CN103223747A - 一种复合胎基载体改性沥青自粘防水卷材 - Google Patents
一种复合胎基载体改性沥青自粘防水卷材 Download PDFInfo
- Publication number
- CN103223747A CN103223747A CN2013101331187A CN201310133118A CN103223747A CN 103223747 A CN103223747 A CN 103223747A CN 2013101331187 A CN2013101331187 A CN 2013101331187A CN 201310133118 A CN201310133118 A CN 201310133118A CN 103223747 A CN103223747 A CN 103223747A
- Authority
- CN
- China
- Prior art keywords
- modified pitch
- sizing material
- waterproof roll
- film coating
- pitch self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种复合胎基载体改性沥青自粘防水卷材,由三部分组成,其中第一部分为HDPE薄膜载体,第二部分为高聚物改性沥青自粘胶料薄膜涂层,第三部分为嵌固在高聚物改性沥青自粘胶料内的低碱玻纤网格布,所述三部分由高聚物改性沥青自粘胶料薄膜层粘接复合在一起,形成防水卷材。本发明公开的复合胎基载体改性沥青自粘防水卷材能够最大限度地减少自然资源消耗的基础上制成高效防水材料,为工程防水提供的安全保障。
Description
技术领域
本发明涉及一种复合胎基载体改性沥青自粘防水卷材,属于建筑防水材料,土木建筑工程防水领域
背景技术
随着自然资源的日益匮乏,土木建筑工程领域的材料节约日益受到重视。作为工程防水必用的防水卷材,不断提高产品的工程性能、降低自然资源消耗有其非常重要的意义。
然而,在本领域传统上的研究多注重防水材料本身的改进,例如CN1110301A、CN2358140Y、CN1105744C、CN2804216Y、CN2926229Y等,尽管上述方案中部分揭示了“将三元乙丙、沥青油毡或氯化聚乙烯作为卷材层,将无机硅酸盐保温材料作为隔热保温层,将玻璃纤维网格布作为增强层的三层结构”,但是此种结构存在一些本质上难于克服的问题:在长期使用中,中间层会携顶层的三元乙丙与玻璃纤维网布分离,失去应有的防水保温作用,并且这种结构铺设时施工费力,而将玻璃纤维设在保温层的底部对卷材本体不具有剪切应变性能,使用久了就会产生开裂。
当前,土木建筑工程渗漏水是多发病害,渗漏水不仅严重影响建筑功能的有效使用,还能够引发多种建筑病害,导致建筑使用寿命的降低。近现代建筑中有大量的建筑物因为没有做好工程防水导致维修、使用过程中的养护成本高昂,有许多建筑不得不提前拆除。
国家现行建筑规范中为了保障建筑防水安全,提倡新建建筑采用多到设防的技术措施,多到设防一方面造成大量防水材料的消耗和自然资源的消耗,另一方面也给用户带来沉重的购买成本负担。
因此,发明高效、实用、安全耐久的防水卷材具有深远的社会意义和价值。
发明内容
