glaze after ball milling, cross 120 mesh sieves, then added silk-screen ink and be uniformly mixed, obtain silk screen glaze slip after drying;
4) get the chinaware body of the bright and clean first-class color glaze of appearance, scrape silk screen glaze slip, the gauge control of the silk screen glaze slip on chinaware body, in 0.05 millimeter ~ 0.08 millimeter, then fires finished product under the oxidizing atmosphere of 1160 DEG C ~ 1200 DEG C.
The glaze paint of the enamal organ obtained by the method for the present embodiment is uneven, and clearly concavo-convex, has feel, exactly likes embossment, and glaze paint pattern is more vivid, and people is looked over so as to check unforgettable, and tooling cost is few, technique is simple.
Above-mentioned three embodiments, the value of having got three scopes in upper, middle and lower of each component weight part respectively detects, the preparation repeatedly through experimenter can be drawn, making method of the present invention still can glaze paint uneven, and it is clearly concavo-convex, have feel, exactly like embossment, glaze paint pattern is more vivid.
Above-described specific embodiment; technical problem of the present invention, technical scheme and beneficial effect are further described; be understood that; the foregoing is only specific embodiments of the invention; be not limited to the present invention; within the spirit and principles in the present invention all, any amendment made, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. energy produces a Decoration production method for concavo-convex embossment in glaze paint, it is characterized in that the step of the method is as follows:
1) get the raw materials ready according to following component and each component mass fraction: frit 50 parts ~ 60 parts; Guizhou clay 7 parts; 15 parts ~ 20 parts, calcite; 8 parts, zinc oxide;
2) by material: ball: water=1:1.5:1.5, wet ball grinding 20 ~ 24 hours;
3) 200 mesh sieves crossed by the glaze after ball milling, cross 120 mesh sieves, then added silk-screen ink and be uniformly mixed, obtain silk screen glaze slip after drying;
4) get the chinaware body of the bright and clean first-class color glaze of appearance, after scraping silk screen glaze slip, under the oxidizing atmosphere of 1160 DEG C ~ 1200 DEG C, fire finished product.
2. the Decoration production method that can produce concavo-convex embossment in glaze paint according to claim 1, is characterized in that: described step 4) in, the thickness of the silk screen glaze slip on chinaware body is 0.05 millimeter ~ 0.08 millimeter.