CN103122163B - Metal protecting coating and hot-dipped metal material - Google Patents
Metal protecting coating and hot-dipped metal material Download PDFInfo
- Publication number
- CN103122163B CN103122163B CN201110369272.5A CN201110369272A CN103122163B CN 103122163 B CN103122163 B CN 103122163B CN 201110369272 A CN201110369272 A CN 201110369272A CN 103122163 B CN103122163 B CN 103122163B
- Authority
- CN
- China
- Prior art keywords
- water
- soluble
- weight part
- forming resin
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a metal protecting coating. The metal protecting coating is obtained after mixing a raw material mixture uniformly, wherein the raw material mixture contains water soluble silicate, an accelerant, a silane coupling agent, a silicon oxide filler, water soluble film-forming resin and water; the accelerant is water-based emulsion of dimethicone and/or polyether modified polysiloxane; the silane coupling agent contains first silane derivatives shown in a formula (1) in the specification; and in the formula (1), R1, R2 and R3 are respectively methoxy or ethoxy, and n is an integer from 1 to 4. The invention also provides a hot-dipped metal material. The hot-dipped metal material comprises a hot-dipped metal substrate and a coating attached to the hot-dipped metal substrate, wherein the coating is a cured product of the metal protecting coating. Protective films formed by the metal protecting coating provided by the invention have excellent corrosion resistance, water resistance, heat resistance, fingerprint resistance and lubricating property.
Description
Technical field
The present invention relates to metal protection field, particularly, relate to a kind of metal protection coating and the hot-dip metal plated material of one.
Background technology
Hot-dip metal plated material, comprises hot-dip galvanized metal material and hot-dip aluminizing zinc metallic substance, in order to prevent corrosion, and all can at the surface application layer of metal protective coating of hot-dip metal plated material to form protective film.Thus the performance of metal protection coating is very important for the rust protection of hot-dip metal plated material.
Such as, CN101608306A discloses a kind of passivating solution, also belongs to a kind of metal protection coating, it is characterized in that, this passivating solution is the aqueous solution containing water-soluble molybdenum compound, boric acid, water soluble organic substance and silicon sol, and wherein, described water soluble organic substance is the mixture of alcohol and organic carboxyl acid.
But experiment proves, the solidity to corrosion of protective film that this metal protection coating is formed, water tolerance, thermotolerance and anti-finger printing are still poor.
Summary of the invention
The object of the invention is the defect that the solidity to corrosion of the protective film overcoming the formation of existing metal protection coating, water tolerance, thermotolerance and anti-finger printing are poor, a kind of metal protection coating that can form the good protective film of solidity to corrosion, water tolerance, thermotolerance and anti-finger printing is provided.
To achieve these goals, the invention provides a kind of metal protection coating, this metal protection coating obtains after being mixed by a kind of raw mixture, and described raw mixture contains water-soluble silicate, promotor, silane coupling agent, cilicon oxide filler, water-soluble film-forming resin and water; Described promotor is the water-based emulsion of dimethyl silicone oil and/or polyether-modified polysiloxane; Described silane coupling agent contains such as formula the first silane derivative shown in (1), wherein, and R
1, R
2and R
3be methoxy or ethoxy separately, n is the integer of 1 to 4;
formula (1).
Present invention also offers a kind of hot-dip metal plated material, this pot galvanize material comprises hot-dip metal plated base material and is attached to the coating on this hot-dip metal plated base material, described hot-dip metal plated base material is pot galvanize metal base and/or hot-dip aluminizing zinc metal base, it is characterized in that, described coating is the cured product of metal protection coating as above.
By technique scheme, the solidity to corrosion of the protective film that metal protection coating provided by the invention is formed, water tolerance, thermotolerance and anti-finger printing are all very excellent.Further, the lubricity of the protective film of metal protection coating formation provided by the invention is excellent especially.
Other features and advantages of the present invention are described in detail in embodiment part subsequently.
Embodiment
Below the specific embodiment of the present invention is described in detail.Should be understood that, embodiment described herein, only for instruction and explanation of the present invention, is not limited to the present invention.
According to metal protection coating provided by the invention, wherein, this metal protection coating obtains after being mixed by a kind of raw mixture, and described raw mixture contains water-soluble silicate, promotor, silane coupling agent, cilicon oxide filler, water-soluble film-forming resin and water; Described promotor is the water-based emulsion of dimethyl silicone oil and/or polyether-modified polysiloxane; Described silane coupling agent contains such as formula the first silane derivative shown in (1), wherein, and R
1, R
2and R
3be methoxy or ethoxy separately, n is the integer of 1 to 4;
formula (1).
