CN103070545A - Combination type dining table and manufacture method thereof - Google Patents
Combination type dining table and manufacture method thereof Download PDFInfo
- Publication number
- CN103070545A CN103070545A CN2013100018284A CN201310001828A CN103070545A CN 103070545 A CN103070545 A CN 103070545A CN 2013100018284 A CN2013100018284 A CN 2013100018284A CN 201310001828 A CN201310001828 A CN 201310001828A CN 103070545 A CN103070545 A CN 103070545A
- Authority
- CN
- China
- Prior art keywords
- parts
- antioxidant
- baffle plate
- table leg
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the technical field of furniture and particularly relates to a combination type dining table. The combination type dining table is characterized in that the combination type dining table comprises baffles, table legs and a table top plate, the baffles consist of retaining strips and bonding strips, both the retaining strips and the bonding strips are cylindrical strips and mutually connected in parallel along the horizontal direction, the retaining strips and the bonding strips are integrally formed, the retaining strips are higher than the bonding strips, the lower bottom surfaces of the retaining strips and the bonding strips are in the same plane, and connecting holes are formed in the bonding strips; the table legs consist of table leg bodies, and fixing holes are formed in the table leg bodies; the cross section of the table top plate is rectangular, triangular or trapezoidal, and the thickness of the table top plate is not bigger than the height difference value of the bonding strips and the retaining strips; the baffles are spliced into a table top shape, the table legs are fixedly arranged below the baffles, the table top plate is arranged on the bonding strips, and a clearance is formed between the table top plate and the retaining strips after assembly. The invention further discloses a manufacture method. The combination type dining table and the manufacture method, disclosed by the invention, have the following main benefits of simple structure, easiness in assembly, easiness in disassembly, light weight, small size, portability, easiness in mass production and low cost.
Description
Technical field
The invention belongs to the furniture technical field, especially relate to a kind of can rapid-assembling and dismounting and the Combined dining table that is easy to produce in enormous quantities and manufacture method thereof.
Background technology
Almost each family has dining table, and restaurant, hotel, school etc. place also has a large amount of dining tables.Existing dining table major part is fixed, and its material can not recycling, therefore, make cumbersomely, spended time is longer, so cost is higher, and owing to fix, therefore be not easy to carry the occasion such as have a dinner party especially in the open air, owing to the dining table that does not have to be convenient for carrying, bother and make the visitor feel to want to work as especially; In addition, fixing dining table also is not suitable with existing shopping at network movement requirement.
Summary of the invention
In order to have solved the problems referred to above, for this reason, the present invention discloses a kind of Combined dining table, discloses further its manufacture method, and they are realized by the following technical solutions.
A kind of Combined dining table is characterized in that it includes polylith baffle plate 1, many table legs 2, a desktop 3; Described baffle plate is made of blend stop 11, applying bar 12, blend stop and applying bar all are that column and along continuous straight runs are bonded with each other abreast, blend stop and applying bar are integrally formed, the height of blend stop is greater than the height of applying bar, the bottom surface of blend stop and applying bar is positioned at same plane, has a plurality of connecting holes 13 that run through up and down on the applying bar; Described table leg is made of table leg body 21, has fixing hole 24 on the upper surface of table leg body; The diameter of connecting hole is not less than the diameter of fixing hole; Described desktop is that cross section is rectangle or triangle or trapezoidal, and the thickness of desktop is not more than the height difference of applying bar and blend stop; The polylith baffle plate pieces together required tabletop shape, and table leg is fixed on the baffle plate below, and desktop is shelved on the applying bar, and is after assembling is finished, slightly gapped between desktop and the blend stop.
Combined dining table described above is characterized in that described connecting hole 13 is made of the first connecting hole 131 that is interconnected, the second connecting hole 132, and above the first connecting hole is positioned at and aperture is greater than the diameter of the second connecting hole; And the diameter of the second connecting hole is not less than the diameter of fixing hole.
Combined dining table described above, the inboard that it is characterized in that described table leg body has not lateral direction penetrating to the groove 22 of table leg body lateral surface, groove is the front and back sides of lateral direction penetrating table leg body, and the outside of table leg body has consolidating of communicating with groove and puts hole 23.
Combined dining table described above, the degree of depth that it is characterized in that described groove be the table leg body width 1/4～1/2.
