CN103254793B - 一种环保型防锈油及其制备方法 - Google Patents
一种环保型防锈油及其制备方法 Download PDFInfo
- Publication number
- CN103254793B CN103254793B CN201310132989.7A CN201310132989A CN103254793B CN 103254793 B CN103254793 B CN 103254793B CN 201310132989 A CN201310132989 A CN 201310132989A CN 103254793 B CN103254793 B CN 103254793B
- Authority
- CN
- China
- Prior art keywords
- mentioned
- add
- oil
- raw material
- antirust oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种环保型防锈油,它是由下述重量份的原料组成的0#轻柴油40-45、100#机械油35-40、羊毛脂3-5、环烷酸锌3-5、异丁醇2-4、己二酸二辛酯3-4、六次甲基四胺2-3、烷基二苯胺1-3、烷基酚聚氧乙烯醚磷酸酯4-5、成膜助剂2-4、癸酸2-3、二烷基二硫代磷酸锌2-4、纳米硅藻土0.6-0.8;本发明生产的防锈油不易变色,不易氧化,不影响工件的外观,综合性能优异,具有高的耐盐雾性、耐湿热性、耐老化性等,可清洗性能好,通过加入的成膜助剂,改善了油膜的表面张力,使得喷涂均匀,在金属工件表面铺展性能好,形成的油膜均匀稳定,提高了对金属保持的保护作用。
Description
技术领域
本发明主要涉及一种油,尤其涉及一种环保型防锈油及其制备方法。
背景技术
随着现在国防、汽车制造等行业的迅速发展,对金属板材的需求量越来越大,对板材的表面质量要求也越来越高,因为如何防腐,降低成产、运输、贮存成本的损失是重中之重,目前,防止金属腐蚀的普遍做饭是将工件表面涂上一层防锈油,目前传统的防锈油大多成分简单,在某种或者几个特定的方面性能不错,但是综合性能不良,有的防锈油防锈期短,有的抗盐雾能力差,有的漆膜不稳定,难以满足防锈需求。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种环保型防锈油及其制备方法。
本发明是通过以下技术方案实现的:
一种环保型防锈油,它是由下述重量份的原料组成的:
0#轻柴油40-45、100#机械油35-40、羊毛脂3-5、环烷酸锌3-5、异丁醇2-4、己二酸二辛酯3-4、六次甲基四胺2-3、烷基二苯胺1-3、烷基酚聚氧乙烯醚磷酸酯4-5、成膜助剂2-4、癸酸2-3、二烷基二硫代磷酸锌2-4、纳米硅藻土0.6-0.8;
所述的成膜助剂是由下述重量份的原料组成的:
氯丁橡胶CR12150-60、eva树脂20-30、二甲苯30-40、聚乙烯醇8-10、羟乙基乙撑双硬脂酰胺1-2、2-正辛基-4-异噻唑啉-3-酮3-4、甲基苯并三氮唑2-3、甲基三乙氧基硅烷1-2、十二烷基聚氧乙烯醚2-3、过氧化二异丙苯1-2、2,5-二甲基-2,5-二(叔丁基过氧化)己烷0.8-1;
所述的成膜助剂的制备包括以下步骤:
将上述氯丁橡胶CR121加入密炼机内,在温度为70-80℃下单独塑炼10-20分钟,然后出料冷却至常温;
将上述eva树脂、羟乙基乙撑双硬脂酰胺、2-正辛基-4-异噻唑啉-3-酮、甲基苯并三氮唑、十二烷基聚氧乙烯醚混合,在90-100℃下反应1-2小时,加入上述塑炼后的氯丁橡胶,降低温度为80-90℃,继续反应40-50分钟,再加入剩余各原料,在温度为60-70℃下反应4-5小时。
一种环保型防锈油的制备方法,包括以下步骤:
(1)将上述0#轻柴油、100#机械油加入到反应釜中,搅拌,加热到110-120℃;
(2)加入上述羊毛脂,加热搅拌使其溶解;
(3)加入上述环烷酸锌、异丁醇、烷基酚聚氧乙烯醚磷酸酯、二烷基二硫代磷酸锌,连续脱水1-1.5小时,降温至于55-60℃;
(4)加入上述烷基二苯胺、己二酸二辛酯,在55-60℃下保温搅拌3-4小时;
(5)加入剩余各原料,充分搅拌,降低温度至35-38℃,过滤出料。
本发明的优点是:
