CN103265742B - A kind of Oil-Resistant Cable Sheath - Google Patents
A kind of Oil-Resistant Cable Sheath Download PDFInfo
- Publication number
- CN103265742B CN103265742B CN201310153369.1A CN201310153369A CN103265742B CN 103265742 B CN103265742 B CN 103265742B CN 201310153369 A CN201310153369 A CN 201310153369A CN 103265742 B CN103265742 B CN 103265742B
- Authority
- CN
- China
- Prior art keywords
- resistance
- modified filler
- resistant
- oil
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Does is the invention discloses a kind of Oil-Resistant Cable Sheath, it made up of the raw material of following weight parts: chloroprene rubber DCR114? 94-100, Japanese JSR paracril N220S16-20, n-BMA 6-8, dimethyl fumarate 4-5, calcium oxide 4-6, talcum powder 2-3, Zinic stearas 5-8, nano-bentonite 16-20, modified filler 23-30, dioctyl maleate 5-7, three ammonium molybdate 1-2, anilinomethyl triethoxysilane 1-2, vulcanizing agent DCBP0.8-1, Vulcanization accelerator TMTD 0.8-1; The cable jacket material excellent physical properties that the present invention produces, dimensional stabilizing, shrinking percentage is low, product draws degree of promoting the strong, tearing toughness, screen resilience performance strong, has good oil resistant, heat-resisting, resistance to combustion, resistance to daylight, resistance to ozone, acid and alkali-resistance, chemical reagent-resistant performance, modified filler of the present invention, good dispersity, surface tension is low, further increases the tensile strength of CABLE MATERIALS, stress at definite elongation, reduce heat-dissipating and compression set, not only can delay the aging speed of CABLE MATERIALS, and energy acid-alkali-corrosive-resisting, reduce production cost.
Description
Technical field
The present invention relates generally to a kind of cable jacket material, particularly relates to a kind of Oil-Resistant Cable Sheath.
Background technology
Chloroprene rubber has good physical and mechanical properties, and oil resistant is heat-resisting, resistance to combustion, resistance to daylight, resistance to ozone, acid and alkali-resistance, chemical-resistant reagent.There is higher tensile strength, elongation and reversible crystallinity, cementability is good, ageing-resistant, heat-resisting, oil resistant, chemical resistance are excellent, can life-time service at 80 ~ 100 DEG C, there is certain flame retardant resistance, but it is poor that shortcoming is package stability, therefore just can ensure that it has very strong heat-resisting, ageing-resistant, oil resistant, the characteristic such as corrosion-resistant with chloroprene rubber as cable jacket material, and improve its package stability by adding some modified fillers, the just further performance improving cable jacket material.
Summary of the invention
The object of the invention is exactly to provide a kind of Oil-Resistant Cable Sheath.
The present invention is achieved by the following technical solutions:
A kind of Oil-Resistant Cable Sheath, it is made up of the raw material of following weight parts:
Chloroprene rubber DCR11494-100, Japanese JSR paracril N220S16-20, n-BMA 6-8, dimethyl fumarate 4-5, calcium oxide 4-6, talcum powder 2-3, Zinic stearas 5-8, nano-bentonite 16-20, modified filler 23-30, dioctyl maleate 5-7, three ammonium molybdate 1-2, anilinomethyl triethoxysilane 1-2, vulcanizing agent DCBP0.8-1, Vulcanization accelerator TMTD 0.8-1;
Described modified filler is made up of the raw material of following weight parts:
Sulphuric acid soln 900-1000, the barium sulphide 80-90 of 0.3-0.5%, ethanol 30-40, aluminium-hydroxide powder 10-15, sorbitan monooleate 10-12, distearyl acyl-oxygen aluminum isopropoxide acid esters 2-3, titanium dioxide 2-4, Union carbide A-162 1-2, sodium polyacrylate 4-6, dicumyl peroxide 1-2, sodium silicate 4-6, stearic acid 2-4, water are appropriate;
Above-mentioned sulphuric acid soln is continued to pass in barium sulphide, after passing into, add sodium polyacrylate, fully 6-10 minute is stirred at 60-80 DEG C, cross and filter filtrate, filter cake is carried out washing 2-3 time, add 1-2 times of water, aluminium-hydroxide powder, titanium dioxide, sorbitan monooleate, Union carbide A-162, dispersed with stirring 10-20 minute under the rotating speed of 2000-2500 rev/min, add each raw material of residue again, fully stir, being heated to temperature is 70-80 DEG C, ball milling, dries fineness is the modified filler of 2-4 μm.