Combined dining table described above is characterized in that it also comprises a board putting things 4, and the side of board putting things has the thing of putting hole 41, and to put the thing hole be corresponding with the position of admittedly putting the hole and the diameter of putting the thing hole is not more than the diameter of admittedly putting the hole; The shape of cross section of board putting things is akin with the shape of cross section of desktop.
Combined dining table described above, the top view that it is characterized in that described baffle plate is rectangle or isosceles trapezoid; When being isosceles trapezoid, less drift angle is [42 degree, 45 degree] or [27 degree, 30 degree].
Combined dining table described above, the material that it is characterized in that described baffle plate are plastics or composite or timber or metal.
Combined dining table described above, the material that it is characterized in that described table leg are plastics or composite or timber or metal.
Combined dining table described above, the material that it is characterized in that described desktop are plastics or composite or glass or stainless steel or timber.
Combined dining table described above, the material that it is characterized in that described board putting things are plastics or composite or glass or stainless steel or timber.
Combined dining table described above is characterized in that described baffle plate and table leg all are to be made by the composite that comprises following component and parts by weight: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates.
Further, Combined dining table described above is characterized in that described baffle plate and table leg all are to be made by the composite that comprises following component and parts by weight: 90 parts of acrylic resins; 10 parts of nucleators; 1 part of antioxidant; 1 part of color master-batch; 0.08 part of lubricant; Increase 20 parts of flux; 1 part of fire retardant; 2 parts of polybutylene terephthalates.
Further, Combined dining table described above is characterized in that described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide.
Combined dining table described above is characterized in that described baffle plate and table leg all are to be made by the composite that comprises following component and parts by weight: 86-98 parts of wood chips; 10-20 parts in glue class adhesive; 0.1-0.3 part of pungent element; 0.1-0.2 part of anti-termite agent; 2-5 parts of rosin.
A kind of manufacture method of Combined dining table is characterized in that it includes the manufacturing step of the manufacturing step of baffle plate, table leg, the manufacturing step of desktop;
Described baffle plate forms by the following steps manufacturing:
The 1st step: the composite that will comprise following component and parts by weight mixes, and then puts into extruding machine baking hopper, and 80 degrees centigrade were dried by the fire temperature 4 hours: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide;
The 2nd step: open the extruding machine heating system, when the extruder head temperature rises to 150 degrees centigrade, the composite in the hopper added gradually plastify in the extruding machine and carry out extrusion molding by head simultaneously;
The 3rd step: the stretching of head extrudate is entered the outer warm water tank of head, and the temperature of warm water tank is 20 degrees centigrade to 28 degrees centigrade, and the length of warm water tank is not less than 30 meters, and draw speed is below 5 m/mins;
The 4th step: the extrudate of pulling out in the warm water tank is cut, then become connecting hole in applying bar upper punch swaging, having formed top view is rectangular plate washer; Die cut is carried out at the two ends that with top view are again rectangular plate washer, and making the less drift angle at two ends all be, [42 degree, 45 degree] or [27 degree, 30 degree] namely to have formed top view be the plate washer of isosceles trapezoid;
Described table leg forms by the following steps manufacturing: the composite that will comprise following component and parts by weight mixes, and then putting into temperature is 150 degrees centigrade of injection machines: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide; Carry out pressure injection, cooling, demoulding formation table leg;
Described desktop forms by the following steps manufacturing: choose the glass that needs thickness, be cut to tabletop shape and big or small getting final product that the polylith baffle plate pieces together.
A kind of manufacture method of Combined dining table is characterized in that it includes the manufacturing step of the manufacturing step of baffle plate, table leg, the manufacturing step of desktop; Described baffle plate forms by the following steps manufacturing: the composite that will comprise following component and parts by weight mixed and puts into the ultraviolet sterilization apparatus disinfection 2 hours, and then putting into temperature is 200 degrees centigrade of injection machines: 86-98 parts of wood chips; 10-20 parts in glue class adhesive; 0.1-0.3 part of pungent element; 0.1-0.2 part of anti-termite agent; 2-5 parts of rosin carry out pressure injection, cooling, the demoulding and form baffle plate; Described table leg forms by the following steps manufacturing: the composite that will comprise following component and parts by weight mixes, and then putting into temperature is 150 degrees centigrade of injection machines: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide; Carry out pressure injection, cooling, demoulding formation table leg; Described desktop forms by the following steps manufacturing: choose the glass that needs thickness, be cut to tabletop shape and big or small getting final product that the polylith baffle plate pieces together.
