CN103146309A - 玻化瓷砖胶黏剂 - Google Patents

玻化瓷砖胶黏剂 Download PDF

Info

Publication number
CN103146309A
CN103146309A CN2013100694164A CN201310069416A CN103146309A CN 103146309 A CN103146309 A CN 103146309A CN 2013100694164 A CN2013100694164 A CN 2013100694164A CN 201310069416 A CN201310069416 A CN 201310069416A CN 103146309 A CN103146309 A CN 103146309A
Authority
CN
China
Prior art keywords
component
parts
material component
weight
liquid material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013100694164A
Other languages
English (en)
Inventor
辉宝琨
卢文书
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG LOMMOL CHEMICAL Co Ltd
Original Assignee
GUANGDONG LOMMOL CHEMICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG LOMMOL CHEMICAL Co Ltd filed Critical GUANGDONG LOMMOL CHEMICAL Co Ltd
Priority to CN2013100694164A priority Critical patent/CN103146309A/zh
Publication of CN103146309A publication Critical patent/CN103146309A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种玻化瓷砖胶黏剂，包括液料组分A和粉料组分B，按重量分数比按1∶3～4称取放置，将液料组分A倒入粉料组分B中搅拌均匀，搅拌均匀无结块，配好的浆料放置5～10分钟，再用搅拌器拌匀即可施工；液料组分A包括如下各组分，各组分按重量分数比表示如下：固含量40%～60%的苯乙烯-丙烯酸酯乳液70～80份；保水剂3～5份；防霉、防藻剂0～1份；防腐剂1～2份；消泡剂0～2份；纯净水10～20份，粉料组分B包括如下各组分，各组分按重量分数比表示如下：水泥47～59份；矿物填料41～53份。其给建筑市场和人身的安全提供一个粘贴玻化瓷质砖的新产品和经得起外界环境和气候影响的安全环保材料。

