CN103224381B - Composition used for producing imitations, and imitation making method - Google Patents
Composition used for producing imitations, and imitation making method Download PDFInfo
- Publication number
- CN103224381B CN103224381B CN201310169835.5A CN201310169835A CN103224381B CN 103224381 B CN103224381 B CN 103224381B CN 201310169835 A CN201310169835 A CN 201310169835A CN 103224381 B CN103224381 B CN 103224381B
- Authority
- CN
- China
- Prior art keywords
- imitation
- parts
- slip
- concentration
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to the chemical engineering material field, and concretely relates to a composition used for producing imitations, and an imitation making method. The composition concretely comprises 30-40 parts of magnesium oxide powder having a purity of 84-86%, 25-30 parts of a magnesium chloride solution having a Baume degree of 22-26, 3-8 parts of gypsum powder, 6-8 parts of light calcium carbonate powder, 1-3 parts of a ferrous sulfate solution having a concentration of 10-20%, 1-3 parts of a sodium hexametaphosphate solution having a concentration of 8-13%, 1-3 parts of a magnesium sulfate solution having a concentration of 10-20%, 16-20 parts of a structure filler, and 4-6 parts of a strength filler. The addition of the structure filler and the strength filler reduces the weight of the imitations and simultaneously increases the strengths of the imitations.
Description
Technical field
The present invention relates to chemical material field, in particular to a kind of for the production of the composition of imitation and the making method of imitation.
Background technology
At first, people, when making imitative wood, imitative stone, generally use concrete slurry, put into reinforcing bar in a mold, concrete slurry is poured into preset die, solidify about 20 days.
Manufacturer adopts aluminosulfate cement to make mostly now, specifically aluminosulfate cement is made slurry, built-in fitting is put into mould, pour in mould by described slurry, natural coagulation 4 hours at 25 DEG C of temperature.
Problems existing: the imitation using Steel Concrete to make is too heavy, moves and carries inconvenience.
Summary of the invention
The object of the present invention is to provide a kind of composition for the production of imitation, the weight of obtained product can be alleviated.
Another object of the present invention is to provide a kind of making method of producing imitation.
A kind of composition for the production of imitation provided in an embodiment of the present invention, specifically comprises following material component:
Purity is magnesium oxide powder 30-40 part of 85%;
Ripple magnesium degree is magnesium chloride solution 25-30 part of 22-26;
Terra alba 3-8 part;
Light calcium carbonate powder 6-8 part;
Concentration is copperas solution 1-3 part of 10%-20%;
Concentration is sodium hexametaphosphate solution 1-3 part of 8%-13%;
Concentration is Adlerika 1-3 part of 10%-20%;
Structure filling thing 16-20 part and intensity weighting material 4-6 part.
Produce a making method for imitation, specifically comprise the steps:
Being dropped into by described magnesium oxide powder is contained with in the stirred vessel of described magnesium chloride solution, stirs 2-4 minute;
Add described copperas solution successively, described sodium hexametaphosphate solution and described Adlerika, add rear stirring 1-2 minute at every turn;
Add described light calcium carbonate powder, terra alba and described structure filling thing, stir 2-5 minute, make slip;
Described slip is evenly coated in die surface;
Described intensity weighting material is arranged on the mould being coated with described slip;
Under 25 DEG C of-30 DEG C of envrionment temperatures, the demoulding after natural coagulation 4-6 hour.
Provided by the invention a kind of for the production of the composition of imitation and the making method of imitation, use the magnesium oxide powder that purity is 84%-86%, ripple magnesium degree is the magnesium chloride solution of 22-26, terra alba, light calcium carbonate powder, concentration is the copperas solution of 10%-20%, concentration is the sodium hexametaphosphate solution of 8%-13%, concentration is that the Adlerika of 10%-20% is mixed and made into the structure congealed solid of novel magnesite material as product, and adds structure filling thing and intensity weighting material wherein can improve the intensity of product while the weight reducing product.
