CN103224362B - 一种无机保温隔热砂浆及其制备方法 - Google Patents
一种无机保温隔热砂浆及其制备方法 Download PDFInfo
- Publication number
- CN103224362B CN103224362B CN201310127498.3A CN201310127498A CN103224362B CN 103224362 B CN103224362 B CN 103224362B CN 201310127498 A CN201310127498 A CN 201310127498A CN 103224362 B CN103224362 B CN 103224362B
- Authority
- CN
- China
- Prior art keywords
- parts
- heat insulating
- thermal insulation
- inorganic
- performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种无机保温隔热砂浆，同时还涉及其制备方法，属于建筑材料技术领域。该无机保温隔热砂浆各组分的重量份比例为：普通硅酸盐水泥：360-500份、消石灰：100-150份、沸石粉：10-50份、复合型无机矿物轻骨料：380-500份、早强剂：2-5份、抗裂纤维：5-20份、可再分散乳胶粉：5-8份、纤维素醚：2-4份、憎水剂：2-5份、引气剂：0-1份。本发明的无机保温隔热砂浆保温性能良好，导热系数低、强度高、抗开裂性能良好，具有优异的建筑保温隔热效果，而且性能稳定、波动小，具有优良的施工性能、粘结性能、不燃防火、避免空鼓开裂、经济成本低等特点。
Description
技术领域
本发明涉及一种砂浆，尤其是一种无机保温隔热砂浆，同时还涉及其制备方法，属于建筑材料技术领域。
背景技术
随着建筑能耗的快速上升，建筑能耗已占到我国全社会总能耗的三分之一，为了社会可持续发展，实行建筑节能已成为我国的基本国策。在建筑能耗中，通过建筑外墙、屋面和地面散失的能量达50%，尤其是建筑外墙散失能量超过30%。因此进行建筑墙体保温节能是降低建筑能耗的重要途径，应用安全高效耐久的建筑墙体保温体系是主要措施。在该保温体系中，保温材料层是决定整个保温体系安全高效耐候的最关键材料。现有保温材料主要分有机保温材料和无机保温材料。目前市场上的有机保温材料大多易燃，而无机保温砂浆的导热系数偏大，保温效果较低，尤其是实际工程应用时保温性能会显著降低，远远不能满足墙体保温节能要求。
发明内容
本发明的目的在于：通过对无机保温隔热砂浆的组分、配比的选择、优化以及制备方法的研究，提出一种性能优良稳定、保温隔热性能好的无机保温隔热砂浆，同时给出其制备方法，从而满足各种建筑墙体保温节能体系要求。
为了达到以上目的，本发明的无机保温隔热砂浆基本技术方案为主要由如下重量份组分的组成：
硅酸盐水泥：360-500份、消石灰：100-150份、沸石粉：10-50份、复合型无机矿物轻骨料：380-500份、早强剂：2-5份、抗裂纤维：5-20份、可再分散乳胶粉：5-8份、纤维素醚：3-7份、憎水剂：2-5份、引气剂：0-1份。
本发明进一步的完善包括：
所述复合型无机矿物轻骨料优选重量份比例9:1-8:2的玻化微珠和沸石颗粒。
所述抗裂纤维是纤维长度1-6mm的木质素纤维，该纤维不仅赋予无机保温隔热砂浆良好的抗裂性能，还能改善保温效果，改善轻骨料与胶凝材料的相容性。
所述可再分散乳胶粉为乙烯-醋酸乙烯酯乳胶粉、乙烯-氯乙烯-月桂酸乙烯酯乳胶粉中的至少一种。
所述早强剂是碳酸钠、硫酸钠中的至少一种，其作用是赋予无机保温隔热砂浆良好的强度，尤其是早期强度，缩短施工周期，降低工程施工成本。
所述憎水剂和引气剂分别是有机硅类憎水剂和十二烷基硫酸钠引气剂。
本发明的无机保温隔热砂浆制备方法为：将称量好的各种组分投入混合装置，搅拌2-5min，混合均匀，即可得到所述的无机保温隔热砂浆产品。
试验表明，本发明的无机保温隔热砂浆成品不仅保温隔热性能好，而且解决了轻质保温砂浆类产品运输储存稳定性差、易离析的难题，施工时只需在施工现场将其与水按给定比例搅拌2-3min即可使用，施工效率高，其检测结果如表1所示。
