CN103102742A - Preparation method of nano graphite conductive ink - Google Patents
Preparation method of nano graphite conductive ink Download PDFInfo
- Publication number
- CN103102742A CN103102742A CN2012105363623A CN201210536362A CN103102742A CN 103102742 A CN103102742 A CN 103102742A CN 2012105363623 A CN2012105363623 A CN 2012105363623A CN 201210536362 A CN201210536362 A CN 201210536362A CN 103102742 A CN103102742 A CN 103102742A
- Authority
- CN
- China
- Prior art keywords
- conductive ink
- epoxy resin
- nano
- preparation
- graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a preparation method of the nano graphite conductive ink. The preparation method comprises the following steps of: 1) reacting polyethylene glycol with 2,4-toluene diisocyanate to obtain isocyanate-terminated polyurethane prepolymer; 2) reacting epoxy resin with ethylene glycol monoethyl ether acetate and the isocyanate-terminated polyurethane prepolymer to obtain polyurethane modified epoxy resin; 3) adding graphite, propylene glycol methyl ether propionate, tributyl phosphate, proprylene glycol monomethyl ether, polydimethylsiloxane, methyl acryloyl oxygen group silane and dyes into a solution of polyurethane modified epoxy resin in acetone, uniformly mixing, and conducting ultrasonic shaking to obtain the nano graphite conductive ink. Through adding the nano graphite, the nano graphite conductive ink disclosed by the invention has the advantage of good electrical conductivity, low viscidity, low fragility, high elasticity and good impact resistance.
Description
Technical field
The invention belongs to technical field of ink, be specifically related to a kind of preparation method of nano-graphite electrically conductive ink.
Background technology
Flexible circuit is to realize electronics and IT products multifunction, integrated, miniaturization and key part cheaply.Along with electronic product and equipment to future developments such as light, thin, little, low-cost, multi-functional, high reliability, the consumption of flexible circuit is increasing, utilize electrically conductive ink or conductive ink by the mode of printing or printing, form the conducting wire and caused scientific research personnel's extensive concern on the flexible insulation substrate.Electrically conductive ink can be divided into structure-type and filled-type two classes by its structure difference.The electrically conductive ink that is applied at present electron trade is mainly compound-type conducting printing ink, conductive filler material used is generally mineral filler, as gold and silver, copper, nickel, carbon black, graphite, carbon fiber etc., and the low-melting ink vehicle resin is selected resol, epoxy resin, urethane etc. usually.Wherein epoxy resin is because of excellent property and raw material widely application in conductive polymers cheap and easy to get, and electroconductibility is weak, the shortcomings such as viscosity is large, fragility is large, elasticity is little, poor impact resistance but also exist, so be necessary it modified toughened.
Summary of the invention
Technical problem to be solved by this invention is: the preparation method that the nano-graphite electrically conductive ink that a kind of electroconductibility is strong, viscosity is little, fragility is little, elasticity is large, shock-resistance is good is provided.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of preparation method of nano-graphite electrically conductive ink the steps include:
1) with polyoxyethylene glycol, heating vacuumizes dewaters to water-content≤0.2%, inflated with nitrogen protection after being cooled to 20 ~ 25 ℃, in regulating, temperature is 80 ~ 85 ℃, adds 2,4 toluene diisocyanate, stirring reaction to-NCO content is≤4%, stopped reaction is cooled to 20 ~ 25 ℃, obtains isocyanate terminated base polyurethane prepolymer for use as;
2) add epoxy resin in reaction, then add the ethylene glycol ether acetate dissolve complete, in keeping, temperature is 75 ~ 80 ℃, the more isocyanate terminated base polyurethane prepolymer for use as that adds step 1) to arrive, and reaction 2.5 ~ 3h obtains polyurethane modified epoxy resin;
3) with step 2) polyurethane modified epoxy resin of gained is dissolved in acetone, adding particle diameter is the graphite of 7～8nm, add again propylene glycol monomethyl ether acetate, tbp, propylene glycol monomethyl ether, polydimethylsiloxane, methacryloxypropyl silane, dyestuff, after mixing, process 30 ~ 50min with ultrasonic oscillation again, obtain the nano-graphite electrically conductive ink.
The mol ratio of the 2,4 toluene diisocyanate described in step 1) and polyoxyethylene glycol is 1.3 ~ 1.4:1.
The mass ratio of the epoxy resin step 2), ethylene glycol ether acetate and isocyanate terminated base polyurethane prepolymer for use as is 9.5 ~ 10:5 ~ 6:1.
The mass ratio of the polyurethane modified epoxy resin described in step 3), graphite, propylene glycol monomethyl ether acetate, tbp, propylene glycol monomethyl ether, polydimethylsiloxane, methacryloxypropyl silane, dyestuff is: 26 ~ 30:5 ~ 6:10 ~ 11:4 ~ 6:5 ~ 7:3 ~ 5:2 ~ 3:5 ~ 8.
Described dyestuff is a kind of in following substances: C.I. directly black 166, C.I. directly deceives directly black 168, C.I. acid yellow 23 of 19, C.I., C.I. Xylene Red 52, C.I. acid blue 9.
Beneficial effect of the present invention: the surface effects, the small-size effect that have due to nano-graphite, quantum effect and macro quanta tunnel effect have more excellent physical chemistry and surface and boundary and character thereby the nano-graphite material is compared with conventional blocky graphite material.Nano-graphite electrically conductive ink disclosed by the invention due to adding of nano-graphite, makes printing ink have the advantages such as electroconductibility is strong, viscosity is little, fragility is little, elasticity is large, shock-resistance is good.