Among the present invention, baffle plate can adopt various materials, and is convenient to mass production, and is lightweight, scope of selecting material is wide, and volume of the present invention is small and exquisite in addition, is easy to carry very much, and especially outdoor sports etc. puts into automobile trunk with part of the present invention to get final product; So and because the present invention is lightweight, the little transportation that is fit to very much in the shopping at network of volume.
Desktop among the present invention can also adopt roll bending or the tabular sheet material of corrugation, is more convenient for like this carrying, volume is less, weight is lighter.
Among the present invention, the polylith baffle plate is pieced together required tabletop shape, table leg is fixed on the baffle plate below, and desktop is shelved on the applying bar, and is after assembling is finished, slightly gapped between desktop and the blend stop; Spread on the table the waterproof tablecloth after installing, just can not make moisture etc. be incorporated into the applying bar place of baffle plate, in addition, the first connecting hole is positioned at top and aperture greater than the design of the diameter of the second connecting hole, so that table leg and baffle plate be fixedly the time, fixture can be imbedded in the applying bar, like this, desktop is more smooth.
Among the present invention, table leg not only can be fixed under the baffle plate, fixes a table leg under the every baffle plate; Can also under every baffle plate, fix many table legs; This situation can be so that the support of Combined dining table be more firm; Certainly, table leg can also be fixed on the baffle plate two ends under, form adjacent baffle plate by the fixing situation of a table leg, this situation is more humane, Combined dining table is more attractive in appearance more practical.
The present invention has following main beneficial effect: simple in structure, easy assembling, quick detachable, lightweight, volume is little, portable, easy production in enormous quantities, cost are low.
Description of drawings
Fig. 1 is a kind of perspective view of the baffle plate of the invention process example 1.
Fig. 2 is a kind of perspective view of the table leg of the invention process example 1.
Fig. 3 is a kind of perspective view of the desktop of the invention process example 1.
Fig. 4 is a kind of perspective view of the board putting things of the invention process example 1.
Fig. 5 is the perspective exploded view under the invention process example 1 assembled state.
Fig. 6 is a kind of perspective view of the baffle plate of the invention process example 2.
Fig. 7 is the top view of Fig. 6.
Fig. 8 is a kind of perspective view of the table leg of the invention process example 2.
Fig. 9 is a kind of perspective view of the desktop of the invention process example 2.
Figure 10 be after the invention process example 2 assembling is finished perspective view.
Figure 11 is a kind of perspective view of the baffle plate of the invention process example 3.
Figure 12 is a kind of perspective view of the table leg of the invention process example 3.
Figure 13 be after the invention process example 3 assembling is finished perspective view.
The specific embodiment
The present invention is described in further detail below in conjunction with accompanying drawing, now Reference numeral unified explanation once: 1---baffle plate, 11---blend stop, 12---applying bar, 13---connecting hole, 131---first connecting hole, 132---the second connecting hole; Admittedly 2---table leg, 21---table leg body, 22---groove, 23---is put hole, 24---fixing holes; 3---desktop; 4---board putting things, 41---are put the thing hole.
Wherein, embodiment 1 to embodiment 3 is embodiments of Combined dining table of the present invention, and embodiment 4 is embodiments of the manufacture method of Combined dining table of the present invention to embodiment 5.
Ask for an interview Fig. 1 to Fig. 5, a kind of Combined dining table is characterized in that it includes four baffle plates 1, four table legs 2, a desktop 3, a board putting things 4; Described every baffle plate is made of blend stop 11, applying bar 12, blend stop and applying bar all are that column and along continuous straight runs are bonded with each other abreast, blend stop and applying bar are integrally formed, the height of blend stop is greater than the height of applying bar, the bottom surface of blend stop and applying bar is positioned at same plane, has a plurality of connecting holes 13 that run through up and down on the applying bar; Described table leg is made of table leg body 21, has fixing hole 24 on the upper surface of table leg body, the inboard of table leg body has not lateral direction penetrating to the groove 22 of table leg body lateral surface, groove is the front and back sides of lateral direction penetrating table leg body, the outside of table leg body has consolidating of communicating with groove and puts hole 23, the degree of depth of groove be the table leg body width 1/4～1/2; The side of board putting things has the thing of putting hole 41, and to put the thing hole be corresponding with the position of admittedly putting the hole and the diameter of putting the thing hole is not more than the diameter of admittedly putting the hole; The shape of cross section of board putting things is akin with the shape of cross section of desktop; The diameter of connecting hole is not less than the diameter of fixing hole; Described desktop is that cross section is rectangle, and the thickness of desktop is not more than the height difference of applying bar and blend stop; The polylith baffle plate pieces together required tabletop shape, and table leg is fixed on the baffle plate below, and desktop is shelved on the applying bar, and is after assembling is finished, slightly gapped between desktop and the blend stop; The material of described baffle plate is plastics; The material of table leg is plastics; The material of desktop is glass; The material of board putting things is plastics.