Accompanying drawing explanation
Fig. 1 is a kind of making method schema producing imitation of embodiment 1 provided by the invention;
Fig. 2 is a kind of making method schema producing imitation of embodiment 2 provided by the invention;
Fig. 3 is a kind of making method schema producing imitation of embodiment 3 provided by the invention.
Embodiment
Also by reference to the accompanying drawings the present invention is described in further detail below by specific embodiment.
Embodiment 1:
For the production of a composition for imitation, specifically comprise following material component:
Purity is magnesium oxide powder 30-40 part of 84%-86%;
Ripple magnesium degree is magnesium chloride solution 25-30 part of 22-26;
Terra alba 3-8 part;
Light calcium carbonate powder 6-8 part;
Concentration is copperas solution 1-3 part of 10%-20%;
Concentration is sodium hexametaphosphate solution 1-3 part of 8%-13%;
Concentration is Adlerika 1-3 part of 10%-20%;
Structure filling thing 16-20 part and intensity weighting material 4-6 part.
Produce a making method for imitation, specifically comprise the steps:
Described magnesium oxide powder input is contained with in the stirred vessel of described magnesium chloride solution by 101., stirs 2-4 minute;
102. add described copperas solution successively, described sodium hexametaphosphate solution and described Adlerika, add rear stirring 1-2 minute at every turn;
103. add described light calcium carbonate powder, described terra alba and described structure filling thing, stir 2-5 minute, make slip;
Described slip is evenly coated in die surface by 104.;
105. described intensity weighting material is arranged on be coated with described slip mould on;
106. under 25 DEG C of-30 DEG C of envrionment temperatures, the demoulding after natural coagulation 4-6 hour.
Provided by the invention a kind of for the production of the composition of imitation and the making method of imitation, use the magnesium oxide powder that purity is 84%-86%, ripple magnesium degree is the magnesium chloride solution of 22-26, light calcium carbonate powder, concentration is the copperas solution of 10%-20%, concentration is the sodium hexametaphosphate solution of 8%-13%, concentration is that the Adlerika of 10%-20% is mixed and made into the structure congealed solid of novel magnesite material as product, and adds structure filling thing and intensity weighting material wherein can improve the intensity of product while the weight reducing product.
Embodiment 2:
For the production of a composition for imitation, specifically comprise following material component:
Purity is the magnesium oxide powder 30 parts of 84.5%-85.5%;
Ripple magnesium degree is the magnesium chloride solution 25 parts of 22-26;
Terra alba 3 parts;
Light calcium carbonate powder 6 parts;
Concentration is the copperas solution 1 part of 10%-20%;
Concentration is the sodium hexametaphosphate solution 1 part of 8%-13%;
Concentration is the Adlerika 1 part of 10%-20%;
17 parts, rice husk;
Glass fiber mesh 4 parts.
Produce a making method for imitation, specifically comprise the steps:
Described magnesium oxide powder input is contained with in the stirred vessel of described magnesium chloride solution by 201., stirs 2-4 minute;
202. add described copperas solution successively, described sodium hexametaphosphate solution and described Adlerika, add rear stirring 1-2 minute at every turn;
203. add described light calcium carbonate powder, described terra alba and described rice husk, stir 2-5 minute, make slip;
Described slip is evenly coated in die surface by 204., and the thickness of the feed pulp layer of formation is 2 centimetres;
205. by 4 layers of described glass fiber mesh successively overlap be laid on described feed pulp layer, smear closely knit;
206. under 28 DEG C of envrionment temperatures under, the demoulding after natural coagulation 4-6 hour.
What provide in the present embodiment is a kind of for the production of the composition of imitation and the making method of imitation, uses rice husk as structure filling thing, can alleviate the weight of product well.And with the intensity enhancing layer of glass fiber mesh as product, the intensity of product can be improved while the weight reducing product.