表1无机保温隔热砂浆基本性能
由表1可以看出，本发明提出的无机保温隔热砂浆物理力学性能良好，达到或超过相关标准要求，因此可以满足建筑节能工程不同要求。其应用范围广，不仅能用于建筑墙体节能工程，还能用于建筑屋面和地面节能工程，不仅能应用于建筑墙体外保温节能工程，还能应用于建筑墙体内保温和内外组合保温节能工程。
综上所述，本发明提出的无机保温隔热砂浆各性能指标优良，制备方法简便易行，产品品质易于控制，施工性能优异，保温隔热性能优良，适用于各种建筑节能工程，便于大规模推广应用。
具体实施方式
下面通过实施例进一步说明本发明。
实施例1
本实施例的无机保温隔热砂浆重量份组分：普通硅酸盐水泥：390份、消石灰：110份、沸石粉：30份、复合型无机矿物轻骨料：443.5份、早强剂：3份、抗裂纤维：10份、可再分散乳胶粉：6份、纤维素醚：4份、憎水剂：3份、引气剂：0.5份。更具体而言：其中复合型无机矿物轻骨料优选重量份比例9:1的玻化微珠和沸石颗粒；抗裂纤维是纤维长度约5mm的木质素纤维；可再分散乳胶粉为乙烯-醋酸乙烯酯乳胶粉；早强剂是碳酸钠；憎水剂和引气剂分别是有机硅类憎水剂和十二烷基硫酸钠引气剂。
制备时，将准确称量好的各种原材料一次性投入卧式重力混合机，根据混合料的多少搅拌混合2-5min，即可得到所需的无机保温隔热砂浆产品。
测试得到的性能均超过国家标准GB/T20473-2006和GB/T26000-2010的技术指标要求，且导热系数仅为0.054W/m.K，不仅保温性能良好，导热系数低、强度高、抗开裂性能良好，具有优异的建筑保温隔热效果，而且性能稳定、波动小，具有优良的施工性能、粘结性能、不燃防火、避免空鼓开裂、经济成本低等特点。
实施例2
本实施例的无机保温隔热砂浆重量份各组分为：普通硅酸盐水泥：420份、消石灰：90份、沸石粉：40份、复合型无机矿物轻骨料：418份、早强剂：2份、抗裂纤维：16份、可再分散乳胶粉：5份、纤维素醚：6份、憎水剂：2份、引气剂：1份。更具体而言：其中复合型无机矿物轻骨料优选重量份比例8:2的玻化微珠和沸石颗粒；抗裂纤维是纤维长度2mm左右的木质素纤维；可再分散乳胶粉为乙烯-氯乙烯-月桂酸乙烯酯乳胶粉；早强剂是硫酸钠；憎水剂和引气剂分别是有机硅类憎水剂和十二烷基硫酸钠引气剂。
测试得到的性能均超过国家标准GB/T20473-2006和GB/T26000-2010的技术指标要求，导热系数仅为0.061W/m.K。
实践证明，以上实施例的无机保温隔热砂浆制备方法简单便捷，能够确保无机保温隔热砂浆的性能和均匀性，投资小，易于操作。并且具有优异的施工性能，可施工时间长，施工便捷，施工前后性能差异小，粘结性能好，一次性涂抹厚度大（达30mm）而不产生流挂流淌等不良现象。此外，与现有同类产品对比，还具有突出的抗收缩开裂性能，能够确保不同应用场合使用时不发生开裂现象。
由以上实施例可见，本发明提出的无机保温隔热砂浆，可根据要求，配制出保温隔热性能良好的无机保温隔热砂浆。各项性能指标均满足或超过相关标准和实际工程要求，作为一种建筑节能高效保温材料，可广泛推广应用于各种建筑节能工程。
Claims (5)
1.一种无机保温隔热砂浆，其特征在于主要由如下重量份组分的组成：
硅酸盐水泥：360－500份
消石灰：100－150份
沸石粉：10－50份
复合型无机矿物轻骨料：380－500份
早强剂：2－5份
抗裂纤维：5－20份
可再分散乳胶粉：5－8份
纤维素醚：3－7份
憎水剂：2－5份
引气剂：0－1份；
所述复合型无机矿物轻骨料为重量份比例9:1-8:2的玻化微珠和沸石颗粒；所述抗裂纤维是纤维长度1-6mm的木质素纤维。
2.根据权利要求1所述的无机保温隔热砂浆，其特征在于：所述可再分散乳胶粉为乙烯-醋酸乙烯酯乳胶粉、乙烯-氯乙烯-月桂酸乙烯酯乳胶粉中的至少一种。
3.根据权利要求1所述的无机保温隔热砂浆，其特征在于：所述早强剂是碳酸钠、硫酸钠中的至少一种。
4.根据权利要求1所述的无机保温隔热砂浆，其特征在于：所述憎水剂和引气剂分别是有机硅类憎水剂和十二烷基硫酸钠引气剂。
5.根据权利要求1至4任一所述无机保温隔热砂浆的制备方法，其特征在于：将称量好的各种组分投入混合装置，搅拌2-5min混合均匀。