Ask for an interview Fig. 6 to Figure 10, a kind of Combined dining table is characterized in that it includes three baffle plates 1, three table legs 2, a desktop 3; Described baffle plate is made of blend stop 11, applying bar 12, blend stop and applying bar all are that column and along continuous straight runs are bonded with each other abreast, blend stop and applying bar are integrally formed, the height of blend stop is greater than the height of applying bar, the bottom surface of blend stop and applying bar is positioned at same plane, have a plurality of connecting holes 13 that run through up and down on the applying bar, connecting hole 13 is made of the first connecting hole 131 that is interconnected, the second connecting hole 132, and above the first connecting hole is positioned at and aperture is greater than the diameter of the second connecting hole; And the diameter of the second connecting hole is not less than the diameter of fixing hole, and the top view of baffle plate is isosceles trapezoid, and less drift angle is [42 degree, 45 degree]; Described table leg is made of table leg body 21, has fixing hole 24 on the upper surface of table leg body; The diameter of connecting hole is not less than the diameter of fixing hole; Described desktop is that cross section is rectangle or triangle or trapezoidal, and the thickness of desktop is not more than the height difference of applying bar and blend stop; The polylith baffle plate pieces together required tabletop shape, and table leg is fixed on the baffle plate below, and desktop is shelved on the applying bar, and is after assembling is finished, slightly gapped between desktop and the blend stop; The material of described baffle plate is plastics; The material of table leg is plastics; The material of desktop is glass.
Ask for an interview Figure 11 to Figure 13, and in conjunction with Fig. 9, a kind of Combined dining table, substantially with embodiment 2, difference is that the connecting hole on the baffle plate is positioned at the place, nearly two ends of baffle plate; Fixing hole on the upper surface of table leg body more disperses, to be connected with baffle plate better; The material of described baffle plate is plastics; The material of table leg is plastics; The material of desktop is glass.
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment is characterized in that it includes polylith baffle plate 1, many table legs 2, a desktop 3; Described baffle plate is made of blend stop 11, applying bar 12, blend stop and applying bar all are that column and along continuous straight runs are bonded with each other abreast, blend stop and applying bar are integrally formed, the height of blend stop is greater than the height of applying bar, the bottom surface of blend stop and applying bar is positioned at same plane, has a plurality of connecting holes 13 that run through up and down on the applying bar; Described table leg is made of table leg body 21, has fixing hole 24 on the upper surface of table leg body; The diameter of connecting hole is not less than the diameter of fixing hole; Described desktop is that cross section is rectangle or triangle or trapezoidal, and the thickness of desktop is not more than the height difference of applying bar and blend stop; The polylith baffle plate pieces together required tabletop shape, and table leg is fixed on the baffle plate below, and desktop is shelved on the applying bar, and is after assembling is finished, slightly gapped between desktop and the blend stop.
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment is characterized in that described connecting hole 13 all can be made of the first connecting hole 131 that is interconnected, the second connecting hole 132, and above the first connecting hole is positioned at and aperture is greater than the diameter of the second connecting hole; And the diameter of the second connecting hole is not less than the diameter of fixing hole.
Certainly, Combined dining table described in above-mentioned arbitrary embodiment, the inboard that it is characterized in that described table leg body has not lateral direction penetrating to the groove 22 of table leg body lateral surface, groove is the front and back sides of lateral direction penetrating table leg body, and the outside of table leg body has consolidating of communicating with groove and puts hole 23.
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment, the degree of depth that it is characterized in that described groove be the table leg body width 1/4～1/2.
