CN103146270A - 一种纳米多功能彩色防腐防水涂料 - Google Patents
一种纳米多功能彩色防腐防水涂料 Download PDFInfo
- Publication number
- CN103146270A CN103146270A CN 201210588828 CN201210588828A CN103146270A CN 103146270 A CN103146270 A CN 103146270A CN 201210588828 CN201210588828 CN 201210588828 CN 201210588828 A CN201210588828 A CN 201210588828A CN 103146270 A CN103146270 A CN 103146270A
- Authority
- CN
- China
- Prior art keywords
- nano
- water
- powder
- proof coating
- corrosive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种建筑防水材料,具体说涉及一种纳米多功能彩色防腐防水涂料,其组合物主要由A组液料:水性氟碳乳液树脂、乙烯一醋乙烯共聚物、丙稀酸树脂乳液、纳米二氧化硅、纳米云母粉、纳米硅美土、酯类增塑剂、乙二醇、分散剂,B组粉料:滑石粉、高铝水泥、无机填料、无机颜料混合而成,本发明的具有耐久性好,维护时间长,耐腐蚀性好等特点,主要适用于自来水水厂等无毒环境的防腐、特别适用于工业和生活污水处理厂混凝土结构的防护、输水管道的防护,也适用垃圾掩埋场砼结构的防腐防水。
Description
技术领域
本发明涉及一种建筑防腐防水材料,具体说涉及一种纳米多功能彩色防腐防水涂料。
背景技术
现有技术中,防腐涂料大多是玻璃钢、聚氨酯、环氧树脂等溶解型的防腐材料,不旦使用起来不方便,而且价格高,施工时有溶剂挥发,对操作人员有害,最为不利的是防防腐防水涂料施工完成以后,涂料表面光滑度较差,表面容易附着脏物,脏物的常期腐蚀使涂料的表面加快老化,产品的耐久性能差。
发明内容
本发明的目的在于解决现有技术的不足,提供一种价格低于玻璃钢、聚氨酯、环氧树脂,性能同等能做到防腐防水的效果,又能使施工完成以后的涂料表面光滑度大副度增加,产品的抗老化性能好,使用更加持久、防腐防水性能更佳优越。
本发明的技术方案是这样实现的:一种纳米多功能彩色防腐防水涂料,其原料的组成及重量份数如下
A组液料
水性氟碳乳液树脂 20-40
乙烯一醋乙烯共聚物(VAE) 10-20
丙稀酸树脂乳液 5-10
纳米二氧化硅 2-5
纳米云母粉 2-5
纳米硅美土 1-3
酯类增塑剂 5-15
乙二醇 0-10
分散剂 0.5-1
B组粉料
滑石粉 5-10
高铝水泥 10-20
无机填料 1-5
无机颜料 3-10
使用时A组和B组混合使用
配制方法是将液态组份水性氟碳乳液树脂、乙烯一醋乙烯共聚物、丙稀酸树脂乳液、纳米二氧化硅、纳米云母粉、纳米硅美土、酯类增塑剂、乙二醇、分散剂,边搅拌边升温至30℃,高速分散60分钟,过滤得A组份,将固态粉料滑石粉、高铝水泥、无机填料、无机颜料高速配料机搅拌30分钟,包装配成B组份;使用时把A组份和B组份放到一起搅拌10分钟左右即可。
此配方也可以加入乙二醇,乙二醇可以起到抗冻,改善流平性的作用。
所述的无机填料选用碳酸钙,玻璃鳞片粉,高岭土或云母粉,可以起到耐磨的作用。
所述的脂类增塑剂选用二丁酯或二辛酯,可以改进涂料涂膜的耐冲击性,柔韧性,附着力等性能。
所述的无机颜料选用氧化铁颜料,可以制成黑色、红色、绿色、黄色等各种颜色的防水涂料,因为是无机颜料,所以耐晒性好。
本发明的一种纳米多功能彩色防腐防水涂料具有耐久性好,维护时间长,耐腐蚀性好等特点,本发明特别适用于可以采用冷作业施工,具有气味小,无毒,施工简单,方便安全,涂膜无接缝,弹性,耐腐蚀,耐老化、使用寿命长、无环境污染等优点。施工时对基面平整度要求不高,能在潮湿基面施工,拓宽了使用范围。主要适用于自来水水厂等无毒环境的防腐、特别适用于工业和生活污水处理厂混凝土结构的防护、输水管道的防护,也适用垃圾掩埋场砼结构的防腐防水。
具体实施方式
实施方式一:
A组液料
水性氟碳乳液树脂 40
乙烯一醋乙烯共聚物(VAE) 10
丙稀酸树脂乳液 5
纳米二氧化硅 2
纳米云母粉 5
纳米硅美土 1
酯类增塑剂 5
乙二醇 1
分散剂 0.5
B组粉料
滑石粉 8
高铝水泥 15
无机填料 4
无机颜料 4.5
实施方式二:
A组液料
水性氟碳乳液树脂 30
乙烯一醋乙烯共聚物(VAE) 14
丙稀酸树脂乳液 10
纳米二氧化硅 3
纳米云母粉 3
纳米硅美土 2
酯类增塑剂 8
乙二醇 0
分散剂 0.7
B组粉料
滑石粉 7.3
高铝水泥 12
无机填料 3
无机颜料 7
实施方式三:
A组液料
水性氟碳乳液树脂 20
乙烯一醋乙烯共聚物(VAE) 20
丙稀酸树脂乳液 7
纳米二氧化硅 5
纳米云母粉 2
纳米硅美土 3
酯类增塑剂 15
乙二醇 0
分散剂 1
B组粉料
滑石粉 5
高铝水泥 11
无机填料 1
无机颜料 10
上述实施例并非穷举。所得的彩色多功能防腐防水涂料有如下技术指标:
干燥时间(25℃):表干≤1h,实干≤5h;
附着力:1.75MPa;
抗拉强度:1.8MPa;
延伸率:350%;
不透水性:0.3MPa(一个小时不透水);
耐化学试剂(干燥时间(25℃):表干≤1h,实干≤4h;
附着力:1.75MPa;
抗拉强度:1.8MPa;
延伸率:400%;
不透水性:0.3MPa(一个小时不透水);
耐化学试剂(7d):5%硫酸不起泡、不脱落;
5%盐酸不起泡、不脱落 ;
10%氢氧化钠不起泡、不脱落;
10%氯化钠 不起泡、不脱落;
100%煤油 不起泡、不脱落;
100%汽油 不起泡、不脱落;
100%柴油 不起泡、不脱落。
Claims (4)
1.一种纳米多功能彩色防腐防水涂料,其特征在于:其原料的组成及重量份数如下:
A组液料
水性氟碳乳液树脂 20-40
乙烯一醋乙烯共聚物(VAE) 10-20
丙稀酸树脂乳液 5-10
纳米二氧化硅 2-5
纳米云母粉 2-5
纳米硅美土 1-3
酯类增塑剂 5-15
乙二醇 0-10
分散剂 0.5-1
B组粉料
滑石粉 5-10
高铝水泥 10-20
无机填料 1-5
无机颜料 3-10。
2.根据权利要求1所述的纳米彩色防腐防水涂料,其特征在于:所述的脂类增塑剂选用二丁酯或二辛脂。
3.根据权利要求1所述的纳米彩色防腐防水涂料,其特征在于:所述的无机填料选用碳酸钙,玻璃鳞片粉,高岭土或云母粉。
4.根据权利要求1所述的纳米彩色防腐防水涂料,其特征在于:所述的无机颜料选用氧化铁颜料。