Wherein, this metal protection coating is obtain after described raw mixture mixes, and is comparatively stable and homogeneous liquid.Under preferable case, each component in described raw mixture mixes before use at this metal protection coating for 1-180 days.Wherein, the order by merging of each composition is not specially required, directly each component in described raw mixture can be carried out mixing simultaneously, in batches or step by step, as long as uniform stable phase can be obtained, make mixing more even preferably by stirring.
According to metal protection coating provided by the invention, wherein, relative to the described water-soluble silicate of 1 weight part, the content of described promotor can be 0.2-1.8 weight part, is preferably 0.5-0.7 weight part.
Wherein, relative to the described water-soluble silicate of 1 weight part, the consumption of described silane coupling agent can be 0.5-4.5 weight part, is preferably 1.4-1.8 weight part.
Wherein, relative to the described water-soluble silicate of 1 weight part, the consumption of described cilicon oxide filler can be 0.25-2.2 weight part, is preferably 0.6-0.85 weight part.
Wherein, relative to the described water-soluble silicate of 1 weight part, in solid, the consumption of described water-soluble film-forming resin can be 0.8-6.8 weight part, is preferably 2.1-2.7 weight part.
Wherein, relative to the described water-soluble silicate of 1 weight part, the consumption of water is 10-100 weight part, is preferably 25-40 weight part.It should be noted that, in the present invention, the consumption of said water refers to the amount of the water added in addition, do not comprise in above-mentioned other component of adding with solution or emulsion mode with the amount of water.
According to metal protection coating provided by the invention, wherein, described water-soluble silicate can be water glass and/or potassium silicate.
According to metal protection coating provided by the invention, wherein, the solid content of the water-based emulsion of described dimethyl silicone oil can be 10-90 % by weight, is preferably 30-80 % by weight.It should be noted that, the water-based emulsion of dimethyl silicone oil is when for preparing metal protection coating provided by the invention, and its consumption refers to the numerical value obtained after the gross weight of water-based emulsion is multiplied by its solid content.It should be noted that, the solid content of the water-based emulsion of described dimethyl silicone oil refers to the content of the dimethyl silicone oil that the water-based emulsion of preparing described dimethyl silicone oil is used.Described dimethyl silicone oil refers to water-insoluble unmodified dimethyl silicone oil.
Wherein, the dimethyl-silicon oil viscosity in the water-based emulsion of described dimethyl silicone oil can be 500-50000mPaS, is preferably 1000-40000mPaS, is more preferably 1500-30000mPaS.
According to metal protection coating provided by the invention, wherein, the viscosity of described polyether-modified polysiloxane (being commonly called as water-soluble dimethyl silicone oil) is 100-10000mPaS, is preferably 500-8000mPaS, be more preferably 1000-6000mPaS, be further preferably 2000-5000mPaS.
It should be noted that, when not doing contrary explanation in the present invention, described viscosity refers to the apparent viscosity numerical value recorded at 25 DEG C.
According to metal protection coating provided by the invention, wherein, such as formula in the first silane derivative shown in (1), R
1, R
2and R
3in at least one be methoxyl group, or R
1, R
2and R
3in at least two be methoxyl group or R
1, R
2and R
3be methoxyl group; N can be 1,2,3 or 4; In order to improve the performance of described metal protection coating further, under preferable case, in the first silane derivative shown in formula (1), R
1, R
2and R
3be methoxyl group, n is 2.That is, the first silane derivative shown in formula (1) is 2-(3,4-epoxycyclohexyl) ethyl trimethoxy silane.
According to metal protection coating provided by the invention, wherein, in order to improve the performance of described metal protection coating further, under preferable case, described silane coupling agent is also containing the second silane derivative, and described second silane derivative is at least one in γ-aminopropyl triethoxysilane, γ-glycidyl ether oxygen propyl trimethoxy silicane, γ-methacryloxypropyl trimethoxy silane and N-2-aminoethyl-3-aminopropyl trimethoxysilane.
According to metal protection coating provided by the invention, wherein, in order to improve the performance of described metal protection coating further, under preferable case, the weight ratio of described first silane derivative and described second silane derivative is 1: 0.1-0.4, more preferably 1: 0.2-0.3.
