CN103059373A - 一种用于制作工艺品的材料及其制备方法 - Google Patents
一种用于制作工艺品的材料及其制备方法 Download PDFInfo
- Publication number
- CN103059373A CN103059373A CN2012105220935A CN201210522093A CN103059373A CN 103059373 A CN103059373 A CN 103059373A CN 2012105220935 A CN2012105220935 A CN 2012105220935A CN 201210522093 A CN201210522093 A CN 201210522093A CN 103059373 A CN103059373 A CN 103059373A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyethylene
- calcium carbonate
- paraffin
- density polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种用于制作工艺品的材料，它包括如下重量份数的组分：石蜡10-15份，碳酸钙20-35份，聚乙烯20-50份，颜料粉0-15份，松香0-2份；所述聚乙烯为高密度聚乙烯、低密度聚乙烯或线性低密度聚乙烯。如上所述的用于制作工艺品的材料的制备方法，是先将10-15份石蜡加热至50-65℃熔解，然后加入20-50份聚乙烯混合，升温至110-220℃熔解，再加入20-35份碳酸钙混合，最后于200-220℃下加入0-15份颜料粉和0-2份松香，熔解，搅拌均匀即得成品。本发明以石蜡，碳酸钙和聚乙烯为主要原料，成品具有硬度高、韧性好、抗击强度高、轻便、成本低等优点，其制备工艺简单，热塑温度低。
Description
技术领域
本发明属于制作工艺品材料领域，尤其涉及一种硬度高、韧性好、抗击强度高且轻便的用于制作工艺品的材料。
背景技术
目前工艺品的制作原料分为三类：一是陶土、面团、石膏。这类原料在制作工艺品时虽然具有塑性好、易制作的特点，但是该类原料制出的工艺品强度差、易变形，易破损，不耐水；二是陶瓷、玻璃、金属。这类原料制作工艺品时要求热塑温度高，制作起来不方便；三是木料、石料等，这类材料只能在设定好后进行减除，若加工出现破损无法做增加。现关于工艺品制作材料的公开文献还较少，我们查到如下材料：申请号：200310111739.1，发明名称：工艺品用环保石膏材料的配方及工艺品制作方法，摘要：本发明涉及制作工艺品材料及制作方法；采用如下重量百分比配方：废弃石膏：55－65％；泥土：25－35％；水泥粉：8－12％；将上述配比的废弃石膏及泥土放入搅拌机中搅拌机粉碎至20目以上，得粉料；粉料中加入糯米胶搅拌均匀，使其成膏状；将膏状物灌入模具中烘干；将成型物由模具取出，表面处理得成品。用本发明方法可以节约大量的石膏，降低生产成本，同时用这种配方及方法制出的工艺品光滑、硬度高，特别适合制作灯饰及各类工艺品。目前尚未查到硬度高、韧性好、抗击强度高、轻便、成本低的用于制作工艺品的材料。
发明内容
本发明的目的在于解决上述技术问题，提供一种用于制作工艺品的材料及其制备方法，该材料以石蜡，碳酸钙和聚乙烯为主要原料，成品具有硬度高、韧性好、抗击强度高、轻便、成本低等优点，其制备工艺简单，热塑温度低。
为实现上述目的，本发明提供以下技术方案：
一种用于制作工艺品的材料，它包括如下重量份数的组分：石蜡10-15份，碳酸钙20-35份，聚乙烯20-50份，颜料粉0-15份，松香0-2份。
以上所述聚乙烯为高密度聚乙烯、低密度聚乙烯或线性低密度聚乙烯。
如上所述的用于制作工艺品的材料的制备方法，是先将10-15份石蜡加热至50-65℃熔解，然后加入20-50份聚乙烯混合，升温至110-220℃熔解，再恒温加入20-35份碳酸钙混合，最后于200-220℃下加入0-15份颜料粉和0-2份松香，熔解，搅拌均匀即得成品。
本发明中各个组分的功能如下：
石蜡，又称晶形蜡，通常是白色、无色无味的蜡状固体，在47℃-64℃熔化，密度约 0.9g/cm3。石蜡加入本产品中可提高产品的抗老化性和增加柔韧性。
碳酸钙，密度2.93g/cm3，莫氏硬度3；当压力为10.4MPa，熔点为1339℃，为本产品的填料，用于提高本产品尺寸的稳定性、硬度和刚性，改善产品的加工性能，提高产品的耐热性，同时可以降低产品成本。