Embodiment
Embodiment 1
1) with the polyoxyethylene glycol of 10mol, heating vacuumizes dewaters to water-content≤0.2%, inflated with nitrogen protection after being cooled to 20 ~ 25 ℃, in regulating, temperature is 80 ~ 85 ℃, adds the 2,4 toluene diisocyanate of 13mol, stirring reaction to-NCO content is≤4%, stopped reaction is cooled to 20 ~ 25 ℃, obtains isocyanate terminated base polyurethane prepolymer for use as;
2) add the epoxy resin of 100g in reaction, the ethylene glycol ether acetate dissolve complete that adds again 50g, in keeping, temperature is 75 ~ 80 ℃, then adds the isocyanate terminated base polyurethane prepolymer for use as of the 10g that step 1) arrives, reaction 2.5 ~ 3h obtains polyurethane modified epoxy resin;
3) polyurethane modified epoxy resin with 30g is dissolved in acetone, adding particle diameter is the 5g graphite of 7～8nm, add again 10g propylene glycol monomethyl ether acetate, 6g tbp, 5g propylene glycol monomethyl ether, 4g polydimethylsiloxane, 2.5g methacryloxypropyl silane, 6g C.I. directly to deceive 166, after mixing, process 30 ~ 50min with ultrasonic oscillation again, obtain the nano-graphite electrically conductive ink.
Embodiment 2
1) with the polyoxyethylene glycol of 10mol, heating vacuumizes dewaters to water-content≤0.2%, inflated with nitrogen protection after being cooled to 20 ~ 25 ℃, in regulating, temperature is 80 ~ 85 ℃, adds the 2,4 toluene diisocyanate of 14mol, stirring reaction to-NCO content is≤4%, stopped reaction is cooled to 20 ~ 25 ℃, obtains isocyanate terminated base polyurethane prepolymer for use as;
2) add 95g epoxy resin in reaction, then add 55g ethylene glycol ether acetate dissolve complete, in keeping, temperature is 75 ~ 80 ℃, then adds the isocyanate terminated base polyurethane prepolymer for use as of 10g, and reaction 3h obtains polyurethane modified epoxy resin;
3) polyurethane modified epoxy resin with 28g is dissolved in acetone, adding particle diameter is the 6g graphite of 7～8nm, add again the C.I. of 10g propylene glycol monomethyl ether acetate, 4g tbp, 7g propylene glycol monomethyl ether, 3g polydimethylsiloxane, 2g methacryloxypropyl silane, 8g directly to deceive 19, after mixing, process 45min with ultrasonic oscillation again, obtain the nano-graphite electrically conductive ink.
Claims (5)
1. the preparation method of a nano-graphite electrically conductive ink, the steps include:
1) with polyoxyethylene glycol, heating vacuumizes dewaters to water-content≤0.2%, inflated with nitrogen protection after being cooled to 20 ~ 25 ℃, in regulating, temperature is 80 ~ 85 ℃, adds 2,4 toluene diisocyanate, stirring reaction to-NCO content is≤4%, stopped reaction is cooled to 20 ~ 25 ℃, obtains isocyanate terminated base polyurethane prepolymer for use as;
2) add epoxy resin in reaction, then add the ethylene glycol ether acetate dissolve complete, in keeping, temperature is 75 ~ 80 ℃, the more isocyanate terminated base polyurethane prepolymer for use as that adds step 1) to arrive, and reaction 2.5 ~ 3h obtains polyurethane modified epoxy resin;
3) with step 2) polyurethane modified epoxy resin of gained is dissolved in acetone, adding particle diameter is the graphite of 7～8nm, add again propylene glycol monomethyl ether acetate, tbp, propylene glycol monomethyl ether, polydimethylsiloxane, methacryloxypropyl silane, dyestuff, after mixing, process 30 ~ 50min with ultrasonic oscillation again, obtain the nano-graphite electrically conductive ink.
2. the preparation method of a kind of nano-graphite electrically conductive ink according to claim 1, it is characterized in that: the mol ratio of the 2,4 toluene diisocyanate described in step 1) and polyoxyethylene glycol is 1.3 ~ 1.4:1.
3. the preparation method of a kind of nano conductive printing ink according to claim 1, is characterized in that: step 2) described in the mass ratio of epoxy resin, ethylene glycol ether acetate and isocyanate terminated base polyurethane prepolymer for use as be 9.5 ~ 10:5 ~ 6:1.
4. the preparation method of a kind of nano-graphite electrically conductive ink according to claim 1, it is characterized in that: the mass ratio of the polyurethane modified epoxy resin described in step 3), graphite, propylene glycol monomethyl ether acetate, tbp, propylene glycol monomethyl ether, polydimethylsiloxane, methacryloxypropyl silane, dyestuff is: 26 ~ 30:5 ~ 6:10 ~ 11:4 ~ 6:5 ~ 7:3 ~ 5:2 ~ 3:5 ~ 8.
5. the preparation method of the described a kind of nano-graphite electrically conductive ink of arbitrary claim of according to claim 1 to 4, it is characterized in that: described dyestuff is a kind of in following substances: C.I. directly deceives 166, C.I. directly deceive 19, C.I. directly deceive 168, C.I. acid yellow 23, C.I. Xylene Red 52, the C.I. acid blue 9.