CN103073939A - Water-base glue powder - Google Patents
Water-base glue powder Download PDFInfo
- Publication number
- CN103073939A CN103073939A CN201310059680XA CN201310059680A CN103073939A CN 103073939 A CN103073939 A CN 103073939A CN 201310059680X A CN201310059680X A CN 201310059680XA CN 201310059680 A CN201310059680 A CN 201310059680A CN 103073939 A CN103073939 A CN 103073939A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- base adhesive
- water base
- control temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-base glue powder. The water-base glue powder comprises the following raw materials in parts by weight: 7 to 9 parts of hydroxymethyl cellulose, 6 to 8 parts of lubricating adhesive, 9 to 11 parts of emulsion powder, 12 to 14 parts of superglue powder, 14 to 16 parts of amylocellulose and 17 to 19 parts of extraction powder, wherein the lubricating adhesive comprises the following raw materials in parts by weight: 3 to 5 parts of citric acid, 2 to 4 parts of hydrophobic granule, 5 to 7 parts of lubricating oil and 7 to 9 parts of caustic soda; and the extraction powder comprises the following raw materials in parts by weight: 4 to 6 parts of water glass, 3 to 5 parts of rubber powder and 1 to 3 parts of anhydrous sodium sulphate. The water-base glue powder is energy-saving, environment-friendly, non-toxic, harmless, odourless, convenient to use, simple in production process, easy to operate and construct and high in adhesion. The water-base glue powder can be stored for a long time without precipitating or deteriorating.
Description
Technical field
The invention belongs to the glue field of building field, specifically, relate to a kind of water base adhesive pigment.
Background technology
Employed glue is different from common glue in the middle of the construction industry, and its requirement has higher adhesive ability, and the time sufficiently long that keeps viscosity.The building glue that uses on the Vehicles Collected from Market has two kinds of modes of production, and a kind of is that manufacturer directly will put on market after the packing behind the liquid packaging of the chemical materials productions such as polyvinyl alcohol, acrylamide; Packing was put on market after another kind was processed into building glue by manufacturer with high molecular polymer rubber powders such as PVA, EVA, CMC.The packing material that these two kinds of modes of production need is large, energy-conservation not; Put carrying cost on market high, economical not; The product of producing uses inconvenience; The toxic substances such as formaldehyde, ammonia, sanitas are arranged, not environmental protection in the glue composition of its production; Product is in transportation, and cracky can cause the wasting of resources; The glue quality is low, the putty poor adhesive force of modulation, easily roll up skin, come off etc.; Use the cement-based material of glue modulation for base materials such as exterior walls, owing to cement based kapillary suction reason causes expansion, cracking, weathering, the problem such as pollute, go mouldy and cause peeling off during freeze-thaw cycle.At present a lot of manufacturers have all carried out improving and upgrading for the feed composition of building glue, but the gluewater in use for construction of prior art or solid glue, although its adhesive ability power differs, but all generally can cause certain pollution to environment, some Long contact time can cause damage to builder's health.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of both environmental protection, simultaneously sticking power strong water base adhesive pigment again.
Technical scheme of the present invention is as follows: a kind of water base adhesive pigment are made by the raw material of following portions by weight:
9～11 parts of 6～8 parts of latex powder of 7～9 parts of lubricated glue pastes of Walocel MT 20.000PV
14～16 parts of 12～14 parts of farinoses of powerful rubber powder are carried 17～19 parts in pulvis
Wherein said lubricated glue paste is made by the raw material of following portions by weight:
3～5 parts of citric acids are hated 7～9 parts in 5～7 parts of caustic soda of 2～4 parts of lubricating oil of granula
The wherein said pulvis of carrying is made by the raw material of following portions by weight:
1～3 part of 3～5 parts of Sodium sulfate anhydrous.min(99) of 4～6 parts of rubber powders of water glass.
