CN103241973A - 一种铝酸钙混凝土速凝剂的配制方法 - Google Patents
一种铝酸钙混凝土速凝剂的配制方法 Download PDFInfo
- Publication number
- CN103241973A CN103241973A CN2012100242783A CN201210024278A CN103241973A CN 103241973 A CN103241973 A CN 103241973A CN 2012100242783 A CN2012100242783 A CN 2012100242783A CN 201210024278 A CN201210024278 A CN 201210024278A CN 103241973 A CN103241973 A CN 103241973A
- Authority
- CN
- China
- Prior art keywords
- calcium aluminate
- concrete
- hardenfast
- preparation
- accelerator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝酸钙混凝土速凝剂的配制方法，该产品属于化工建材领域。本发明是以铝酸钙粉、矾泥、二水石膏、生石灰、喷射混凝土粘稠剂为原料，通过磨细，过筛来制备混凝土速凝剂，该配制方法工艺简单，生产成本低，产品质量好，添加到混凝土中之后，能使混凝土在5分钟内初凝，10分钟内终凝，对后期强度影响小，且无毒无味，对从事喷射混凝土操作人员身体健康无影响。
Description
技术领域
本发明产品属于化工建材领域，尤其涉及一种铝酸钙混凝土速凝剂的配制方法。
背景技术
混凝土速凝剂是一种掺入混凝土中能使混凝土迅速凝结硬化的外加剂，外观为粉状固体或液体，它们的作用是加速水泥的水化硬化，在很短的时间内形成足够的强度，以保证特殊施工的要求，其掺用量一般为水泥用量2%～3%，却能使混凝土在3-5分钟内初凝，7-10分钟内终凝，是喷射混凝土施工法中不可缺少的添加剂。铝酸钙是配制混凝土速凝剂的原料之一，其优点是价格低廉， 铝酸钙外观为灰白色粉末，分子式为：Al2CaO4，分子量为：158.039，工业上使用的铝酸钙粉纯度不高且成分复杂，但主要成份是二铝酸钙和一铝酸钙的混合物，微溶于水，水溶液呈碱性，pH值约为11，铝酸钙粉与无机强酸反应活性很高，在常温下即可启动发生，且放热量大，升温快。工业级铝酸钙粉主要用途是：1.生产聚合氯化铝、硫酸铝、铝酸钠等铝盐的产品；2.也可用于碱化度的调整；3.可用于耐火材料；4.土木工程方面作为混凝土速凝剂的原料。单一的铝酸钙粉就是一种混凝土速凝剂，为了使其速凝效果更好，需添加部分材料来增强其速凝效果。本发明是一种铝酸钙粉为主要原料配制的速凝剂，以铝酸钙粉、矾泥、二水石膏、生石灰、喷射混凝土粘稠剂为原料，通过磨细，过筛来制备混凝土速凝剂，该配制方法工艺简单，生产成本低，产品质量好，添加到混凝土中之后，能使混凝土在5分钟内初凝，10分钟内终凝，对后期强度影响小，且无毒无味，对从事喷射混凝土操作人员身体健康无影响。
发明内容
本发明要解决的问题是提供一种批量制备铝酸钙混凝土速凝剂的方法，该剂是以铝酸钙粉、矾泥、二水石膏、生石灰、喷射混凝土粘稠剂为原料，通过磨细，过筛来制备混凝土速凝剂，该配制方法工艺简单，生产成本低，产品质量好。生产该产品使用的原料配比是：铝酸钙粉50%-55%、矾泥20%-25%、二水石膏10%、生石灰10%、喷射混凝土粘稠剂5%。
本发明可以通过以下技术方案来实现：
一种铝酸钙混凝土速凝剂的制备方法，其特征由以下步骤构成：
1.将配方量的铝酸钙粉、矾泥、二水石膏、生石灰、喷射混凝土粘稠剂先混合均匀，然后送入破碎机破碎。
2.将破碎后的物料过筛，其颗粒的细度为25-35微米，大于35微米的颗粒应筛去。
3. 使用时，先将粉状铝酸钙混凝土速凝剂加水搅拌均匀，从喷射混凝土的喷口处添加即可。
本发明的有益效果是：提供了一种铝酸钙混凝土速凝剂的制备方法，该制备方法工艺简单，生产成本低，产品质量好，添加到混凝土中之后，能使混凝土在5分钟内初凝，10分钟内终凝，对后期强度影响小，且无毒无味，对从事喷射混凝土操作人员身体健康无影响。
具体实施方式
实施例1
将占总量为50%的铝酸钙粉、占总量为25%的矾泥、占总量为10%的二水石膏、占总量为10%的生石灰、占总量为5%的喷射混凝土粘稠剂先混合均匀，然后送入破碎机破碎；将破碎后的物料过筛，其颗粒的细度为25-35微米，大于35微米的颗粒应筛去；使用时，先将粉状铝酸钙混凝土速凝剂加水搅拌均匀，从喷射混凝土的喷口处添加即可。
实施例2
将占总量为52.5%的铝酸钙粉、占总量为22.5%的矾泥、占总量为10%的二水石膏、占总量为10%的生石灰、占总量为5%的喷射混凝土粘稠剂先混合均匀，然后送入破碎机破碎；将破碎后的物料过筛，其颗粒的细度为25-35微米，大于35微米的颗粒应筛去；使用时，先将粉状铝酸钙混凝土速凝剂加水搅拌均匀，从喷射混凝土的喷口处添加即可。
实施例3
将占总量为55%的铝酸钙粉、占总量为20%的矾泥、占总量为10%的二水石膏、占总量为10%的生石灰、占总量为5%的喷射混凝土粘稠剂先混合均匀，然后送入破碎机破碎；将破碎后的物料过筛，其颗粒的细度为25-35微米，大于35微米的颗粒应筛去；使用时，先将粉状铝酸钙混凝土速凝剂加水搅拌均匀，从喷射混凝土的喷口处添加即可。
Claims (3)
1.一种铝酸钙混凝土速凝剂的配制方法，其原料配方按重量百分比计算，包括：铝酸钙粉50%-55%、矾泥20%-25%、二水石膏10%、生石灰10%、喷射混凝土粘稠剂5%；其特征是：步骤一，将配方量的铝酸钙粉、矾泥、二水石膏、生石灰、喷射混凝土粘稠剂先混合均匀，然后送入破碎机破碎；步骤二，将破碎后的物料过筛，其颗粒的细度为25-35微米，大于35微米的颗粒应筛去。
2.根据权利要求1所述的一种铝酸钙混凝土速凝剂的配制方法，其步骤二的特征是：铝酸钙混凝土速凝剂颗粒的细度为30微米。
3.根据权利要求1所述的一种铝酸钙混凝土速凝剂的配制方法，其铝酸钙混凝土速凝剂的使用方法是，先将粉状铝酸钙混凝土速凝剂加水搅拌均匀，从喷射混凝土的喷口处添加即可。