CN103145377A - 一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石 - Google Patents
一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石 Download PDFInfo
- Publication number
- CN103145377A CN103145377A CN2012105806424A CN201210580642A CN103145377A CN 103145377 A CN103145377 A CN 103145377A CN 2012105806424 A CN2012105806424 A CN 2012105806424A CN 201210580642 A CN201210580642 A CN 201210580642A CN 103145377 A CN103145377 A CN 103145377A
- Authority
- CN
- China
- Prior art keywords
- machine
- made sand
- cement
- decoration rubbish
- building decoration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及道路基层材料,特别是一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,以建筑装潢垃圾生产的机制砂与集料、水泥和水进行搅拌,制成建筑装潢垃圾机制砂水泥稳定碎石;以质量百分比计,各原料的加入量为:建筑装潢垃圾生产的机制砂13%~18%;粒径小于4.75mm的集料13%~18%;粒径为4.75~13.2mm的集料26%~34%;粒径为13.2~26.5mm的集料30%~48%;外掺3%~7%的水泥; 外掺4%~13%的水。通过本发明,可替代45%~55%的水泥稳定碎石细集料。
Description
技术领域
本发明涉及道路基层材料,特别是一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石的道路基层。
背景技术
建筑装潢垃圾是随着城市生活水平的改善而在近十年间迅猛发展的一类固体废弃物,据相关数据报道,上海每年将产生400多万吨的建筑装潢垃圾,而这些建筑装潢垃圾利用率有限,利用水平低下,给城市管理带来了极大的挑战。目前我国基本采用将建筑装潢垃圾运至填埋场进行填埋的处理方式,但这又消耗了大量城市空间。而且,随着城市化的继续深入,建筑装潢垃圾的数量还将继续增长,建筑装潢垃圾的利用工作迫在眉睫。
十二五期间国家重视道路材料的研发工作,将新材料、新技术和新工艺的研究作为工作重点,推行低碳、环保的发展理念。将建筑装潢垃圾成产的机制砂替代部分水泥稳定碎石中的细集料,这有利于建筑装潢垃圾的再利用,保护环境,节约建筑材料,具有很大的优越性和发展前景。
发明内容
本发明的目的是使建筑装潢垃圾得以充分利用,提高建筑装潢垃圾综合利用价值,提供一种成本低廉的建筑装潢垃圾生产机制砂替代部分细集料的水泥稳定碎石。
本发明的具体技术方案如下:
一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,以建筑装潢垃圾生产的机制砂与集料、水泥和水进行搅拌,制成建筑装潢垃圾机制砂水泥稳定碎石;以质量百分比计,各原料的加入量为:
建筑装潢垃圾生产的机制砂 13% ~ 18%;
粒径小于4.75mm 的集料 13% ~ 18%;
粒径为4.75~13.2mm的集料 26% ~ 34%;
粒径为13.2~26.5mm的集料 30 % ~ 48%;
外掺3%~7%的水泥;
外掺4%~13%的水。
上述建筑装潢垃圾生产的机制砂,是使用建筑垃圾处理技术,通过制砂机和其它附属设备加工而成的砂子,通过给料、破碎、筛分、水洗后,生产制得的机制砂。建筑装潢垃圾机制砂细度模数控制在3.0~3.3,颗粒级配应在级配区II区内,小于0.075mm颗粒含量1%~2%。
所述集料又称骨料;主要起骨架作用和减小由于胶凝材料在凝结硬化过程中干缩湿胀所引起的体积变化,同时还作为胶凝材料的廉价填充料。上述集料为天然集料,如碎石、卵石、浮石、天然砂等;最大粒径小于31.5mm,碎石集料压碎值小于28%;碎石集料中小于0.5mm颗粒材料的液限小于26%,塑性指数小于7。
上述水泥是强度等级为32.5Mpa或42.5Mpa的普通硅酸盐水泥或复合硅酸盐水泥。
