CN103173140A - 一种木工用氯丁橡胶胶粘剂 - Google Patents
一种木工用氯丁橡胶胶粘剂 Download PDFInfo
- Publication number
- CN103173140A CN103173140A CN2013100600044A CN201310060004A CN103173140A CN 103173140 A CN103173140 A CN 103173140A CN 2013100600044 A CN2013100600044 A CN 2013100600044A CN 201310060004 A CN201310060004 A CN 201310060004A CN 103173140 A CN103173140 A CN 103173140A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive
- rubber
- carpenter
- trees ashes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种木工用氯丁橡胶胶粘剂,由下列重量份的原料制成:苯乙烯100-120、乙酸乙酯100-150、氯丁橡胶CR12120-25、二甲苯15-20、4,4’-二苯基甲烷二异氰酸酯1-2、聚异丁烯8-12、3-氨丙基三甲氧基硅烷2-3、聚四氢呋喃醚二醇2-3、SG-2型PVC树脂3-5、二茂铁1-2、顺-1,4-聚异戊二烯橡胶8-12、三元乙丙橡胶5-8等。本发明胶黏剂具有优良的耐热性、耐寒性,粘结强度高,耐水防潮,贮存稳定性好,环保性好,使用效果好且方便。
Description
技术领域
本发明涉及一种胶黏剂,具体涉及一种木工用氯丁橡胶胶黏剂。
背景技术
氯丁橡胶胶粘剂性能优异、价格低廉,对橡胶、钢铁、混凝土、木材、皮革、织物等材料均有良好的粘接力。氯丁胶黏剂特性是:初始粘力大、粘接强度高、耐久性好、胶层柔韧,弹性良好,耐冲击与振动,有较好的耐油、耐水、耐碱、耐酸、耐溶剂性能,对木材有较好的粘接性,使用方便,价格低廉,但其耐热性较差,耐寒性不佳,贮存稳定性差。为了克服传统的氯丁胶黏剂耐热性较差,耐寒性不佳,贮存稳定性差等缺点,通过改进配方,从而生产出一种木工用氯丁橡胶胶黏剂。
发明内容
本发明的目的是提供一种耐温性好、粘结强度高、贮存稳定性好的木工用氯丁橡胶胶黏剂。
本发明采用的技术方案如下:
一种木工用氯丁橡胶胶粘剂,由下列重量份的原料制成:苯乙烯100-120、乙酸乙酯100-150、氯丁橡胶CR121 20-25、二甲苯15-20、4,4’-二苯基甲烷二异氰酸酯1-2、聚异丁烯8-12、3-氨丙基三甲氧基硅烷2-3、聚四氢呋喃醚二醇2-3、SG-2型PVC树脂3-5、二茂铁1-2、顺-1,4-聚异戊二烯橡胶8-12、三元乙丙橡胶5-8、氧化镁2-3、纳米蛭石10-15、纳米天青石粉5-8、防老剂OD 1-2、防老剂RD 1-2、聚酰胺蜡微粉5-10、促进剂CZ 1-2、促进剂Na-22 1-2、丙三醇三甘油酸酯8-12、苯胺甲基三乙氧基硅烷1-2、交联剂 TAC 1-2、抗氧剂1010 1-2、快压出炭黑15-20、硬脂酸锌1-2、乙酰柠檬酸三(2-乙基已)酯5-8、邻苯二甲酸聚酯3-5、改性大豆蛋白粉2-4、环氧大豆油10-15、改性树木灰烬1-2。
所述的改性大豆蛋白粉由以下步骤制得:取10-15份大豆蛋白粉,加入30-40份蒸馏水,在40-50℃下搅拌20-30min,用10-15%氢氧化钠溶液调节pH至8.5-9.0,再向其加入2-3%的十二烷基磺酸钠、3-4%的木质素磺酸钠、2-3%的乙基黄原酸钾,在50-60℃下搅拌20-30min,浓缩,烘干,粉碎研磨成超细粉末即可。
所述的改性树木灰烬由以下步骤制得:先用10-15%盐酸浸泡树木灰烬3-4h,去离子水洗涤干净,再用10-12%氢氧化钠溶液浸泡3-4h,再用去离子水洗涤至中性,烘干,加入相当于树木灰烬重量2-3%的月桂醇硫酸钠、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%的活性氧化铝,高速1200-1500r/min搅拌1-2h,烘干,粉碎研磨成超细粉末即可。
木工用氯丁橡胶胶粘剂的制备方法,包括以下步骤:
(1)将氯丁橡胶CR121 、二甲苯、4,4’-二苯基甲烷二异氰酸酯、聚异丁烯、3-氨丙基三甲氧基硅烷、聚四氢呋喃醚二醇、SG-2型PVC树脂、二茂铁、顺-1,4-聚异戊二烯橡胶、三元乙丙橡胶混合,在100-120℃下反应1-2h;
(2)将其它物料与反应物混合,搅拌30-40min,得到成品,包装即可。
本发明的有益效果:
