CN103232792B - Protective system of a kind of high rigidity and preparation method thereof - Google Patents
Protective system of a kind of high rigidity and preparation method thereof Download PDFInfo
- Publication number
- CN103232792B CN103232792B CN201310107156.5A CN201310107156A CN103232792B CN 103232792 B CN103232792 B CN 103232792B CN 201310107156 A CN201310107156 A CN 201310107156A CN 103232792 B CN103232792 B CN 103232792B
- Authority
- CN
- China
- Prior art keywords
- protective system
- epoxy resin
- weight part
- compound
- ethyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses protective system of a kind of high rigidity and preparation method thereof, its constitutive material is: epoxy resin E-55, supervinyi chloride resin, 1,2,3-benzotriazole, dehydrated alcohol, vermiculite power, alcohol ester 12, linking agent TAC, 2-ethyl-4-methylimidazole, dispersing agent MF, polydimethylsiloxane, 4,4-methylene-bis (2,6 di t butyl phenol), antioxidant MB and dimethylbenzene; Present invention employs epoxy resin E-55 and the supervinyi chloride resin major ingredient as protective system, dimethylbenzene is as solvent, after applying coating solidification, form polymeric material, become nonpoisonous and tasteless environment-friendly coating, there is fabulous sticking power to steel surface, with the addition of vermiculite power, alcohol ester 12, linking agent TAC and 2-ethyl-4-methylimidazole simultaneously, the mechanical property of whole coating system can be made to significantly improve.
Description
Technical field
The present invention relates to a kind of protective system, be specifically related to protective system of a kind of high rigidity and preparation method thereof.
Background technology
Metallic corrosion be due to metallic surface by the chemistry of surrounding medium or electrochemical action destroyed phenomenon, effective, the most the most frequently used method of protection against corrosion is at metallic surface coating erosion shield, matrix and corrosive medium is completely cut off.The Corrosion Protection of coating is mainly reflected in the solidity to corrosion of coating to corrosive medium, and the permeability resistance to medium.Therefore, improve the Corrosion Protection of coating, one is select solidity to corrosion resin, and two is protection against corrosion fillers that use properties is excellent; The advantages such as it is high that epoxypaint has sticking power, and chemicals-resistant and solvent nature are excellent, hardness is high, mill property is good, alkaline-resisting, salt fog resistance is good, are widely used in protective system field.
Summary of the invention
The object of the present invention is to provide protective system of a kind of high rigidity and preparation method thereof.
The present invention adopts following technical scheme to achieve these goals:
The protective system of high rigidity, the weight part of its constitutive material is: epoxy resin E-5555-60, supervinyi chloride resin 20-26,1,2,3-benzotriazole 1.7-2.3, dehydrated alcohol 13-18, vermiculite power 40-45, alcohol ester 12 2.8-3.5, linking agent TAC4.5-5.5,2-ethyl-4-methylimidazole 16-20, dispersing agent MF 2.8-3.2, polydimethylsiloxane 4.0-5.5,4,4
,-methylene-bis (2,6 di t butyl phenol) 1.5-1.7, antioxidant MB 1.4-2.0, dimethylbenzene 50-55.
The protective system of high rigidity, the weight part of its constitutive material is: epoxy resin E-5558, supervinyi chloride resin 23,1,2,3-benzotriazole 2.0, dehydrated alcohol 15, vermiculite power 42, alcohol ester 12, linking agent TAC5.0,2-ethyl-4-methylimidazole 18, dispersing agent MF 3.0, polydimethylsiloxane 4.8,4,4-methylene-bis (2,6 di t butyl phenol) 1.6, antioxidant MB 1.7, dimethylbenzene 52.
The preparation method of the protective system of high rigidity, comprises the following steps:
(1) modification of epoxy resin E-55: take epoxy resin E-55 by the weight part of constitutive material, then 80: 27-33: 1.0-1.5:15-20 mixes by weight ratio by epoxy resin E-55, trolamine, nanometer deposed brick slag powder and nano titanium oxide;
(2) compound A: the solvent xylene of step (1) raw material and 2/5-2/3 is mixed, then supervinyi chloride resin, 1 is added by the weight part of constitutive material, 2,3-benzotriazole, dehydrated alcohol, vermiculite power, alcohol ester 12, linking agent TAC, dispersing agent MF, polydimethylsiloxane, 4,4-methylene-bis (2,6-DI-tert-butylphenol compounds) and antioxidant MB, be uniformly mixed and obtain compound;
(3) compound B: 2-ethyl-4-methylimidazole and remaining solvent xylene are mixed by the weight part of constitutive material;
(4) the compound B mix and blend 2.0-3.5h of the compound A of step (2) and step (3) is got final product protective system.