Description

玻化瓷砖胶黏剂
技术领域
本发明涉及一种玻化瓷砖胶黏剂，尤其是涉及一种用于建筑行业的玻化瓷砖胶黏剂。
背景技术
目前,家居装饰与大型会所、超市和建筑物的内外装饰市场，原来用高吸水率（5%～10%）的陶质砖进行装修，但因其强度低、款式单一、规格尺寸小，已不适合高速发展的市场需要。玻化瓷质砖具有低吸水（其吸水率降至千分之五以下）、强度高、规格和品种多等优点，已经广泛应用在建筑装饰市场。玻化瓷质砖因其具有高致密和低吸水率的特点，使用普通刚性瓷砖胶粘结材料和现场拌合的水泥砂浆材料，粘贴该类型的瓷质砖，往往出现胶粘材料与砖面之间出现裂面而导致瓷砖的脱落，严重影响了建筑和人身的安全。
目前，建筑装饰和建筑胶粘材料领域普通刚性瓷砖胶粘结材料仅适合致密度低、面层粗燥的高吸水率（5%～10%）的陶质砖的使用，其缺点是：
①、粘结强度低。
②、粘结后的瓷砖，受到雨水的浸蚀后，刚性瓷砖胶粘结材料粘结强度降低，瓷砖容易脱落。
③、气候冷热变化，使胶凝材料受到变形的影响，而导致胶凝材料与瓷砖界面出现裂层，而引起瓷砖的脱落。
④、粘贴高致密、仿石材、规格和品种多、低吸水率的抛光砖和玻化瓷质砖粘结力低，通常会在与瓷砖界面出现裂层导致瓷砖的脱落。
随着市场的发展，高致密、仿石材、规格和品种多、低吸水率（其吸水率降至千分之五以下）及强度高的玻化瓷质砖，已经广泛被建筑装饰市场所采用。普通刚性瓷砖胶粘结材料粘贴该类型的瓷质砖，往往出现胶粘材料与砖面之间出现裂面，经不起雨水的浸蚀和气候冷热的影响，而导致瓷砖的脱落，严重影响了建筑和人身的安全，给建筑市场带来严重的安全隐患。
发明内容
为了给建筑市场和人身的安全提供一个粘贴玻化瓷质砖的新产品和经得起外界环境和气候影响的安全环保材料。本发明提出一种玻化瓷砖胶黏剂，本发明利用苯乙烯-丙烯酸酯乳液与水泥及矿物材料的混合,在水泥的水化过程中，乳液水分用于水泥水化反应后被蒸发，聚合乳液把水泥及矿物填料颗粒紧紧地包裹起来，并填充水泥和矿物骨架之间的空隙，使高分子微粒脱水而与水泥及矿物填料粘连在一起，加强了聚合体的内聚力,使其在与玻化瓷质砖的界面处增大了两者之间的吸附粘着力,从而大大提高了材料的粘结性能，解决了玻化瓷质砖与刚性水泥基胶凝材料易脱落的技术问题。
本发明采用如下技术方案实现：
一种玻化瓷砖胶黏剂，包括液料组分A和粉料组分B，按重量分数比将液料组分A和粉料组分B按1∶3～4称取放置，将液料组分A倒入粉料组分B中搅拌均匀，搅拌均匀无结块，配好的浆料放置5～10分钟，再用搅拌器拌匀即可施工；
所述液料组分A包括如下各组分，各组分按重量分数比表示如下：固含量40%～60%的苯乙烯-丙烯酸酯乳液70～80份；保水剂3～5份；防霉、防藻剂0～1份；防腐剂1～2份；消泡剂0～2份；纯净水10～20份，
所述粉料组分B包括如下各组分，各组分按重量分数比表示如下：水泥47～59份；矿物填料41～53份。
另一种优选方案为按重量分数比将液料组分A和粉料组分B按1∶3.5称取放置，
所述液料组分A包括如下各组分，各组分按重量分数比表示如下：固含量40%～60%的苯乙烯-丙烯酸酯乳液75～80份；保水剂3～5份；防霉、防藻剂0～1份；防腐剂1～2份；消泡剂0～2份；纯净水10～15份，
所述粉料组分B包括如下各组分，各组分按重量分数比表示如下：水泥50份；矿物填料50份。
所述水泥为符合GB175-2007《通用硅酸盐水泥》标准的水泥。
所述矿物填料为硅灰石、微硅粉末、高岭土和二氧化硅中的任意一种或几种的混合物按重量分数含量＞99%的细集料。
所述保水剂为甲基纤维素醚或羟丙基纤维素醚。
所述防霉、防藻剂为四氯间苯二腈无溶剂。
所述防腐剂为5-氯-2-甲基-4-异噻唑啉-3-酮、和2-甲基-4-异噻唑啉-3-酮。
所述消泡剂为疏水二氧化硅、多羟基化合物疏水型和有机脂多羟基化合物中任意一种。
与现有技术相比，本发明具有如下有益效果：
本发明利用苯乙烯-丙烯酸酯乳液与水泥及矿物材料的混合,乳液水分用于水泥水化反应后被蒸发，聚合乳液把水泥及矿物填料颗粒紧紧地包裹起来，并填充水泥和矿物骨架之间的空隙，使高分子微粒脱水而与水泥及矿物填料粘连在一起，加强了聚合体的内聚力,使其在与玻化瓷质砖的界面处增大了两者之间的吸附粘着力,从而大大提高了材料的粘结性能。解决了玻化瓷质砖与刚性水泥基胶凝材料易脱落的技术问题。聚合乳液与无机胶凝材料、矿物填料等活性材料成为高分子聚合体，胶凝材料与瓷砖的界面的粘结力不会因受到雨水的浸蚀和温度高低变化带来的影响，提高了其适应外界环境的能力，确保了瓷砖粘结的稳固性，增强了建筑物和人身了安全性。
具体实施方式
实施例1
一种玻化瓷砖胶黏剂，包括液料组分A和粉料组分B，按重量分数比将液料组分A和粉料组分B按1∶3～4称取放置，将液料组分A倒入粉料组分B中搅拌均匀，搅拌均匀无结块，配好的浆料放置5～10分钟，再用搅拌器拌匀即可施工；
所述液料组分A包括如下各组分，各组分按重量分数比表示如下：固含量40%～60%的苯乙烯-丙烯酸酯乳液70～80份；保水剂3～5份；防霉、防藻剂0～1份；防腐剂1～2份；消泡剂0～2份；纯净水10～20份，