针对现有技术的需要,申请人结合长期的实践经验,发明了一种复合胎基载体改性沥青自粘防水卷材,应用于建筑领域,尤其是建筑地下室、屋顶防水工程,不仅具有良好的保温防水特性,并且施工简单,使用寿命长。
为实现上述目的,本发明是通过下述技术方案实现的:
一种复合胎基载体改性沥青自粘防水卷材,由三部分组成,第一部分为HDPE薄膜载体,第二部分为改性沥青自粘胶料薄膜涂层,第三部分为嵌固在高聚物改性沥青自粘胶料内的玻璃纤维网格布,所述三部分通过高聚物改性沥青自粘胶料薄膜层粘接复合在一起,形成防水卷材。
通过上述结构,HDPE薄膜载体使得防水卷材能够耐酸碱,耐有机溶剂,具有良好的韧性、表面硬度,拉伸强度,刚性等机械强度,有效保证了产品的使用寿命;而将玻璃纤维网格布内嵌在改性沥青自粘胶料内防止了其开裂;高聚物改性沥青自粘胶料薄膜涂层则具有良好的防水保温作用。
在本发明中,所用三层的厚度不受到特别限定,优选的,HDPE薄膜载体厚度为0.1-0.2mm,改性沥青自粘胶料薄膜涂层厚度为1.0-2.0mm,玻璃纤维网格布规格为30-120g/m2。
在本发明中,所用HDPE薄膜的HDPE是一种工业上常见的聚合物材料,可用的分子量在40000-300000之间,优选的的分子量范围为150000-300000。
在本发明中,所述高聚物改性沥青自粘胶料薄膜涂层所用的高聚物改性沥青自粘胶料的化学组成为:
在上述成分中,石油沥青是石油加工过程中的一种产品,在常温下是黑色或黑褐色的粘稠的液体、半固体或固体,主要含有可溶于三氯乙烯的烃类及非烃类衍生物,尽管其组成比较复杂,但是目前市场上广泛销售的石油沥青产品都具有相同或者非常相近的理化参数,均可用于本发明,优选的是建筑用石油沥青系列产品。
在上述成分中,环烷油是从环烷基原油中提炼出来的馏分,具有饱和环状碳链结构,具有低倾点、高密度、高粘度、无毒副作用等特点,而且在它的环上通常还会连接着饱和支链。因为这种结构,使环烷油既具有芳香烃类的部分性质,又具有直链烃的部分性质,又由于环烷油来自天然石油,有价格低廉、来源可靠等优点,其理化参数可以从常见的化工词典中查询,市场上销售的此类产品均可用于本发明。
在上述成分中,SBS、SBR是化工领域常见的两种改性沥青材料,此处不再赘述。
在上述成分中,所用的聚异丁烯为低分子量聚异丁烯(1000<分子量<3500),主要作用是提高产品的初粘性。
在上述成分中,所用的加氢树脂是C5加氢石油树脂。
在上述成分中,聚醋酸乙烯酯即PVAc,优选其聚合度n在250-600之间。
在上述成分中,增韧剂为本领域常用材料,包括但不限于常见的丙烯酸酯橡胶、氯磺化聚乙烯、ABS、聚乙烯醇缩丁醛、聚醋酸乙烯等。
在上述成分中,紫外线吸收剂采用本领域常用产品,水杨酸苯酯、紫外线吸收剂UV-P、UV-O、UV-531、光稳定剂GW-540等。
在上述成分中,抗老化剂又称交联剂,加入后可打开双链,从而形成网络结构,使结构更紧密,主要为硫磺或有机过氧化物。
在上述成分中,抗剥落剂又名沥青抗剥离剂,常见的产品如TJ066、ASA9304、卡洛胺、AR-68等均可用于本发明。
在上述成分中,填料是常用的化工辅料,如PP、PE、RPP、PVC、CPVC、PVDF等填料均可用于本发明。
2.产品性能
在本发明中,所述玻璃纤维网格布为低碱玻纤网格布或无碱玻纤网格布(碱性金属氧化物含量低于0.5%),优选为低碱玻纤网格布,其中的碱性金属氧化物含量不高于3%,生产成本低,又具有良好的化学稳定性和结构强度。