Embodiment 3:
For the production of a composition for imitation, specifically comprise following material component:
Purity is the magnesium oxide powder 40 parts of 84.5%-85.5%;
Ripple magnesium degree is the magnesium chloride solution 30 parts of 22-26;
Terra alba 8 parts;
Light calcium carbonate powder 8 parts;
Concentration is the copperas solution 3 parts of 10%-20%;
Concentration is the sodium hexametaphosphate solution 3 parts of 8%-13%;
Concentration is the Adlerika 3 parts of 10%-20%;
Yellow sand 3 parts;
12 parts, sawdust;
3 parts, bamboo reinforcement circle.
Produce a making method for imitation, specifically comprise the steps:
Described magnesium oxide powder input is contained with in the stirred vessel of described magnesium chloride solution by 301., stirs 2-4 minute;
302. add described copperas solution successively, described sodium hexametaphosphate solution and described Adlerika, add rear stirring 1-2 minute at every turn;
303. add described light calcium carbonate powder, described terra alba, described yellow sand and described sawdust, stir 2-5 minute, make slip;
304. smear one deck mold oil at die surface;
Described slip is evenly coated in the die surface having smeared mold oil by 305., and the thickness of the feed pulp layer of formation is 1 centimetre;
Described bamboo reinforcement circle is located in mould by 306.;
307. under 30 DEG C of envrionment temperatures, the demoulding after natural coagulation 4-6 hour.
What provide in the present embodiment is a kind of for the production of the composition of imitation and the making method of imitation, uses yellow sand and sawdust as structure filling thing, and the weight that can alleviate product well can also improve the intensity of product simultaneously.And in mould, be provided with bamboo reinforcement circle to strengthen the intensity of product.To die surface coating slip before, first smear one deck mold oil to die surface, contribute to conveniently stripped, in case have this die bonds not easily the demoulding situation produce and damage shaping product.
Adopt glass fiber mesh or glasscloth or glass cord or bamboo reinforcement net or bamboo reinforcement circle, make various goods, cost of manufacture is low.The folding strength of the inspection well cover that the Novel magnesite material using the present invention to make makes has exceeded the folding strength of the inspection well cover of concrete or cast iron making; Do not use metallic substance at whole goods, so made product does not have regeneration recovery value, do not have the possibility that well lid is lost.
Also there is other a little simultaneously:
1. energy-conserving and environment-protective, the product produced can replace natural timber, stone material;
2. good anti-theft effect;
3. pollution-free, low cost of manufacture;
4. product can make the product of shades of colour as requested;
5. shock resistance is comparatively strong, and supporting capacity is strong, and resistance to deterioration is good;
6. rotproofness is good;
7. lightweight;
8. anti-bounce-back, car is crossed without sound;
9. good insulating;
10. long service life.
According to provided by the invention a kind of for the production of the composition of imitation and the making method of imitation, the product example of making is as follows:
Experimental example 1: ecological chair
(1) material mixture ratio: the broken glass fiber silk 0.5 part that the magnesium chloride solution 27 parts that 35 parts, magnesium oxide, ripple magnesium degree are 25, brown iron oxide pigment 0.5 part, 3 parts, gypsum, fine particle calcium carbonate 5 parts, 18 parts, sawdust, length are 2 centimetres.The yellow sand used and sawdust or powdered rice hulls are dry.
(2) operating procedure:
Magnesium oxide, gypsum, fine particle calcium carbonate and brown iron oxide pigment are put into stirrer to stir 3 minutes;
Magnesium chloride solution is put into stirrer to stir 5 minutes;
Sawdust and broken glass fiber silk are put into and stirs 3 minutes to stirrer, namely become slurry.
First in special mould, layer of glass cloth is spread after uniform brush one deck mold oil, painting one deck slurry less when making ecological chair, after above step repeatable operation 2 times, put into special bamboo reinforcement circle, pour the slurry of magnesite material in mould into, uniform application 2cm on mould is thick to be advisable; Under the environment of 25 DEG C, wait for natural coagulation, both become the ecological chair of imitative wood of making.
