CN1031720C - Anti-static electricity internal wall emulsion coating - Google Patents
Anti-static electricity internal wall emulsion coating Download PDFInfo
- Publication number
- CN1031720C CN1031720C CN 90101241 CN90101241A CN1031720C CN 1031720 C CN1031720 C CN 1031720C CN 90101241 CN90101241 CN 90101241 CN 90101241 A CN90101241 A CN 90101241A CN 1031720 C CN1031720 C CN 1031720C
- Authority
- CN
- China
- Prior art keywords
- coating
- static inhibitor
- emulsion
- internal wall
- static electricity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to antistatic emulsion coating for internal walls, which is indoor architectural coating and is prepared by adding a liquid two-element antistatic agent in the processing of the emulsion coating containing high polymer emulsion, stuffing, coloring material and auxiliary agents. The coating is used as internal wall coating in the industries of electronics, chemical engineering, production of textiles and precision instruments, etc., and the coating can avoid fire hazards, explosion and other accidents caused by static electricity.
Description
The present invention relates to a kind of interior architecture finishing material, belong to the invention of building coating aspect.
Along with industrial expansion, the static hazard in industries such as chemical industry, electronics, weaving and precision instrument manufacturing becomes increasingly conspicuous, in producing assembling or storage process, because electrostatic accumulation and discharge fire hazardous and explosion hazard.At present, it is few to be used for the Antistatic Paint kind of building trade.The described Antistatic Paint technology of Japanese Patent JP63000368 is the coating that is used for floor, top ceiling, wall, and its film forming matter is the polyformate resin, and conductive additive is a Zinc oxide powder.Macromolecular material all is electrically insulating material basically, adopt some means can make them become the macromolecular material of conduction, two kinds of conducting polymer composite separation structure type and mixed types, the former does not develop into the practical stage as yet, and the conductive additive that the latter uses in the prior art (as the JP63000368 patented technology) adopt pressed powder, comprise metal powder, metal oxide powder, carbon black powder etc., adopt the metal-powder of non-valuable class to have the problem of burning.Carbon black powder is only applicable to dark coating, and list is more difficult to get low-resistance coating with the metal oxide powder.
The purpose of this invention is to provide a kind of interior wall coating that conductive additive can conduct and leak static electric charge that adds.
The present invention seeks to realize like this, it comprises polymer emulsion, filler, colorant and film coalescence aid, dispersion agent, defoamer and thickening material, in the coating component, add the double base static inhibitor, their total content accounts for 1-20% of coating gross weight, and every kind of static inhibitor can account for 1-15% of coating weight in selected two kinds of static inhibitor.
Filmogen that the present invention contains is a kind of polymer emulsion, can adopt benzene emulsion (being the multipolymer of vinylbenzene-propionic acid alkene-acrylate or the multipolymer of vinylbenzene-vinylformic acid-methacrylic ester) or with vinyl acetate emulsion (multipolymer of vinyl acetate between to for plastic-acrylate).Auxiliary agent in the coating comprises film coalescence aid, dispersion agent, defoamer, thickening material etc.
The conductive additive (static inhibitor) that this coating adopts has following several:
1, maleic anhydride macrogol ester.
2, sim alkylphenol Soxylat A 25-7, its its name of product are static inhibitor 0 π-10.
3, polyvinyl 1# finish.
4, trihydroxyethyl methyl quaternary ammonium Methylsulfate, its name of product is an antistatic agent TM
In four kinds of above-mentioned coating any two kinds all capable of being combined.
The present invention adds two kinds in the above-mentioned static inhibitor on the basis of copolymer emulsion coating.The moisture content that the ion that static inhibitor ionization forms, film coated surface absorb and film inner polar molecule and polar group play conduction and leak charge jointly, thereby the static inhibitor that has prevented the combination of electrostatic accumulation adding double base can make two kinds of static inhibitor performance complements, increases anti-static ability.
The interior wall that this coating can be used for the requirement anti-electrostatic is cement, concrete and the surfaces such as timber of having considered problem with grounding.
This coating can be used for weaving, the inner wall surface of the industries such as production of chemical industry, oil, electronics, precision instrument.Adopt this coating to help avoid accidents such as fire that indoor static causes and blast.
Narrate below in conjunction with embodiment.