Beneficial effect of the present invention:
Present invention employs epoxy resin E-55 and the supervinyi chloride resin major ingredient as protective system, dimethylbenzene is as solvent, after applying coating solidification, form polymeric material, become nonpoisonous and tasteless environment-friendly coating, there is fabulous sticking power to steel surface, with the addition of vermiculite power, alcohol ester 12, linking agent TAC and 2-ethyl-4-methylimidazole simultaneously, the mechanical property of whole coating system can be made to significantly improve.
Embodiment
Embodiment 1: the protective system of high rigidity, the weight part (kg) of its constitutive material is: epoxy resin E-5558, supervinyi chloride resin 23,1,2,3-benzotriazole 2.0, dehydrated alcohol 15, vermiculite power 42, alcohol ester 12, linking agent TAC5.0,2-ethyl-4-methylimidazole 18, dispersing agent MF 3.0, polydimethylsiloxane 4.8,4,4
,-methylene-bis (2,6 di t butyl phenol) 1.6, antioxidant MB 1.7, dimethylbenzene 52.
The preparation method of the protective system of high rigidity, comprises the following steps:
(1) modification of epoxy resin E-55: take epoxy resin E-55 by the weight part of constitutive material, then 80: 30: 1.2:18 mixes by weight ratio by epoxy resin E-55, trolamine, nanometer deposed brick slag powder and nano titanium oxide;
(2) compound A: the solvent xylene of step (1) raw material and 2/5-2/3 is mixed, then supervinyi chloride resin, 1 is added by the weight part of constitutive material, 2,3-benzotriazole, dehydrated alcohol, vermiculite power, alcohol ester 12, linking agent TAC, dispersing agent MF, polydimethylsiloxane, 4,4-methylene-bis (2,6-DI-tert-butylphenol compounds) and antioxidant MB, be uniformly mixed and obtain compound;
(3) compound B: by the weight part of constitutive material, 2-ethyl-4-methylimidazole and remaining solvent xylene are mixed, fully dissolve;
(4) the compound B of the compound A of step (2) and step (3) is got final product protective system by weight 1:2 mix and blend 2.8h.
The basic mechanical design feature Indexs measure of protective system of the present invention:
Protective system of the present invention is sprayed on steel plate, time of drying: surface drying≤6.0h, does solid work≤27h; Thermotolerance 260 DEG C: 5.5h passes through; Resistance to 45% sulfuric acid: 34 days without exception; Resistance to 5% sodium hydroxide: 31 days without exception; Viscosity (being coated with 4# cup): >=86s; Impact strength: 53-55cm.
Claims (2)
1. the protective system of a high rigidity, it is characterized in that the weight part of its constitutive material is: epoxy resin E-5555-60, supervinyi chloride resin 20-26,1,2,3-benzotriazole 1.7-2.3, dehydrated alcohol 13-18, vermiculite power 40-45, alcohol ester 12 2.8-3.5, linking agent TAC4.5-5.5,2-ethyl-4-methylimidazole 16-20, dispersing agent MF 2.8-3.2, polydimethylsiloxane 4.0-5.5,4,4,-methylene-bis (2,6 di t butyl phenol) 1.5-1.7, antioxidant MB 1.4-2.0, dimethylbenzene 50-55;
The preparation method of the protective system of described high rigidity, comprises the following steps:
(1) modification of epoxy resin E-55: take epoxy resin E-55 by the weight part of constitutive material, then 80: 27-33: 1.0-1.5:15-20 mixes by weight ratio by epoxy resin E-55, trolamine, nanometer deposed brick slag powder and nano titanium oxide;
(2) compound A: the solvent xylene of step (1) raw material and 2/5-2/3 is mixed, then supervinyi chloride resin, 1 is added by the weight part of constitutive material, 2,3-benzotriazole, dehydrated alcohol, vermiculite power, alcohol ester 12, linking agent TAC, dispersing agent MF, polydimethylsiloxane, 4,4-methylene-bis (2,6-DI-tert-butylphenol compounds) and antioxidant MB, be uniformly mixed and obtain compound;
(3) compound B: 2-ethyl-4-methylimidazole and remaining solvent xylene are mixed by the weight part of constitutive material;
(4) the compound B mix and blend 2.0-3.5h of the compound A of step (2) and step (3) can be obtained protective system.
2. the protective system of high rigidity according to claim 1, it is characterized in that the weight part of its constitutive material is: epoxy resin E-5558, supervinyi chloride resin 23,1,2,3-benzotriazole 2.0, dehydrated alcohol 15, vermiculite power 42, alcohol ester 12, linking agent TAC5.0,2-ethyl-4-methylimidazole 18, dispersing agent MF 3.0, polydimethylsiloxane 4.8,4,4-methylene-bis (2,6 di t butyl phenol) 1.6, antioxidant MB 1.7, dimethylbenzene 52.