高密度聚乙烯，简称为HDPE。HDPE是一种结晶度高、非极性的热塑性树脂。原态HDPE的外表呈乳白色，在微薄截面呈一定程度的半透明状。PE具有优良的耐大多数生活和工业用化学品的特性。具有极好的抗冲击性，在常温甚至在-40F低温度下均如此。
低密度聚乙烯和线性低密度聚乙烯，为无毒、无味、无臭的乳白色颗粒，具有较高的软化温度和熔融温度，有强度大、韧性好、刚性大、耐热、耐寒性好等优点，还具有良好的耐环境应力开裂性，耐冲击强度、耐撕裂强度等性能，并可耐酸、碱、有机溶剂等。
颜料粉，用于增加产品的色彩美观程度。包括有机矿物颜料粉、植物颜料粉或无机颜料粉等。
松香为微黄至黄红色的透明固体，软化点70～90℃，用于提高产品的粘接强度。本发明松香是从市场上直接购买，其加入方法是先将松香先粉碎，再加入上述的混合物中。
与现有技术相比，本发明的有益效果为：
1.本发明针对工艺品如雕塑用料而研制的，是一种具有橡皮泥的特性和塑料的特点，硬度似木头，韧度似藤蔓，质地似胶泥，是一种热可塑型冷可雕刻的材料，30-50℃时像胶泥一样柔软，能搓能捏，能塑能和，冷却时像木头，能雕能铲，是一种原创作品使用的最好材料，大大减轻创作时的难度，还可以得到意想不到的效果。
2.本发明还可以粘附在木料、石料、陶土等材料上，因此可用于根雕、木雕和石雕的修补改造，在颜料粉的颜色调配下，使得废木根等废料得到再利用。
3.本发明通过合适的配比加入石蜡、碳酸钙和聚乙烯等组分，使得产品的成本低，硬度、韧度和抗击强度高，材质轻便、无毒，不易损坏，损坏修补方便快捷，可作为各种大小型雕塑的用料，容易操作，省工省事，无边角废料，能长久存放，耐水耐高温，耐酸碱，不开裂，耐老化。
具体实施方式
下面结合实施例对本发明作进一步详细的描述，但本发明的实施方式并不局限于实施例表示的范围。
一种用于制作工艺品的材料，它包括如下重量份数的组分：石蜡10-15份，碳酸钙20-35份，聚乙烯20-50份，颜料粉0-15份，松香0-2份。作为优选，以上所述聚乙烯为高密度聚乙烯、低密度聚乙烯或线性低密度聚乙烯。实施例如表1~表3所示。
表1
实施例1和6的制备方法，先将石蜡加热至50℃熔解，然后加入聚乙烯混合，升温至110℃熔解，再加入碳酸钙混合，熔解，搅拌均匀即得成品。
实施例2的制备方法，先将石蜡加热至60℃熔解，然后加入聚乙烯混合，升温至150℃熔解，再恒温加入碳酸钙混合，最后于200℃下加入颜料粉，熔解，搅拌均匀即得成品。
实施例3~5的制备方法，先将石蜡加热至65℃熔解，然后加入聚乙烯混合，升温至220℃熔解，再恒温加入碳酸钙混合，最后于220℃下加入颜料粉和粉碎后的松香，熔解，搅拌均匀即得成品。
表2
实施例7和12的制备方法，先将石蜡加热至50℃熔解，然后加入聚乙烯混合，升温至110℃熔解，再加入碳酸钙混合，熔解，搅拌均匀即得成品。
实施例8的制备方法，先将石蜡加热至60℃熔解，然后加入聚乙烯混合，升温至150℃熔解，再恒温加入碳酸钙混合，最后于200℃下加入颜料粉，熔解，搅拌均匀即得成品。
实施例9~11的制备方法，先将石蜡加热至65℃熔解，然后加入聚乙烯混合，升温至220℃熔解，再恒温加入碳酸钙混合，最后于220℃下加入颜料粉和粉碎后的松香，熔解，搅拌 均匀即得成品。
表3
实施例13和18的制备方法，先将石蜡加热至50℃熔解，然后加入聚乙烯混合，升温至110℃熔解，再加入碳酸钙混合，熔解，搅拌均匀即得成品。
实施例14的制备方法，先将石蜡加热至60℃熔解，然后加入聚乙烯混合，升温至150℃熔解，再恒温加入碳酸钙混合，最后于200℃下加入颜料粉，熔解，搅拌均匀即得成品。
实施例15~17的制备方法，先将石蜡加热至65℃熔解，然后加入聚乙烯混合，升温至220℃熔解，再恒温加入碳酸钙混合，最后于220℃下加入颜料粉和粉碎后的松香，熔解，搅拌均匀即得成品。
应用实施例
本发明的应用方式有三种：
一、是将产品冷却，即可进行雕刻；如同木料、石料的雕刻方法。
二、是将产品加热至30-50℃，产品软化如胶泥，即可对产品进行捏合塑形。
三、是将产品加热至30-50℃，产品软化如胶泥，即可对损坏的雕塑、或雕塑废料进行修补粘结。
Claims (3)
1.一种用于制作工艺品的材料，其特征在于，它包括如下重量份数的组分：石蜡10-15份，碳酸钙20-35份，聚乙烯20-50份，颜料粉0-15份，松香0-2份。
2.根据权利要求1所述的用于制作工艺品的材料，其特征在于：所述聚乙烯为高密度聚乙烯、低密度聚乙烯或线性低密度聚乙烯。
3.一种如权利要求1~2中任一项所述的用于制作工艺品的材料的制备方法，其特征在于：先将10-15份石蜡加热至50-65℃熔解，然后加入20-50份聚乙烯混合，升温至110-220℃熔解，再恒温加入20-35份碳酸钙混合，最后于200-220℃下加入0-15份颜料粉和0-2份松香，熔解，搅拌均匀即得成品。