CN103215716A - 一种低粘高伸缩涤纶长丝及其制备工艺 - Google Patents

一种低粘高伸缩涤纶长丝及其制备工艺 Download PDF

Info

Publication number
CN103215716A
CN103215716A CN201310165768XA CN201310165768A CN103215716A CN 103215716 A CN103215716 A CN 103215716A CN 201310165768X A CN201310165768X A CN 201310165768XA CN 201310165768 A CN201310165768 A CN 201310165768A CN 103215716 A CN103215716 A CN 103215716A
Authority
CN
China
Prior art keywords
polyester filament
terylene thread
viscosity
terylene
low
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310165768XA
Other languages
English (en)
Inventor
徐醒我
关乐
赵满才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Longjie Special Fiber Co Ltd
Original Assignee
Suzhou Longjie Special Fiber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Longjie Special Fiber Co Ltd filed Critical Suzhou Longjie Special Fiber Co Ltd
Priority to CN201310165768XA priority Critical patent/CN103215716A/zh
Publication of CN103215716A publication Critical patent/CN103215716A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种低粘高伸缩涤纶长丝，其特征在于：是由若干根涤纶单丝经过卷绕工艺制成的涤纶长丝，并且涤纶长丝的截面呈圆形或正多边形。作为一种改进，所述涤纶单丝包括粘度为0.3-0.5dl/g的涤纶丝甲和粘度为0.6-0.9dl/g的涤纶丝乙，涤纶丝甲和涤纶丝乙两种涤纶丝经过卷绕工艺制成的涤纶长丝。本发明可取代氨纶丝，并且价格低廉，成本大大降低。

Description

一种低粘高伸缩涤纶长丝及其制备工艺
技术领域
本发明属于化学纤维领域，具体地说，涉及一种低粘高伸缩涤纶长丝及其制备工艺。
背景技术
涤纶作为合成纤维中的三大主力纤维之一，因其优良的物理和化学特性被广泛应用于服装面料以及其它非服装领域。涤沦产品自问世以来，也曾以其悬垂好、强度高、挺括、不易起皱而被下游用户当作主要纺织原料来织造各类纺织品。最早生产的涤纶其截面形状主要是以圆形为主，随着人们对纺织产品要求的变化，以及纤维技术的开发与进步，技术人员开发出具有功能性的各种各样异形截面纤维，最常见的有三角形、中空、一字形、十字形或这些形状的变异，其目的是改善涤纶的手感、光泽、吸湿性、蓬松性等等特性，使化学纤维在触摸时会给人以或干爽，或粗犷，或细腻，或滑柔的感觉，并具有吸湿排汗、防水、保暖等其它功能。
然而随着经济全球化，市场国际化，人们对化学纤维材料的性能要求越来越高。在织造玩具绒面料、地毯时，一字形的扁平纤维，已经不能满足人们对纤维性能的需求了，不仅仅要求光泽、手感了，还要要求纤维的毛高更高，并具有抗倒伏性能，使手感更加柔软。
发明内容
本发明要解决的技术问题是克服上述缺陷，提供一种质量好、可取代氨纶丝并且价格低廉的低粘高伸缩涤纶长丝。
为解决上述问题，本发明所采用的技术方案是：
一种低粘高伸缩涤纶长丝，其特征在于：是由若干根涤纶单丝经过纺丝卷绕等工艺制成的涤纶纤维，并且涤纶单丝的截面呈圆形或正多边形。
作为一种改进，所述涤纶长丝包括粘度为0.3-0.5dl/g的涤纶丝甲和粘度为0.6-0.9dl/g的涤纶丝乙，涤纶丝甲和涤纶丝乙两种涤纶丝经过纺丝卷绕等工艺制成的涤纶长丝。
作为一种改进，所述涤纶丝甲为粘度0.4dl/g的涤纶丝。
作为一种改进，所述涤纶丝甲的直径为600-900纳米。
作为一种改进，所述涤纶丝乙为粘度0.8dl/g的涤纶丝。
作为一种改进，所述涤纶丝乙的直径为800-1200纳米。
作为一种改进，所述涤纶长丝的截面为正六边形。
作为一种改进，所述涤纶长丝中涤纶丝甲的直径为750纳米，涤纶丝乙的直径为1050纳米。
本发明还提供了一种低粘高伸缩涤纶长丝的制备工艺，其特征在于：步骤如下：
将粘度为0.4dl/g的涤纶丝甲和0.8dl/g的涤纶丝乙，通过两条不同的深浅槽螺杆熔融后挤出，再经过复合箱体从喷丝板喷出卷绕成型，制得低粘高伸缩涤纶长丝。
由于采用了上述技术方案，与现有技术相比，本发明由若干根涤纶单丝经过纺丝卷绕等工艺制成的涤纶长丝，并且涤纶长丝的截面呈圆形或正多边形。同时，所述单丝涤纶丝包括粘度为0.3-0.5dl/g的涤纶丝甲和粘度为0.6-0.9dl/g的涤纶丝乙，涤纶丝甲和涤纶丝乙两种涤纶丝经过卷绕工艺制成的涤纶长丝。本发明可取代氨纶丝，并且价格低廉，成本大大降低。
同时下面结合附图和具体实施方式对本发明作进一步说明。
附图说明
图1为本发明一种实施例的结构示意图。
图中：1-涤纶丝甲；2-涤纶丝乙。
具体实施方式
实施例：
如图1所示，一种低粘高伸缩涤纶长丝，是由若干根涤纶单丝经过纺丝卷绕等工艺制成的涤纶长丝，并且涤纶长丝的截面呈圆形或正多边形。
在本实施例中，所述单丝涤纶丝包括粘度为0.3-0.5dl/g的涤纶丝甲1和粘度为0.6-0.9dl/g的涤纶丝乙2，涤纶丝甲1和涤纶丝乙2两种涤纶丝经过纺丝卷绕等工艺制成的涤纶长丝。
所述涤纶丝甲为粘度0.4dl/g的涤纶丝。所述涤纶丝甲的直径为600-900纳米。所述涤纶丝乙的直径为800-1200纳米。
在本实施例中，所述涤纶丝乙为粘度0.8dl/g的涤纶丝。所述涤纶长丝的截面为正六边形。
同时，在本实施例中，所述涤纶长丝中涤纶丝甲的直径为750纳米，涤纶丝乙的直径为1050纳米。
本发明还提供了一种低粘高伸缩涤纶长丝的制备工艺，步骤如下：
将粘度为0.4dl/g的涤纶丝甲和0.8dl/g的涤纶丝乙，通过两条不同的深浅槽螺杆熔融后挤出，再经过复合箱体从喷丝板喷出卷绕成型，制得低粘高伸缩涤纶长丝。
本发明由若干根单丝涤纶丝经过卷绕工艺制成的涤纶长丝，并且涤纶长丝的截面呈圆形或正多边形。同时，所述单丝涤纶丝包括粘度为0.3-0.5dl/g的涤纶丝甲和粘度为0.6-0.9dl/g的涤纶丝乙，涤纶丝甲和涤纶丝乙两种涤纶丝经过卷绕工艺制成的涤纶长丝。本发明可取代氨纶丝，并且价格低廉，成本大大降低。
本发明不局限于上述的优选实施方式，任何人应该得知在本发明的启示下做出的结构变化，凡是与本发明具有相同或者相近似的技术方案，均属于本发明的保护范围。