A kind of preparation method of water base adhesive pigment makes as follows with following raw materials according and parts by weight proportioning:
(1), taking by weighing 3～5 parts of citric acids hates 7～9 parts in 5～7 parts of caustic soda of 2～4 parts of lubricating oil of granula to mix, add in the vessel and heat, the control temperature is 40～60 ℃, follows simultaneously and stirs until mixture melts stopped heating fully, both must lubricate glue paste;
(2), take by weighing 1～3 part of 3～5 parts of Sodium sulfate anhydrous.min(99) of 4～6 parts of rubber powders of water glass and mix, add in the vessel and heat, the control temperature is 60～80 ℃, follows simultaneously and stirs until mixture melts stopped heating fully, both must carry pulvis;
(3), taking by weighing 14～16 parts of 12～14 parts of farinoses of 9～11 parts of powerful rubber powders of 6～8 parts of latex powder of 7～9 parts of lubricated glue pastes of Walocel MT 20.000PV carries 17～19 parts in pulvis and mixes, add in the vessel and heat, the control temperature is 25～38 ℃, follow simultaneously and stir until mixture melts stopped heating fully, both got the water base adhesive pigment.
Adopt technique scheme; be nontoxic, harmless, odorless in the composition of the present invention, belong to Green Product, preparation technology is simple; not in equipment and the process engineering of needs complexity; preparation process is at needs high temperature, the environment of having saved Energy conservation, and product is easy to use; and hate granula to increase viscosity; improved the suspension degree of coating products, stayed for a long time and do not precipitate, never degenerated.
In order to save cost, simplify technique, in the described step (1), by thermometer control temperature.
In order to save cost, simplify technique, in the described step (2), by thermometer control temperature.
In order to save cost, simplify technique, be convenient to the terminal point of observing response, in the described step (3), by thermometer control temperature, whether react completely by the magnifying glass observation.
Described water base adhesive pigment directly cold water dilution dissolving use.Bring larger convenience for people's use, saved manpower and materials.
The assay of this product:
Detect foundation: GB18583-2008 " limits of harmful substances in the indoor decorating and refurnishing materials tackiness agent "
The detection of the limits of harmful substances of this product of table one
| Sequence number | Test item | Technical indicator | Detected result | Judge |
| 1 | Free formaldehyde (g/kg) | ≤1.0 | Do not detect (detection limit: 0.05g/kg) | Qualified |
| 2 | Benzene (g/kg) | ≤0.20 | Do not detect (detection limit: 0.02g/kg) | Qualified |
| 3 | Toluene+dimethylbenzene (g/kg) | ≤10 | Do not detect (detection limit: 0.04g/kg) | Qualified |
| 4 | Total volatile organism (g/L) | ≤350 | 200 | Qualified |
Table one detected result shows, this product is according to GB18583-2008 " limits of harmful substances in the indoor decorating and refurnishing materials tackiness agent " check, the whole conformance with standard requirements of institute's test item.
Beneficial effect: the present invention has energy-conserving and environment-protective, nontoxic, harmless, odorless, and is easy to use, and production technique is simple, simple to operate, and construction is light, bond degree is good, stays for a long time and does not precipitate, and never degenerates.
Embodiment
Embodiment 1
A kind of preparation method of water base adhesive pigment makes as follows with following raw materials according and parts by weight proportioning:
(1), take by weighing citric acid 0.4kg, hate granula 0.3kg, lubricating oil 0.6kg and caustic soda 0.8kg mix, and adds in the vessel and heat, the control temperature is 50 ℃, follows simultaneously and stirs until mixture melts stopped heating fully, both must lubricate glue paste;
(2), take by weighing water glass 0.5kg, rubber powder 0.4kg and Sodium sulfate anhydrous.min(99) 0.2kg mixes, add that the control temperature is 70 ℃ in the vessel, follow simultaneously and stir until mixture melts stopped heating fully, both must carry pulvis;
(3), take by weighing Walocel MT 20.000PV 0.8kg, lubricated glue paste 0.7kg, latex powder 1kg, powerful rubber powder 1.3kg, farinose 1.5kg and carry pulvis 1.8kg and mix, add in the vessel and heat, the control temperature is 30 ℃, follow simultaneously and stir until mixture melts stopped heating fully, both got the water base adhesive pigment.
