CN103173126A - 一种油漆 - Google Patents

一种油漆 Download PDF

Info

Publication number
CN103173126A
CN103173126A CN 201310088201 CN201310088201A CN103173126A CN 103173126 A CN103173126 A CN 103173126A CN 201310088201 CN201310088201 CN 201310088201 CN 201310088201 A CN201310088201 A CN 201310088201A CN 103173126 A CN103173126 A CN 103173126A
Authority
CN
China
Prior art keywords
paint
parts
powder
polyvinyl butyral
phosphoric acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201310088201
Other languages
English (en)
Inventor
孙丽美
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201310088201 priority Critical patent/CN103173126A/zh
Publication of CN103173126A publication Critical patent/CN103173126A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种油漆，包括漆粉、聚乙烯醇缩丁醛、松香树脂和亚麻油混合物、沸石粉、磷酸和水溶剂，本发明的有益效果是：1、原料主要为一些市场上常见的材料，容易取得，并且成本不高；2、本发明的加入了磷酸和聚乙烯醇缩丁醛，使其油漆干燥快，粘性好，涂刷在物体上可保持长时间不脱落。

Description

一种油漆
技术领域
本发明涉及一种油漆。
背景技术
油漆的一般成分包括：成膜物质，颜料、溶剂、助剂。油漆是一种能牢固覆盖在物体表面，起保护、装饰、标志和其他特殊用途的化学混合物涂料。中国涂料界比较权威的涂料工艺一书是这样定义的：涂料是一种材料，这种材料可以用不同的实施工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型。按照现代通行的化工产品的分类，涂料属于精细化工产品。现代的油漆的粉刷好以后不仅会传出一股刺鼻的味道，而且在一定的时间能不容易干，而且在粘性很差，经过风吹雨打后很容易脱落。
发明内容
本发明要解决的技术问题是提供一种粘性好，干燥快且适合任意环境中使用，在长时间不易脱落的油漆。
为解决上述问题，本发明采用如下技术方案：
一种油漆，包括漆粉、聚乙烯醇缩丁醛、松香树脂和亚麻油混合物、沸石粉、磷酸和水溶剂。
作为优选的技术方案，所述油漆及各组分的含量分别为：
漆粉                      20-30份；
聚乙烯醇缩丁醛            5-8份；
松香树脂和亚麻油混合物    10-18份；
沸石粉                    5-10份；
磷酸                      1-3份；
水溶剂                    40-50份。
作为优选的技术方案，所述油漆的制备步骤如下：
a)按各含量的份量分别提取：漆粉25份，聚乙烯醇缩丁醛6份，松香树脂和亚麻油混合物15份，沸石粉7份，磷酸2份，水溶剂45份；
b)将漆粉25份，聚乙烯醇缩丁醛6份，沸石粉7份，水溶剂45份放入加工设备中进行，温度控制在45℃-75℃，接着进行搅拌10-15分钟，使其均匀，形成较稀的油漆；
c)然后在稀释的油漆中加入具有凝固作用的松香树脂和亚麻油混合物15份，均匀搅拌15分钟后再加入磷酸2份，在放入设备中加工成品油漆；
d)最后油漆通过专用设备安装在漆筒内。
本发明的有益效果是：1、原料主要为一些市场上常见的材料，容易取得，并且成本不高；
2、本发明的加入了磷酸和聚乙烯醇缩丁醛，使其油漆干燥快，粘性好，涂刷在物体上可保持长时间不脱落。
具体实施方式
一种油漆，包括漆粉、聚乙烯醇缩丁醛、松香树脂和亚麻油混合物、沸石粉、磷酸和水溶剂。
其中，所述油漆及各组分的含量分别为：
漆粉                      20-30份；
聚乙烯醇缩丁醛            5-8份；
松香树脂和亚麻油混合物    10-18份；
沸石粉                    5-10份；
磷酸                      1-3份；
水溶剂                    40-50份。
所述油漆的制备步骤如下：
a)按各含量的份量分别提取：漆粉25份，聚乙烯醇缩丁醛6份，松香树脂和亚麻油混合物15份，沸石粉7份，磷酸2份，水溶剂45份；
b)将漆粉25份，聚乙烯醇缩丁醛6份，沸石粉7份，水溶剂45份放入加工设备中进行，温度控制在45℃-75℃，接着进行搅拌10-15分钟，使其均匀，形成较稀的油漆；
c)然后在稀释的油漆中加入具有凝固作用的松香树脂和亚麻油混合物15份，均匀搅拌15分钟后再加入磷酸2份，在放入设备中加工成品油漆；
d)最后油漆通过专用设备安装在漆筒内。
本发明的有益效果是：1、原料主要为一些市场上常见的材料，容易取得，并且成本不高；
2、本发明的加入了磷酸和聚乙烯醇缩丁醛，使其油漆干燥快，粘性好，涂刷在物体上可保持长时间不脱落。
具体实施1
一种油漆，包括漆粉、聚乙烯醇缩丁醛、松香树脂和亚麻油混合物、沸石粉、磷酸和水溶剂。
漆粉20-30份；聚乙烯醇缩丁5-8份；松香树脂和亚麻油混合物10-18份；沸石粉5-10份；磷酸1-3份；水溶剂40-50份。
所述油漆的制备步骤如下：
a)按各含量的份量分别提取：漆粉25份，聚乙烯醇缩丁醛6份，松香树脂和亚麻油混合物15份，沸石粉7份，磷酸2份，水溶剂45份；
b)将漆粉25份，聚乙烯醇缩丁醛6份，沸石粉7份，水溶剂45份放入加工设备中进行，温度控制在45℃-75℃，接着进行搅拌10-15分钟，使其均匀，形成较稀的油漆；
c)然后在稀释的油漆中加入具有凝固作用的松香树脂和亚麻油混合物15份，均匀搅拌15分钟后再加入磷酸2份，在放入设备中加工成品油漆；
d)最后油漆通过专用设备安装在漆筒内。
在经过测试时，油漆粉刷在外墙上经过2个月的风吹雨打和烈日下暴晒，仍完整的凝固在墙面上，因此此配方油漆适合在郊外等恶劣环境使用。
具体实施2
一种油漆，包括漆粉、聚乙烯醇缩丁醛、松香树脂和亚麻油混合物、沸石粉、磷酸和水溶剂。
漆粉20-30份；聚乙烯醇缩丁5-8份；松香树脂和亚麻油混合物10-18份；沸石粉5-10份；磷酸1-3份；水溶剂40-50份。
所述油漆的制备步骤如下：
a)按各含量的份量分别提取：漆粉20份，聚乙烯醇缩丁醛8份，松香树脂和亚麻油混合物18份，沸石粉7份，磷酸2份，水溶剂45份；
b)将漆粉20份，聚乙烯醇缩丁醛8份，沸石粉7份，水溶剂45份放入加
工设备中进行，温度控制在45℃-75℃，接着进行搅拌10-15分钟，使其均匀，形成较稀的油漆；
c)然后在稀释的油漆中加入具有凝固作用的松香树脂和亚麻油混合物18份，均匀搅拌15分钟后再加入磷酸2份，在放入设备中加工成品油漆；
d)最后油漆通过专用设备安装在漆筒内。
在经过测试时，油漆粉刷在家中内墙上经过2个月的时间，在没有经过风吹和高温烘干，粉刷在墙上的油漆已完整的黏结的墙上，其用工具挖取也不易脱落。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。