Claims (9)

1.一种低粘高伸缩涤纶长丝，其特征在于：是由若干根涤纶单丝经过卷绕工艺制成的涤纶长丝，并且涤纶长丝的截面呈圆形或正多边形。
2.根据权利要求1中所述低粘高伸缩涤纶长丝，其特征在于：所述涤纶单丝包括粘度为0.3-0.5dl/g的涤纶丝甲和粘度为0.6-0.9dl/g的涤纶丝乙，涤纶丝甲和涤纶丝乙两种涤纶丝经过卷绕工艺制成的涤纶长丝。
3.根据权利要求2中所述低粘高伸缩涤纶长丝，其特征在于：所述涤纶丝甲为粘度0.4dl/g的涤纶丝。
4.根据权利要求3中所述低粘高伸缩涤纶长丝，其特征在于：所述涤纶丝甲的直径为600-900纳米。
5.根据权利要求3中所述低粘高伸缩涤纶长丝，其特征在于：所述涤纶丝乙为粘度0.8dl/g的涤纶丝。
6.根据权利要求5中所述低粘高伸缩涤纶长丝，其特征在于：所述涤纶丝乙的直径为800-1200纳米。
7.根据权利要求3或5中所述低粘高伸缩涤纶长丝，其特征在于：所述涤纶长丝的截面为正六边形。
8.根据权利要求4或6中所述低粘高伸缩涤纶长丝，其特征在于：所述涤纶长丝中涤纶丝甲的直径为750纳米，涤纶丝乙的直径为1050纳米。
9.一种低粘高伸缩涤纶长丝的制备工艺，其特征在于：步骤如下：
将粘度为0.4dl/g的涤纶丝甲和0.8dl/g的涤纶丝乙，通过两条不同的深浅槽螺杆熔融后挤出，再经过复合箱体从喷丝板喷出卷绕成型，制得低粘高伸缩涤纶长丝。
CN201310165768XA 2013-05-08 2013-05-08 一种低粘高伸缩涤纶长丝及其制备工艺 Pending CN103215716A (zh)