According to metal protection coating provided by the invention, wherein, described cilicon oxide filler does not have special requirement, can be the various fillers based on silicon oxide, and such as, described cilicon oxide filler can be nano-silica powder and/or silicon sol; Under preferable case, described cilicon oxide filler is nano-silica powder, and the particle diameter of described nano-silica powder can be 10-90nm.
According to metal protection coating provided by the invention, wherein, described water-soluble film-forming resin can for various water miscible and can be used in the modification of film forming or unmodified resin, described resin can use with suitable dosage form, such as water-soluble emulsion, at least one in water-soluble solution and water-soluble solid, the not special requirement of the present invention, such as, described water-soluble film-forming resin can be that water-soluble polyester film-forming resin is (such as purchased from Guangzhou Lapo Fine Chemicals Co., Ltd., the vibrin of trade mark CB2200), water-soluble phenylpropyl alcohol film-forming resin is (such as purchased from Guangzhou Chao Long Chemical Industry Science Co., Ltd, the trade mark is the benzene emulsion of xy-108b), soluble epoxide film-forming resin is (such as purchased from Dongguan City Heima Chemical Co., Ltd., the trade mark is the epoxy resin of BH620), aqurous ployurethane film-forming resin is (such as purchased from Jinjiang, Fujian Province Jian Hua company, the urethane resin of the trade mark 812), water-soluble silicon third film-forming resin (make the country prosperous paint company TC-05 type organosilicon crylic acid latex by such as Qingdao, solid content is 48 % by weight), water-soluble acrylic film-forming resin (trade mark such as purchased from Guangzhou Ou Peng chemical industry is the acrylic resin of A-3418) and water-soluble fluorine carbon film-forming resin are (such as purchased from Beijing Shouchuang Nano Techn Co., Ltd., the trade mark is the water-base fluorocarbon emulsion of SKFT-I) at least one, under preferable case, described water-soluble film-forming resin is at least one in water-soluble phenylpropyl alcohol film-forming resin, soluble epoxide film-forming resin, water-soluble silicon third film-forming resin, water-soluble acrylic film-forming resin, aqurous ployurethane film-forming resin and water-soluble polyester film-forming resin.
Except containing except mentioned component, metal protection coating of the present invention can also contain other various component not affecting metal protection coating property, as one or more in dyestuff, pigment, dispersion agent and defoamer.With the gross weight of this metal protection coating for benchmark, the content of other component is no more than 20 % by weight, preferably more than 10 % by weight.Described defoamer can be various defoamer well known in the art, such as, in polyethers defoamer, higher alcohols and silicon defoamer etc. one or more.More particularly, described defoamer can one or more for being purchased in the SD-401 of such as limited liability company of Dongying dan large Creative Science and Technology Co. Ltd series defoamer.Under preferable case, with the total amount of described metal protection coating for benchmark, the content of described defoamer is 0.01-0.05 % by weight.
According to hot-dip metal plated material provided by the invention, this hot-dip metal plated material comprises pot galvanize metal base and is attached to the coating on this hot-dip metal plated base material, described hot-dip metal plated base material is pot galvanize metal base and/or hot-dip aluminizing zinc metal base, it is characterized in that, described coating is the cured product of metal protection coating as above.
Wherein, described pot galvanize metal base can for the metal base containing zinc coating, and in described zinc coating, the content of zinc can be 92.5-95.5 % by weight.Described zinc coating also can contain other conventional ingredient, as silicon.
Wherein, described hot-dip aluminizing zinc metallic substance can for the metal base containing zinc-aluminium coating, and in described zinc-aluminium coating, the content of zinc can be 41.5-43.5 % by weight, and the content of aluminium can be 51.5-55.0 % by weight.Described zinc-aluminium coating also can contain other conventional ingredient, as silicon.
According to hot-dip metal plated material provided by the invention, wherein, the thickness of described coating can be the general thickness of the erosion shield on hot-dip metal plated base material, in order to improve the performance of described coating, under preferable case, the thickness of described coating is 0.05-2 micron, can be preferably 0.1-1 micron.
According to hot-dip metal plated material provided by the invention, wherein, the method that hot-dip metal plated base material adheres to described coating can comprise and is attached on the surface of hot-dip metal plated base material by described metal protection coating, then dry, dry temperature can be 60-120 DEG C, be preferably 90-110 DEG C, the time can be 0.5-3 second.The consumption of described metal protection coating can be determined according to the thickness of coating.
Wherein, the method for described drying can be one or more in warm air drying, induction heating and infrared radiation heating.
In the present invention, when not doing contrary explanation, the volume of all liquid and solid all refers to 20 DEG C, the volume of 1 standard atmosphere pressure.