所述粉料组分B包括如下各组分，各组分按重量分数比表示如下：水泥47～59份；矿物填料41～53份。
实施例2
按重量分数比将液料组分A和粉料组分B按1∶3.5称取放置，
所述液料组分A包括如下各组分，各组分按重量分数比表示如下：固含量40%～60%的苯乙烯-丙烯酸酯乳液75～80份；保水剂3～5份；防霉、防藻剂0～1份；防腐剂1～2份；消泡剂0～2份；纯净水10～15份，
所述粉料组分B包括如下各组分，各组分按重量分数比表示如下：水泥50份；矿物填料50份。
所述水泥材料为普通硅酸盐水泥（PO42.5R）。
所述矿物填料为硅灰石、微硅粉末、高岭土、二氧化硅含量＞99%的细集料中的任何一种。
所述保水剂为有优异的保水性能的，可以有效锁住水分的一种甲基纤维素醚、羟丙基纤维素醚的一种物质。
所述防霉、防藻剂为四氯间苯二腈无溶剂型、环保不含甲醛、能有效杀灭藻类、防霉变的一种物质。
所述防腐剂为5-氯-2-甲基-4-异噻唑啉-3-酮、和2-甲基-4-异噻唑啉-3-酮具有广谱长效高稳定性杀菌防腐的一种物质。
所述消泡剂为疏水二氧化硅、多羟基化合物疏水型和有机脂多羟基化合物中的一种物质。
本发明与现有技术相比技术指标比较如下：
Figure BDA00002883477900061
从以上比较看出,本发明的优点是:
①、玻化瓷砖胶黏剂材料拉伸胶黏原强度(28d）指标大大高于国家行业标准，表征了此类材料在原始水泥基面上的粘结力极强。
②、玻化瓷砖胶黏剂材料浸水后拉伸胶黏强度(28d）指标高于国家行业标准的3倍，表征了此类材料在长期受到雨水的浸蚀后，此材料与瓷砖的粘结力不会降低，确保了瓷砖粘结的稳定性。
③、玻化瓷砖胶黏剂材料热老化拉伸胶黏强度(28d）指标高于国家行业标准的4倍，表征了此类材料在长期受到高温的环境条件下，此材料与瓷砖的粘结力不会降低，也确保了瓷砖粘结的稳定性。
④、玻化瓷砖胶黏剂材料冻融循环拉伸胶黏强度(28d）指标高于国家行业标准的3倍，表征了此类材料在长期受到低温寒冷的环境条件下，此材料与瓷砖的粘结力也不会降低，确保了瓷砖粘结的安全性（一般称耐候性）。
⑤、玻化瓷砖胶黏剂材料20min晾置后拉伸胶黏强度(28d）指标高于国家行业标准的2倍以上，表征了此类材料在瓷砖粘贴施工过程中，瓷砖铺贴调整后，材料的粘结力不会降低，确保了瓷砖粘结性能不变。
检测结果如下：
①、拉伸胶黏原强度(28d）大于1.1mPa
②、浸水后拉伸胶黏强度(28d）大于1.0mPa
③、热老化拉伸胶黏强度(28d）大于2.0mPa
④、冻融循环拉伸胶黏强度(28d）大于1.5mPa
⑤、20min晾置后拉伸胶黏强度(28d）大于1.2mPa
从以上分析看出，本发明的材料粘结强度高，环境的适应力强，为建筑物和人身安全提供了保证。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.一种玻化瓷砖胶黏剂，其特征在于，包括液料组分A和粉料组分B，按重量分数比将液料组分A和粉料组分B按1∶3～4称取放置，将液料组分A倒入粉料组分B中搅拌均匀，搅拌均匀无结块，配好的浆料放置5～10分钟，再用搅拌器拌匀即可施工；
所述液料组分A包括如下各组分，各组分按重量分数比表示如下：固含量40%～60%的苯乙烯-丙烯酸酯乳液70～80份；保水剂3～5份；防霉、防藻剂0～1份；防腐剂1～2份；消泡剂0～2份；纯净水10～20份，
所述粉料组分B包括如下各组分，各组分按重量分数比表示如下：水泥47～59份；矿物填料41～53份。
2.根据权利要求1所述玻化瓷砖胶黏剂，其特征在于，按重量分数比将液料组分A和粉料组分B按1∶3.5称取放置，
所述液料组分A包括如下各组分，各组分按重量分数比表示如下：固含量40%～60%的苯乙烯-丙烯酸酯乳液75～80份；保水剂3～5份；防霉、防藻剂0～1份；防腐剂1～2份；消泡剂0～2份；纯净水10～15份，
所述粉料组分B包括如下各组分，各组分按重量分数比表示如下：水泥50份；矿物填料50份。
3.根据权利要求1或2所述玻化瓷砖胶黏剂，其特征在于，所述水泥为符合GB175-2007《通用硅酸盐水泥》标准的水泥。
4.根据权利要求1或2所述玻化瓷砖胶黏剂，其特征在于，所述矿物填料为硅灰石、微硅粉末、高岭土和二氧化硅中的任意一种或几种的混合物按重量分数含量＞99%的细集料。
5.根据权利要求1或2所述玻化瓷砖胶黏剂，其特征在于，所述保水剂为甲基纤维素醚或羟丙基纤维素醚。
6.根据权利要求1或2所述玻化瓷砖胶黏剂，其特征在于，所述防霉、防藻剂为四氯间苯二腈无溶剂。
7.根据权利要求1或2所述玻化瓷砖胶黏剂，其特征在于，所述防腐剂为5-氯-2-甲基-4-异噻唑啉-3-酮、和2-甲基-4-异噻唑啉-3-酮。
8.根据权利要求1或2所述玻化瓷砖胶黏剂，其特征在于，所述消泡剂为疏水二氧化硅、多羟基化合物疏水型和有机脂多羟基化合物中任意一种。
CN2013100694164A 2013-03-05 2013-03-05 玻化瓷砖胶黏剂 Pending CN103146309A (zh)