CN103122225A - Production method of non-toxic adhesive - Google Patents
Production method of non-toxic adhesive Download PDFInfo
- Publication number
- CN103122225A CN103122225A CN2013101012139A CN201310101213A CN103122225A CN 103122225 A CN103122225 A CN 103122225A CN 2013101012139 A CN2013101012139 A CN 2013101012139A CN 201310101213 A CN201310101213 A CN 201310101213A CN 103122225 A CN103122225 A CN 103122225A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl alcohol
- production method
- parts
- weight
- aqueous solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of chemical adhesives and in particular relates to a production method of a non-toxic adhesive. The production method of the non-toxic adhesive comprises the following steps of: firstly, heating 2-5 parts by weight of polyvinyl alcohol and 45-90 parts by weight of deionized water to the temperature of 85-90 DEG C, insulating for 1-2 hours until polyvinyl alcohol and deionized water are completely dissolved, and filtering; secondly, respectively preparing 0.15-1.5 parts of sodium bicarbonate and 0.08-0.12 part by weight of potassium peroxodisulphate into aqueous solutions with the concentration of 10%; and thirdly, adding the polyvinyl alcohol solution, 0.2-0.5 part of n-octyl alcohol and 0.3-1 part of emulsifier into a reaction kettle, mixing to be uniform, and heating to temperature of 60-65 DEG C. According to the production method of the non-toxic adhesive, the polyvinyl alcohol solution is adopted as an adhesive, and the polyvinyl alcohol solution takes water as dispersion medium, contains no toxic solution or formaldehyde and can avoid a fire disaster and toxication, so that human health and environmental protection can be facilitated; besides, the adhesive prepared by the invention has the characteristics of water resistance, heat resistance and the like; and usage amount of the emulsifier is reduced, raw material is saved, and cost is reduced.
Description
Technical field
The present invention relates to chemical glue stick technical field, be specifically related to the production method of avirulent adhesion agent.
Background technology
Need to use in a large number tackiness agent in existing woodwork manufacturing processed, but existing tackiness agent contains the material that human body is had grand evil, as formaldehyde, benzene, toluene and multiple harmful volatile organic matter, these objectionable impuritiess have carinogenicity to human body, have a strong impact on the healthy of people.
Summary of the invention
The purpose of this invention is to provide a kind of water-fast, heat-resisting, do not contain poisonous solvent, be conducive to the production method of the avirulent adhesion agent of HUMAN HEALTH and environment protection.
In order to solve the existing problem of background technology, the present invention is by the following technical solutions: the production method of avirulent adhesion agent comprises the following steps:
(1), by weight 45~90 parts of 2~5 parts of polyvinyl alcohol and deionized waters are heated to 85~90 ℃, be incubated 1~2 hour to all dissolvings, filter;
(2), by weight 0.08~0.12 part of 0.15~1.5 part of sodium bicarbonate and Potassium Persulphate is made into respectively 10% the aqueous solution;
(3), add 0.3~1 part of polyvinyl alcohol solution, 0.2~0.5 part of n-Octanol and emulsifying agent in reactor, after stirring, be warming up to 60~65 ℃;
(4), when equitemperature is warming up to 80~82 ℃, drip mix monomer and persulfate aqueous solution, described mix monomer adds with 10% speed per hour, persulfate aqueous solution adds with 5% speed per hour, be incubated 6~8 hours, be warming up to 90~95 ℃, be incubated 30 minutes;
(5), when being cooled to 50 ℃, add sodium bicarbonate aqueous solution, stirred 1.5 hours, discharging gets final product.
The present invention has following beneficial effect: the production method of avirulent adhesion agent of the present invention, adopt polyvinyl alcohol water solution as tackiness agent, because polyvinyl alcohol water solution is take water as dispersion medium, do not contain poisonous solution, formaldehydeless, fire and poisoning be can avoid, HUMAN HEALTH and environment protection are conducive to; In addition, the tackiness agent that the present invention makes has the characteristics such as water-fast, heat-resisting, wherein, has reduced the consumption of emulsifying agent, has saved raw material, has reduced cost, is widely used in the bonding of the woodwork plates such as glued board, shaving board.
Embodiment
Below the present invention will be further described in detail.