Below will be explained in further detail the present invention by embodiment.
Embodiment 1
By the water-soluble silicate (Na of 1 weight part
2siO
3), (water-based emulsion of dimethyl silicone oil and polyether-modified polysiloxane obtain after 1: 1 mixing for the promotor of 0.6 weight part, the water-based emulsion of dimethyl silicone oil is purchased from Nanjing Hua Tuo Chemical Co., Ltd., the trade mark is HTR-1, solid content is 30 % by weight, is be obtain after the dimethyl silicone oil emulsification of 25000mPaS by the apparent viscosity at 25 DEG C, polyether-modified polysiloxane is purchased from dyeing and finishing auxiliaries for textile Co., Ltd., Factory of Dongguan Acer, apparent viscosity at 25 DEG C is 3000mPaS), silane coupling agent (the first silane derivative (2-(3 of 1.6 weight parts, 4-epoxycyclohexyl) ethyl trimethoxy silane, purchased from Hubei De Bang Fine Chemical Co., Ltd) and the second silane derivative (γ-aminopropyl triethoxysilane, purchased from Hubei De Bang Fine Chemical Co., Ltd) be mixed to get by weight 1: 0.25), cilicon oxide filler (the nano-silica powder of 0.72 weight part, purchased from American GE company, RNS-E, mean particle size 20nm), (water-soluble silicon third film-forming resin (make the country prosperous paint company TC-05 type organosilicon crylic acid latex by Qingdao for the water-soluble film-forming resin of 2.4 weight parts (in solid), solid content is 48 % by weight)) and the water of 28 weight parts, be mixed to evenly under the stirring velocity of 1500 revs/min, obtain the metal protection coating of the present embodiment.
Embodiment 2
By the water-soluble silicate (K of 1 weight part
2siO
3), promotor (the water-based emulsion of dimethyl silicone oil of 0.5 weight part, purchased from Guangzhou Si Luoke Chemical Co., Ltd., solid content is 80 % by weight, be obtain after the dimethyl silicone oil emulsification of 1500mPaS by the apparent viscosity at 25 DEG C), silane coupling agent (the first silane derivative (2-(3 of 1.4 weight parts, 4-epoxycyclohexyl) ethyl triethoxysilane, purchased from Hubei De Bang Fine Chemical Co., Ltd) and the second silane derivative (γ-glycidyl ether oxygen propyl trimethoxy silicane, purchased from Hubei De Bang Fine Chemical Co., Ltd) be mixed to get by weight 1: 0.4), cilicon oxide filler (the nano silicon of 0.6 weight part, purchased from American GE company, RNS-E, mean particle size 20nm), the water-soluble film-forming resin (water-soluble acrylic film-forming resin (trade mark purchased from Guangzhou Ou Peng chemical industry is the acrylic resin of A-3418)) of 2.1 weight parts (in solid) and the water of 25 weight parts, be mixed to evenly under the stirring velocity of 1500 revs/min, obtain the metal protection coating of the present embodiment.
Embodiment 3
By the water-soluble silicate (Na of 1 weight part
2siO
3), promotor (the polyether-modified polysiloxane of 0.7 weight part, polyether-modified polysiloxane prevents dyeing and finishing auxiliaries Co., Ltd., Factory purchased from Dongguan Acer, apparent viscosity at 25 DEG C is 2000mPaS), silane coupling agent (the first silane derivative (2-(3 of 1.8 weight parts, 4-epoxycyclohexyl) propyl trimethoxy silicane, purchased from Hubei De Bang Fine Chemical Co., Ltd) and the second silane derivative (γ-glycidyl ether oxygen propyl trimethoxy silicane, purchased from Hubei De Bang Fine Chemical Co., Ltd) be mixed to get by weight 1: 0.1), cilicon oxide filler (the silicon sol of 30 % by weight of 0.85 weight part, usage quantity is in solid), (aqurous ployurethane film-forming resin is (purchased from Jinjiang, Fujian Province Jian Hua company for the water-soluble film-forming resin of 2.7 weight parts (in solid), the urethane resin of the trade mark 812)) and the water of 40 weight parts, be mixed to evenly under the stirring velocity of 1500 revs/min, obtain the metal protection coating of the present embodiment.
Embodiment 4
Metal protection coating is prepared according to the method for embodiment 1, unlike, described promotor is polyether-modified polysiloxane, and polyether-modified polysiloxane prevents dyeing and finishing auxiliaries Co., Ltd., Factory purchased from Dongguan Acer, and the apparent viscosity at 25 DEG C is 5000mPaS.