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment is characterized in that it also comprises a board putting things 4, and the side of board putting things has the thing of putting hole 41, and to put the thing hole be corresponding with the position of admittedly putting the hole and the diameter of putting the thing hole is not more than the diameter of admittedly putting the hole; The shape of cross section of board putting things is akin with the shape of cross section of desktop.
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment, the top view that it is characterized in that described baffle plate is rectangle or isosceles trapezoid; When being isosceles trapezoid, less drift angle is [42 degree, 45 degree] or [27 degree, 30 degree].
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment, the material that it is characterized in that described baffle plate are moldable or composite or timber or metal.
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment is characterized in that the material of described table leg can be plastics or composite or timber or metal.
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment is characterized in that the material of described desktop can be plastics or composite or glass or stainless steel or timber.
Combined dining table described above is characterized in that the material of described board putting things can be plastics or composite or glass or stainless steel or timber.
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment is characterized in that described baffle plate and table leg can be to be made by the composite that comprises following component and parts by weight: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates.
Further, the Combined dining table described in above-mentioned arbitrary embodiment is characterized in that described baffle plate and table leg all are to be made by the composite that comprises following component and parts by weight: 90 parts of acrylic resins; 10 parts of nucleators; 1 part of antioxidant; 1 part of color master-batch; 0.08 part of lubricant; Increase 20 parts of flux; 1 part of fire retardant; 2 parts of polybutylene terephthalates.
Further, the Combined dining table described in above-mentioned arbitrary embodiment is characterized in that described nucleator all can be calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide.
Certainly, the Combined dining table described in above-mentioned arbitrary embodiment is characterized in that described baffle plate and table leg can be to be made by the composite that comprises following component and parts by weight: 86-98 parts of wood chips; 10-20 parts in glue class adhesive; 0.1-0.3 part of pungent element; 0.1-0.2 part of anti-termite agent; 2-5 parts of rosin.
A kind of manufacture method of Combined dining table is characterized in that it includes the manufacturing step of the manufacturing step of baffle plate, table leg, the manufacturing step of desktop;
Described baffle plate forms by the following steps manufacturing:
The 1st step: the composite that will comprise following component and parts by weight mixes, and then puts into extruding machine baking hopper, and 80 degrees centigrade were dried by the fire temperature 4 hours: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide;
The 2nd step: open the extruding machine heating system, when the extruder head temperature rises to 150 degrees centigrade, the composite in the hopper added gradually plastify in the extruding machine and carry out extrusion molding by head simultaneously;
The 3rd step: the stretching of head extrudate is entered the outer warm water tank of head, and the temperature of warm water tank is 20 degrees centigrade to 28 degrees centigrade, and the length of warm water tank is not less than 30 meters, and draw speed is below 5 m/mins;
The 4th step: the extrudate of pulling out in the warm water tank is cut, then become connecting hole in applying bar upper punch swaging, having formed top view is rectangular plate washer; Die cut is carried out at the two ends that with top view are again rectangular plate washer, and making the less drift angle at two ends all be, [42 degree, 45 degree] or [27 degree, 30 degree] namely to have formed top view be the plate washer of isosceles trapezoid;
Described table leg forms by the following steps manufacturing: the composite that will comprise following component and parts by weight mixes, and then putting into temperature is 150 degrees centigrade of injection machines: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide; Carry out pressure injection, cooling, demoulding formation table leg;
Described desktop forms by the following steps manufacturing: choose the glass that needs thickness, be cut to tabletop shape and big or small getting final product that the polylith baffle plate pieces together.
Embodiment 5
A kind of manufacture method of Combined dining table is characterized in that it includes the manufacturing step of the manufacturing step of baffle plate, table leg, the manufacturing step of desktop; Described baffle plate forms by the following steps manufacturing: the composite that will comprise following component and parts by weight mixed and puts into the ultraviolet sterilization apparatus disinfection 2 hours, and then putting into temperature is 200 degrees centigrade of injection machines: 86-98 parts of wood chips; 10-20 parts in glue class adhesive; 0.1-0.3 part of pungent element; 0.1-0.2 part of anti-termite agent; 2-5 parts of rosin carry out pressure injection, cooling, the demoulding and form baffle plate; Described table leg forms by the following steps manufacturing: the composite that will comprise following component and parts by weight mixes, and then putting into temperature is 150 degrees centigrade of injection machines: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide; Carry out pressure injection, cooling, demoulding formation table leg; Described desktop forms by the following steps manufacturing: choose the glass that needs thickness, be cut to tabletop shape and big or small getting final product that the polylith baffle plate pieces together.
