CN103184007A - 一种易洁疏水涂料 - Google Patents
一种易洁疏水涂料 Download PDFInfo
- Publication number
- CN103184007A CN103184007A CN2013100843826A CN201310084382A CN103184007A CN 103184007 A CN103184007 A CN 103184007A CN 2013100843826 A CN2013100843826 A CN 2013100843826A CN 201310084382 A CN201310084382 A CN 201310084382A CN 103184007 A CN103184007 A CN 103184007A
- Authority
- CN
- China
- Prior art keywords
- hydrophobic coating
- easy clean
- clean hydrophobic
- easy
- coating according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种易洁疏水涂料,其特征在于,包括以下重量百分比含量的组分:有机溶剂35%~60%,硅油20%~45%,三甲基丙氧基硅烷15%~25%,有机酸或无机酸0.1%~1%。本发明的易洁疏水涂料具备环保和疏水的优点,将该易洁疏水涂料用于玻璃表面,能使普通玻璃具备易洁疏水功能,且具有抗菌抗霉效果,使用寿命延长、抗黄变、抗紫外线,给人们生活带来方便且节约成本。
Description
技术领域
本发明涉及一种涂料,具体地,涉及一种易洁疏水涂料。
背景技术
常见的普通玻璃表面是亲水性的,一般空气中的污浊物、水气或雨水较容易附着于玻璃表面。为了清洁其表面污渍,人们常用的方法是用水或水溶性洗涤剂进行清洗。例如:用于卫浴的玻璃、汽车玻璃和建筑用的玻璃幕墙等经常面临玻璃不够清洁而需要清洗的问题。
用于卫浴的玻璃,在人们洗漱或沐浴过后玻璃上常常充满水分,有时夹带灰尘或污物,给人不清爽的感觉。如果长期不清洗又容易产生卫生问题,如果经常清洗则给人们带来额外的劳动。
雨季时汽车玻璃上容易形成水膜,即便使用雨刮也仍然容易模糊汽车驾驶员视线,构成安全隐患;如遇寒冬还容易在汽车玻璃上形成霜冻,清理更需要一定成本;如果采用常规清洗方法,不仅花费时间,且清洗费用高,不利于环保,这对今日快节奏生活、惜时如金的人们来说,需要常常清洗汽车玻璃则极为不便。
而用于高楼大厦中的玻璃幕墙,正由于玻璃的透明性营造了一种明亮怡人的办公环境,但其外墙表面由于外界环境的变化,容易粘附一些物质而造成玻璃幕墙不够透明,透光性大大下降,影响其作用的发挥。玻璃幕墙的清洁一般需要专业人士进行,且清洗成本较高。
因此,如何使得普通玻璃具备易洁疏水特性,是本领域研究的方向和热点。
发明内容
本发明的目的是克服现有技术的不足,提供一种易洁疏水涂料,具备环保和疏水的优点,将该易洁疏水涂料用于玻璃表面,能使普通玻璃具备易洁疏水功能,且具有抗菌抗霉效果,使用寿命延长、抗黄变、抗紫外线,给人们生活带来方便且节约成本。
本发明解决所述技术问题采用的技术方案是:
一种易洁疏水涂料,其特征在于,由以下重量百分含量的组分组成:
进一步地,所述有机溶剂选自异丙醇、乙醇。
进一步地,所述硅油选用含氢量1.58%~1.60%的硅油。
再进一步,所述有机酸是冰醋酸。
再进一步,所述无机酸是盐酸。
所述易洁疏水涂料的制备方法,其特征在于,先将有机溶剂和硅油混合并搅拌均匀后,再加入三甲基丙氧基硅烷,最后加入有机酸或无机酸调配均匀,制得所述易洁疏水涂料。
所述的易洁疏水涂料的应用。
所述易洁疏水涂料的应用,其特征在于,包括以下步骤:
(1)清洗对象物并干燥;
(2)将所述易洁疏水涂料涂抹于对象物;
(3)干燥。
进一步地,所述的易洁疏水涂料的应用,其特征在于,包括以下步骤:
(1)清洗:将对象物表面的油污、油脂、灰尘等用清洗剂祛除,然后用清水将清洗剂冲洗干净,并保证对象物完全干燥;
(2)涂抹:在通风环境下,用沾有所述易洁疏水涂料的无纺布在对象物表面均匀涂抹,直至在对象物表面所形成的涂层呈透明状为止;
(3)干燥:在自然通风环境下干燥,干燥时间不少于10分钟。
再进一步,所述的易洁疏水涂料的应用,其特征在于,所述对象物是玻璃。
本发明的技术方案可以达到以下有益效果:
1、本发明的易洁疏水涂料有防污抗菌抗霉的效果;
2、本发明的易洁疏水涂料适用于玻璃,涂覆于玻璃上,在玻璃表面会出现一种荷叶效应,也叫做疏水效应,表现为水在物体表面呈水珠状,并向低处滑动,水珠会把灰尘等细小杂物裹走,使玻璃表面保持明亮清洁,并变得非常易于清洗;