在本发明中,HDPE薄膜对于改性沥青自粘胶料薄膜涂层的覆盖可以是不完全的,也就是说所述HDPE薄膜部分覆盖改性沥青自粘胶料薄膜涂层,一端留有未覆盖的暴露带。
在这种情形下,较优的覆盖范围是所述HDPE薄膜一端留有20-30mm(这个大小是可以改变的,根据施工需要)的改性沥青自粘胶料薄膜涂层暴露带,另一边覆盖至边沿。
在本发明中,玻璃纤维网格布在防水卷材的全断面范围内设置,玻璃纤维网格布嵌固于改性沥青自粘胶料薄膜涂层内的深度包含任何嵌固深度,也就是说玻璃纤维网格布可以位于改性沥青自粘胶料薄膜涂层的任意内部深度。
本发明的防水卷材的安装使用方法,通过自粘贴、采用粘接界面处理剂粘贴或采用粘接胶粘贴,通常是黏贴在建筑物表面。
由于在实际的工业封装时会外包上硅油隔离膜,因此在工业上的应用方法通常是如下几种:
1、撕去硅油隔离膜、将卷材直接粘贴在经过基层处理剂处理过的混凝土结构基面上、或其它材质的结构基面上。
2、撕去硅油隔离膜、使用辅助性粘接胶将卷材直接粘贴在混凝土结构基面上、或其它材质的结构基面上。
3、撕去硅油隔离纸,采用搭接带自粘结的方式完成防水卷材的拼接。
申请人的实验证实,本发明的防水卷材,通过上述的特定的结构改进,低资源消耗、高防水效能。
附图说明
图1为本发明防水卷材结构示意图。
具体实施方式
为了能更清楚地理解本发明的技术实质,申请人结合附图在下面对本发明的具体实施方式作详细说明。这些说明均不是构成对本发明方案的限制,因此,任何人只要在本发明方案的启示下所做出的纯属形式上的而并非为实质性的等效变化和改型都应当视为本发明所公开的技术方案范畴并且视为主张权利保护的范围。
实施例1
本发明的防水卷材其具体的产品结构可以入附图1所示,在附图1中,申请人提供了一种典型的本发明防水卷材的具体结构:其中HDPE(分子量160000)薄膜厚度为0.15mm,改性沥青自粘胶料薄膜涂层厚度为1.35mm,玻璃纤维网格布规格为60g/m2,防水卷材的整体长度为1000mm,HDPE薄膜一端完全覆盖改性沥青自粘胶料薄膜涂层,另一端留有25mm暴露带,玻璃纤维网格布横穿整个改性沥青自粘胶料薄膜涂层,位于其表层下1mm深度。
附图中的隔离纸(上表面两侧分别为浸蜡硅油隔离纸,下层表面为硅油隔离膜/纸)是将产品整体施工应用时根据需要所增加的附属组件,并不限制本发明的保护范围。
其中的玻璃纤维网格布为低碱玻纤网格布,其中的金属钠钾氧化物含量不高于1.5%。
其中的改性沥青自粘胶料薄膜涂层典型配方及制备方法如下:
配方:(聚异丁烯分子量1200、聚醋酸乙烯酯聚合度300、增韧剂为丙烯酸酯橡胶、紫外线吸收剂UV-P、抗老化剂为硫磺、抗剥落剂AR68、填料PP)
制备工艺:
①加入基质沥青和环烷油,升温至180℃;
②加入配方量SBS、SBR,控制温度在180~185℃范围内溶胀l h,之后启动胶体磨进行研磨2h,直到无肉眼可见小颗粒为止;
③加入配方量聚异丁烯、树脂、聚醋酸乙烯酯,控制温度在180~185℃范围内溶胀l h,直到无肉眼可见小颗粒为止;
④加入增韧剂、抗老化剂、紫外线吸收剂、抗剥落剂,高速搅拌30min以上
⑤加入填料,搅拌45min以上;
⑦打入储存罐准备上线生产。
实施例2