(3) purposes: this product adopts Suresh Kumar, many colors to produce; Can be placed on park, leisure place, home garden, etc. be suitable for and do not lose elegant.
Experimental example 2: imitative wood flower case, barrel of beer, flowerpot
(1) material mixture ratio: magnesium oxide powder 40 parts, magnesium chloride solution 30 parts, brown iron oxide pigment 0.8 part, yellow sand 17 parts, 12 parts, sawdust, length are the broken glass fiber silk 0.2 part of 3 centimetres.
(2) operating procedure: when making imitative wood flower case, barrel of beer, flowerpot,
Magnesium oxide, yellow sand and brown iron oxide pigment are put into stirrer to stir 2 minutes;
Magnesium chloride solution is put into stirrer to stir 2 minutes;
Sawdust and broken glass fiber silk are put into and stirs 5 minutes to stirrer, namely become slurry.
Uniform brush one deck mold oil less in mould;
Be coated with one deck magnesite slurry;
Paving layer of glass net, puts into mould special bamboo reinforcement network planning model after above step repetitive operation 2 times;
Paving layer of glass net; The slurry of magnesite material to be evenly applied on mould that 1.5cm is thick to be advisable.
Natural coagulation under the envrionment temperature of 27 DEG C; Namely imitative wood flower case, barrel of beer, flowerpot, the goods made are become.
(3) purposes widely: this product adopts Suresh Kumar, many colors to produce; , can be placed on park, leisure place home garden, indoor; Cultivate flowers, plants and trees.
Experimental example 3: imitative wooden table stool
(1) material mixture ratio: 35 parts, magnesium oxide, magnesium chloride solution 28 parts, brown iron oxide pigment 0.6 part, fine particle calcium carbonate 6 parts, 5 parts, gypsum, powdered rice hulls 10 parts, broken glass fiber silk 0.4 part.
(2) operating procedure: when making imitative wooden imitative wooden table stool,
Magnesium oxide, gypsum, fine particle calcium carbonate and brown iron oxide pigment are put into stirrer to stir 10 minutes;
Magnesium chloride solution is put into stirrer to stir 10 minutes;
Powdered rice hulls and broken glass fiber silk are put into and stirs 3 minutes to stirrer, namely become slurry.
First uniform brush one deck mold oil less in mould;
Be coated with one deck magnesite slurry;
Paving layer of glass net, puts into mould special bamboo reinforcement network planning model after above step repetitive operation 2 times;
Paving layer of glass net; Evenly be applied on mould by the slurry of magnesite material, 1.5cm is thick to be advisable, under the environment of 25 DEG C, wait for natural coagulation, has both become the imitative wooden table stool of making.
(3) purposes widely: this product adopts Suresh Kumar, many colors, production; Can meet different local; The requirement of different-style; Client can be realized aspire after perfection; Pursue the requirement of oneself style.
Embodiment 4: imitative wooden refuse container
(1) material mixture ratio: 40 parts, magnesium oxide, magnesium chloride solution 30 parts, brown iron oxide pigment 0.5 part, yellow sand 19 parts, 10 parts, sawdust, length are the broken glass fiber silk 0.5 part of 8 centimetres.
(2) operating procedure: when making imitative wooden refuse container,
Magnesium oxide, yellow sand and brown iron oxide pigment are put into stirrer to stir 1 minute;
Magnesium chloride solution is put into stirrer to stir 1 minute;
Sawdust and broken glass fiber silk are put into and stirs 5 minutes to stirrer, namely become slurry.
Uniform brush one deck mold oil less in mould;
Be coated with one deck magnesite slurry;
Paving layer of glass net;
Special bamboo reinforcement net is put into mould;
Paving layer of glass net; The slurry of magnesite material is evenly applied to thick being advisable of 1.5cm on mould and waits for natural coagulation under the environment of 25 DEG C; Both the imitative wooden refuse container of making had been become.