本发明生产的防锈油不易变色,不易氧化,不影响工件的外观,综合性能优异,具有高的耐盐雾性、耐湿热性、耐老化性等,可清洗性能好,通过加入的成膜助剂,改善了油膜的表面张力,使得喷涂均匀,在金属工件表面铺展性能好,形成的油膜均匀稳定,提高了对金属保持的保护作用。
具体实施方式
实施例1
一种环保型防锈油,它是由下述重量份(公斤)的原料组成的:
0#轻柴油45、100#机械油40、羊毛脂5、环烷酸锌5、异丁醇4、己二酸二辛酯4、六次甲基四胺3、烷基二苯胺3、烷基酚聚氧乙烯醚磷酸酯5、成膜助剂4、癸酸2、二烷基二硫代磷酸锌4、纳米硅藻土0.8;
所述的成膜助剂是由下述重量份的原料组成的:
氯丁橡胶CR12160、eva树脂(VA含量28)30、二甲苯40、聚乙烯醇10、羟乙基乙撑双硬脂酰胺1、2-正辛基-4-异噻唑啉-3-酮4、甲基苯并三氮唑3、甲基三乙氧基硅烷2、十二烷基聚氧乙烯醚3、过氧化二异丙苯2、2,5-二甲基-2,5-二(叔丁基过氧化)己烷0.8;
所述的成膜助剂的制备包括以下步骤:
将上述氯丁橡胶CR121加入密炼机内,在温度为80℃下单独塑炼20分钟,然后出料冷却至常温;
将上述eva树脂、羟乙基乙撑双硬脂酰胺、2-正辛基-4-异噻唑啉-3-酮、甲基苯并三氮唑、十二烷基聚氧乙烯醚混合,在100℃下反应2小时,加入上述塑炼后的氯丁橡胶,降低温度为90℃,继续反应50分钟,再加入剩余各原料,在温度为70℃下反应5小时。
一种环保型防锈油的制备方法,包括以下步骤:
(1)将上述0#轻柴油、100#机械油加入到反应釜中,搅拌,加热到120℃;
(2)加入上述羊毛脂,加热搅拌使其溶解;
(3)加入上述环烷酸锌、异丁醇、烷基酚聚氧乙烯醚磷酸酯、二烷基二硫代磷酸锌,连续脱水1小时,降温至于60℃;
(4)加入上述烷基二苯胺、己二酸二辛酯,在60℃下保温搅拌4小时;
(5)加入剩余各原料,充分搅拌,降低温度至38℃,过滤出料。
性能测试:
表观:无沉淀、无分层、无结晶物析出;
耐盐雾实验:36℃,170小时,无腐蚀;
耐湿热实验:50℃,700小时,无腐蚀;
耐候性实验:实验工件为100块45#钢,大小均为200mm*200mm*10mm,表面无锈蚀,其中50块工件施用传统的防锈油,50块工件施用本发明防锈油,至于同一室内,实验时间2年,经测试,施用本发明防锈油的工件腐蚀程度最高的为1.5%,腐蚀程度最低的为0.8%,平均腐蚀率为0.98%;施用传统防锈油的工件腐蚀程度最高的为4.4%,腐蚀程度最低的为3.6%,平均腐蚀率为3.98%。
Claims (2)
1.一种环保型防锈油,其特征在于它是由下述重量份的原料组成的:
0#轻柴油40-45、100#机械油35-40、羊毛脂3-5、环烷酸锌3-5、异丁醇2-4、己二酸二辛酯3-4、六次甲基四胺2-3、烷基二苯胺1-3、烷基酚聚氧乙烯醚磷酸酯4-5、成膜助剂2-4、癸酸2-3、二烷基二硫代磷酸锌2-4、纳米硅藻土0.6-0.8;
所述的成膜助剂是由下述重量份的原料组成的:
氯丁橡胶CR12150-60、EVA树脂20-30、二甲苯30-40、聚乙烯醇8-10、羟乙基乙撑双硬脂酰胺1-2、2-正辛基-4-异噻唑啉-3-酮3-4、甲基苯并三氮唑2-3、甲基三乙氧基硅烷1-2、十二烷基聚氧乙烯醚2-3、过氧化二异丙苯1-2、2,5-二甲基-2,5-二(叔丁基过氧化)己烷0.8-1;
所述的成膜助剂的制备包括以下步骤:
将上述氯丁橡胶CR121加入密炼机内,在温度为70-80℃下单独塑炼10-20分钟,然后出料冷却至常温;
将上述EVA树脂、羟乙基乙撑双硬脂酰胺、2-正辛基-4-异噻唑啉-3-酮、甲基苯并三氮唑、十二烷基聚氧乙烯醚混合,在90-100℃下反应1-2小时,加入上述塑炼后的氯丁橡胶,降低温度为80-90℃,继续反应40-50分钟,再加入剩余各原料,在温度为60-70℃下反应4-5小时。
2.一种如权利要求1所述的环保型防锈油的制备方法,其特征在于包括以下步骤:
(1)将上述0#轻柴油、100#机械油加入到反应釜中,搅拌,加热到110-120℃;
(2)加入上述羊毛脂、己二酸二辛酯,加热搅拌使其溶解;
(3)加入上述环烷酸锌、异丁醇、烷基酚聚氧乙烯醚磷酸酯,连续脱水1-1.5小时,降温至55-60℃;
(4)加入上述烷基二苯胺、二烷基二硫代磷酸锌,在55-60℃下保温搅拌3-4小时;
(5)加入剩余各原料,充分搅拌,降低温度至35-38℃,过滤出料。