Embodiment 1: first component materials name weigh (%)
Ethylene glycol 0.8
Propylene glycol 1.2
10% Sodium hexametaphosphate 99 1.5
Polyacrylic acid is received CP 2.0
Tributyl phosphate 0.15
Defoamer KHZ-87 0.15
Sim alkylphenol Soxylat A 25-7 1.0
Static inhibitor maleic anhydride macrogol ester 15.0
Water 12.0
Titanium dioxide (rutile-type) 14.1
Zinc sulfide white 8.0
Talcum powder 2.7 component B title material weight (%)
Sodium pentachlorophenate 0.05
Sodium Nitrite 0.1
Sodium Benzoate 0.1
Water 1.8
Dibutyl phthalate 0.05
Multipolymer supernatant liquid BC-01 39
Ammoniacal liquor (containing ammonia 25-28%) 0.3
Above-mentioned first component is put into the high speed dispersion device in order, treat that the wetting back of solid matter disperseed 30 minutes under high speed.First three is planted material and adds in the entry earlier and dissolve in the component B, add in first component together with other material in the component B then, under low speed, mix, it is qualified to be milled to fineness through mechanical grinder, promptly obtains coating of the present invention, is a kind of whitewash.
Embodiment 2:
Prepared a kind of sky blue Antistatic Paint.Component B among the embodiment 1 is constant, and the first component is done following adjustment.
Title material weight (%)
Ethylene glycol 0.8
Propylene glycol 1.0
Phenylcarbinol 0.3
10% Sodium hexametaphosphate 99 1.5
2% polyvinyl alcohol 2.0
Silicon froth breaking clear KHZ-87 0.3
Trihydroxyethyl methyl quaternary ammonium Methylsulfate 1.5
Sim alkylphenol Soxylat A 25-7 1.5
Water 15.0
Titanium dioxide (rutile-type) 21.0
Phthalocyanine blue 0.1
Zinc sulfide white 9.5
Talcum powder 4.1
Press the program processing coating of embodiment 1.This coating purifies the construction of refrigerating industry company in May, 1989 through Tianjin, be used for the dado of nearly thousand square metres of Shijiazhuang City electric light Electronics Co., Ltd. production plants.Practical application proves that this coating application is convenient, and brushing is all flat, and clinging power is strong, colour stable.Test metope resistance to ground major part is in 3-4 megaohms after half a year, and vertex 15 megaohms meet the anti-electrostatic requirement.
Embodiment 3:
Prepared a kind of whitewash, the composition among the embodiment 1 is constant substantially, but changes copolymer emulsion into LT-3, and consumption is 35%, changes static inhibitor into polyvinyl 1# finish and maleic anhydride Macrogol Ester, and its consumption is 10%.Use sodium polyacrylate CP instead the water-borne coatings thickening material, consumption is constant.Do not add defoamer KHZ-87, and only add 0.3% tributyl phosphate.
The foregoing description polyvinyl 1# finish belongs to the alkyl phosphate triethanolamine salt, and manufacturer is auxiliary reagent factory, Shanghai and auxiliary reagent factory, Tianjin.Antistatic agent TM is auxiliary reagent factory, a Shanghai product.Sodium polyacrylate CP is the product of Beijing Chemical Engineering College's Fine Chemical Works.Silicon defoaming agent KHZ-87 manufacturer is the auxiliary reagent factory, Tianjin, is organosilicone compounds.Copolymer emulsion BC-01 manufacturer is the Dongfang Chemical Plant, Beijing, The East Chemical Plant,Beijing, and main component is the multipolymer of vinylbenzene and acrylate.Copolymer emulsion LT-3 is the product of Shijiazhuang City, Hebei Province Paint Factory, and main component is esters of acrylic acid and cinnamic multipolymer.
Used maleic anhydride macrogol ester can make with the maleic anhydride esterification with polyoxyethylene glycol among the present invention, buys molecular weight on the market and is 200,400,800,1000,2000,4000,6000 different polyoxyethylene glycol and all can be used as esterification feed.Monoesters, dibasic acid esters or both mixtures all can be used as static inhibitor usefulness, and they are respectively applied in the coating of the present invention, and coating resistance to ground value is 10
5-10
7Ω, and the good anti-static performance is arranged.
Claims (1)
1, a kind of anti-static electricity internal wall emulsion coating, wherein contain polymer emulsion, filler, colorant and film coalescence aid, dispersion agent, defoamer and thickening material, it is characterized in that containing in the coating component double base static inhibitor, the content of contained double base static inhibitor accounts for 1-20% of coating gross weight in the coating, wherein the composition of every kind of static inhibitor can account for 1-15% of coating gross weight, described double base static inhibitor is any two kinds in following four kinds, and they comprise the maleic anhydride Macrogol Ester, the sim alkylphenol Soxylat A 25-7, polyvinyl 1# finish and trihydroxyethyl methyl quaternary ammonium Methylsulfate.