Advantage of the present invention is:
The cable jacket material excellent physical properties that the present invention produces, dimensional stabilizing, shrinking percentage is low, product draws degree of promoting the strong, tearing toughness, screen resilience performance strong, has good oil resistant, heat-resisting, resistance to combustion, resistance to daylight, resistance to ozone, acid and alkali-resistance, chemical reagent-resistant performance, modified filler of the present invention, good dispersity, surface tension is low, further increases the tensile strength of CABLE MATERIALS, stress at definite elongation, reduce heat-dissipating and compression set, not only can delay the aging speed of CABLE MATERIALS, and energy acid-alkali-corrosive-resisting, reduce production cost.
Embodiment
Embodiment 1
A kind of Oil-Resistant Cable Sheath, is characterized in that what it was made up of the raw material of following weight parts (kilogram):
Chloroprene rubber DCR114100, Japanese JSR paracril N220S20, n-BMA 8, dimethyl fumarate 5, calcium oxide 6, talcum powder 3, Zinic stearas 8, nano-bentonite 20, modified filler 30, dioctyl maleate 5, three ammonium molybdate 2, anilinomethyl triethoxysilane 2, vulcanizing agent DCBP0.8, Vulcanization accelerator TMTD 0.8;
Described modified filler is made up of the raw material of following weight parts:
Concentration be 0.5% sulphuric acid soln 1000, barium sulphide 90, ethanol 40, aluminium-hydroxide powder 15, sorbitan monooleate 12, distearyl acyl-oxygen aluminum isopropoxide acid esters 3, titanium dioxide 4, Union carbide A-162 2, sodium polyacrylate 6, dicumyl peroxide 2, sodium silicate 6, stearic acid 3, water appropriate;
Above-mentioned sulphuric acid soln is continued to import in above-mentioned barium sulphide, after importing, adds sodium polyacrylate, fully stir 10 minutes at 80 DEG C, cross and filter filtrate, filter cake is carried out washing 3 times, add 2 times of water, aluminium-hydroxide powder, titanium dioxide, sorbitan monooleate, Union carbide A-162s, stirring and segregation 20 minutes under the rotating speed of 2500 revs/min, add each raw material of residue, fully stir, being heated to temperature is 80 DEG C, ball milling, dries fineness is the modified filler of 4 μm.
The preparation method of described anti-Oil-Resistant Cable Sheath comprises the following steps:
(1) above-mentioned chloroprene rubber DCR114 is mixed with Japanese JSR paracril N220S, n-BMA, dimethyl fumarate, dioctyl maleate add Banbury mixer, at temperature is 90 DEG C mixing 3 minutes;
(2) above-mentioned calcium oxide, talcum powder, Zinic stearas, nano-bentonite 20, modified filler is added again, at temperature is 90 DEG C, mixing 6 minutes;
(3) add each raw material of residue again, at temperature is 60 DEG C mixing 3 minutes, discharging cooled and obtains described cable jacket material.
Performance test:
Tensile strength: 16.5MPa;
Elongation at break: 685%;
Oil-proofness: 20# machine oil 100 DEG C × 80h, elongation at break conservation rate 68.3%, tensile strength retention 70.1%;
Resistance to ozone: 25 DEG C, 24h, ozone concn 0.025%, without cracking;
Ageing-resistant: 120 DEG C, 150h, tensile strength retention 81.7%, elongation at break conservation rate 72.4%.
Claims (1)
1. an Oil-Resistant Cable Sheath, is characterized in that what it was made up of the raw material of following weight parts:
Chloroprene rubber DCR11494-100, Japanese JSR paracril N220S16-20, n-BMA 6-8, dimethyl fumarate 4-5, calcium oxide 4-6, talcum powder 2-3, Zinic stearas 5-8, nano-bentonite 16-20, modified filler 23-30, dioctyl maleate 5-7, three ammonium molybdate 1-2, anilinomethyl triethoxysilane 1-2, vulcanizing agent DCBP0.8-1, Vulcanization accelerator TMTD 0.8-1;
Described modified filler is made up of the raw material of following weight parts:
Sulphuric acid soln 900-1000, the barium sulphide 80-90 of 0.3-0.5%, ethanol 30-40, aluminium-hydroxide powder 10-15, sorbitan monooleate 10-12, distearyl acyl-oxygen aluminum isopropoxide acid esters 2-3, titanium dioxide 2-4, Union carbide A-162 1-2, sodium polyacrylate 4-6, dicumyl peroxide 1-2, sodium silicate 4-6, stearic acid 2-4, water are appropriate;
Above-mentioned sulphuric acid soln is continued to pass in barium sulphide, after passing into, add sodium polyacrylate, fully 6-10 minute is stirred at 60-80 DEG C, cross and filter filtrate, filter cake is carried out washing 2-3 time, add 1-2 times of water, aluminium-hydroxide powder, titanium dioxide, sorbitan monooleate, Union carbide A-162, dispersed with stirring 10-20 minute under the rotating speed of 2000-2500 rev/min, add each raw material of residue again, fully stir, being heated to temperature is 70-80 DEG C, ball milling, dries fineness is the modified filler of 2-4 μm.