Embodiment 2
A kind of preparation method of water base adhesive pigment makes as follows with following raw materials according and parts by weight proportioning:
(1), take by weighing citric acid 0.3kg, hate granula 0.2kg, lubricating oil 0.5kg and caustic soda 0.7kg mix, and adds in the vessel and heat, the control temperature is 40 ℃, follows simultaneously and stirs until mixture melts stopped heating fully, both must lubricate glue paste;
(2), take by weighing water glass 0.4kg, rubber powder 0.3kg and Sodium sulfate anhydrous.min(99) 0.1kg mixes, add in the vessel and heat, the control temperature is 60 ℃, follows simultaneously and stirs until mixture melts stopped heating fully, both must carry pulvis;
(3), take by weighing Walocel MT 20.000PV 0.7kg, lubricated glue paste 0.6kg, latex powder 0.9kg, powerful rubber powder 1.2kg, farinose 1.4kg and carry pulvis 1.7kg and mix, add in the vessel and heat, the control temperature is 25 ℃, follow simultaneously and stir until mixture melts stopped heating fully, both got the water base adhesive pigment.
Embodiment 3
A kind of preparation method of water base adhesive pigment makes as follows with following raw materials according and parts by weight proportioning:
(1), take by weighing citric acid 0.5kg, hate granula 0.4kg, lubricating oil 0.7kg and caustic soda 0.9kg mix, and adds in the vessel and heat, the control temperature is 60 ℃, follows simultaneously and stirs until mixture melts stopped heating fully, both must lubricate glue paste;
(2), take by weighing water glass 0.6kg, rubber powder 0.5kg and Sodium sulfate anhydrous.min(99) 0.3kg mixes, add in the vessel and heat, the control temperature is 80 ℃, follows simultaneously and stirs until mixture melts stopped heating fully, both must carry pulvis;
(3), take by weighing Walocel MT 20.000PV 0.9kg, lubricated glue paste 0.8kg, latex powder 1.1kg, powerful rubber powder 1.4kg, farinose 1.6kg and carry pulvis 1.9kg and mix, add in the vessel and heat, the control temperature is 38 ℃, follow simultaneously and stir until mixture melts stopped heating fully, both got the water base adhesive pigment.
Claims (6)
1. water base adhesive pigment is characterized in that being made by the raw material of following portions by weight:
9～11 parts of 6～8 parts of latex powder of 7～9 parts of lubricated glue pastes of Walocel MT 20.000PV
14～16 parts of 12～14 parts of farinoses of powerful rubber powder are carried 17～19 parts in pulvis
Wherein said lubricated glue paste is made by the raw material of following portions by weight:
3～5 parts of citric acids are hated 7～9 parts in 5～7 parts of caustic soda of 2～4 parts of lubricating oil of granula
The wherein said pulvis of carrying is made by the raw material of following portions by weight:
1～3 part of 3～5 parts of Sodium sulfate anhydrous.min(99) of 4～6 parts of rubber powders of water glass.
2. preparation method of water base adhesive pigment as claimed in claim 1 is characterized in that making as follows with following raw materials according and parts by weight proportioning:
(1), taking by weighing 3～5 parts of citric acids hates 7～9 parts in 5～7 parts of caustic soda of 2～4 parts of lubricating oil of granula to mix, add in the vessel and heat, the control temperature is 40～60 ℃, follows simultaneously and stirs until mixture melts fully, stopped heating both must lubricate glue paste;
(2), take by weighing 1～3 part of 3～5 parts of Sodium sulfate anhydrous.min(99) of 4～6 parts of rubber powders of water glass and mix, add in the vessel and heat, the control temperature is 60～80 ℃, follows simultaneously and stirs until mixture melts stopped heating fully, both must carry pulvis;
(3), take by weighing 7～9 parts of Walocel MT 20.000PVs, 6～8 parts of lubricated glue pastes, 9～11 parts of latex powder, 12～14 parts of powerful rubber powders, 14～16 parts of farinoses are carried 17～19 parts in pulvis and are mixed, add in the vessel and heat, the control temperature is 25～38 ℃, follows simultaneously and stirs until mixture melts rear stopped heating fully, has both got the water base adhesive pigment.
3. the preparation method of a kind of water base adhesive pigment according to claim 2 is characterized in that: in the described step (1), by thermometer control temperature.
4. the preparation method of a kind of water base adhesive pigment according to claim 2 is characterized in that: in the described step (2), by thermometer control temperature.
5. whether the preparation method of a kind of water base adhesive pigment according to claim 2 is characterized in that: in the described step (3), by thermometer control temperature, react completely by the magnifying glass observation.
6. water base adhesive pigment according to claim 1 is characterized in that: the directly cold water dilution dissolving use of described water base adhesive pigment.