Among the present invention, baffle plate can adopt various materials, and is convenient to mass production, and is lightweight, scope of selecting material is wide, and volume of the present invention is small and exquisite in addition, is easy to carry very much, and especially outdoor sports etc. puts into automobile trunk with part of the present invention to get final product; So and because the present invention is lightweight, the little transportation that is fit to very much in the shopping at network of volume.
Desktop among the present invention can also adopt roll bending or the tabular sheet material of corrugation, is more convenient for like this carrying, volume is less, weight is lighter.
Among the present invention, the polylith baffle plate is pieced together required tabletop shape, table leg is fixed on the baffle plate below, and desktop is shelved on the applying bar, and is after assembling is finished, slightly gapped between desktop and the blend stop; Spread on the table the waterproof tablecloth after installing, just can not make moisture etc. be incorporated into the applying bar place of baffle plate, in addition, the first connecting hole is positioned at top and aperture greater than the design of the diameter of the second connecting hole, so that table leg and baffle plate be fixedly the time, fixture can be imbedded in the applying bar, like this, desktop is more smooth.
Among the present invention, table leg not only can be fixed under the baffle plate, fixes a table leg under the every baffle plate; Can also under every baffle plate, fix many table legs; This situation can be so that the support of Combined dining table be more firm; Certainly, table leg can also be fixed on the baffle plate two ends under, form adjacent baffle plate by the fixing situation of a table leg, this situation is more humane, Combined dining table is more attractive in appearance more practical.
Related various composition raw material among the present invention can have been bought in market.
The present invention has following main beneficial effect: simple in structure, easy assembling, quick detachable, lightweight, volume is little, portable, easy production in enormous quantities, cost are low.
The present invention is not limited to above-mentioned preferred forms, should be appreciated that design of the present invention can be by other various forms enforcement utilizations, and they drop in protection scope of the present invention equally.
Claims (10)
1. a Combined dining table is characterized in that it includes polylith baffle plate, many table legs, a desktop; Described baffle plate is made of blend stop, applying bar, blend stop and applying bar all are that column and along continuous straight runs are bonded with each other abreast, blend stop and applying bar are integrally formed, the height of blend stop is greater than the height of applying bar, the bottom surface of blend stop and applying bar is positioned at same plane, has a plurality of connecting holes (13) that run through up and down on the applying bar; Described table leg is made of the table leg body, has fixing hole on the upper surface of table leg body; The diameter of connecting hole is not less than the diameter of fixing hole; Described desktop is that cross section is rectangle or triangle or trapezoidal, and the thickness of desktop is not more than the height difference of applying bar and blend stop; The polylith baffle plate pieces together required tabletop shape, and table leg is fixed on the baffle plate below, and desktop is shelved on the applying bar, and is after assembling is finished, gapped between desktop and the blend stop.
2. Combined dining table according to claim 1 is characterized in that described connecting hole (13) is made of the first connecting hole that is interconnected, the second connecting hole, and above the first connecting hole is positioned at and aperture is greater than the diameter of the second connecting hole; And the diameter of the second connecting hole is not less than the diameter of fixing hole.
3. according to claim 1 or any one Combined dining table claimed in claim 2, the inboard that it is characterized in that described table leg body has not lateral direction penetrating to the groove of table leg body lateral surface, groove is the front and back sides of lateral direction penetrating table leg body, and the outside of table leg body has consolidating of communicating with groove and puts the hole; The degree of depth of described groove be the table leg body width 1/4～1/2.
4. according to claim 1 or any one Combined dining table claimed in claim 2, it is characterized in that it also comprises a board putting things, the side of board putting things has the thing of putting hole, and to put the thing hole be corresponding with the position of admittedly putting the hole and the diameter of putting the thing hole is not more than the diameter of admittedly putting the hole; The shape of cross section of board putting things is akin with the shape of cross section of desktop.
5. according to claim 1 or any one Combined dining table claimed in claim 2, the top view that it is characterized in that described baffle plate is rectangle or isosceles trapezoid; When being isosceles trapezoid, less drift angle is [42 degree, 45 degree] or [27 degree, 30 degree].