Embodiment 5
Metal protection coating is prepared according to the method for embodiment 1, unlike, described promotor is the water-based emulsion of dimethyl silicone oil, purchased from Guangzhou Si Luoke Chemical Co., Ltd., solid content is 25 % by weight, is be obtain after the dimethyl silicone oil emulsification of 50000mPaS by the apparent viscosity at 25 DEG C.
Embodiment 6
Metal protection coating is prepared according to the method for embodiment 1, unlike, use water-soluble phenylpropyl alcohol film-forming resin (purchased from Guangzhou Chao Long Chemical Industry Science Co., Ltd, the trade mark is the benzene emulsion of xy-108b) as water-soluble film-forming resin.
Embodiment 7
Metal protection coating is prepared according to the method for embodiment 1, unlike, do not add the second silane derivative.
Comparative example 1
Metal protection coating is prepared according to the method for embodiment 1, unlike, do not add promotor.
Comparative example 2
Metal protection coating is prepared according to the method for embodiment 1, unlike, do not add the first silane derivative.
Preparation embodiment 1
The metal protection coating that Example 1-7 and comparative example 1-2 obtains is coated on steel plate galvanized respectively (purchased from Pangang Group Panzhihua Steel Vanadium Co., Ltd., model DX54D, containing zinc 95 % by weight in zinc coating) surface, warm air drying 2 seconds at 90-110 DEG C, obtains the steel plate galvanized 1-9 after processing.Wherein, coating amount makes the thickness of the coating on steel plate galvanized 1-9 be 0.8 micron.The thickness of coating is the numerical value measured with XRF (fluorescence spectrophotometer) survey meter.
Preparation embodiment 2
The metal protection coating that Example 1-7 and comparative example 1-2 obtains is coated on Al-Zn coated steel respectively (purchased from Pangang Group Panzhihua Steel Vanadium Co., Ltd., model DX51D+AZ, containing zinc 42.5 % by weight in zinc layers of aluminizing, containing aluminium 52.3 % by weight) surface, warm air drying 2 seconds at 90-110 DEG C, obtains the Al-Zn coated steel 1-9 after processing.Wherein, coating amount makes the thickness of the coating on Al-Zn coated steel 1-9 be 0.8 micron.The thickness of coating is the numerical value measured with XRF (fluorescence spectrophotometer) survey meter.
Testing example 1
By the requirement of regulation in GB/T 101251997, carry out neutral salt spray test, measure the corrosion resistance nature of steel plate galvanized 1-9 and Al-Zn coated steel 1-9.It is qualified to be considered as by " salt-fog test 96h, corrosion area < 20% ".
As follows, the water resistance of steel plate galvanized 1-9 and Al-Zn coated steel 1-9 is measured.
On the steel plate galvanized 1-9 of horizontal positioned and the surface of Al-Zn coated steel 1-9, drip the boiling water of about 2 milliliters, after seasoning in 24 hours, to drip with 3M adhesive tape and locate to adhere to, to the spot count under adhesive tape is stained with, according to the counting of lower spot sticky on every square centimeter of adhesive tape, judge the quality of rete water tolerance, spot under sticky is more, and water tolerance is poorer.
As follows, the thermotolerance of steel plate galvanized 1-9 and Al-Zn coated steel 1-9 is measured.
Steel plate galvanized 1-9 and Al-Zn coated steel 1-9 is placed in hotblast stove, toast 20 minutes at 300 DEG C, then take out and observe coating morphology change, and adopt color difference meter to test Δ L (lightness variable), Δ a (red green variable), Δ b (champac variable) value of specimen surface before and after baking, and calculate Δ E (aberration)=(Δ L
2+ Δ a
2+ Δ b
2)
1/2.Namely the less coating of Δ E has more excellent thermotolerance.
As follows, the anti-finger printing of steel plate galvanized 1-9 and Al-Zn coated steel 1-9 is measured.
Adopt color difference meter test steel plate galvanized 1-9 and Al-Zn coated steel 1-9 to apply Δ L (lightness variable), Δ a (red green variable) before and after 0.5 gram/m of Vaseline, Δ b (champac variable) value, and calculate Δ E (aberration)=(Δ L
2+ Δ a
2+ Δ b
2)
1/2, namely the less coating of Δ E has more excellent anti-finger printing energy.