Embodiment one:
The production method of avirulent adhesion agent comprises the following steps:
(1), by weight 45 parts of 2 parts of polyvinyl alcohol and deionized waters are heated to 85 ℃, be incubated 1 hour to all dissolvings, filter;
(2), by weight 0.08 part of 0.15 part of sodium bicarbonate and Potassium Persulphate is made into respectively 10% the aqueous solution;
(3), add 0.3 part of polyvinyl alcohol solution, 0.2 part of n-Octanol and emulsifying agent in reactor, after stirring, be warming up to 60 ℃;
(4), when equitemperature is warming up to 80 ℃, drip mix monomer and persulfate aqueous solution, described mix monomer adds with 10% speed per hour, and persulfate aqueous solution adds with 5% speed per hour, is incubated 6 hours, is warming up to 90 ℃, is incubated 30 minutes;
(5), when being cooled to 50 ℃, add sodium bicarbonate aqueous solution, stirred 1.5 hours, discharging gets final product.
Embodiment two:
The production method of avirulent adhesion agent comprises the following steps:
(1), by weight 70 parts of 3 parts of polyvinyl alcohol and deionized waters are heated to 87 ℃, be incubated 1.5 hours to all dissolvings, filter;
(2), by weight 0.1 part of 0.95 part of sodium bicarbonate and Potassium Persulphate is made into respectively 10% the aqueous solution;
(3), add 0.7 part of polyvinyl alcohol solution, 0.3 part of n-Octanol and emulsifying agent in reactor, after stirring, be warming up to 63 ℃;
(4), when equitemperature is warming up to 81 ℃, drip mix monomer and persulfate aqueous solution, described mix monomer adds with 10% speed per hour, and persulfate aqueous solution adds with 5% speed per hour, is incubated 7 hours, is warming up to 93 ℃, is incubated 30 minutes;
(5), when being cooled to 50 ℃, add sodium bicarbonate aqueous solution, stirred 1.5 hours, discharging gets final product.
Embodiment three:
The production method of avirulent adhesion agent comprises the following steps:
(1), by weight 90 parts of 5 parts of polyvinyl alcohol and deionized waters are heated to 90 ℃, be incubated 2 hours to all dissolvings, filter;
(2), by weight 0.12 part of 1.5 parts of sodium bicarbonates and Potassium Persulphate is made into respectively 10% the aqueous solution;
(3), add 1 part of polyvinyl alcohol solution, 0.5 part of n-Octanol and emulsifying agent in reactor, after stirring, be warming up to 65 ℃;
(4), when equitemperature is warming up to 82 ℃, drip mix monomer and persulfate aqueous solution, described mix monomer adds with 10% speed per hour, and persulfate aqueous solution adds with 5% speed per hour, is incubated 8 hours, is warming up to 95 ℃, is incubated 30 minutes;
(5), when being cooled to 50 ℃, add sodium bicarbonate aqueous solution, stirred 1.5 hours, discharging gets final product.
Explanation is at last, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, other modifications that those of ordinary skills make technical scheme of the present invention or be equal to replacement, only otherwise break away from the spirit and scope of technical solution of the present invention, all should be encompassed in the middle of claim scope of the present invention.
Claims (1)
1. the production method of avirulent adhesion agent, is characterized in that, comprises the following steps:
(1), by weight 45~90 parts of 2~5 parts of polyvinyl alcohol and deionized waters are heated to 85~90 ℃, be incubated 1~2 hour to all dissolvings, filter;
(2), by weight 0.08~0.12 part of 0.15~1.5 part of sodium bicarbonate and Potassium Persulphate is made into respectively 10% the aqueous solution;
(3), add 0.3~1 part of polyvinyl alcohol solution, 0.2~0.5 part of n-Octanol and emulsifying agent in reactor, after stirring, be warming up to 60~65 ℃;
(4), when equitemperature is warming up to 80~82 ℃, drip mix monomer and persulfate aqueous solution, described mix monomer adds with 10% speed per hour, persulfate aqueous solution adds with 5% speed per hour, be incubated 6~8 hours, be warming up to 90~95 ℃, be incubated 30 minutes;
(5), when being cooled to 50 ℃, add sodium bicarbonate aqueous solution, stirred 1.5 hours, discharging gets final product.