6. according to claim 1 or any one Combined dining table claimed in claim 2, it is characterized in that described baffle plate and table leg all are to be made by the composite that comprises following component and parts by weight: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide.
7. according to claim 1 or any one Combined dining table claimed in claim 2, it is characterized in that described baffle plate and table leg all are to be made by the composite that comprises following component and parts by weight: 90 parts of acrylic resins; 10 parts of nucleators; 1 part of antioxidant; 1 part of color master-batch; 0.08 part of lubricant; Increase 20 parts of flux; 1 part of fire retardant; 2 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide.
8. according to claim 1 or any one Combined dining table claimed in claim 2, it is characterized in that described baffle plate and table leg all are to be made by the composite that comprises following component and parts by weight: 86-98 parts of wood chips; 10-20 parts in glue class adhesive; 0.1-0.3 part of pungent element; 0.1-0.2 part of anti-termite agent; 2-5 parts of rosin.
9. the manufacture method of a Combined dining table is characterized in that it includes the manufacturing step of the manufacturing step of baffle plate, table leg, the manufacturing step of desktop;
Described baffle plate forms by the following steps manufacturing:
The 1st step: the composite that will comprise following component and parts by weight mixes, and then puts into extruding machine baking hopper, and 80 degrees centigrade were dried by the fire temperature 4 hours: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide;
The 2nd step: open the extruding machine heating system, when the extruder head temperature rises to 150 degrees centigrade, the composite in the hopper added gradually plastify in the extruding machine and carry out extrusion molding by head simultaneously;
The 3rd step: the stretching of head extrudate is entered the outer warm water tank of head, and the temperature of warm water tank is 20 degrees centigrade to 28 degrees centigrade, and the length of warm water tank is not less than 30 meters, and draw speed is below 5 m/mins;
The 4th step: the extrudate of pulling out in the warm water tank is cut, then become connecting hole in applying bar upper punch swaging, having formed top view is rectangular plate washer; Die cut is carried out at the two ends that with top view are again rectangular plate washer, and making the less drift angle at two ends all be, [42 degree, 45 degree] or [27 degree, 30 degree] namely to have formed top view be the plate washer of isosceles trapezoid;
Described table leg forms by the following steps manufacturing: the composite that will comprise following component and parts by weight mixes, and then putting into temperature is 150 degrees centigrade of injection machines: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide; Carry out pressure injection, cooling, demoulding formation table leg;
Described desktop forms by the following steps manufacturing: choose the glass that needs thickness, be cut to tabletop shape and big or small getting final product that the polylith baffle plate pieces together.
10. the manufacture method of a Combined dining table is characterized in that it includes the manufacturing step of the manufacturing step of baffle plate, table leg, the manufacturing step of desktop; Described baffle plate forms by the following steps manufacturing: the composite that will comprise following component and parts by weight mixed and puts into the ultraviolet sterilization apparatus disinfection 2 hours, and then putting into temperature is 200 degrees centigrade of injection machines: 86-98 parts of wood chips; 10-20 parts in glue class adhesive; 0.1-0.3 part of pungent element; 0.1-0.2 part of anti-termite agent; 2-5 parts of rosin carry out pressure injection, cooling, the demoulding and form baffle plate; Described table leg forms by the following steps manufacturing: the composite that will comprise following component and parts by weight mixes, and then putting into temperature is 150 degrees centigrade of injection machines: 80-95 parts of acrylic resins; 0.1-15 parts of nucleators; 0.1-5 parts of antioxidants; 0.8-1.8 parts of color master-batch; 0.05-2 parts of lubricants; Increase 10-25 parts of flux; 0.1-1.2 parts of fire retardants; 0.1-5 parts of polybutylene terephthalates; Described nucleator is calcium carbonate or talcum powder; Described antioxidant is antioxidant 1010 or antioxidant 300 or antioxidant 168; Described color master-batch is PE Masterbatch or PP Masterbatch; Described lubricant is lubricant ESS or lubricant MB50; The described flux that increases is polyethylene or ethylene-acrylic acid copolymer; Described fire retardant is aluminium hydroxide or magnesium hydroxide or Firebrake ZB or antimony oxide; Carry out pressure injection, cooling, demoulding formation table leg; Described desktop forms by the following steps manufacturing: choose the glass that needs thickness, be cut to tabletop shape and big or small getting final product that the polylith baffle plate pieces together.