本发明的建筑装潢垃圾生产机制砂替代部分细集料的水泥稳定碎石具有以下优点:
1.建筑装潢垃圾来源广泛,通过本发明,可替代45% ~ 55%的水泥稳定碎石细集料,节约天然资源,提高建筑装潢垃圾的利用率,具有保护环境、低碳环保的特点;
2.施工方法简单、对于机械设备没有特殊要求;
3.适用范围广泛,可以在市政道路、公路、高速公路等领域广泛推广应用。
具体实施方式
以下结合实施例对本发明作更进一步说明:
实施例1
一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,使用建筑垃圾处理技术,通过给料、破碎、筛分、水洗后,最后生产出机制砂(筛分结果见表1)。采用建筑装潢垃圾生产的机制砂17%,粒径小于4.75mm 的天然集料16%,粒径为4.75~13.2mm的天然集料26%,粒径为13.2~26.5mm的天然集料39%,强度等级为42.5Mpa普通硅酸盐水泥4.5%和5%的水,搅拌混合而成。
其加工步骤为;先加入所需机制砂和集料混合,再将普通硅酸盐水泥采用外掺的形式加入,最后加入水一起搅拌混合。采用的集料继配和用量见表2。
表1建筑装潢垃圾生产的机制砂筛分表。
表2集料继配和用量。
实施例2
一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,是由建筑装潢垃圾生产的机制砂13%,粒径小于4.75mm 的天然集料13%,粒径为4.75~13.2mm的集料26%,粒径为13.2~26.5mm的集料48%,外掺强度等级为42.5Mpa普通硅酸盐水泥5.5%和6%的水,搅拌混合而成。通过7天无侧限抗压强度检测,测得7天无侧限抗压强度达到4.2Mpa。满足《城市道路工程与质量验收规范》(CJJ1-2008)对城市快速路、主干道基层要求为3~4Mpa的要求。
实施例3
一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,是由建筑装潢垃圾生产的机制砂18%,粒径小于4.75mm 的天然集料18%,粒径为4.75~13.2mm的天然集料34%,粒径为13.2~26.5mm的天然集料30%,外掺强度等级为32.5Mpa普通硅酸盐水泥4%和5.5%的水,搅拌混合而成。通过7天无侧限抗压强度检测,测得7天无侧限抗压强度达到2.5Mpa。满足《城市道路工程与质量验收规范》(CJJ1-2008)对底基层要求为1.5~2.5Mpa的要求。
实施例4
一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,是由建筑装潢垃圾生产的机制砂15%,粒径小于4.75mm 的天然集料16%,粒径为4.75~13.2mm的天然集料30%,粒径为13.2~26.5mm的天然集料39%,外掺强度等级为42.5Mpa普通硅酸盐水泥4%和5%的水,搅拌混合而成。通过7天无侧限抗压强度检测,测得7天无侧限抗压强度达到3.6Mpa。满足《城市道路工程与质量验收规范》(CJJ1-2008)对城市快速路、主干道基层要求为3~4Mpa,以及对其他等级道路基层为2.4~3.0Mpa的要求。
Claims (4)
1.一种以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,其特征在于,以建筑装潢垃圾生产的机制砂与集料、水泥和水进行搅拌,制成建筑装潢垃圾机制砂水泥稳定碎石;以质量百分比计,各原料的加入量为:
建筑装潢垃圾生产的机制砂 13% ~ 18%;
粒径小于4.75mm 的集料 13% ~ 18%;
粒径为4.75~13.2mm的集料 26% ~ 34%;
粒径为13.2~26.5mm的集料 30 % ~ 48%;
外掺3%~7%的水泥;
外掺4%~13%的水。
2.根据权利要求1所述的以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,其特征在于,所述建筑装潢垃圾生产的机制砂,细度模数在3.0~3.3,颗粒级配在级配区II区内,小于0.075mm颗粒含量1%~2%。
3.根据权利要求1所述的以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,其特征在于,所述集料为天然集料,最大粒径小于31.5mm,碎石集料压碎值小于28%;碎石集料中小于0.5mm颗粒材料的液限小于26%,塑性指数小于7。
4.根据权利要求1所述的以建筑装潢垃圾生产的机制砂替代部分细集料的水泥稳定碎石,其特征在于,所述水泥是强度等级为32.5Mpa或42.5Mpa的普通硅酸盐水泥或复合硅酸盐水泥。