CN103253917B - A kind of light lath for building partition wall Kaolin binder - Google Patents
A kind of light lath for building partition wall Kaolin binder Download PDFInfo
- Publication number
- CN103253917B CN103253917B CN201310135537.4A CN201310135537A CN103253917B CN 103253917 B CN103253917 B CN 103253917B CN 201310135537 A CN201310135537 A CN 201310135537A CN 103253917 B CN103253917 B CN 103253917B
- Authority
- CN
- China
- Prior art keywords
- powder
- kaolin
- partition wall
- building partition
- light lath
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of light lath for building partition wall Kaolin binder, be made up of the raw material of following weight part: 42.5 fast hard aluminum sulfate salt cement 100-120, vinyl acetate homopolymerization rubber powder 8-12, mountain sand 100-150, vegetable fibre 4-6, limestone powder 3-5, gypsum 5-7, instant powdery sodium silicate 12-18, talcum powder 5-8, kaolin 8-12, sludge dry powder 4-6, Vltra tears 1-1.5.Light lath for building partition wall Kaolin binder cohesive force of the present invention is strong, the chance reducing layering and peel off, and ensures construction quality, avoids the hollowing after life-time service, problems of crack, thus improves weather resistance; Invention adhesive dry mixing in advance mixes, and steady quality, adds the stirring of suitable quantity of water during use, construct simple and convenient; The present invention effectively utilizes the waste materials such as sludge dry powder, without poisonous and harmful additive, meets environmental requirement completely, safety non-pollution.
Description
Technical field
The present invention relates to a kind of material of construction binding agent, be specifically related to a kind of light lath for building partition wall Kaolin binder.
Background technology
Light lath for building partition wall take ordinary Portland cement as gelling material, with light-weight aggregates such as haydite, pearlstone, industrial residues for main raw material, and the porous air core type batten produced by extrusion molding.A certain amount of binding agent is needed to fix during its construction and installation.But existing binding agent exists that operating efficiency is low, cementability is poor, useful life longevity is poor and the shortcoming such as poor stability, can not meet the bonding requirement of light lath for building partition wall.Therefore, a kind of brand-new high performance light lath for building partition wall tackiness agent of research and development is badly in need of.
Summary of the invention
The object of the invention is to for the deficiencies in the prior art, provide that a kind of cohesive strength is high, good endurance, construction are simple, the light lath for building partition wall Kaolin binder of safety non-toxic evil.
The technical solution used in the present invention is as follows:
A kind of light lath for building partition wall Kaolin binder, is made up of the raw material of following weight part:
42.5 quick hardening sulphoaluminate cement 100-120
Vinyl acetate homopolymerization rubber powder 8-12
Mountain sand 100-150
Vegetable fibre 4-6
Limestone powder 3-5
Gypsum 5-7
Instant powdery sodium silicate 12-18
Talcum powder 5-8
Kaolin 8-12
Sludge dry powder 4-6
Vltra tears 1-1.5.
Preferably, a kind of light lath for building partition wall Kaolin binder, is made up of the raw material of following weight part:
42.5 quick hardening sulphoaluminate cement 100
Vinyl acetate homopolymerization rubber powder 10
Mountain sand 120
Vegetable fibre 5
Limestone powder 4
Gypsum 5
Instant powdery sodium silicate 16
Talcum powder 6
Kaolin 10
Sludge dry powder 5
Vltra tears 1.
Above-mentioned raw materials dry mixing is even, and ball milling, crosses 200-300 mesh sieve, packs.
Beneficial effect of the present invention:
Light lath for building partition wall Kaolin binder cohesive force of the present invention is strong, the chance reducing layering and peel off, and ensures construction quality, avoids the hollowing after life-time service, problems of crack, thus improves weather resistance; Invention adhesive dry mixing in advance mixes, and steady quality, adds the stirring of suitable quantity of water during use, construct simple and convenient; The present invention effectively utilizes the waste materials such as sludge dry powder, without poisonous and harmful additive, meets environmental requirement completely, safety non-pollution.
Embodiment
A kind of light lath for building partition wall Kaolin binder, is made up of the raw material of following weight part (kilogram):
42.5 quick hardening sulphoaluminate cement 100
Vinyl acetate homopolymerization rubber powder 10
Mountain sand 120
Vegetable fibre 5
Limestone powder 4
Gypsum 5
Instant powdery sodium silicate 16
Talcum powder 6
Kaolin 10
Sludge dry powder 5
Vltra tears 1.
Above-mentioned raw materials dry mixing is even, and ball milling, crosses 300 mesh sieves, packs.
Binding agent Specifeca tion speeification of the present invention is as follows:
Tensile bond strength (Mpa): 1.3
Tensile bond strength (Mpa) after immersion: 1.1
Tensile bond strength (Mpa) after thermal ageing: 0.9
Tensile bond strength (Mpa) after freeze-thaw cycle: 0.7.
Claims (3)
1. a light lath for building partition wall Kaolin binder, is characterized in that, is made up of the raw material of following weight part:
42.5 quick hardening sulphoaluminate cement 100-120
Vinyl acetate homopolymerization rubber powder 8-12
Mountain sand 100-150
Vegetable fibre 4-6
Limestone powder 3-5
Gypsum 5-7
Instant powdery sodium silicate 12-18
Talcum powder 5-8
Kaolin 8-12
Sludge dry powder 4-6
Vltra tears 1-1.5.
2. a kind of light lath for building partition wall Kaolin binder according to claim 1, is characterized in that, be made up of the raw material of following weight part:
42.5 quick hardening sulphoaluminate cement 100
Vinyl acetate homopolymerization rubber powder 10
Mountain sand 120
Vegetable fibre 5
Limestone powder 4
Gypsum 5
Instant powdery sodium silicate 16
Talcum powder 6
Kaolin 10
Sludge dry powder 5
Vltra tears 1.
3. light lath for building partition wall Kaolin binder according to claim 1, is characterized in that, the preparation method of described binding agent is as follows: above-mentioned raw materials dry mixing is even, and ball milling is crossed 200-300 mesh sieve, packed.