Claims (3)

1.一种油漆，其特征在于：包括漆粉、聚乙烯醇缩丁醛、松香树脂和亚麻油混合物、沸石粉、磷酸和水溶剂。
2.根据权利要求1所述的油漆，其特征在于：所述油漆及各组分的含量分别为：
漆粉                      20-30份；
聚乙烯醇缩丁醛            5-8份；
松香树脂和亚麻油混合物    10-18份；
沸石粉                    5-10份；
磷酸                      1-3份；
水溶剂                    40-50份。
3.根据权利要求1和2所述的油漆及其制备方法，其特征在于：所述油漆的制备步骤如下：
a)按各含量的份量分别提取：漆粉25份，聚乙烯醇缩丁醛6份，松香树脂和亚麻油混合物15份，沸石粉7份，磷酸2份，水溶剂45份；
b)将漆粉25份，聚乙烯醇缩丁醛6份，沸石粉7份，水溶剂45份放入加工设备中进行，温度控制在45℃-75℃，接着进行搅拌10-15分钟，使其均匀，形成较稀的油漆；
c)然后在稀释的油漆中加入具有凝固作用的松香树脂和亚麻油混合物15份，均匀搅拌15分钟后再加入磷酸2份，在放入设备中加工成品油漆；
d)最后油漆通过专用设备安装在漆筒内。
CN 201310088201 2013-03-07 2013-03-07 一种油漆 Pending CN103173126A (zh)