CN103232768B - 免打磨型木纹填充剂 - Google Patents
免打磨型木纹填充剂 Download PDFInfo
- Publication number
- CN103232768B CN103232768B CN201310124779.3A CN201310124779A CN103232768B CN 103232768 B CN103232768 B CN 103232768B CN 201310124779 A CN201310124779 A CN 201310124779A CN 103232768 B CN103232768 B CN 103232768B
- Authority
- CN
- China
- Prior art keywords
- weighting agent
- wood grain
- exempt
- polishing type
- type wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种用于实木、贴皮家具填充剂领域，特别涉及一种免打磨型木纹填充剂；所述免打磨型木纹填充剂，所述是单液型油漆，包括以下重量百分数的组分：大豆植物长油类触变型醇酸树脂4-6%、氯醚树脂1-2%、环氧大豆油3-4%、分散剂1-2%、硅微粉60-65%、复合溶剂20-25%、半透明色粉4-8%；本发明是通过木纹着色加强木纹纹理，提高立体感和层次感；且节省底漆的用量，防止底漆下限，减少导管起泡；此填充剂具有良好的擦拭施工性，用于机械化操作，着色均匀，待干20-30分钟后不打磨直接上涂底漆，呈现出良好的附着力；同时具有优异的填充性及透明性，可提高家具产品档次，节省生产成本；适合用于实木、贴皮家具的全封闭，达到有效填充导管和素材着色。
Description
技术领域
本发明涉及一种用于实木、贴皮家具填充剂领域，特别涉及一种免打磨型木纹填充剂。
背景技术
传统的填充剂因擦拭性及附着力较差，施工待干需要4小时以上后才能打磨，打磨会把素材表面的颜色打掉，且严重影响施工效率；由于目前的家具行业竞争激烈，劳工成本上升，利润空间越来越低；需要机械自动化生产、简化生产工艺、降低劳工成本是越来越多家具厂所追求的目标；填充剂对橡木、胡桃木等深导管素材的全封闭涂装有很重要的作用。
发明内容
本发明的目的是通过木纹着色加强木纹纹理，提高立体感和层次感，节省底漆的用量，防止底漆下限，减少导管起泡，且具有良好的擦拭性、着色力强、填充性好，透明度高的一种免打磨型木纹填充剂。
本发明是采用如下的配方来实现上述目的的，一种免打磨型木纹填充剂，其特征在于：所述是单液型油漆，包括以下重量百分数的组分：
大豆植物长油类触变型醇酸树脂4-6%
氯醚树脂1-2%
环氧大豆油3-4%
分散剂1-2%
硅微粉60-65%
复合溶剂20-25%
半透明色粉4-8%。
所述大豆植物长油类触变型醇酸树脂的干燥速度快、擦拭滑爽。
所述氯醚树脂对粉质的稳定性好、对素材，上涂底漆附着力好。
所述触变型醇酸树脂和氯醚树脂搭配综合性能更好，性能佳。
所述硅微粉最佳采用二氧化硅；所述硅微粉的纯度高，粒径分布窄，有良好的透明度表现。
所述分散剂最佳采用聚醚改性二甲基硅氧烷共聚体溶液。
所述复合溶剂采用醋酸丁酯、丙二醇甲醚醋酸脂、二甲苯、混酸甲酯一种或多种混合；所述复合溶剂毒性低、气味小，可完全生物降解，且VOC（挥发性有机化合物）含量符合健康要求。
所述半透明色粉最佳采用透明氧化铁。
本发明是针对现有木纹填充剂的缺陷而加以改进，具有如下优点：
1.加强木纹纹理，提高立体感和层次感；
2.节省底漆的用量，防止底漆下限，减少导管起泡；
3.具有良好的擦拭施工性，用于机械化操作，着色均匀，待干20-30分钟后不打磨直接上涂底漆，呈现出良好的附着力；
4.具有优异的填充性及透明性，可提高家具产品档次，节省生产成本；
5.适合用于实木、贴皮家具的全封闭工艺，达到有效填充导管和素材着色。
具体实施方式
下面结合具体实施例来对本发明进行详细的说明。
实施例1：
一种免打磨型木纹填充剂，所述是单液型油漆，包括以下重量百分数的组分：
大豆植物长油类触变型醇酸树脂6%
氯醚树脂2%
环氧大豆油2%
分散剂2%
硅微粉60%
复合溶剂21%
半透明色粉7%。
实施例2：
一种免打磨型木纹填充剂，所述是单液型油漆，包括以下重量百分数的组分：
大豆植物长油类触变型醇酸树脂4%
氯醚树脂2%
环氧大豆油3%
分散剂2%
硅微粉65%
复合溶剂19%
半透明色粉5%。
实施例3：
一种免打磨型木纹填充剂，所述是单液型油漆，包括以下重量百分数的组分：
大豆植物长油类触变型醇酸树脂5%
氯醚树脂1%
环氧大豆油2%
分散剂2%
硅微粉65%
复合溶剂20%
半透明色粉5%。
本发明最佳的实施例：
一种免打磨型木纹填充剂，所述是单液型油漆，包括以下重量百分数的组分：
大豆植物长油类触变型醇酸树脂4%
氯醚树脂1%
环氧大豆油3%
分散剂1.5%
硅微粉63%
复合溶剂19.5%
半透明色粉8%。
所述免打磨型木纹填充剂的技术指标见下表：
表一免打磨型木纹填充剂的技术要求
| 项 目 | 技术要求 |
| 固含量 | 75.5% |
| 外观 | 半透明色（红棕、黑棕） |
| 粘度（mpa.s/25℃） | 2300 |
| 施工比例 | 主剂：稀释剂=100:5-20 |
| 细度（um） | ≤80 |
Claims (5)
1.一种免打磨型木纹填充剂，其特征在于：所述免打磨型木纹填充剂是单液型油漆，包括以下重量百分数的组分：
2.根据权利要求1所述免打磨型木纹填充剂，其特征在于：所述硅微粉最佳采用二氧化硅。
3.根据权利要求1所述免打磨型木纹填充剂，其特征在于：所述分散剂最佳采用聚醚改性二甲基硅氧烷共聚体溶液。
4.根据权利要求1所述免打磨型木纹填充剂，其特征在于：所述复合溶剂采用醋酸丁酯、丙二醇甲醚醋酸酯、二甲苯、混酸甲酯一种或多种混合。
5.根据权利要求1所述免打磨型木纹填充剂，其特征在于：所述半透明色粉最佳采用透明氧化铁。