本发明通过对大豆蛋白粉进行改性,改善了胶黏剂耐水性、保质期和稠度;通过对树木灰烬进行改性,提高了其在在胶黏剂组分中的分散均匀性,从而可以明显改善制鞋用高性能用高性能胶黏剂的粘接强度和耐水性,并具有成本低,效果优良的特点。本发明胶黏剂具有优良的耐热性、耐寒性,粘结强度高,耐水防潮,贮存稳定性好,环保性好,使用效果好且方便。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例
一种木工用氯丁橡胶胶粘剂,由下列重量份的原料制成:苯乙烯112份、乙酸乙酯125份、氯丁橡胶CR121 22份、二甲苯18份、4,4’-二苯基甲烷二异氰酸酯1.6份、聚异丁烯10份、3-氨丙基三甲氧基硅烷2份、聚四氢呋喃醚二醇3份、SG-2型PVC树脂4份、二茂铁1.8份、顺-1,4-聚异戊二烯橡胶10份、三元乙丙橡胶6份、氧化镁3份、纳米蛭石12份、纳米天青石粉8份、防老剂OD 2份、防老剂RD 1份、聚酰胺蜡微粉8份、促进剂CZ 1.5份、促进剂Na-22 1.5份、丙三醇三甘油酸酯10份、苯胺甲基三乙氧基硅烷1.6份、交联剂 TAC 1.5份、抗氧剂1010 1.6份、快压出炭黑18份、硬脂酸锌2份、乙酰柠檬酸三(2-乙基已)酯6份、邻苯二甲酸聚酯4份、改性大豆蛋白粉3份、环氧大豆油12份、改性树木灰烬2份。
所述的改性大豆蛋白粉由以下步骤制得:取15份大豆蛋白粉,加入40份蒸馏水,在45℃下搅拌30min,用12%氢氧化钠溶液调节pH至8.5,再向其加入3%的十二烷基磺酸钠、4%的木质素磺酸钠、3%的乙基黄原酸钾,在50℃下搅拌30min,浓缩,烘干,粉碎研磨成超细粉末即可。
所述的改性树木灰烬由以下步骤制得:先用15%盐酸浸泡树木灰烬4h,去离子水洗涤干净,再用12%氢氧化钠溶液浸泡4h,再用去离子水洗涤至中性,烘干,加入相当于树木灰烬重量3%的月桂醇硫酸钠、2%的平平加O、3%的柠檬酸三丁酯、5%的活性氧化铝,高速1500r/min搅拌2h,烘干,粉碎研磨成超细粉末即可。
木工用氯丁橡胶胶粘剂的制备方法,包括以下步骤:
(1)将氯丁橡胶CR121 、二甲苯、4,4’-二苯基甲烷二异氰酸酯、聚异丁烯、3-氨丙基三甲氧基硅烷、聚四氢呋喃醚二醇、SG-2型PVC树脂、二茂铁、顺-1,4-聚异戊二烯橡胶、三元乙丙橡胶混合,在110℃下反应2h;
(2)将其它物料与反应物混合,搅拌40min,得到成品,包装即可。
本实施例制得的胶黏剂的主要性能如下表1。
表1
耐水,在水中浸泡12个月,剥离强度下降5%。
Claims (4)
1.一种木工用氯丁橡胶胶粘剂,其特征在于,由下列重量份的原料制成:苯乙烯100-120、乙酸乙酯100-150、氯丁橡胶CR121 20-25、二甲苯15-20、4,4’-二苯基甲烷二异氰酸酯1-2、聚异丁烯8-12、3-氨丙基三甲氧基硅烷2-3、聚四氢呋喃醚二醇2-3、SG-2型PVC树脂3-5、二茂铁1-2、顺-1,4-聚异戊二烯橡胶8-12、三元乙丙橡胶5-8、氧化镁2-3、纳米蛭石10-15、纳米天青石粉5-8、防老剂OD 1-2、防老剂RD 1-2、聚酰胺蜡微粉5-10、促进剂CZ 1-2、促进剂Na-22 1-2、丙三醇三甘油酸酯8-12、苯胺甲基三乙氧基硅烷1-2、交联剂 TAC 1-2、抗氧剂1010 1-2、快压出炭黑15-20、硬脂酸锌1-2、乙酰柠檬酸三(2-乙基已)酯5-8、邻苯二甲酸聚酯3-5、改性大豆蛋白粉2-4、环氧大豆油10-15、改性树木灰烬1-2。
2.根据权利要求1所述的木工用氯丁橡胶胶粘剂,其特征在于,所述的改性大豆蛋白粉由以下步骤制得:取10-15份大豆蛋白粉,加入30-40份蒸馏水,在40-50℃下搅拌20-30min,用10-15%氢氧化钠溶液调节pH至8.5-9.0,再向其加入2-3%的十二烷基磺酸钠、3-4%的木质素磺酸钠、2-3%的乙基黄原酸钾,在50-60℃下搅拌20-30min,浓缩,烘干,粉碎研磨成超细粉末即可。
3.根据权利要求1所述的木工用氯丁橡胶胶粘剂,其特征在于,所述的改性树木灰烬由以下步骤制得:先用10-15%盐酸浸泡树木灰烬3-4h,去离子水洗涤干净,再用10-12%氢氧化钠溶液浸泡3-4h,再用去离子水洗涤至中性,烘干,加入相当于树木灰烬重量2-3%的月桂醇硫酸钠、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%的活性氧化铝,高速1200-1500r/min搅拌1-2h,烘干,粉碎研磨成超细粉末即可。
4.一种如权利要求1所述的木工用氯丁橡胶胶粘剂的制备方法,其特征在于包括以下步骤:
(1)将氯丁橡胶CR121 、二甲苯、4,4’-二苯基甲烷二异氰酸酯、聚异丁烯、3-氨丙基三甲氧基硅烷、聚四氢呋喃醚二醇、SG-2型PVC树脂、二茂铁、顺-1,4-聚异戊二烯橡胶、三元乙丙橡胶混合,在100-120℃下反应1-2h;
(2)将其它物料与反应物混合,搅拌30-40min,得到成品,包装即可。