CN103059637A - 聚醋酸乙烯乳液涂料的生产方法 - Google Patents
聚醋酸乙烯乳液涂料的生产方法 Download PDFInfo
- Publication number
- CN103059637A CN103059637A CN2012105788040A CN201210578804A CN103059637A CN 103059637 A CN103059637 A CN 103059637A CN 2012105788040 A CN2012105788040 A CN 2012105788040A CN 201210578804 A CN201210578804 A CN 201210578804A CN 103059637 A CN103059637 A CN 103059637A
- Authority
- CN
- China
- Prior art keywords
- acetate emulsion
- polyvinyl acetate
- coating
- production method
- emulsion coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚醋酸乙烯乳液涂料的生产方法，其步骤如下：把去离子水，20%六偏磷酸钠酸钠水溶液、丙二醇加入玻璃容器中搅拌，缓慢加入钛白粉和滑石粉，快速搅拌分散均匀，再慢慢加入磷酸三丁酯，继续快速搅拌15分钟后，慢速加入醋酸乙烯酯乳液，直到搅拌均匀为止，得到白色涂料。本发明的工艺方法生产出的涂料具有较好的颜色和遮盖力，较低成本并有耐洗刷性，易使用、及好的颜料结合性。本聚醋酸乙烯乳液涂料属于内用无光乳胶漆，用于中高档居室涂料装饰。
Description
技术领域
本发明涉及一种聚醋酸乙烯乳液涂料的生产方法。
背景技术
建筑涂料包括水性建筑涂料和溶剂型建筑涂料，溶剂型建筑涂料因其固化过程释放有毒溶剂，不符合环保要求而在建筑涂料中受到限制，但由于溶剂型涂料的高分子成膜物耐老化性强、附着力好、涂层光洁、耐沾污、耐磨性、耐酸碱、耐水性等优于一般水性涂料，在高层建筑的外墙装饰中仍在使用。从长远看，会被水性氟碳、硅丙等高性能涂料取代。
发明内容
本发明的目的是提供一种聚醋酸乙烯乳液涂料。
本发明的技术方案是这样实现的：聚醋酸乙烯乳液涂料的生产方法，其特征在于，其步骤如下：把去离子水，20%六偏磷酸钠酸钠水溶液、丙二醇加入玻璃容器中搅拌，缓慢加入钛白粉和滑石粉，快速搅拌分散均匀，再慢慢加入磷酸三丁酯，继续快速搅拌15分钟后，慢速加入醋酸乙烯酯乳液，直到搅拌均匀为止，得到白色涂料。进一步地，在白色涂料中加入彩色颜料浆，可得彩色涂料。进一步地，加入钛白粉和滑石粉同时加入少量碳酸钙。
本发明的有益效果为：本发明的工艺方法生产出的涂料具有较好的颜色和遮盖力，较低成本并有耐洗刷性，易使用、及好的颜料结合性。本聚醋酸乙烯乳液涂料属于内用无光乳胶漆，用于中高档居室涂料装饰。
具体实施方式
聚醋酸乙烯乳液涂料的生产方法，其特征在于，其步骤如下：把去离子水，20%六偏磷酸钠酸钠水溶液、丙二醇加入玻璃容器中搅拌，缓慢加入钛白粉和滑石粉，快速搅拌分散均匀，再慢慢加入磷酸三丁酯，继续快速搅拌15分钟后，慢速加入醋酸乙烯酯乳液，直到搅拌均匀为止，得到白色涂料。进一步地，在白色涂料中加入彩色颜料浆，可得彩色涂料。进一步地，加入钛白粉和滑石粉同时加入少量碳酸钙。本发明的工艺方法生产出的涂料具有较好的颜色和遮盖力，较低成本并有耐洗刷性，易使用、及好的颜料结合性。本聚醋酸乙烯乳液涂料属于内用无光乳胶漆，用于中高档居室涂料装饰。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (3)
1. 聚醋酸乙烯乳液涂料的生产方法，其特征在于，其步骤如下：
把去离子水，20%六偏磷酸钠酸钠水溶液、丙二醇加入玻璃容器中搅拌，缓慢加入钛白粉和滑石粉，快速搅拌分散均匀，再慢慢加入磷酸三丁酯，继续快速搅拌15分钟后，慢速加入醋酸乙烯酯乳液，直到搅拌均匀为止，得到白色涂料。
2.根据权利要求1所述的聚醋酸乙烯乳液涂料的生产方法，其特征在于，在白色涂料中加入彩色颜料浆，可得彩色涂料。
3.根据权利要求1所述的聚醋酸乙烯乳液涂料的生产方法，其特征在于，加入钛白粉和滑石粉同时加入少量碳酸钙。