与实施例1类似的产品结构,其中HDPE(分子量280000)薄膜厚度为0.2mm,改性沥青自粘胶料薄膜涂层厚度为1.95mm,玻璃纤维网格布规格为110g/m2,防水卷材的整体长度为1000mm,HDPE薄膜一端完全覆盖改性沥青自粘胶料薄膜涂层,另一端留有20mm暴露带,玻璃纤维网格布横穿整个改性沥青自粘胶料薄膜涂层,位于其表层下0.6mm深度。
其中的玻璃纤维网格布为低碱玻纤网格布,其中的金属钠钾氧化物含量不高于1.5%。
其中的改性沥青自粘胶料薄膜涂层典型配方如下:
配方(聚异丁烯分子量2000、聚醋酸乙烯酯聚合度480、增韧剂为ABS、紫外线吸收剂UV-531、抗老化剂为过氧化二异丙苯、抗剥落剂TJ066、填料PVC):
制备方法参考实施例1所示。
实施例3
与实施例1类似的产品结构,其中HDPE(分子量200000)薄膜厚度为0.1mm,改性沥青自粘胶料薄膜涂层厚度为1.04mm,玻璃纤维网格布规格为40g/m2,防水卷材的整体长度为1000mm,HDPE薄膜一端完全覆盖改性沥青自粘胶料薄膜涂层,另一端留有30mm暴露带,玻璃纤维网格布横穿整个改性沥青自粘胶料薄膜涂层,位于其表层下1.4mm深度。
其中的玻璃纤维网格布为低碱玻纤网格布,其中的金属钠钾氧化物含量不高于1.5%。
其中的改性沥青自粘胶料薄膜涂层典型配方如下:
配方(聚异丁烯分子量3400、聚醋酸乙烯酯聚合度600、增韧剂为聚醋酸乙烯、紫外线吸收剂UV-531、抗老化剂为过氧化二异丙苯、抗剥落剂ASA9304、填料PE):
制备方法参考实施例1所示。
申请人测试了本发明防水卷材的理化特性,显示上述实施例1-3的防水卷材在零下30度均无裂纹、开裂等现象,其拉力不低于500N/50mm,断裂伸长率不低于400%,与铝板的剥离强度不低于2.4N/mm,不透水性在0.3MPa下保持时间不低于50min。
采用的检测方法为GB/T328.14-2007、GB/T328.9-2007、GB/T328.10-2007、GB/T328.20-2007、GB23441-2009,所检指标均符合并高于自粘聚合物改性沥青防水卷材GB23441-2009标准要求。
Claims (9)
1.一种复合胎基载体改性沥青自粘防水卷材,由三部分组成,其特征在于第一部分为HDPE薄膜载体,第二部分为高聚物改性沥青自粘胶料薄膜涂层,第三部分为嵌固在高聚物改性沥青自粘胶料内的玻璃纤维网格布,所述三部分通过高聚物改性沥青自粘胶料薄膜层粘接复合在一起,形成防水卷材。
2.根据权利要求1所述的防水卷材,其特征在于所述HDPE薄膜载体厚度为0.1-0.2mm,改性沥青自粘胶料薄膜涂层厚度为1.0-2.0mm,玻璃纤维网格布规格为30-120g/m2。
3.根据权利要求1所述的防水卷材,其特征在于HDPE薄膜所用的HDPE的分子量范围为150000-300000。
5.根据权利要求1所述的防水卷材,其特征在于所述玻璃纤维网格布为低碱玻纤网格布或无碱玻纤网格布。
6.根据权利要求1所述的防水卷材,其特征在于所述HDPE薄膜部分覆盖改性沥青自粘胶料薄膜涂层,一端留有未覆盖的暴露带。
7.根据权利要求5所述的防水卷材,其特征在于所述HDPE薄膜一端留有20-30mm的改性沥青自粘胶料薄膜涂层暴露带,另一边覆盖至边沿。
8.根据权利要求1所述的防水卷材,其特征在于玻璃纤维网格布在防水卷材的全断面范围内设置,玻璃纤维网格布嵌固于改性沥青自粘胶料薄膜涂层内的深度包含任何嵌固深度。
9.上述任一权利要求所述的防水卷材的安装使用方法,其特征在于通过自粘贴、采用粘接界面处理剂粘贴或采用粘接胶粘贴。