On M-2000 ring block type friction and wear tester, measure the kinetic friction coefficient of the coating of test steel plate galvanized 1-9 and Al-Zn coated steel 1-9 according to its specification sheets.
Test result as above is as shown in table 1.
Table 1
Visible according to the data of table 1, the solidity to corrosion of the protective film that metal protection coating provided by the invention is formed, water tolerance, thermotolerance and anti-finger printing are all very excellent.Further, the lubricity of the protective film of metal protection coating formation provided by the invention is excellent especially.
Further, when preferred described silane coupling agent is also containing described second silane derivative, the solidity to corrosion of the protective film that described metal protection coating is formed, water tolerance, thermotolerance and anti-finger printing can be improved further.
More than describe the preferred embodiment of the present invention in detail; but the present invention is not limited to the detail in above-mentioned embodiment, within the scope of technical conceive of the present invention; can carry out multiple simple variant to technical scheme of the present invention, these simple variant all belong to protection scope of the present invention.
It should be noted that in addition, each concrete technical characteristic described in above-mentioned embodiment, in reconcilable situation, can be combined by any suitable mode, in order to avoid unnecessary repetition, the present invention illustrates no longer separately to various possible array mode.
In addition, also can carry out arbitrary combination between various different embodiment of the present invention, as long as it is without prejudice to thought of the present invention, it should be considered as content disclosed in this invention equally.
Claims (7)
1. a metal protection coating, this metal protection coating obtains after being mixed by a kind of raw mixture, and described raw mixture contains water-soluble silicate, promotor, silane coupling agent, cilicon oxide filler, water-soluble film-forming resin and water; Described promotor is the water-based emulsion of dimethyl silicone oil and/or polyether-modified polysiloxane; Described silane coupling agent contains such as formula the first silane derivative shown in (1), wherein, and R
1, R
2and R
3be methoxy or ethoxy separately, n is the integer of 1 to 4, and described silane coupling agent is also containing the second silane derivative, and the weight ratio of described first silane derivative and described second silane derivative is 1:0.1-0.4; Described second silane derivative is at least one in γ-aminopropyl triethoxysilane, γ-glycidyl ether oxygen propyl trimethoxy silicane, γ-methacryloxypropyl trimethoxy silane and N-2-aminoethyl-3-aminopropyl trimethoxysilane; Relative to the described water-soluble silicate of 1 weight part, the content of described promotor is 0.2-1.8 weight part, the consumption of described silane coupling agent is 0.5-4.5 weight part, the consumption of described cilicon oxide filler is 0.25-2.2 weight part, in solid, the consumption of described water-soluble film-forming resin is 0.8-6.8 weight part, and the consumption of water is 10-100 weight part;
2. metal protection coating according to claim 1, wherein, relative to the described water-soluble silicate of 1 weight part, the content of described promotor is 0.5-0.7 weight part, the consumption of described silane coupling agent is 1.4-1.8 weight part, and the consumption of described cilicon oxide filler is 0.6-0.85 weight part, in solid, the consumption of described water-soluble film-forming resin is 2.1-2.7 weight part, and the consumption of water is 25-40 weight part.
3. according to the metal protection coating in claim 1-2 described in any one, wherein, the solid content of the water-based emulsion of described dimethyl silicone oil is 10-90 % by weight, and the dimethyl-silicon oil viscosity in the water-based emulsion of described dimethyl silicone oil is 500-50000mPaS; The viscosity of described polyether-modified polysiloxane is 100-10000mPaS.
4. according to the metal protection coating in claim 1-2 described in any one, wherein, R
1, R
2and R
3be methoxyl group, n is 2.
5. according to the metal protection coating in claim 1-2 described in any one, wherein, described cilicon oxide filler is nano-silica powder and/or silicon sol.
6. according to the metal protection coating in claim 1-2 described in any one, wherein, described water-soluble film-forming resin is at least one in water-soluble polyester film-forming resin, water-soluble phenylpropyl alcohol film-forming resin, soluble epoxide film-forming resin, aqurous ployurethane film-forming resin, water-soluble silicon third film-forming resin, water-soluble acrylic film-forming resin and water-soluble fluorine carbon film-forming resin.
7. a hot-dip metal plated material, this pot galvanize material comprises hot-dip metal plated base material and is attached to the coating on this hot-dip metal plated base material, described hot-dip metal plated base material is pot galvanize metal base and/or hot-dip aluminizing zinc metal base, it is characterized in that, described coating is the cured product of the metal protection coating in claim 1-6 described in any one.