CN103114281B - 一种不含铬的钝化液 - Google Patents

一种不含铬的钝化液 Download PDF

Info

Publication number
CN103114281B
CN103114281B CN201210478618.XA CN201210478618A CN103114281B CN 103114281 B CN103114281 B CN 103114281B CN 201210478618 A CN201210478618 A CN 201210478618A CN 103114281 B CN103114281 B CN 103114281B
Authority
CN
China
Prior art keywords
solution
chromium
boric acid
water
hydrogen peroxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210478618.XA
Other languages
English (en)
Other versions
CN103114281A (zh
Inventor
孙长志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANCHANG FEILONG BRAND STEEL GRID CO Ltd
Original Assignee
TIANCHANG FEILONG BRAND STEEL GRID CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANCHANG FEILONG BRAND STEEL GRID CO Ltd filed Critical TIANCHANG FEILONG BRAND STEEL GRID CO Ltd
Priority to CN201210478618.XA priority Critical patent/CN103114281B/zh
Publication of CN103114281A publication Critical patent/CN103114281A/zh
Application granted granted Critical
Publication of CN103114281B publication Critical patent/CN103114281B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种不含铬的钝化液，按照重量份计配比的原料包括：磷酸三钠(20-70)、硫酸钴(1-4)、磷酸(1-3)、硼酸(0.5-0.7)、双氧水(1-3)、水(80-200)。不含铬，对环境友好，且通过其钝化的镀锡板具有更高的耐腐蚀性能和耐氧化性能。

Description

一种不含铬的钝化液
技术领域
本发明涉及一种不含铬的钝化液。
背景技术
镀锡经电镀、软熔后，为了提高镀锡板的耐腐蚀性能、抗氧化性能和抗硫化变黑性能，要对镀锡板进行钝化处理，现有技术中，对镀锡板的钝化是采用6价铬的铬酸盐进行钝化，由于6价铬是一种剧毒物质，对人体及环境都有很大危害，特别是镀锡板的用途一般是用作食品的包装材料，危害极大，亟待改进。
发明内容
针对现有技术存在的问题，本发明的目的在于提出一种不含铬的钝化液，不含铬，对环境友好，且通过其钝化的镀锡板具有更高的耐腐蚀性能和耐氧化性能。
为达到上述目的，本发明采用如下技术方案：
一种不含铬的钝化液，按照重量份计配比的原料包括：
磷酸三钠(20-70)、硫酸钴(1-4)、磷酸(1-3)、硼酸(0.5-0.7)、双氧水(1-3)、水(80-200)。
按照重量份计配比的原料包括：
磷酸三钠(40-70)、硫酸钴(3-4)、磷酸(1-2)、硼酸(0.5-0.6)、双氧水(1-2)、水(100-150)。
所述不含铬的钝化液通过以下步骤得到：
取磷酸三钠晶体和硫酸钴晶体的混合物倒入水中，搅拌均匀，形成溶液A；
取一定量的磷酸，慢慢加入所述溶液A中，边加入边搅拌，形成溶液B；
将一定量硼酸倒入一定量水中，充分搅拌至硼酸完全溶解，形成溶液C，再将溶液B倒入溶液C中，边倒入边搅拌，形成溶液D；
取一定量的双氧水，加入到溶液D中，边加入边搅拌，形成溶液E；
调节溶液E的PH至1.5-2.5。
基于以上技术方案的公开，本发明具备如下有益效果：
本发明提出的钝化液采用磷酸三钠、硫酸钴代替传统的铬盐作为主要成膜物质，可与镀锌层表面发生化学反应，形成具有保护作用的钝化膜；以磷酸代替传统钝化液常使用的硫酸或硝酸，作为主要成膜物质的溶剂和成膜反应所需要的氢离子的主要提供原，同时，还能与镀锌层发生磷化反应，从而提高钝化膜的耐腐蚀性能，在钝化液中加入适量硼酸，可以对PH值起到一定的缓冲作用，从而提高钝化液的稳定性；利用双氧水的氧化性，加快成膜过程，提高钝化效率。
具体实施方式
下面结合附图并通过具体实施方式来进一步说明本发明的技术方案：
实施例1
一种不含铬的钝化液，按照重量份计配比的原料包括：
磷酸三钠(20-70)、硫酸钴(1-4)、磷酸(1-3)、硼酸(0.5-0.7)、双氧水(1-3)、水(80-200)。
实施例2
一种不含铬的钝化液，按照重量份计配比的原料包括：
磷酸三钠(40-70)、硫酸钴(3-4)、磷酸(1-2)、硼酸(0.5-0.6)、双氧水(1-2)、水(100-150)。
实施例3
不含铬的钝化液的制造方法，所述不含铬的钝化液通过以下步骤得到：
S1、取磷酸三钠晶体和硫酸钴晶体的混合物倒入水中，搅拌均匀，形成溶液A；
S2、取一定量的磷酸，慢慢加入所述溶液A中，边加入边搅拌，形成溶液B；
S3、将一定量硼酸倒入一定量水中，充分搅拌至硼酸完全溶解，形成溶液C，再将溶液B倒入溶液C中，边倒入边搅拌，形成溶液D；
S4、取一定量的双氧水，加入到溶液D中，边加入边搅拌，形成溶液E；
S5、调节溶液E的PH至1.5-2.5。
钝化液采用磷酸三钠、硫酸钴代替传统的铬盐作为主要成膜物质，可与镀锌层表面发生化学反应，形成具有保护作用的钝化膜；以磷酸代替传统钝化液常使用的硫酸或硝酸，作为主要成膜物质的溶剂和成膜反应所需要的氢离子的主要提供原，同时，还能与镀锌层发生磷化反应，从而提高钝化膜的耐腐蚀性能，在钝化液中加入适量硼酸，可以对PH值起到一定的缓冲作用，从而提高钝化液的稳定性；利用双氧水的氧化性，加快成膜过程，提高钝化效率。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (2)

1.一种不含铬的钝化液，其特征在于，按照重量份计配比的原料包括：
磷酸三钠40-70份、硫酸钴3-4份、磷酸1-3份、硼酸0.5-0.7份、双氧水1-3份、水80-200份；
所述不含铬的钝化液通过以下步骤得到：
取磷酸三钠晶体和硫酸钴晶体的混合物倒入水中，搅拌均匀，形成溶液A；
取一定量的磷酸，慢慢加入所述溶液A中，边加入边搅拌，形成溶液B；
将一定量硼酸倒入一定量水中，充分搅拌至硼酸完全溶解，形成溶液C，再将溶液B倒入溶液C中，边倒入边搅拌，形成溶液D；
取一定量的双氧水，加入到溶液D中，边加入边搅拌，形成溶液E；
调节溶液E的pH至1.5-2.5。
2.如权利要求1所述的一种不含铬的钝化液，其特征在于，按照重量份计配比的原料包括：
磷酸三钠40-70份、硫酸钴3-4份、磷酸1-2份、硼酸0.5-0.6份、双氧水1-2份、水100-150份。
CN201210478618.XA 2012-11-22 2012-11-22 一种不含铬的钝化液 Active CN103114281B (zh)