3、本发明的易洁疏水涂料涂覆于玻璃上,还可以杜绝有机清洁剂的直接接触和滞留,有效的阻止了老化,保护玻璃透明度,延长保洁间隔时间;
4、本发明的易洁疏水涂料与现有技术的疏水涂料相比,用于玻璃表面,可以使玻璃使用寿命延长,且抗黄变、抗紫外线。
具体实施方式
下面结合具体实施例对本发明作进一步的说明,但本发明不受下述实施例的限定。
实施例1
按照以下重量百分含量的组分来配制本实施例的易洁疏水涂料:
上述有机溶剂选用乙醇,硅油选用含氢量是1.60%的硅油。
制备方法如下:
先将有机溶剂和硅油混合并搅拌均匀后,再加入三甲基丙氧基硅烷,最后加入冰醋酸调配均匀,即制得本实施例的易洁疏水涂料。
实施例2
按照以下重量百分含量的组分来配制本实施例的易洁疏水涂料:
上述有机溶剂选用异丙醇,硅油选用含氢量是1.58%的硅油。
制备方法如下:
先将有机溶剂和硅油混合并搅拌均匀后,再加入三甲基丙氧基硅烷,最后加入盐酸调配均匀,即制得本实施例的易洁疏水涂料。
实施例3
按照以下重量百分含量的组分来配制本实施例的易洁疏水涂料:
上述有机溶剂选用乙醇,硅油选用含氢量是1.59%的硅油。
制备方法如下:
先将有机溶剂和硅油混合并搅拌均匀后,再加入三甲基丙氧基硅烷,最后加入冰醋酸调配均匀,即制得本实施例的易洁疏水涂料。
实施例4
按照以下重量百分含量的组分来配制本实施例的易洁疏水涂料:
上述有机溶剂选用异丙醇,硅油选用含氢量是1.58%的硅油。
制备方法如下:
先将有机溶剂和硅油混合并搅拌均匀后,再加入三甲基丙氧基硅烷,最后加入盐酸调配均匀,即制得本实施例的易洁疏水涂料。
实施例5
按照以下重量百分含量的组分来配制本实施例的易洁疏水涂料:
上述有机溶剂选用异丙醇,硅油选用含氢量是1.6%的硅油。
制备方法如下:
先将有机溶剂和硅油混合并搅拌均匀后,再加入三甲基丙氧基硅烷,最后加入冰醋酸调配均匀,即制得本实施例的易洁疏水涂料。
实施例6
按照以下重量百分含量的组分来配制本实施例的易洁疏水涂料:
上述有机溶剂选用乙醇,硅油选用含氢量是1.59%的硅油。
制备方法如下:
先将有机溶剂和硅油混合并搅拌均匀后,再加入三甲基丙氧基硅烷,最后加入盐酸调配均匀,即制得本实施例的易洁疏水涂料。
实施例7
实施例1~3的易洁疏水涂料的应用方法是按照以下步骤进行:
(1)清洗对象物并干燥;
(2)将所述易洁疏水涂料涂抹于对象物;
(3)干燥。
实施例8
实施例4~6的易洁疏水涂料的应用方法是按照以下步骤进行:
(1)清洗:将玻璃表面的油污、油脂、灰尘等用清洗剂祛除,然后用清水将清洗剂冲洗干净,并保证玻璃完全干燥;
(2)涂抹:在通风环境下,用沾有所述易洁疏水涂料的无纺布在玻璃表面均匀涂抹,直至在玻璃表面所形成的涂层呈透明状为止;
(3)干燥:在自然通风环境下干燥,干燥时间不少于10分钟。
由于易洁疏水涂料在玻璃上涂抹均匀,玻璃在易洁疏水涂料涂覆完毕后仍然具有良好的透光性,在达到易洁疏水涂料带来的有益效果的同时,美观且玻璃本身的性质不受影响。
将本发明的易洁疏水涂料应用于玻璃表面,遇到水性污物时,玻璃表面会出现疏水效应,水在玻璃表面呈水珠状,并向低处滑动,水珠同时把灰尘等细小杂物裹走,使玻璃表面保持明亮清洁,并变得非常易于清洗。
最后应说明的是:以上仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换,但是凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (10)
2.根据权利要求1所述的易洁疏水涂料,其特征在于,所述有机溶剂选自异丙醇或乙醇。
3.根据权利要求1所述的易洁疏水涂料,其特征在于,所述硅油选用含氢量1.58%~1.60%的硅油。
4.根据权利要求1所述的易洁疏水涂料,其特征在于,所述有机酸是冰醋酸。
5.根据权利要求1所述的易洁疏水涂料,其特征在于,所述无机酸是盐酸。
6.根据权利要求1所述的易洁疏水涂料的制备方法,其特征在于,先将有机溶剂和硅油混合并搅拌均匀后,再加入三甲基丙氧基硅烷,最后加入有机酸或无机酸调配均匀,即制得所述易洁疏水涂料。
7.根据权利要求1所述的易洁疏水涂料的应用。
8.根据权利要求7所述的易洁疏水涂料的应用,其特征在于,包括以下步骤:
(1)清洗对象物并干燥;
(2)将所述易洁疏水涂料涂抹于对象物;
(3)干燥。
9.根据权利要求8所述的易洁疏水涂料的应用,其特征在于,包括以下步骤:
(1)清洗:将对象物表面的油污、油脂、灰尘等用清洗剂祛除,然后用清水将清洗剂冲洗干净,并保证对象物完全干燥;
(2)涂抹:在通风环境下,用沾有所述易洁疏水涂料的无纺布在对象物表面均匀涂抹,直至在对象物表面所形成的涂层呈透明状为止;
(3)干燥:在自然通风环境下干燥,干燥时间不少于10分钟。
10.根据权利要求8或9所述的易洁疏水涂料的应用,其特征在于,所述对象物是玻璃。