(3) purposes widely: this product adopts Suresh Kumar, many colors to produce; Park can be placed on, leisure place, home garden can combine together with it more in any case; Reaching True Beauty sees practical.
Experimental example 5: imitative wooden flower stand
(1) material mixture ratio: 35 parts, magnesium oxide, magnesium chloride solution 40 parts, brown iron oxide pigment 0.6 part, yellow sand 14 parts, powdered rice hulls 10 parts, broken glass fiber silk 0.4 part.
(2) operating procedure:
Magnesium oxide, yellow sand and brown iron oxide pigment are put into stirrer to stir 2 minutes;
Magnesium chloride solution is put into stirrer to stir 2 minutes;
Powdered rice hulls and broken glass fiber silk are put into and stirs 3 minutes to stirrer, namely become slurry.
First uniform brush one deck mold oil less in mould; Be coated with one deck magnesite slurry; Paving layer of glass net, puts into mould special bamboo reinforcement network planning model after above step repetitive operation 2 times;
Paving layer of glass net; Evenly be applied on mould by the slurry of magnesite material, 1.5cm is thick to be advisable, under the environment of 25 DEG C, wait for natural coagulation, has both become the imitative wooden flower stand that magnesite slurry makes.
(3) purposes widely: this product adopts built-up type installations, Suresh Kumar, the production of many colors; Can in park, leisure place, home garden; Shaping can be assembled rapidly under different landform; Surrounding environment combines together with it; Reaching True Beauty sees practical.
Experimental example 6: imitative wooden wayside pavilion
(1) material mixture ratio: 38 parts, magnesium oxide, magnesium chloride solution 34 parts, brown iron oxide pigment 1 part, yellow sand 17 parts, 9 parts, sawdust, broken glass fiber silk 1 part; Other and embodiment 1 together, are omited.
(2) operating procedure: when making wayside pavilion,
According to the good size of Site Design;
During making in mould first uniform brush one deck mold oil less; Be coated with one deck magnesite slurry; Paving layer of glass net, puts into mould special bamboo reinforcement network planning model after above step repetitive operation 2 times;
Paving layer of glass net; The slurry of magnesite material to be evenly applied on mould that 1.5cm is thick to be advisable, under the environment of 25 DEG C, to wait for natural coagulation; Both the imitative wooden wayside pavilion of making had been become.
(3) purposes widely: this product adopts built-up type installations, Suresh Kumar, many colors are produced, can arrange in pairs or groups below wayside pavilion and imitate wooden table stool with some; Can in park, leisure place, home garden; Shaping can be assembled rapidly under different landform; Surrounding environment combines together with it; Attractive in appearance, leisure, practical.
Experimental example 7: imitative wooden railing
(1) material mixture ratio: 38 parts, magnesium oxide, magnesium chloride solution 34 parts, brown iron oxide pigment 1 part, yellow sand 17 parts, 9 parts, sawdust, broken glass fiber silk 1 part; Other and embodiment 1 together, are omited.
(2) operating procedure: make railing
First according to the good size of Site Design, product pattern;
During making in mould first uniform brush one deck mold oil less; Be coated with one deck magnesite slurry; Paving layer of glass net, puts into mould special bamboo reinforcement network planning model after above step repetitive operation 2 times;
Paving layer of glass net; The slurry of magnesite material to be evenly applied on mould that 1.5cm is thick to be advisable;
Under the environment of 25 DEG C, wait for natural coagulation, both become the imitative wooden railing of making.
(3) purposes widely: this product adopts coupling type or welded type to install, the pattern that can specify according to client is produced, and intensity is good; Lightly; Function easy for installation, convenient carrying.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (9)
1., for the production of a composition for imitation, it is characterized in that, concrete containing following material component:
Purity is magnesium oxide powder 30-40 part of 84%-86%;
Ripple magnesium degree is magnesium chloride solution 25-30 part of 22-26;
Terra alba 3-8 part;
Light calcium carbonate powder 6-8 part;
Concentration is copperas solution 1-3 part of 10%-20%;
Concentration is sodium hexametaphosphate solution 1-3 part of 8%-13%;
Concentration is Adlerika 1-3 part of 10%-20%;
Structure filling thing 16-20 part and intensity weighting material 4-6 part;
Described structure filling thing is one or more in sawdust, rice husk, yellow sand;
Described imitation is prepared by following methods:
Being dropped into by described magnesium oxide powder is contained with in the stirred vessel of described magnesium chloride solution, stirs 2-4 minute;
Add described copperas solution successively, described sodium hexametaphosphate solution and described Adlerika, add rear all stirrings 1-2 minute at every turn;
Add described light calcium carbonate powder, described terra alba and described structure filling thing, stir 2-5 minute, make slip;
Described slip is evenly coated in die surface;
Described intensity weighting material is arranged on the mould being coated with described slip;
Under 25 DEG C of-30 DEG C of envrionment temperatures, the demoulding after natural coagulation 4-6 hour.
2. a kind of composition for the production of imitation according to claim 1, is characterized in that, specifically comprise following material component:
Purity is magnesium oxide powder 32-38 part of 84.5%-85.5%;
Ripple magnesium degree is magnesium chloride solution 26-27 part of 22-26;
Terra alba 4-7 part;
Light calcium carbonate powder 6.5-7.5 part;
Concentration is copperas solution 1.5-2.5 part of 10%-20%;
Concentration is sodium hexametaphosphate solution 1-2 part of 8%-13%;
Concentration is Adlerika 1-2.5 part of 10%-20%;
Structure filling thing 17-19 part and intensity weighting material 4-5 part.
3. a kind of composition for the production of imitation according to claim 1 and 2, is characterized in that, described intensity weighting material is glass fiber mesh, or glasscloth, or glass fiber, or bamboo reinforcement net, or one or more in bamboo reinforcement circle.
4. a kind of composition for the production of imitation according to claim 3, is characterized in that, described intensity weighting material is glass fiber, and the length of described glass fiber is 1-8 centimetre.
5. the making method of a kind of imitation according to any one of claim 1-4, is characterized in that, specifically comprise the steps:
Being dropped into by described magnesium oxide powder is contained with in the stirred vessel of described magnesium chloride solution, stirs 2-4 minute;
Add described copperas solution successively, described sodium hexametaphosphate solution and described Adlerika, add rear all stirrings 1-2 minute at every turn;
Add described light calcium carbonate powder, described terra alba and described structure filling thing, stir 2-5 minute, make slip;
Described slip is evenly coated in die surface;
Described intensity weighting material is arranged on the mould being coated with described slip;
Under 25 DEG C of-30 DEG C of envrionment temperatures, the demoulding after natural coagulation 4-6 hour.
6. according to the making method of a kind of imitation shown in claim 5, it is characterized in that, add described light calcium carbonate powder, described terra alba and described structure filling thing, stir 2-5 minute, after making the step of slip; Before described slip being evenly coated in the step of die surface, comprise further:
One deck mold oil is applied at die surface.
7. according to the making method of a kind of imitation shown in claim 5, it is characterized in that, described slip be evenly coated in the step of die surface, specifically comprise:
At the described slip of die surface coating 1-3 cm thick.
8. according to the making method of a kind of imitation shown in claim 5, it is characterized in that, when described intensity weighting material is glasscloth, described intensity weighting material is arranged in the step on the mould being coated with described slip, specifically comprises:
Described glasscloth is layered on the surface of the mould being coated with described slip, and is close to die surface.
9. according to Claim 8 shown in a kind of making method of imitation, it is characterized in that, described glasscloth is layered on the surface of the mould being coated with described slip, and in the step be close to die surface, specifically comprise:
By the 4-5 layer glasscloth successively overlapping surface being laid on the mould being coated with described slip.